CN102020823A - 一种尼龙包胶专用粒料及其生产方法 - Google Patents

一种尼龙包胶专用粒料及其生产方法 Download PDF

Info

Publication number
CN102020823A
CN102020823A CN2009101825994A CN200910182599A CN102020823A CN 102020823 A CN102020823 A CN 102020823A CN 2009101825994 A CN2009101825994 A CN 2009101825994A CN 200910182599 A CN200910182599 A CN 200910182599A CN 102020823 A CN102020823 A CN 102020823A
Authority
CN
China
Prior art keywords
nylon
special
production method
product
maleic anhydride
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2009101825994A
Other languages
English (en)
Inventor
何翔宇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2009101825994A priority Critical patent/CN102020823A/zh
Publication of CN102020823A publication Critical patent/CN102020823A/zh
Pending legal-status Critical Current

Abstract

一种尼龙包胶专用粒料及其生产方法，涉及包装材料，特别是用于电动工具(尼龙产品)的包覆用材料。采用苯乙烯弹性体、白油、三元乙丙橡胶接枝马来酸酐和尼龙共混后造粒制成。本发明生产工艺简单、合理，成本是市场上产品成本的一半，符合工业化批量生产的低成本生产基本要求。形成的产品性能稳定，粘接性能比较的稳定，不受尼龙基材的影响。

Description

一种尼龙包胶专用粒料及其生产方法
技术领域
本发明涉及包装材料，特别是用于电动工具(尼龙产品)的包覆用材料。
背景技术
现在市场上的用于电动工具(尼龙产品)的包覆材料主要是通过苯乙烯弹性体和聚氨酯弹性体的共混制得。其缺陷是价格比较的高，粘接性能不稳定，受尼龙基材的影响比较的大，有时候粘，有时候不粘。
发明内容
本发明目的是提供一种价格低、粘接性好的尼龙包胶专用粒料。
本发明包括苯乙烯弹性体、白油、三元乙丙橡胶接枝马来酸酐和尼龙。其中，苯乙烯弹性体、白油、三元乙丙橡胶接枝马来酸酐和尼龙占总重量百分比分别为10～20％、20～40％、35～65％、8～15％。
本发明另一目的是提供以上尼龙包胶专用粒料的制备方法。
采用苯乙烯弹性体、白油、三元乙丙橡胶接枝马来酸酐和尼龙共混后造粒制成。
本发明生产工艺简单、合理，成本是市场上产品成本的一半，符合工业化批量生产的低成本生产基本要求。形成的产品性能稳定，粘接性能比较的稳定，不受尼龙基材的影响。
为了保障产品性能稳定，本发明造粒的环境温度为265℃。
具体实施方式
一、备料：
分别称取SEBS(苯乙烯弹性体)10-20kg、白油20-40kg、EPDM-g(三元乙丙橡胶接枝马来酸酐产品)35-65kg、PA(尼龙)8-15kg。
二、混合：
将以上各原料分别投入搅拌釜内，混合均匀。
三、造粒：
将釜内温度提升至265℃，使原料熔化，通过保温的双螺杆挤出机挤出至保温的模板，造粒冷却成型。

Claims (4)

1.一种尼龙包胶专用粒料，其特征在于包括苯乙烯弹性体、白油、三元乙丙橡胶接枝马来酸酐和尼龙。
2.根据权利要求1所述尼龙包胶专用粒料，其特征在于所述苯乙烯弹性体、白油、三元乙丙橡胶接枝马来酸酐和尼龙占总重量百分比分别为10～20％、20～40％、35～65％、8～15％。
3.一种如权利要求1所述尼龙包胶专用粒料的生产方法，其特征在于采用苯乙烯弹性体、白油、三元乙丙橡胶接枝马来酸酐和尼龙共混后造粒制成。
4.根据权利要求3所述尼龙包胶专用粒料的生产方法，其特征在于造粒的环境温度为265℃。
CN2009101825994A 2009-09-17 2009-09-17 一种尼龙包胶专用粒料及其生产方法 Pending CN102020823A (zh)