CN101914318B - 一种建筑物内墙用腻子的配方 - Google Patents
一种建筑物内墙用腻子的配方 Download PDFInfo
- Publication number
- CN101914318B CN101914318B CN2010102466101A CN201010246610A CN101914318B CN 101914318 B CN101914318 B CN 101914318B CN 2010102466101 A CN2010102466101 A CN 2010102466101A CN 201010246610 A CN201010246610 A CN 201010246610A CN 101914318 B CN101914318 B CN 101914318B
- Authority
- CN
- China
- Prior art keywords
- putty
- powder
- wall
- prescription
- building
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种建筑物内墙用腻子的配方，所述配方包括脱硫石膏、石英粉、调节剂、无机凝胶、缓凝剂、抗裂剂、可再分散胶粉。所述调节剂为羟丙基甲基纤维素，无机凝胶为钠基膨润土，缓凝剂为多聚磷酸盐，抗裂剂为木质纤维素，可再分散胶粉为聚醋酸乙烯酯或乙烯树脂。本发明建筑物内墙腻子具有良好的耐水性和粘接强度，抹刮后的基面不空鼓，不开裂，不掉粉，同时施工方便，刮涂后腻子层结构致密，保持透气又自然成膜，使墙面更加平滑，节省乳胶漆的使用量。
Description
技术领域
本发明属于建筑材料技术领域，具体涉及一种建筑物内墙腻子的配方。
背景技术
目前，建筑物内墙腻子一般采用老粉、白水泥、灰钙粉或者滑石粉、立德粉等作为基料，现场掺拌甲醛类胶黏剂，此类腻子成本低、施工性好，但是存在耐水性差、粘接强度差、粉尘有刺激性、老墙面有泛黄现象等不足。中国专利文献公开了一些制备腻子的方法，如公告号为CN101037557的中国发明专利2007年9月19日公开了脱硫石膏制备干粉批墙腻子的制备方法，公告号为CN1454945的中国发明专利于2003年11月12日公开了环保型石膏基建筑腻子粉，公告号为CN101423679的中国发明专利于2009年5月6日公开了氟石膏生产抗裂腻子的外加剂。这些专利以建筑石膏及脱硫石膏、氟石膏作为基料制备腻子，但是上述现有技术仍存在稳定性不佳、强度和硬度达不到具体施工要求等缺点。
发明内容
本发明所要解决的技术问题就是提供一种建筑物内墙腻子的配方，其制成的腻子，稳定性好、强度、硬度高。
为解决上述技术问题，本发明采用如下技术方案：一种建筑物内墙用腻子的配方，其特征在于：所述配方包括脱硫石膏、石英粉、调节剂、无机凝胶、缓凝剂、抗裂剂。
进一步的，所述配方各组分间的重量比例为，
脱硫石膏200～500，
石英粉 485～785，
调节剂 1～3，
无机凝胶 1～5，
缓凝剂 0.2～0.5，
抗裂剂 1～3。
作为优选，所述配方还包括可再分散胶粉。
进一步的，所述配方各组分间的重量比例为，
脱硫石膏 200～500，
石英粉 485～785，
调节剂 1～3，
无机凝胶 1～5，
缓凝剂 0.2～0.5，
抗裂剂 1～3，
可再分散胶粉 1～5。
更进一步的，所述配方各组分间的重量比例为，
脱硫石膏 400，
100目石英粉 85，
200目石英粉 250，
400目石英粉 250，
调节剂 3，
无机凝胶 5，
缓凝剂 0.4，
抗裂剂 2，
可再分散胶粉 5。
作为优选，所述调节剂为羟丙基甲基纤维素，无机凝胶为钠基膨润土，缓凝剂为多聚磷酸盐，抗裂剂为木质纤维素，可再分散胶粉为聚醋酸乙烯酯或乙烯树脂。
作为优选，所述脱硫石膏细度200目，石英粉为细度60目、80目、120目石英粉中的一种或两种以上的混合。
作为优选，所述脱硫石膏为电厂烟气脱硫石膏制得的建筑石膏，初凝时间为8min，终凝时间为15min；抗折强度为3.8mpa，抗压强度为8.7Mpa。
本发明建筑物内墙腻子具有良好的耐水性和粘接强度，抹刮后的基面不空鼓，不开裂，不掉粉，同时施工方便，刮涂后腻子层结构致密，保持透气又自然成膜，使墙面更加平滑，节省乳胶漆的使用量，与传统的老粉加胶水工艺相比，性价比优势更加突出，且操作简单，质量稳定，为内墙装饰提供了一种更优秀的选择；本发明采用石英粉代替传统粉状填充料，具有更好的稳定性和强度。
具体实施方式
实施例1
其中实施例1-9所称的脱硫石膏耐水抗裂腻子，以重量份计，各组分重量比例如下，均采用无重力双飞刀混合设备混合。
烟气脱硫石膏 200 100目石英粉 360
200目石英粉 150 400目石英粉 275
HPMC70000 3 钠基膨润土 5
Retardan P 0.2 ARBOCEL ZZC500 2
VINNAPAS5044N 5
实施例2
烟气脱硫石膏 250 100目石英粉 335
200目石英粉 150 400目石英粉 250
HPMC70000 3 钠基膨润土 5
Retardan P 0.25 ARBOCEL ZZC500 2
VINNAPAS5044N 5
实施例3
烟气脱硫石膏 300 100目石英粉 350
200目石英粉 85 400目石英粉 250
HPMC70000 3 钠基膨润土 5
Retardan P 0.3 ARBOCEL ZZC500 2
VINNAPAS5044N 5
实施例4
烟气脱硫石膏 350 100目石英粉 300
200目石英粉 100 400目石英粉 250
HPMC70000 3 钠基膨润土 5
Retardan P 0.35 ARBOCEL ZZC500 2
VINNAPAS5044N 5
实施例5
烟气脱硫石膏 400 100目石英粉 585
HPMC70000 3 钠基膨润土 5
Retardan P 0.4 ARBOCEL ZZC500 2
VINNAPAS5044N 5
实施例6
烟气脱硫石膏 400 400目石英粉 585
HPMC70000 3 钠基膨润土 5
Retardan P 0.3 ARBOCEL ZZC500 2
VINNAPAS5044 5
实施例7
烟气脱硫石膏 500 400目石英粉 485
HPMC70000 3 钠基膨润土 5
Retardan P 0.5 ARBOCEL ZZC500 2
VINNAPAS5044N 5
实施例8
烟气脱硫石膏 400 100目石英粉 85
200目石英粉 250 400目石英粉 250
钠基膨润土 5 HPMC70000 3
Retardan P 0.4 ARBOCEL ZZC500 2
实施例9
烟气脱硫石膏 400 100目石英粉 85
200目石英粉 250 400目石英粉 250
HPMC70000 3 钠基膨润土 5
Retarden P 0.4 ARVOCEL ZZC500 2
VINNAPAS5044N 5
其中，以上实施例的腻子经以下项目检测，均具有良好的结果：
| 项目 | 国家标准要求 | 实测结果 |
| 容器中状态 | 无结块、均匀 | 无结块、均匀 |
| 施工性 | 刮涂无障碍 | 刮涂无障碍 |
| 干燥时间(表干，h) | ＜5 | 2 |
| 打磨性(％) | 20-80 | 63 |
| 耐水性(48h) | 未发现起泡、开裂及脱落 | 无异常 |
| 耐碱性(24h) | 未发现起泡、开裂及脱落 | 无异常 |
其中，对照组合实施例组的标准状态和浸水后的粘结强度结果见下表，对照组为国家标准规定的腻子：
本发明腻子采用的脱硫石膏为电厂烟气脱硫石膏制得的建筑石膏。它是以β半水石膏(βCaSO4·1/2H2O)为主要成分，建筑石膏凝结硬化是石膏吸收结晶水后的结晶过程，其体积不仅不会收缩，而且还稍有膨胀，这种膨胀不会对石膏造成危害，还能使石膏的表面较为光滑饱满，棱角清晰完整、避免了普通材料干燥时的开裂。硬化后石膏的主要成分是二水石膏，当受到高温作用时或遇火后会脱出21％左右的结晶水，并能在表面蒸发形成水蒸气幕，可有效地阻止火势的蔓延，具有良好的防火效果。该脱硫石膏的细度为200目，初凝时间为8min，终凝时间为15min；抗折强度为3.8mpa，抗压强度为8.7Mpa。
石英粉的粗细程度，是指不同粒径的颗粒，在混凝土中，石英粉的表面需要由石膏浆包裹，粉体的总表面积愈大，则需要包裹颗粒表面的石膏浆就愈多，在相同用量条件下，石英粉的总表面积较大，而粗粉的总表面积较小，传统工艺都采用超细的石英粉，但是采用超细的石英粉在超过一定厚度后会带来防开裂性能的下降。
本发明采用石英粉由细度60目、80目和120目石英粉的一种或其混合连续级配而成。连续级配使得粉的颗粒呈连续性，即颗粒由小到大，每级细度占一定比例。用连续级配的粉来配制的腻子粉混合料，和易性较好，不易发生离析现象，对石膏基料的需求少，从而保证产品的粘接强度的提高，同时产品具有良好的厚刮不开裂性。
本发明所用的调节剂主要成分为羟丙基甲基纤维素，可采用日本信越化学公司生产的HPMC70000或其他含有羟丙基甲基纤维素的调节剂。
本发明所称无机凝胶为钠基膨润土，其中蒙脱石60％-88％，膨胀容25-50ml/g，胶质价不小于99ml/15g，2h吸水率250-350％，水分不大于12，湿压强度不小于0.23Mpa，吸蓝量不小于80mmol/g，Na2O不小于1.28。
本发明所称缓凝剂为多聚磷酸盐类石膏专用缓凝剂，可采用德国TRICOSAL公司生产的Retardan P产品，用量少，缓凝效果好，不影响石膏硬化后的强度。
本发明所称抗裂剂主要成分为木质纤维素，可选用德国JRS公司开发生产的ARBOCEL ZZC500，能形成三维结构，并有显著的交联作用，这种交联的结构可以减少产品的收缩性能，从而辅助达到抗开裂的作用。
本发明所称可再分散胶粉为德国瓦克化学公司所生产的VINNAPAS5044N聚醋酸乙烯酯及乙烯树脂，作为有机胶黏剂，增加体系的耐水性和粘接强度。
Claims (2)
1.一种建筑物内墙用腻子的配方，其特征在于：所述配方包括脱硫石膏、石英粉、调节剂、无机凝胶、缓凝剂、抗裂剂，所述配方还包括可再分散胶粉，所述配方各组分间的重量比例为，
脱硫石膏 400，
100目石英粉 85，
200目石英粉 250，
400目石英粉 250，
调节剂 3，
无机凝胶 5，
缓凝剂 0.4，
抗裂剂 2，
可再分散胶粉 5；
所述调节剂为羟丙基甲基纤维素，无机凝胶为钠基膨润土，缓凝剂为多聚磷酸盐，抗裂剂为木质纤维素，可再分散胶粉为聚醋酸乙烯酯或乙烯树脂。
2.根据权利要求1所述的一种建筑物内墙用腻子的配方，其特征在于：所述脱硫石膏为电厂烟气脱硫石膏制得的建筑石膏，初凝时间为8min，终凝时间为15min；抗折强度为3.8MPa，抗压强度为8.7MPa。