CN101966724B - 挤出成型碳化硅棚板的制备方法 - Google Patents

挤出成型碳化硅棚板的制备方法 Download PDF

Info

Publication number
CN101966724B
CN101966724B CN2010102710149A CN201010271014A CN101966724B CN 101966724 B CN101966724 B CN 101966724B CN 2010102710149 A CN2010102710149 A CN 2010102710149A CN 201010271014 A CN201010271014 A CN 201010271014A CN 101966724 B CN101966724 B CN 101966724B
Authority
CN
China
Prior art keywords
extrusion molding
silicon carbide
refractory slab
preparation
hours
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2010102710149A
Other languages
English (en)
Other versions
CN101966724A (zh
Inventor
唐竹兴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong University of Technology
Original Assignee
Shandong University of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shandong University of Technology filed Critical Shandong University of Technology
Priority to CN2010102710149A priority Critical patent/CN101966724B/zh
Publication of CN101966724A publication Critical patent/CN101966724A/zh
Application granted granted Critical
Publication of CN101966724B publication Critical patent/CN101966724B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供一种挤出成型碳化硅棚板的制备方法，包括陶瓷泥料制备、成型、烘干、烧成，其特征在于：将硅锭线切割废料、粒度为0.01-3μm的硅粉、粒度为0.01-3μm二氧化硅粉体、酚醛树脂和液体石蜡按重量比为45～75∶3～20∶3～20∶10～20∶5～10均匀混合在真空练泥机中混练制成碳化硅陶瓷塑性泥料，将碳化硅陶瓷塑性泥料挤出成型，切割制成碳化硅陶瓷塑性棚板，经烘干后制成挤出成型碳化硅棚板坯体，然后在1500～2000℃×2～4小时氮气气氛烧制成挤出成型碳化硅棚板。本发明制备方法可连续化大批量生产，生产效率高，制得的产品强度高。

Description

挤出成型碳化硅棚板的制备方法
技术领域
本发明涉及一种挤出成型碳化硅棚板的制备方法，属于陶瓷制备技术领域。
背景技术
挤出成型碳化硅棚板目前采用注浆成型技术生产，这种方法的缺点是生产效率低，人工操作，占地面积大，产品性能不稳定。
发明内容
本发明的目的在于提供一种能克服上述缺陷、适应连续化大生产、性能优良的挤出成型碳化硅棚板的制备方法。其技术方案为：
包括陶瓷泥料制备、成型、烘干、烧成，将硅锭线切割废料、粒度为0.01-3μm的硅粉、粒度为0.01-3μm二氧化硅粉体、酚醛树脂和液体石蜡按重量比为45～75∶3～20∶3～20∶10～20∶5～10均匀混合在真空练泥机中混练制成碳化硅陶瓷塑性泥料，将碳化硅陶瓷塑性泥料挤出成型，切割制成碳化硅陶瓷塑性棚板，经烘干后制成挤出成型碳化硅棚板坯体，然后在1500～2000℃×2～4小时氮气气氛烧制成挤出成型碳化硅棚板。
实验所用的配料原料的纯度均为工业纯。
其中，硅锭线切割废料的粒度小于5μm。
挤出成型碳化硅棚板坯体的烘干温度为室温～60℃烘干12～24小时，60℃～100℃烘干12～24小时，100℃～170℃烘干6～12小时。
本发明与现有技术相比，其优点为：
1、由于采用了酚醛树脂和水溶性酚醛树脂为塑性剂，使得挤出成型碳化硅棚板坯体烘干后的坯体强度得到较大提高，可进行素坯加工，外形尺寸精确；
2、由于添加了硅粉和二氧化硅粉体，在烧结过程中形成了氧氮碳化硅，使得挤出成型碳化硅棚板的显微结构均匀，强度高，整体可靠性高。
3、使用液体石蜡可物料表面润滑在挤出成型过程中可提高泥料的塑性。
4、挤出成型，可连续化生产，生产效率高，制得的产品强度高。
具体实施方式
实施例1
1、挤出成型碳化硅棚板的成型
将硅锭线切割废料、粒度为1μm的硅粉、粒度为1μm二氧化硅粉体、酚醛树脂和液体石蜡按重量比为60∶20∶3∶10∶7均匀混合在真空练泥机中混练制成碳化硅陶瓷塑性泥料，将碳化硅陶瓷塑性泥料挤出成型，切割制成碳化硅陶瓷塑性棚板，经烘干后制成挤出成型碳化硅棚板坯体。
2、烘干：
将成型后的碳化硅陶瓷棚板坯体在40～50℃烘干12小时，80℃～90℃烘干12小时，130℃～140℃烘干6小时。
3、烧成：
将烘干后的挤出成型碳化硅棚板坯体在2000℃×2小时氮气气氛烧制，制成挤出成型碳化硅棚板。
所获得挤出成型碳化硅棚板耐压强度为260MPa.。
实施例2
1、挤出成型碳化硅棚板的成型
将硅锭线切割废料、粒度为0.01μm的硅粉、粒度为0.01μm二氧化硅粉体、酚醛树脂和液体石蜡按重量比为45∶13∶12∶20∶10均匀混合在真空练泥机中混练制成碳化硅陶瓷塑性泥料，将碳化硅陶瓷塑性泥料挤出成型，切割制成碳化硅陶瓷塑性棚板，经烘干后制成挤出成型碳化硅棚板坯体。
2、烘干：
将成型后的碳化硅陶瓷棚板坯体在40～50℃烘干20小时，60℃～70℃烘干24小时，100℃～110℃烘干12小时。
3、烧成：
将烘干后的挤出成型碳化硅棚板坯体在1580℃×4小时氮气气氛烧制，制成挤出成型碳化硅棚板。
所获得挤出成型碳化硅棚板耐压强度为280MPa.。
实施例3
1、挤出成型碳化硅棚板的成型
将硅锭线切割废料、粒度为3μm的硅粉、粒度为3μm二氧化硅粉体、酚醛树脂和液体石蜡按重量比为75∶3∶3∶14∶5均匀混合在真空练泥机中混练制成碳化硅陶瓷塑性泥料，将碳化硅陶瓷塑性泥料挤出成型，切割制成碳化硅陶瓷塑性棚板，经烘干后制成挤出成型碳化硅棚板坯体。
2、烘干：
将成型后的碳化硅陶瓷棚板坯体在25～35℃烘干18小时，70℃～80℃烘干18小时，110℃～120℃烘干9小时。
3、烧成：
将烘干后的挤出成型碳化硅棚板坯体在1750℃×3小时氮气气氛烧制，制成挤出成型碳化硅棚板。
所获得挤出成型碳化硅棚板耐压强度为240MPa.。
实施例4
1、挤出成型碳化硅棚板的成型
将硅锭线切割废料、粒度为3μm的硅粉、粒度为3μm二氧化硅粉体、酚醛树脂和液体石蜡按重量比为52∶9∶20∶14∶5均匀混合在真空练泥机中混练制成碳化硅陶瓷塑性泥料，将碳化硅陶瓷塑性泥料挤出成型，切割制成碳化硅陶瓷塑性棚板，经烘干后制成挤出成型碳化硅棚板坯体。
2、烘干：
将成型后的碳化硅陶瓷棚板坯体在40～50℃烘干12小时，80℃～90℃烘干12小时，120℃～130℃烘干6小时。
3、烧成：
将烘干后的挤出成型碳化硅棚板坯体在1580℃×4小时氮气气氛烧制，制成挤出成型碳化硅棚板。
所获得挤出成型碳化硅棚板耐压强度为100MPa.。

Claims (3)

1.一种挤出成型碳化硅棚板的制备方法，包括陶瓷泥料制备、成型、烘干、烧成，其特征在于：将硅锭线切割废料、粒度为0.01-3μm的硅粉、粒度为0.01-3μm二氧化硅粉体、酚醛树脂和液体石蜡按重量比为45～75∶3～20∶3～20∶10～20∶5～10均匀混合在真空练泥机中混练制成碳化硅陶瓷塑性泥料，将碳化硅陶瓷塑性泥料挤出成型，切割制成碳化硅陶瓷塑性棚板，经烘干后制成挤出成型碳化硅棚板坯体，然后在1500～2000℃温度下、2～4小时氮气气氛烧制成挤出成型碳化硅棚板。
2.根据权利要求1所述的挤出成型碳化硅棚板的制备方法，其特征在于：硅锭线切割废料的粒度小于5μm。
3.根据权利要求1所述的挤出成型碳化硅棚板的制备方法，其特征在于：挤出成型碳化硅棚板坯体的烘干温度为室温～60℃烘干12～24小时，60℃～100℃烘干12～24小时，100℃～170℃烘干6～12小时。
CN2010102710149A 2010-09-03 2010-09-03 挤出成型碳化硅棚板的制备方法 Expired - Fee Related CN101966724B (zh)