CN101879433B - 改性水淬渣吸附剂及其制备方法 - Google Patents

改性水淬渣吸附剂及其制备方法 Download PDF

Info

Publication number
CN101879433B
CN101879433B CN201010231112XA CN201010231112A CN101879433B CN 101879433 B CN101879433 B CN 101879433B CN 201010231112X A CN201010231112X A CN 201010231112XA CN 201010231112 A CN201010231112 A CN 201010231112A CN 101879433 B CN101879433 B CN 101879433B
Authority
CN
China
Prior art keywords
water quenching
quenching slag
adsorbent
improved water
improved
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201010231112XA
Other languages
English (en)
Other versions
CN101879433A (zh
Inventor
陈莉荣
张连科
贾飞虎
李玉梅
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Inner Mongolia University of Science and Technology
Original Assignee
Inner Mongolia University of Science and Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Inner Mongolia University of Science and Technology filed Critical Inner Mongolia University of Science and Technology
Priority to CN201010231112XA priority Critical patent/CN101879433B/zh
Publication of CN101879433A publication Critical patent/CN101879433A/zh
Application granted granted Critical
Publication of CN101879433B publication Critical patent/CN101879433B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种改性水淬渣吸附剂及其制备方法，属于工业废水的治理领域。本发明按重量百分比计：高炉水淬渣93.5-96.7％、硫酸铈1.4-2.8％、氯化铁1.9-3.7％，制备方法如下：高炉水淬渣用水冲洗干净，烘干，研磨后过100目筛，将处理过的高炉水淬渣与硫酸铈、氯化铁混合，搅拌均匀，用水润湿，再搅拌均匀，烘干，研磨、过100目筛，筛分后的混合物置马弗炉中500℃-600℃温度焙烧处理1-2h，既得改性水淬渣吸附剂。本发明原料采用工业废弃物，降低生产成本，处理效果较好、易操作。本发明表面包覆有铁铈涂层，提高了其比表面积和吸附能力，在室温时，pH＝3-10范围内，能有效吸附水体中的铜离子和氨氮。

Description

改性水淬渣吸附剂及其制备方法
技术领域
本发明涉及一种改性水淬渣吸附剂及其制备方法，属于工业废水的治理领域。
背景技术
目前用来处理废水的吸附剂主要是活性炭及离子交换树脂，这些吸附剂处理成本高。
发明内容
本发明提供一种能够有效提高了吸附剂比表面积，吸附能力强，生产成本低的改性水淬渣吸附剂及其制备方法。
技术解决方案：本发明以高炉水淬渣为原料，以氯化铁和硫酸铈为改性剂，按重量百分比计：高炉水淬渣93.5-96.7％、硫酸铈1.4-2.8％、氯化铁1.9-3.7％。
本发明改性水淬渣吸附剂的制备方法如下：
1)高炉水淬渣用水反复冲洗3-4次，然后置于烘箱中烘干，经研钵充分研磨后过100目分样筛进行筛分；
2)将步骤1)预处理过的高炉水淬渣与硫酸铈、氯化铁按重量百分比：高炉水淬渣93.5-96.7％、硫酸铈1.4-2.8％、氯化铁1.9-3.7％进行混合，充分搅拌均匀，用水将上述混合物充分润湿，按重量比混合物∶水＝1∶0.5-1，再搅拌均匀，然后将充分湿润后的混合物置于烘箱中烘干；
3)利用研钵将步骤2)烘干后的混合物充分研磨，过100目分样筛进行筛分，将筛分后的混合物置于马弗炉中于500℃-600℃温度下进行焙烧处理1-2h，既得改性水淬渣吸附剂。
本发明原料采用工业废弃物，降低生产成本，处理效果较好、易操作。由于本发明表面包覆有铁铈涂层，有效地提高了其比表面积和吸附能力，在室温时，pH＝3-10范围内，能有效吸附水体中的铜离子和氨氮。
附图说明
图1本发明的表面扫描电镜图。
图2本发明的XRD图谱。
具体实施方式
实施例1：本发明原料取自包头钢铁集团公司炼铁厂第四号高炉的高炉水淬渣，制备方法如下：1)将高炉水淬渣用水反复冲洗3-4次，然后置于烘箱中于100℃温度下烘干，经研钵充分研磨后过100目分样筛进行筛分。2)取步骤1)预处理过的高炉水淬渣100g与1.5g硫酸铈和2g氯化铁混合，充分搅拌均匀，并且用80g水对该混合物进行充分润湿，再搅拌均匀，然后将充分湿润后的混合物置于烘箱中于100℃温度下烘干。3)将步骤2)烘干后的混合物充分研磨均匀，然后过100目分样筛进行筛分，筛分后的混合物置于马弗炉中于500℃温度下进行焙烧处理1-2h，既得改性水淬渣吸附剂。在pH＝8的条件下，称取制得的改性水淬渣吸附剂1g加入到100mL含铜废水中，含铜废水的浓度为20mg/L，置于振荡器上振荡处理1h，铜去除率可达97.1％；在pH＝8的条件下，称取制得的改性水淬渣吸附剂1g加入到100mL氨氮废水中，氨氮废水的浓度为127mg/L，置于振荡器上，振荡处理1h，氨氮去除率可达83.4％。
实施例2：本发明原料取自包头钢铁集团公司炼铁厂第四号高炉的高炉水淬渣，制备方法如下：1)将高炉水淬渣用水反复冲洗3-4次，然后置于烘箱中于100℃温度下烘干，经研钵充分研磨后过100目分样筛进行筛分。2)取步骤1)预处理过的原水淬渣100g与3g硫酸铈和4g氯化铁混合，充分搅拌均匀，并且用85g水对该混合物进行充分润湿，再搅拌均匀，然后将充分湿润后的混合物置于烘箱中于100℃温度下烘干；3)利用研钵对步骤2)烘干后的混合物充分研磨均匀，然后过100目分样筛进行筛分，将筛分后的混合物置于马弗炉中于500℃温度下进行焙烧处理1-2h，既得改性水淬渣吸附剂。在pH＝8的条件下，称取制得的改性水淬渣吸附剂1g加入到100mL含铜废水中，含铜废水浓度为20mg/L，置于振荡器上振荡处理1h，铜去除率可达96.6％；在pH＝8的条件下，称取制得的改性水淬渣吸附剂1g加入到100mL氨氮废水中，氨氮废水的浓度127mg/L，置于振荡器上振荡处理1h，氨氮去除率可达81％。

Claims (1)

1.改性水淬渣吸附剂，其特征是：以高炉水淬渣为原料，以氯化铁和硫酸铈为改性剂，吸附剂制备方法如下：1)高炉水淬渣用水反复冲洗3-4次，然后置于烘箱中烘干，经研钵充分研磨后过100目分样筛进行筛分；2)将步骤1)预处理过的高炉水淬渣与硫酸铈、氯化铁按重量百分比：高炉水淬渣93.5-96.7％、硫酸铈1.4-2.8％、氯化铁1.9-3.7％进行混合，充分搅拌均匀，用水将混合物充分润湿，按重量比混合物∶水＝1∶0.5-1，再搅拌均匀，然后将充分湿润后的混合物置于烘箱中烘干；3)利用研钵对步骤2)烘干后的混合物充分研磨后过100目分样筛进行筛分，将筛后的混合物置于马弗炉中于500℃-600℃温度下进行焙烧处理1-2h，即得改性水淬渣吸附剂。
CN201010231112XA 2010-07-10 2010-07-10 改性水淬渣吸附剂及其制备方法 Expired - Fee Related CN101879433B (zh)