CN102019696B - 以热糊化淀粉为粘合剂制备轻质保温板材的方法 - Google Patents
以热糊化淀粉为粘合剂制备轻质保温板材的方法 Download PDFInfo
- Publication number
- CN102019696B CN102019696B CN201010502013A CN201010502013A CN102019696B CN 102019696 B CN102019696 B CN 102019696B CN 201010502013 A CN201010502013 A CN 201010502013A CN 201010502013 A CN201010502013 A CN 201010502013A CN 102019696 B CN102019696 B CN 102019696B
- Authority
- CN
- China
- Prior art keywords
- starch
- heating
- gelatinized starch
- polystyrene foam
- waste
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明提供了一种以热糊化淀粉为粘合剂、废弃植物纤维和废弃聚苯乙烯泡沫为原料制备轻质保温板材的方法,该方法是将淀粉与水混合后,加热糊化,然后将糊化淀粉与废弃植物纤维粉末和废弃聚苯乙烯泡沫混合均匀,加入到模具内,经常压或加压成型、脱模及干燥,即可制得轻质保温板。本发明制备的板材保温性能好,质量轻,且不含甲醛等有害物质,可广泛应用于包装、家居装饰等行业,具有广阔的市场前景。
Description
技术领域
本发明涉及一种轻质保温板材的制备方法,特别是涉及一种以热糊化淀粉为粘合剂、废弃植物纤维和废弃聚苯乙烯泡沫为原料制备轻质保温板材的方法,该方法制备的板材适用于包装、家居装饰和建筑墙体内外保温等领域。
背景技术
世界各国的废弃植物纤维及废弃聚苯乙烯泡沫越来越多,大部分采用垃圾填埋或焚烧,对坏境造成了很大的污染;而其他的板材,例如:刨花板,中密度纤维板及胶合板是以木材或其他植物制成,而伐木对地球生态亦会产生很大程度的影响。聚苯乙烯泡沫板是以发泡聚苯乙烯为原料,该物质大量散落对环境造成严重的污染与危害,即便是深埋,因其不易老化,难以分解,还会污染地下水源,破坏土壤结构,使粮食作物减产;如简单焚烧处理,则又会严重污染环境。
发明内容
本发明就是针对以上问题,提供一种以热糊化淀粉为粘合剂、废弃植物纤维和废弃聚苯乙烯泡沫为原料制备轻质保温板材的方法。
本发明的技术方案如下:将淀粉与水混合后,加热至60-70℃糊化1-2分钟,将热糊化的淀粉与废弃植物纤维粉末和直径为2-10mm颗粒状的废弃聚苯乙烯泡沫混合均匀后加入到模具内,经常压或加压成型、脱模及干燥,即可制得轻质保温板材,其中淀粉与水、废弃植物纤维、废弃聚苯乙烯泡沫的质量比为1∶4-8∶1-5∶0.05-0.10。
上述技术方案中所述的废弃植物纤维为废弃木质纤维、废弃瓦楞纸、办公 及生活废纸、废弃植物秸秆等。
本发明的优点是:
1、本发明制备的板材比以纯聚苯乙烯为原料制得的保温材料强度大,相对一般板材又具有保温作用,可适用于不同领域的需要。
2、本发明采用的粘合剂为热糊化淀粉,其制备成本低,工艺简单,有利于大规模生产。
3、本发明所用原料为废弃植物纤维和废弃聚苯乙烯泡沫,不仅成本低,来源广泛,而且还有节能、环保、低碳等优点,实现了真正意义上的变废为宝。
4、本发明制备的板材保温性能好,质量轻,且不含甲醛等有害物质,可广泛应用于包装、家居装饰等领域,因此具有广阔的市场前景。
具体实施方式
实施例1:称取110g淀粉加入到660ml水中,搅拌下逐渐加热到69℃,在该温度下糊化2分钟;称取220g废弃瓦楞纸粉末和6g直径为2-10mm的颗粒状废弃聚苯乙烯泡沫,将二者混合均匀,然后与热糊化的淀粉混匀,放入220mm×216mm×20mm的模具内,经常压成型、脱模及干燥,即可制得轻质保温板,本实施例所制得的轻质保温板材的检验结果如下表所示。
实施例2:称取150g淀粉加入到750ml水中,搅拌下逐渐加热到70℃,在该温度下糊化2分钟;称取250g废弃纸箱粉末和6g直径为2-10mm的颗粒状废弃聚苯 乙烯泡沫,将二者混合均匀,然后与热糊化的淀粉混匀,放入230mm×230mm×18mm的模具内,经常压成型、脱模及干燥,即可制得轻质保温板。
实施例3:称取100g淀粉加入到550ml水中,搅拌下逐渐加热到69℃,在该温度下糊化2分钟;称取200g废弃纸箱粉末和5g直径为2-10mm的颗粒状废弃聚苯乙烯泡沫,将二者混合均匀,然后与热糊化的淀粉混匀,放入190mm×190mm×20mm的模具内,经常压成型、脱模及干燥,即可制得轻质保温板。
Claims (1)
1.以热糊化淀粉为粘合剂制备轻质保温板材的方法,其特征是:将淀粉与水混合后,加热至60-70℃糊化1-2分钟,将热糊化的淀粉与废弃植物纤维粉末和直径为2-10mm颗粒状的废弃聚苯乙烯泡沫混合均匀后加入到模具内,经常压或加压成型、脱模及干燥,即可制得轻质保温板,其中淀粉与水、废弃植物纤维、废弃聚苯乙烯泡沫的质量比为1∶4-8 ∶1-5∶0.05-0.1。