CN101781821A - 聚四氟乙烯/玻璃纤维包芯线及其生产方法 - Google Patents
聚四氟乙烯/玻璃纤维包芯线及其生产方法 Download PDFInfo
- Publication number
- CN101781821A CN101781821A CN200910155621A CN200910155621A CN101781821A CN 101781821 A CN101781821 A CN 101781821A CN 200910155621 A CN200910155621 A CN 200910155621A CN 200910155621 A CN200910155621 A CN 200910155621A CN 101781821 A CN101781821 A CN 101781821A
- Authority
- CN
- China
- Prior art keywords
- polytetrafluoroethylene
- glass fiber
- spun yarn
- ptfe
- fiber core
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
聚四氟乙烯/玻璃纤维包芯线由玻璃纤维的芯和包覆在该芯外表面上的聚四氟乙烯包覆层构成。其生产方法是，先在玻璃纤维表面上涂覆聚四氟乙烯涂料，再通过刮涂器进行刮涂，然后将涂覆聚四氟乙烯涂料的玻璃纤维引入烘箱，进行烧结，即制成聚四氟乙烯/玻璃纤维包芯线。涂覆-刮涂-烧结生产过程可以重复进行1～10次。聚四氟乙烯/玻璃纤维包芯线的外层是聚四氟乙烯，因此具有良好的耐腐蚀性、热稳定性和耐气候性以及自洁性；同时它的芯线又是玻璃纤维，有着较好的力学性能。
Description
技术背景
聚四氟乙烯纤维具有优良的耐腐蚀性、热稳定性和耐气候性，高的绝缘性和自洁性，极小的吸水性，透光性好，无毒害等优点，被广泛用于张拉膜，除尘和过滤织物等。但是其强度低、价格高，织造等后续加工困难，这些缺陷在一定程度上限制了它的广泛应用。玻璃纤维具有较好的力学性能且价格低廉，但是玻璃纤维的耐腐蚀性、热稳定性和耐气候性以及自洁性和透光性等方面远不及聚四氟乙烯，这些不足也制约了玻璃纤维在更多领域的推广应用。
技术领域
本发明涉及一种纤维及其生产方法，尤其是，涉及聚四氟乙烯/玻璃纤维包芯线及其生产方法。
发明内容
本发明的目的是提供一种聚四氟乙烯/玻璃纤维包芯线及其生产方法，使该纤维能兼具玻璃纤维和聚四氟乙烯纤维的优点，同时又能克服它们的缺点。
本发明是通过以下技术方案实现的，聚四氟乙烯/玻璃纤维包芯线由玻璃纤维的芯和包覆在该芯外表面上的聚四氟乙烯包覆层构成。所述的包覆层的厚度为2～200微米。
聚四氟乙烯/玻璃纤维包芯线的生产方法是，先在玻璃纤维表面上涂覆聚四氟乙烯涂料，再通过模具进行刮涂，然后将涂覆聚四氟乙烯涂料的玻璃纤维引入烘箱，进行烧结，即制成聚四氟乙烯/玻璃纤维包芯线。所述的涂覆-刮涂-烧结生产过程可以进行1～10次。
所述的聚四氟乙烯涂料是水性聚四氟乙烯防粘涂料。
所述的烧结的温度是265～315℃。
所述的烧结时间是20～50秒。
所述的刮涂器的内孔为锥孔；锥孔出口处的直径比待刮涂的玻璃纤维直径大2～100微米。
本发明的有益效果是，聚四氟乙烯/玻璃纤维包芯线的外层是聚四氟乙烯，因此具有良好的耐腐蚀性、热稳定性、耐气候性和自洁性；同时它的芯线又是玻璃纤维，从而又有着较好的力学性能。
附图说明
图1是聚四氟乙烯/玻璃纤维包芯线的横截面图。
图2是刮涂器的示意图。
图3是涂覆-刮涂-烧结过程的示意图
具体实施方式
下面结合实施例对本发明作进一步的描述。
实施例
如图3，直径为0.32毫米的玻璃纤维从储线器31上退出，在牵引罗拉32的拉动下穿过涂布器33，使之在玻璃纤维表面上涂上水性聚四氟乙烯高温防粘涂料，然后将涂布后的玻璃纤维引人刮涂器34，使得玻璃纤维表面的聚四氟乙烯涂料均匀地分布在玻璃纤维的表面上，使涂层的厚度均匀化。然后对引入烘箱37的涂覆聚四氟乙烯的玻璃纤维进行烧结，烧结的温度为285℃，烧结时间为30秒。把烧结后的聚四氟乙烯/玻璃纤维包芯线通过罗拉35，引入收卷装置36，进行收卷。
为了使涂层更为均匀，且具有一定厚度，在本例中，上述的涂覆-刮涂-烧结过程重复3次。如图2所示，各次的刮涂器21的出口处22的尺寸分别如下：(1)0.32毫米；(2)0.35毫米；(3)0.39毫米。烧结的时间和温度都相同。
如图1所示，经检测，聚四氟乙烯/玻璃纤维包芯线最终的平均直径为0.372毫米，即聚四氟乙烯包覆层11的厚度为0.052毫米，作为芯线的玻璃纤维12的直径仍为0.32毫米。
Claims (8)
1.聚四氟乙烯/玻璃纤维包芯线，其特征是，所述的聚四氟乙烯/玻璃纤维包芯线由玻璃纤维的芯和包覆在该芯外表面上的聚四氟乙烯包覆层构成。
2.根据权利要求1所述的聚四氟乙烯/玻璃纤维包芯线，所述的包覆层的厚度为2～200微米。
3.聚四氟乙烯/玻璃纤维包芯线的生产方法，其特征是，生产步骤如下，先在玻璃纤维表面上涂覆聚四氟乙烯涂料，再通过刮涂器进行刮涂，然后将涂覆聚四氟乙烯涂料的玻璃纤维引入烘箱，进行烧结，即制成聚四氟乙烯/玻璃纤维包芯线。
4.根据权利要求3所述的聚四氟乙烯/玻璃纤维包芯线的生产方法，所述的涂覆-刮涂-烧结生产过程可以重复进行1～10次。
5.根据权利要求3所述的聚四氟乙烯/玻璃纤维包芯线的生产方法，所述的聚四氟乙烯涂料是水性聚四氟乙烯防粘涂料。
6.根据权利要求3所述的聚四氟乙烯/玻璃纤维包芯线的生产方法，所述的烧结的温度是265℃～315℃。
7.根据权利要求3所述的聚四氟乙烯/玻璃纤维包芯线的生产方法，所述的烧结时间是20～50秒。
8.根据权利要求3所述的聚四氟乙烯/玻璃纤维包芯线的生产方法，所述的刮涂器的内孔为锥孔；锥孔出口处的直径比待刮涂的玻璃纤维直径大2～100微米。