CN102019697A - 以氧化淀粉为粘合剂制备轻质保温板材的方法 - Google Patents
以氧化淀粉为粘合剂制备轻质保温板材的方法 Download PDFInfo
- Publication number
- CN102019697A CN102019697A CN 201010502037 CN201010502037A CN102019697A CN 102019697 A CN102019697 A CN 102019697A CN 201010502037 CN201010502037 CN 201010502037 CN 201010502037 A CN201010502037 A CN 201010502037A CN 102019697 A CN102019697 A CN 102019697A
- Authority
- CN
- China
- Prior art keywords
- oxidized starch
- light thermal
- thermal insulation
- waste
- insulation board
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供了一种以氧化淀粉为粘合剂、废弃植物纤维和废弃聚苯乙烯泡沫为原料制备轻质保温板材的方法，该方法是先将尿素溶解于水中，再加入淀粉，搅拌下混合均匀，然后滴加浓度为30％-50％的氢氧化钠溶液，使淀粉糊化，最后滴加次氯酸钠溶液，即制得氧化淀粉溶液；将制得的氧化淀粉溶液与废弃植物纤维粉末和废弃聚苯乙烯泡沫混合均匀，加入到模具内，经常压或加压成型、脱模及干燥，即可制得轻质保温板。本发明所用的原料为废弃植物纤维和废弃聚苯乙烯泡沫，不仅成本低，来源广泛，而且还有节能、环保、低碳等优点，制得的轻质保温板保温性能好，质量轻，且不含甲醛等有害物质，可广泛应用于包装、家居装饰等行业，具有广阔的市场前景。
Description
技术领域
本发明涉及一种轻质保温板材的制备方法，特别是涉及一种以氧化淀粉为粘合剂、废弃植物纤维和废弃聚苯乙烯泡沫为原料制备轻质保温板材的方法，该方法制备的板材适用于包装、家居装饰和建筑墙体内外保温等领域。
背景技术
世界各国的废弃植物纤维及废弃聚苯乙烯泡沫越来越多，大部分采用垃圾填埋或焚烧处理，对坏境造成了很大的污染；而其他的板材，例如：刨花板，中密度纤维板及胶合板是以木材或其他植物制成，而伐木对地球生态亦会产生很大程度的影响。聚苯乙烯泡沫板是以发泡聚苯乙烯为原料，该物质大量散落对环境造成严重的污染与危害，即便是深埋，因其不易老化，难以分解，还会污染地下水源，破坏土壤结构，使粮食作物减产；如简单焚烧处理，则又会严重污染环境。
发明内容
本发明就是针对以上问题，提供一种以氧化淀粉为粘合剂、废弃植物纤维和废弃聚苯乙烯泡沫为原料制备轻质保温板材的方法。
本发明的技术方案如下：先将尿素溶解于水中，再加入淀粉，搅拌下混合均匀，然后滴加浓度为30％-50％的氢氧化钠溶液，使淀粉糊化，最后滴加有效氯含量为0.177％-15.992％的次氯酸钠溶液，即制得氧化淀粉溶液；将制得的氧化淀粉溶液与废弃植物纤维粉末和直径为2-10mm颗粒状的废弃聚苯乙烯泡沫混合均匀后加入到模具内，经常压或加压成型、脱模及干燥，即可制得轻质保温板材，其中淀粉与总水量、尿素、氢氧化钠、次氯酸钠溶液、废弃植物纤维的质 量比为1∶4-8∶0.05-0.08∶0.04-0.10∶0.3-7.5∶2-10。
上述技术方案中所述废弃植物纤维为废弃木质纤维、废弃瓦楞纸箱、废纸、废弃植物秸秆等。
方案中所述的总水量为溶解尿素、氢氧化钠及分散淀粉所用的总水量。
本发明的优点是：
1、本发明制备的板材比以纯聚苯乙烯为原料制得的保温材料强度大，相对一般板材又具有保温作用，可适用于不同领域的需要。
2、本发明采用次氯酸钠做氧化剂制备氧化淀粉，其价格比其他氧化剂便宜，来源充足。
3、本发明所用原料为废弃植物纤维和废弃聚苯乙烯泡沫，不仅成本低，来源广泛，而且还有节能、环保、低碳等优点，实现了真正意义上的变废为宝。
4、本发明制备的板材保温性能好，质量轻，且不含甲醛等有害物质，可广泛应用于包装、家具及家居装饰等行业，具有广阔的市场前景。
具体实施方式
实施例1：称取6.0g尿素放入到560ml水中溶解，再加入96g淀粉，混合均匀后，缓慢滴加12ml浓度为40％的氢氧化钠溶液，最后滴加100ml有效氯含量为10.000％-15.992％的次氯酸钠溶液，制得氧化淀粉溶液；称取250g废弃瓦楞纸粉末和6.0g直径为2-10mm的颗粒状废弃聚苯乙烯泡沫，将二者混合均匀，然后与制得的氧化淀粉溶液混合均匀，放入到210mm×210mm×18mm的模具内，经常压成型、脱模及干燥，即可制得轻质保温板，本实施例所制得的轻质保温板材的检验结果如下表所示。
实施例2：称取7.5g尿素放入到700ml水中溶解，再加入120g淀粉，混合均匀后，缓慢滴加15ml浓度为40％的氢氧化钠溶液，最后滴加110ml有效氯含量为10.000％-15.992％的次氯酸钠溶液，制得氧化淀粉溶液；称取350g废弃瓦楞纸粉末和6.0g直径为2-10mm的颗粒状废弃聚苯乙烯泡沫，将二者混合均匀，然后与制得的氧化淀粉溶液混合均匀，放入到230mm×230mm×20mm的模具内，经常压成型、脱模及干燥，即可制得轻质保温板。
实施例3：称取5.0g尿素放入到450ml水中溶解，再加入80g淀粉，混合均匀后，缓慢滴加10ml浓度为39％的氢氧化钠溶液，最后滴加85ml有效氯含量为10.000％-15.992％的次氯酸钠溶液，制得氧化淀粉溶液；称取200g废弃瓦楞纸粉末和5.0g直径为2-10mm的颗粒状废弃聚苯乙烯泡沫，将二者混合均匀，然后与制得的氧化淀粉溶液混合均匀，放入到190mm×190mm×20mm的模具内，经常压成型、脱模及干燥，即可制得轻质保温板。
Claims (2)
1.以氧化淀粉为粘合剂制备轻质保温板材的方法，其特征是：先将尿素溶解于水中，再加入淀粉，搅拌下混合均匀，然后滴加浓度为30％-50％的氢氧化钠溶液，使淀粉糊化，最后滴加有效氯含量为0.177％-15.992％的次氯酸钠溶液，即制得氧化淀粉溶液；将制得的氧化淀粉溶液与废弃植物纤维粉末和直径为2-10mm颗粒状的废弃聚苯乙烯泡沫混合均匀后加入到模具内，经常压或加压成型、脱模及干燥，即可制得轻质保温板，其中淀粉与总水量、尿素、氢氧化钠、次氯酸钠溶液、废弃植物纤维的质量比为1∶4-8∶0.05-0.08∶0.04-0.10∶0.3-7.5∶2-10。
2.如权利要求1所述，以氧化淀粉为粘合剂制备轻质保温板材的方法，其特征是：所述的废弃植物纤维为废弃木质纤维、废弃瓦楞纸、办公及生活废纸、废弃植物秸秆。