CN104402334A - 阻燃型水泥基垫层自流平 - Google Patents
阻燃型水泥基垫层自流平 Download PDFInfo
- Publication number
- CN104402334A CN104402334A CN201410630934.3A CN201410630934A CN104402334A CN 104402334 A CN104402334 A CN 104402334A CN 201410630934 A CN201410630934 A CN 201410630934A CN 104402334 A CN104402334 A CN 104402334A
- Authority
- CN
- China
- Prior art keywords
- flame retardant
- bed course
- leveling
- cement
- retardant type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种阻燃型水泥基垫层自流平,各物料组分的重量百分比如下:水泥18%~25%,骨料10%~20%,细料5%~10%,超塑化剂0.15%~0.2%,丙苯乳液15%~25%,减水剂0.1%~0.2%,阻燃剂0.1%~0.25%等,其余为水。本发明不仅能够有效的解决建筑工程迎水面或背水面的防水问题,而且具有粘结牢固,阻燃效果好、生产简单、方便、投资小等特点,并且施工厚度在3mm~4mm之间都具有良好的防水和阻燃性能。
Description
技术领域
本发明涉及建筑材料技术领域,具体涉及一种具有阻燃型水泥基垫层自流平。
背景技术
自流平砂浆包括水泥基自流平/自流平砂浆/找平砂浆等,其科技含量高、技术环节比较复杂的产品。它是由多种活性成分组成的干混型粉状材料,现场拌水即可使用。稍经刮刀展开,即可获得高平整基面。硬化速度快,24小时即可在上行走,或进行后续工程(如铺木地板、金刚板等),施工快捷、简便是传统人工找平所无法比拟的。自流平砂浆使用安全、无污染、美观、快速施工与投入使用是自流平水泥的特色。它提升了文明的施工程序,创建了优质舒适平坦的空间,多样化标致饰面材的铺贴,让生活增添了绚丽的色彩。自流平砂浆用途广泛,可用于工业厂房、车间、仓储、商业卖场、展厅、体育馆、医院、各种开放空间、办公室等,也用于居家、别墅、温馨小空间等。可作为饰面面层,亦可作为耐磨基层。
但是现有的水泥基自流平砂浆还具有一些缺点:(1)防火性能差:在遭受高温和着火点的影响后,自流平容易出现自燃的现象,引起火灾;(2)防水性能差:当水泥基自流平不具备防水功能时,在遭受水侵蚀及温度变化的影响后,自流平容易出现热烈、渗漏、空鼓及脱落的现象;(3)粘接不够牢固:使用一段时间后,在遭受水侵蚀和拉扯的影响后,自流平容易出现脱落的想象。
发明内容
针对水泥基自流平砂浆由于技术缺陷导致防火、防水性能差及粘接不够牢固等问题,本发明提供了一种阻燃型水泥基垫层自流平,通过在组份中加入阻燃剂、防水灰浆和提高粘接性能的组份,不仅能够有效的解决建筑工程迎水面或背水面的防水问题,而且具有粘结牢固,阻燃效果好、生产简单、方便、投资小等特点,并且施工厚度在3mm~4mm之间都具有良好的防水和阻燃性能。
本发明提供了一种阻燃型水泥基垫层自流平,各物料组分的重量百分比如下:
水泥 18%~25%
骨料 10%~20%
细料 5%~10%
超塑化剂 0.15%~0.2%
消泡剂 0.15%~0.3%
稳定剂 0.05%~0.2%
乳胶粉 1.5%~2%
缓凝剂 0.2%~0.3%
促凝剂 0.1%~0.2%
丙苯乳液 15%~25%
防腐剂 0.18%~0.25%
分散剂 0.15%~0.2%
石英砂 12%~22%
纤维素醚 0.1%~0.14%
减水剂 0.1%~0.2%
阻燃剂 0.1%~0.25%,其余为水。
优选的是,所述的阻燃型水泥基垫层自流平,所述的水泥为普通硅酸盐水泥与高铝水泥合成的复合水泥,二者重量比为80∶20~40。
优选的是,所述的骨料为粒径50~90目与60~120目的水洗河砂,重量比60~100∶40~80复配。
优选的是,所述的细料为硬石膏跟重质碳酸钙复配,二者重量比为90∶200~350。
优选的是,所述的超塑化剂为改性聚羧酸醚;所述的消泡剂为液态碳氢化合物、聚乙二醇和非结晶性二氧化矽的混合物;所述的乳胶粉为乙烯共聚胶粉;所述的缓凝剂为柠檬酸钠;所述促凝剂为碳酸锂;所述的稳定剂是人工合成的非缔合型高分子共聚物。
优选的是,所述的石英砂为粒径50~110目与210~350目两个规格石英砂复配而成,二者的复配重量比1~6∶1~11。
优选的是,所述的纤维素醚为羟乙基甲基纤维素醚或羟丙基甲基纤维素醚,粘度在30000mPa.s~50000mPa.s;所述的阻燃剂为十溴二苯乙烷或氢氧化镁。
优选的是,所述的减水剂为磺化三聚氢胺高效减水剂或聚羧酸减水剂;所述的分散剂为聚丙烯酸钠盐类分散剂。
优选的是,所述的丙苯乳液玻璃化温度在-10℃以上。
本发明的有益效果:
本发明不仅能够有效的解决建筑工程迎水面或背水面的防水问题,而且具有粘结牢固,阻燃效果好、生产简单、方便、投资小等特点,并且施工厚度在3mm~4mm之间都具有良好的防水和阻燃性能。
具体实施方式
下面对本发明做进一步的详细说明,以令本领域技术人员参照说明书文字能够据以实施。
实施例1
本发明提供的阻燃型水泥基垫层自流平,各物料组分的重量百分比如下:
水泥 18%
骨料 10%
细料 5%
超塑化剂 0.15%
消泡剂 0.15%
稳定剂 0.05%
乳胶粉 1.5%
缓凝剂 0.2%
促凝剂 0.1%
丙苯乳液 15%
防腐剂 0.18%
分散剂 0.15%
石英砂 12%
纤维素醚 0.1%
减水剂 0.1%
阻燃剂 0.1%,其余为水。
实施例2
本发明提供的阻燃型水泥基垫层自流平,各物料组分的重量百分比如下:
水泥 20%
骨料 15%
细料 6%
超塑化剂 0.16%
消泡剂 0.18%
稳定剂 0.15%
乳胶粉 1.6%
缓凝剂 0.24%
促凝剂 0.13%
丙苯乳液 20%
防腐剂 0.2%
分散剂 0.16%
石英砂 18%
纤维素醚 0.12%
减水剂 0.15%
阻燃剂 0.18%,其余为水。
实施例3
本发明提供的阻燃型水泥基垫层自流平,各物料组分的重量百分比如下:
水泥 25%
骨料 20%
细料 10%
超塑化剂 0.2%
消泡剂 0.3%
稳定剂 0.2%
乳胶粉 2%
缓凝剂 0.3%
促凝剂 0.2%
丙苯乳液 25%
防腐剂 0.25%
分散剂 0.2%
石英砂 22%
纤维素醚 0.14%
减水剂 0.2%
阻燃剂 0.25%,其余为水。
本产品先将各组份置于无重力混合搅拌机进行搅拌,搅拌120分钟使之混合均匀,然后放置300分钟,然后通过200目筛子,并作密封包装保存。
使用时将制备好的产品浆液置于无重力混合搅拌机中,并不断的加水进行搅拌,直到稠度适中,停止加水;再搅拌至少100分钟使之混合均匀,才可使用。
通过上述步骤后对其按照JC/T985-2005《地面用水泥基自流平砂浆》进行各项质量技术指标检测,实施例1-3中的阻燃型水泥基垫层自流平的试验结果如下表所示:
尽管本发明的实施方案已公开如上,但其并不仅仅限于说明书和实施方式中所列运用,它完全可以被适用于各种适合本发明的领域,对于熟悉本领域的人员而言,可容易地实现另外的修改,因此在不背离权利要求及等同范围所限定的一般概念下,本发明并不限于特定的细节。
Claims (9)
1.一种阻燃型水泥基垫层自流平,各物料组分的重量百分比如下:
水泥18%~25%
骨料10%~20%
细料5%~10%
超塑化剂0.15%~0.2%
消泡剂0.15%~0.3%
稳定剂0.05%~0.2%
乳胶粉1.5%~2%
缓凝剂0.2%~0.3%
促凝剂0.1%~0.2%
丙苯乳液15%~25%
防腐剂0.18%~0.25%
分散剂0.15%~0.2%
石英砂12%~22%
纤维素醚0.1%~0.14%
减水剂0.1%~0.2%
阻燃剂0.1%~0.25%,其余为水。
2.根据权利要求1所述的阻燃型水泥基垫层自流平,其特征在于所述的水泥为普通硅酸盐水泥与高铝水泥合成的复合水泥,二者重量比为80∶20~40。
3.根据权利要求1所述的阻燃型水泥基垫层自流平,其特征在于所述的骨料为粒径50~90目与60~120目的水洗河砂,重量比60~100∶40~80复配。
4.根据权利要求1所述的阻燃型水泥基垫层自流平,其特征在于所述的细料为硬石膏跟重质碳酸钙复配,二者重量比为90∶200~350。
5.根据权利要求1所述的阻燃型水泥基垫层自流平,其特征在于所述的超塑化剂为改性聚羧酸醚;所述的消泡剂为液态碳氢化合物、聚乙二醇和非结晶性二氧化矽的混合物;所述的乳胶粉为乙烯共聚胶粉;所述的缓凝剂为柠檬酸钠;所述促凝剂为碳酸锂;所述的稳定剂是人工合成的非缔合型高分子共聚物。
6.根据权利要求1所述的阻燃型水泥基垫层自流平,其特征在于所述的石英砂为粒径50~110目与210~350目两个规格石英砂复配而成,二者的复配重量比1~6∶1~11。
7.根据权利要求1所述的阻燃型水泥基垫层自流平,其特征在于所述的纤维素醚为羟乙基甲基纤维素醚或羟丙基甲基纤维素醚,粘度在30000mPa.s~50000mPa.s;所述的阻燃剂为十溴二苯乙烷或氢氧化镁。
8.根据权利要求1所述的阻燃型水泥基垫层自流平,其特征在于所述的减水剂为磺化三聚氢胺高效减水剂或聚羧酸减水剂;所述的分散剂为聚丙烯酸钠盐类分散剂。
9.根据权利要求1所述的阻燃型水泥基垫层自流平,其特征在于:所述的丙苯乳液玻璃化温度在-10℃以上。