CN101899899A - 外墙仿真石漆面层的施工方法 - Google Patents
外墙仿真石漆面层的施工方法 Download PDFInfo
- Publication number
- CN101899899A CN101899899A CN2009101434558A CN200910143455A CN101899899A CN 101899899 A CN101899899 A CN 101899899A CN 2009101434558 A CN2009101434558 A CN 2009101434558A CN 200910143455 A CN200910143455 A CN 200910143455A CN 101899899 A CN101899899 A CN 101899899A
- Authority
- CN
- China
- Prior art keywords
- spray
- type paint
- construction method
- stone
- spraying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种外墙仿真石漆面层的施工方法,主要工艺过程是将墙面清除干净,用聚合物砂浆将墙面、门窗口、麻面、风裂、接磋缝隙及破损处分别找平补好,干燥后用砂纸将凸起处磨平,涂封闭底漆两遍,弹分格线和分色线,用喷枪喷涂中层仿真石漆,涂抹两道,最后采用400-600目砂纸抹平仿真石漆表面凸起的砂粒即可。本施工方法简便快捷,施工后的涂层具有良好的附着性和抗冻融性能及颜色丰富持久、保色性能优异的特点,适合各类建筑物的室内外装饰装修。本施工方法还具有降低造价和节省石材资源的特点。
Description
技术领域
本发明涉及一种外墙喷涂施工方法,特别指外墙仿真石漆面层的施工方法。
背景技术
在民用建筑外墙装饰施工中,这几年仿真石漆涂料面层得到了广泛应用。涂层显天然石材的麻石质感和自然色泽生动逼真,具有庄重、典雅、和谐及回归大自然之感。而外墙仿真石漆面层的施工方法即成为十分重要的技术。为满足高档建筑装饰行业日益个性化发展的需要,如仿大理石,仿花岗石涂料的开发,就更加显示出喷涂工艺的重要性。只有研制更完善、更配套的施工工艺,才能充分展示出仿真石漆的独特外观及优越性能。
发明内容
本发明要解决的技术问题是提供一种外墙仿真石漆面层的施工方法,采用这种工艺方法精选天然岩石晶体颗粒及进口合成树脂乳液,参照花岗岩晶体结构加工,可塑出天然石材质感的水性建筑漆。
本发明要解决的技术问题由如下方案来实现:外墙仿真石漆面层的施工方法,其特征是:将墙面上的灰渣、油污清除干净,用聚合物砂浆将墙面、门窗口、麻面、风裂、接磋缝隙及破损处分别找平补好,干燥后用砂纸将凸起处磨平,涂封闭仿真石漆两遍,施工温度在10℃以上,喷涂量0.3-0.4kg/m2,弹分格线和分色线,用喷枪喷涂中层仿真石漆,喷涂压力0.5-1.0mPa/cm2,施工温度在10℃以上,厚度1-2mm,涂抹两道,间隔两小时,干燥24小时后打磨,在阴阳角裂缝处,用喷枪每隔半小时即表面干燥后,采取远距离快速散射喷涂两个面,一次次薄薄的覆喷直至盖住裂缝,让雾花的边缘扫入阴阳角,喷涂量3-5kg/m2,最后用400-600目砂纸抹平仿真石漆表面凸起的砂粒即可。
本发明还包括如下方案:所述弹分格线和分色线是先涂刷浅色涂料,后涂刷深色涂料,分格线条宽度为8mm-10mm。
本发明的优点是:本施工方法简便快捷,施工后的涂层防火、耐水、耐碱、耐污染、无毒无味,具有良好的附着性和抗冻融性能及颜色丰富持久、保色性能优异的特点,适合各类建筑物的室内外装饰装修,成为石材替代产品,是目前理想选择。本施工方法具有广阔的推广应用前景,还具有降低造价和节省石材资源的特点,这对于缓解资源紧张,减少环境污染具有重要意义。
附图说明
附图1是本施工方法的工艺流程图
具体实施方式
下面结合附图1举一实施例:施工底材及要求:基层处理后,适用于混凝土或水泥内外墙及砖墙体及石棉水泥板、木板、石膏板、聚氨酯泡沫板等底材。施工底材表面基层应平整、干净,并具有较好的强度,新墙体则应实干一个月,方可施工。旧墙翻新先要整平基层,除去松脱、剥落表层及粉尘油垢等杂质后方可施工。
1仿真石漆施工:
1)基层处理:将墙面上的灰渣与油污等杂物清理干净,用扫帚将墙面上浮土清扫干净。用聚合物砂浆或石膏腻子将墙面、门窗口、角等磕碰破损处、麻面、风裂、接磋缝隙等分别找平补好,干燥后用砂纸将凸起处磨平。
2)涂封闭仿真石漆底漆两遍:喷涂(刷涂、滚涂均可)用无气喷枪均匀薄喷两遍,施工温度10℃,喷涂量0.4kg/m2。
3)弹分格线和分色线:在涂仿真石漆前,弹分格线和分色线,先涂刷浅色涂料,后涂刷深色涂料。分格线条宽度为10mm。
4)喷涂中层仿真石漆:采用喷涂方法,喷涂压力在1.0mPa/cm2,根据样板要求选择合适喷嘴,施工温度在10℃,厚度2mm,涂抹两道,间隔两小时,干燥24小时后打磨。喷枪应垂直于待喷涂面施工,距离约60厘米。对于阴阳角施工过程中,喷涂时特别注意不能一次喷厚,采用薄喷多层法,即表面干燥后重喷,喷枪距离为80厘米,运动速度快,且不能垂直阴阳角喷,只能采用散射,即喷涂两个面,上雾花的边缘扫入阴阳角。喷涂量5kg/m2。
5)打磨:采用500目砂纸,轻轻抹平仿真石漆表面凸起的砂粒即可。注意用力不可太猛,否则会破坏漆膜,引起底部松动,严重时会造成附着力不良,仿真石漆脱落。
6)喷罩面漆:选用下壶喷枪,压力5kg/m2,施工温度不10℃,喷涂两遍,间隔2小时,厚度约30微米,完全干燥需7天。
7)处理分格线条:将分格缝两边的毛刺及飞溅物清理干净,用油刷或排笔将分格缝用高级涂料(一般醇酸漆涂料)涂刷。
2不同颜色仿真石漆施工:
1)白色、浅色的仿真石漆施工:
墙体先批刮一遍白水泥,要求平整、无明显批痕;或者直接涂刷有色液体底漆,再按规定喷涂中层、面层;
2)深色的仿真石漆施工:
底漆按规定喷涂,在施工中层时,只需薄喷一层,厚度控制在1mm再罩面。
3对于不同喷涂对象的仿真石漆施工:
1)砖形仿真石漆:先按要求设计好砖形尺寸,然后在已涂好底油的墙面用木框架做好砖形模型,在喷上仿真石漆,在仿真石漆还没有表干前取下木框即可。
2)垂直面喷涂:采用划圈法,距离40cm,以半径约15cm横向划圈喷涂,并不时上下抖动喷枪,这样喷速度快而均匀,且易控制。如果采用一排一排的主式重叠喷涂,速度慢,上下交接处难控制均匀,将影响外观,造成涂料缺陷。
3)罗马圆柱喷涂:因其是圆柱形,所以采用″M″线形喷涂,距离略远约40cm,喷枪要垂直柱面喷涂,自上而下,喷好一面再转向另一面,转向角度约60度为宜。
4)方形柱喷涂:方形柱棱角分明,很容易因喷涂不匀而使棱角模糊,为了喷涂方便,以约50cm的距离喷涂棱角,远距离喷涂,雾花散得开,面积大而均匀,如果距离太近,稍不注意就会喷厚,喷不均匀,使棱角线条显现不出来,失去了原有建筑的整体外观美感。
5)圆柱形小葫芦喷涂:现代建筑采用圆柱形小葫芦做栏杆装饰,大都要求喷上仿真石漆,因其小巧玲珑,极具装饰性,对它们的喷涂工艺也更为细致。做栏杆装饰的葫芦柱,距离太近,有些地方根本无法正面喷涂,所以按一般常规喷法是无法达到理想效果的。喷涂选用小喷嘴,距离约40cm,快速散喷仿真石漆,自上而下一面一面来喷,不能正面喷涂的,用抖动喷枪的方法,令其周围尽量喷上仿真石漆,然后用毛刷刷平仿真石漆,没有喷到的地方也可以用毛刷略微抹上一层,再用喷枪散喷一遍,不能太薄,也不能太厚,盖住刷痕即可,薄了不能起到很好的保护效果,厚了则遮盖住了原有的线条美感,也可能出现裂缝等不良表面现象。
Claims (2)
1.外墙仿真石漆面层的施工方法,其特征是:将墙面上的灰渣、油污清除干净,用聚合物砂浆将墙面、门窗口、麻面、风裂、接磋缝隙及破损处分别找平补好,干燥后用砂纸将凸起处磨平,涂封闭仿真石漆两遍,施工温度在10℃以上,喷涂量0.3-0.4kg/m2,弹分格线和分色线,用喷枪喷涂中层仿真石漆,喷涂压力0.5-1.0mPa/cm2,施工温度在10℃以上,厚度1-2mm,涂抹两道,间隔两小时,干燥24小时后打磨,在阴阳角裂缝处,用喷枪每隔半小时即表面干燥后,采取远距离快速散射喷涂两个面,一次次薄薄的覆喷直至盖住裂缝,让雾花的边缘扫入阴阳角,喷涂量3-5kg/m2,最后用400-600目砂纸抹平仿真石漆表面凸起的砂粒即可。
2.根据权利要求1所述的外墙仿真石漆面层的施工方法,其特征是:所述弹分格线和分色线是先涂刷浅色涂料,后涂刷深色涂料,分格线条宽度为8mm-10mm。