CN101831110B - 一种可高频焊接的聚丙烯复合材料及其制备方法 - Google Patents
一种可高频焊接的聚丙烯复合材料及其制备方法 Download PDFInfo
- Publication number
- CN101831110B CN101831110B CN2010101596216A CN201010159621A CN101831110B CN 101831110 B CN101831110 B CN 101831110B CN 2010101596216 A CN2010101596216 A CN 2010101596216A CN 201010159621 A CN201010159621 A CN 201010159621A CN 101831110 B CN101831110 B CN 101831110B
- Authority
- CN
- China
- Prior art keywords
- composite material
- districts
- frequency welding
- polypropylene
- wax
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Description
原料名称及物性参数 | 实例1 | 实例2 | 实例3 | 实例4 | 实例5 | 实例6 | 实例7 |
聚丙烯树脂(质量份数) | 100 | 100 | 100 | 100 | 100 | 100 | 100 |
主改性剂(质量份数) | 25 | 50 | 100 | 100 | 75 | 50 | 25 |
相容剂(质量份数) | 3 | 5 | 10 | 10 | 8 | 5 | 3 |
填充剂(质量份数) | 0 | 25 | 50 | 50 | 40 | 20 | 0 |
润滑剂(质量份数) | 0.5 | 0.5 | 1.0 | 0.5 | 0.8 | 0.6 | 0.5 |
抗氧剂(质量份数) | 0.2 | 0.2 | 0.4 | 0.6 | 0.4 | 0.3 | 0.2 |
拉伸强度(MPa) | 38 | 47 | 58 | 16 | 18 | 19 | 20 |
弯曲强度(MPa) | 57 | 64 | 77 | 22 | 24 | 25 | 24 |
IZOD缺口冲击强度(KJ/M2) | 40 | 55 | 60 | 26 | 23 | 22 | 20 |
焊接件的拉伸断口 | 焊接区外 | 焊接区外 | 焊接区外 | 焊接区外 | 焊接区外 | 焊接区外 | 焊接区外 |
Claims (5)