CN101775629A - 铁-镍-钼软磁合金箔生产电镀液 - Google Patents

铁-镍-钼软磁合金箔生产电镀液 Download PDF

Info

Publication number
CN101775629A
CN101775629A CN 201010122012 CN201010122012A CN101775629A CN 101775629 A CN101775629 A CN 101775629A CN 201010122012 CN201010122012 CN 201010122012 CN 201010122012 A CN201010122012 A CN 201010122012A CN 101775629 A CN101775629 A CN 101775629A
Authority
CN
China
Prior art keywords
nickel
iron
molybdenum alloy
solution
electroplating solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201010122012
Other languages
English (en)
Inventor
乔瀚文
赵汝山
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 201010122012 priority Critical patent/CN101775629A/zh
Publication of CN101775629A publication Critical patent/CN101775629A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种铁-镍-钼软磁合金箔生产电镀液，属于材料表面处理领域中的合金电镀液，该电镀液的配方如下：硫酸镍：80～150克/升；钼酸钠：5～10克/升；硫酸亚铁：30～90克/升；硫酸铵：20～40克/升；络合剂：40～65克/升；光亮添加剂：2～5毫升/升；加去离子水至1000毫升；所述的络合剂为柠檬酸和乳酸的混合物；所述的光亮添加剂为1，4丁炔二醇和二甲基己炔醇的混合物。通过该电镀液及工艺可以得到任意长度和宽度的铁镍钼合金箔，该合金箔是一种优异的软磁材料，其中饱和磁感应强度FluxDensity(Gauss)在10000Gs左右；有效磁导率范围μe＝10～780；温度稳定性极佳。

Description

铁-镍-钼软磁合金箔生产电镀液
技术领域
本发明涉及材料表面处理领域中的合金电镀液，具体地说是一种铁-镍-钼软磁合金箔生产电镀液。
背景技术
随着电子信息产业的飞速发展，世界对软磁铁氧体的需求将不断增加，每年保持10％～15％的增长率水平。其中主要来自于对高档产品的需求的增长，低档产品的需求将保持较为稳定的趋势。这主要是由于未来电子产品向小型化、贴片化、低功耗化发展，这就要求磁性材料功耗越来越低、工作频率越来越高、体积越来越小。铁镍钼合金具备优异的磁性能，现在有通过将铁、镍、钼金属粉混合一些绝缘物质(二氧化硅)做成高性能的复合软磁材料，该工艺得到的铁镍钼合金粉，受到厚度、机械强度、生产成本等因素的影响，大大降低了使用领域。目前亚微米级别厚度的铁镍钼合金箔还没有合适的技术生产。
发明内容
本发明的技术任务是提供一种铁-镍-钼软磁合金箔生产电镀液。
本发明的技术任务是按以下方式实现的，该电镀液的配方如下：
硫酸镍：80～150克/升； 钼酸钠：5～10克/升；
硫酸亚铁：30～90克/升；硫酸铵：20～40克/升；
络合剂：40～65克/升；  光亮添加剂：2～5毫升/升；
加去离子水至1000毫升；
所述的络合剂为柠檬酸和乳酸的混合物；
所述的光亮添加剂为1，4丁炔二醇和二甲基己炔醇的混合物；
加工方法如下：
称取适量的络合剂，加入去离子水，搅拌至溶解；然后加入适量的硫酸镍、硫酸亚铁和硫酸铵，在常温下搅拌至溶解；然后将上述溶液用水浴锅加热至55～75℃，再称取适量钼酸钠加入到该溶液中，搅拌至溶解；然后加入适量的光亮剂，用氢氧化钠溶液调节上述溶液的pH值；之后再用水浴锅加热至55～75℃，用不锈钢网做阳极，钛轮做阴极，在电流密度为30～70A/dm2下进行电镀，电镀5～30分钟后，即可从钛轮上剥离5～100微米厚度的铁镍钼合金箔。
所述的用氢氧化钠溶液调节溶液的pH值为5～6。
所述的络合剂为柠檬酸、乳酸按质量比为6∶1的混合物。
本发明的铁-镍-钼软磁合金箔生产电镀液对环境危害小，工艺稳定，镀液组分简单且便于操作，配置后可以长期存放。通过该电镀液及工艺可以得到5-100微米厚度，任意长度和宽度的铁镍钼合金箔，该合金箔是一种优异的软磁材料，综合性能优于钼坡莫合金粉芯(MPP)，制作成本远低于钼坡莫合金粉芯(MPP)，其中饱和磁感应强度Flux Density(Gauss)在10000Gs左右；有效磁导率范围μe＝10～780；温度稳定性极佳，可应用于300kHz以下的高品质因素Q滤波器、感应负载线圈、谐振电路、在对温度稳定性要求高的LC电路上常用、输出电感、功率因素补偿电路等。
具体实施方式
实施例1：
称取42g柠檬酸、7g乳酸加入到500ml去离子水中，搅拌至溶解；然后加入80g硫酸镍、30g硫酸亚铁和20g硫酸铵，在常温下搅拌至溶解；然后将上述溶液用水浴锅加热至55℃，再称取5g钼酸钠加入到该溶液中，搅拌至溶解；然后加入2ml1，4丁炔二醇和二甲基己炔醇的混合物，再加入去离子水至溶液为1000ml，用氢氧化钠溶液调节上述溶液的pH值为5；之后再用水浴锅加热至55℃，用不锈钢网做阳极，钛轮做阴极，在电流密度为30A/dm2下进行电镀，电镀5分钟后，即可从钛轮上剥离5微米厚度的铁镍钼合金箔。
实施例2：
称取48g柠檬酸、8g乳酸加入到500ml去离子水中，搅拌至溶解；然后加入115g硫酸镍、60g硫酸亚铁和30g硫酸铵，在常温下搅拌至溶解；然后将上述溶液用水浴锅加热至60℃，再称取7g钼酸钠加入到该溶液中，搅拌至溶解；然后加入4ml1，4丁炔二醇和二甲基己炔醇的混合物，再加入去离子水至溶液为1000ml，用氢氧化钠溶液调节上述溶液的pH值为5.5；之后再用水浴锅加热至60℃，用不锈钢网做阳极，钛轮做阴极，在电流密度为50A/dm2下进行电镀，电镀10分钟后，即可从钛轮上剥离15微米厚度的铁镍钼合金箔。
实施例3：
称取54g柠檬酸、9g乳酸加入到500ml去离子水中，搅拌至溶解；然后加入150g硫酸镍、90g硫酸亚铁和40g硫酸铵，在常温下搅拌至溶解；然后将上述溶液用水浴锅加热至75℃，再称取10g钼酸钠加入到该溶液中，搅拌至溶解；然后加入5ml1，4丁炔二醇和二甲基己炔醇的混合物，再加入去离子水至溶液为1000ml，用氢氧化钠溶液调节上述溶液的pH值为6；之后再用水浴锅加热至75℃，用不锈钢网做阳极，钛轮做阴极，在电流密度为70A/dm2下进行电镀，电镀30分钟后，即可从钛轮上剥离100微米厚度的铁镍钼合金箔。

Claims (3)

1.铁-镍-钼软磁合金箔生产电镀液，该电镀液的配方如下：
硫酸镍：80～150克/升；     钼酸钠：5～10克/升；
硫酸亚铁：30～90克/升；    硫酸铵：20～40克/升；
络合剂：40～65克/升；      光亮添加剂：2～5毫升/升；
加去离子水至1000毫升；
所述的络合剂为柠檬酸和乳酸的混合物；
所述的光亮添加剂为1，4丁炔二醇和二甲基己炔醇的混合物；
加工方法如下：
称取适量的络合剂，加入去离子水，搅拌至溶解；然后加入适量的硫酸镍、硫酸亚铁和硫酸铵，在常温下搅拌至溶解；然后将上述溶液用水浴锅加热至55～75℃，再称取适量钼酸钠加入到该溶液中，搅拌至溶解；然后加入适量的光亮剂，用氢氧化钠溶液调节上述溶液的pH值；之后再用水浴锅加热至55～75℃，用不锈钢网做阳极，钛轮做阴极，在电流密度为30～70A/dm2下进行电镀，电镀5～30分钟后，即可从钛轮上剥离5～100微米厚度的铁镍钼合金箔。
2.根据权利要求1所述的铁-镍-钼软磁合金箔生产电镀液，其特征在于所述的用氢氧化钠溶液调节溶液的pH值为5～6。
3.根据权利要求1所述的铁-镍-钼软磁合金箔生产电镀液，其特征在于所述的络合剂为柠檬酸、乳酸按质量比为6∶1的混合物。
CN 201010122012 2010-03-11 2010-03-11 铁-镍-钼软磁合金箔生产电镀液 Pending CN101775629A (zh)