CN103043974B - 一种高耐磨水泥基自流平砂浆及其制备方法 - Google Patents

一种高耐磨水泥基自流平砂浆及其制备方法 Download PDF

Info

Publication number
CN103043974B
CN103043974B CN201210515416.8A CN201210515416A CN103043974B CN 103043974 B CN103043974 B CN 103043974B CN 201210515416 A CN201210515416 A CN 201210515416A CN 103043974 B CN103043974 B CN 103043974B
Authority
CN
China
Prior art keywords
parts
mass parts
iron sand
self
cement
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201210515416.8A
Other languages
English (en)
Other versions
CN103043974A (zh
Inventor
周盾白
李国荣
陈岳林
马超
黄佩坚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANGHAI SUPE CHEMICAL CO Ltd
Original Assignee
SHANGHAI SUPE CHEMICAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI SUPE CHEMICAL CO Ltd filed Critical SHANGHAI SUPE CHEMICAL CO Ltd
Priority to CN201210515416.8A priority Critical patent/CN103043974B/zh
Publication of CN103043974A publication Critical patent/CN103043974A/zh
Application granted granted Critical
Publication of CN103043974B publication Critical patent/CN103043974B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种高耐磨水泥基自流平砂浆,其是由以下质量份的原料组成:8-20质量份的铁砂、22-32质量份的普硅水泥、4-8质量份的高铝水泥、4-8质量份的膨胀剂、3-6 质量份的硬石膏粉、2-4 质量份的可分散胶粉、20-40 质量份的石英砂、10-20 质量份的重质碳酸钙、0.5-0.8 质量份的减水剂、0-6 质量份的早强剂、0.1-0.2 质量份的缓凝剂、0.1-0.2 质量份的木质纤维素、0.1-0.2 质量份的消泡剂。制备一种高耐磨水泥基自流平砂浆的方法,包括以下步骤:1)对铁砂进行防锈处理:将铁砂置于煮沸的碱液中10-20min,再分离出铁砂,烘干;2)将经过防锈处理的铁砂、自流平砂浆的其他组份混合均匀即可。本发明制备的砂浆具有较好的流动性,同时用本发明的砂浆施工而成的地坪具有较好的表面耐磨性。

Description

一种高耐磨水泥基自流平砂浆及其制备方法
技术领域
[0001] 本发明涉及一种高耐磨水泥基自流平砂浆及其制备方法。
背景技术
[0002] 水泥基自流平砂浆是指由水泥基胶凝材料、细骨料、填料及添加剂等组成的粉状 材料,经与水或乳液混合搅拌后具有一定流动性地面找平用砂浆。近年来,自流平水泥不但 作为自找平材料有了广泛的应用,在作为终饰面材料上也得到了较大的发展,一些面层自 流平水泥以其平整光滑、颜色较为一致的表面工程效果得到了市场认可,在地下停车场、车 间、仓库、商场、展厅、办公楼及商住楼等都得到了应用。
[0003] 现有技术的水泥基自流平砂浆,亟需提高的性能有:表面耐磨性,用现有技术的砂 浆施工而成的地坪,表面耐磨性不高,流动性和物理力学性能方面也亟需进一步的提高。
发明内容
[0004] 本发明的目的是提供一种高耐磨水泥基自流平砂浆及其制备方法。
[0005] 本发明所采取的技术方案是:
[0006] -种高耐磨水泥基自流平砂浆,其是由以下质量份的原料组成:8-20质量份的铁 砂、22-32质量份的普硅水泥、4-8质量份的高铝水泥、4-8质量份的膨胀剂、3-6质量份的 硬石膏粉、2-4质量份的可分散胶粉、20-40质量份的石英砂、10-20质量份的重质碳酸 钙、0.5-0. 8质量份的减水剂、0-6质量份的早强剂、0.1-0. 2质量份的缓凝剂、0.1-0. 2 质量份的木质纤维素、〇. 1-0. 2质量份的消泡剂。
[0007] 所述的膨胀剂为硫铝酸盐系UEA-H型高效膨胀剂。
[0008] 所述的可分散胶粉为丙烯酸酯、醋酸乙烯酯类胶粉中的至少一种。
[0009] 所述的早强剂为硫酸钠、硫酸钙、硝酸盐类中的至少一种。
[0010] 所述的缓凝剂为柠檬酸、葡萄糖、蔗糖和纤维素醚中的至少一种。
[0011] 所述的消泡剂为 DREWPLUS 46000EG、AGITAN P803、T-20GB、WP2 粉末消泡剂中的 至少一种。
[0012] 制备一种高耐磨水泥基自流平砂浆的方法,包括以下步骤:
[0013] 1)对铁砂进行防锈处理:将铁砂置于煮沸的碱液中10-20min,再分离出铁砂,烘 干;
[0014] 2)将经过防锈处理的铁砂、自流平砂浆的其他组份混合均匀即可。
[0015] 所述的碱液为5-15wt%的氢氧化钠或氢氧化钾溶液。
[0016] 所述的铁砂与碱液的质量比为1: (10-20)。
[0017] 本发明的有益效果是:本发明制备的砂浆具有较好的流动性,同时用本发明的砂 浆施工而成的地坪具有较好的表面耐磨性。
具体实施方式
[0018] 下面结合具体实施例对本发明做进一步的说明:
[0019] 实施例1:
[0020] 一种高耐磨水泥基自流平水泥砂浆,其原料配方组成如下表1 :
[0021]
Figure CN103043974BD00041
[0022] 用上表中的原料制成砂浆,制备方法如下:
[0023] 1)对铁砂进行防锈处理:将铁砂置于煮沸的浓度为5wt%的氢氧化钠溶液中 IOmin,分离出铁砂,烘干;
[0024] 2)将经过防锈处理的铁砂和自流平砂浆的其它组份按配比投入到混合釜中,搅拌 20-50分钟,出料包装即可。
[0025] 实施例2:
[0026] -种高耐磨水泥基自流平水泥砂浆,其原料配方组成如下表2 :
[0027]
Figure CN103043974BD00051
[0028] 用上表中的原料制成砂浆,制备方法如下:
[0029] 1)对铁砂进行防锈处理:将铁砂置于煮沸的浓度为5wt%的氢氧化钠溶液中 IOmin,分离出铁砂,烘干;
[0030] 2)将经过防锈处理的铁砂和自流平砂浆的其它组份按配比投入到混合釜中,搅拌 20-50分钟,出料包装即可。
[0031] 实施例3:
[0032] -种高耐磨水泥基自流平水泥砂浆,其原料配方组成如下表3 :
[0033]
Figure CN103043974BD00061
[0034] 用上表中的原料制成砂浆,制备方法如下:
[0035] 1)对铁砂进行防锈处理:将铁砂置于煮沸的浓度为5wt%的氢氧化钠溶液中 IOmin,分离出铁砂,烘干;
[0036] 2)将经过防锈处理的铁砂和自流平砂浆的其它组份按配比投入到混合釜中,搅拌 20-50分钟,出料包装。
[0037] 对实施例1的砂浆进行相关的性能测试(测试的标准为JC/T985-2005),其测试结 果如下:
[0038]
Figure CN103043974BD00071

Claims (2)

1. 一种高耐磨水泥基自流平砂浆,其特征在于:其是由以下质量份的原料组成:1〇质 量份的40-70目的铁砂、25质量份的425#普硅水泥、4质量份的凯诺斯高铝水泥、4质量份 的UEA-H高效膨胀剂、4质量份的硬石膏粉、2质量份的ZJ6010可再分散乳胶粉、30质量份 的70-140目的石英砂、20质量份的400目的重I丐粉、0. 5质量份的减水剂F10、0. 1质量份 的HPMC纤维素醚、0. 2质量份的木质纤维素、0. 15质量份的消泡剂AGITANP803。
2. 制备权利要求1所述的一种高耐磨水泥基自流平砂浆的方法,其特征在于:包括以 下步骤: 1) 对铁砂进行防锈处理:将铁砂置于煮沸的浓度为5wt%的氢氧化钠溶液中lOmin,分 离出铁砂,烘干; 2) 将经过防锈处理的铁砂和自流平砂浆的其它组份按配比投入到混合釜中,搅拌 20-50分钟,出料包装即可。
CN201210515416.8A 2012-12-05 2012-12-05 一种高耐磨水泥基自流平砂浆及其制备方法 Active CN103043974B (zh)