CN101760826A - Cashmere, triangular terylene and cation-modified terylene blended yarn and technology thereof - Google Patents
Cashmere, triangular terylene and cation-modified terylene blended yarn and technology thereof Download PDFInfo
- Publication number
- CN101760826A CN101760826A CN200910182607A CN200910182607A CN101760826A CN 101760826 A CN101760826 A CN 101760826A CN 200910182607 A CN200910182607 A CN 200910182607A CN 200910182607 A CN200910182607 A CN 200910182607A CN 101760826 A CN101760826 A CN 101760826A
- Authority
- CN
- China
- Prior art keywords
- terylene
- cashmere
- yarn
- cation
- modified
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides cashmere, triangular terylene and cation-modified terylene blended yarn and a technology thereof, belonging to the field of spinning. By blending with the cashmere, the triangular terylene and the cation-modified terylene, the fabric not only has comfortable hand feel as the cashmere but also has good visual effect. The cashmere, triangular terylene and cation-modified terylene blended yarn consists of the cashmere, the cation-modified terylene and the triangular cross-section terylene, and is characterized in that the components has the following weight percentage: 60-70% of the cashmere, 25-30% of the triangular cross-section terylene, 5-10% of the triangular cross-section terylene, and 2/26 Nm of the numbers of the yarn. The processing method of the yarn comprises the steps of: blending; removing the static with blending oil and a small quantity of antistatic agent; adding oil water on the cashmere; simmering for 12-24h and layering with the terylene; looming and regaining moisture at 17-19%; carding; controlling the humiture of a workshop, wherein the spring, the temperature of autumn and the winter is higher than 20 DEG C, the temperature of summer is lower than 32 DEG C, and the humidity is controlled at 65-75%; adjusting the technological parameter, wherein the gauge is large and the speed ratio is small; splitting, splitting standard yarn, heavy yarn and light yarn, and cutting the exceeded range to be taken as hard waste; spooling, and connecting heads with an air yarn joiner; joining the yarn; and obtaining a final product, and the moisture regaining is controlled at 11-13%.
Description
Technical field
The invention belongs to cashmere spinning field, a kind of specifically cashmere, triangle polyester and cation-modified dacron blended yarn and processing method.
Background technology
Cashmere is commonly called as " soft gold ", is a kind of textile raw material of top grade, and its fabric feeling is abundant, and lubricated as silk is with in gentle toughly, and resilience, warmth retention property are good.Special polyester, promptly the triangular-section terylene is a kind of special-shaped fibre in differentiation.Produce flash effect because of the angle of incidence of light degree is different, make human eye accept different optical signallings and produce good visual experience in different angles, have the gloss of soft elegant silkiness, style is solely different.Opposite sex terylene, promptly cation-modified terylene can boil at normal temperatures and dye, and realizes the co-bathing dyeing with wool.Cation-modified terylene spectral range is wide, dyes and looks for coloured silk more bright-coloured, and gloss is soft naturally, and this kind terylene has unique feel, and is well-pressed soft again.With cashmere and triangle polyester and cation-modified blend polyester, both kept the soft glutinous smooth hand feeling of fleece fabrics, overcome the mashed sense of drifting of the excessive pine of pure fleece fabrics again, strengthened the body bone of fabric, make the visual effect of fleece fabrics bright and colourful, utilize the colouring of cation-modified terylene and triangular-section terylene, because of color development effect difference, cloth cover is tangible mixed color effect then.
Summary of the invention
The present invention be directed to deficiency of the prior art, a kind of cashmere and polyester blended fabric and processing technology are provided,, make the abundant feel of the existing cashmere of fabric that good visual effect be arranged again by cashmere and triangle polyester and cation-modified blend polyester.
The present invention realizes by following technology, and a kind of cashmere and triangle polyester and cation-modified dacron blended yarn are made up of cashmere, cation-modified terylene and triangle section terylene, it is characterized in that by weight:
Cashmere: 60-70%
Cation-modified terylene: 25-30%
Triangular-section terylene: 5-10%
Yam count: 2/26Nm.
Above-mentioned cashmere and triangle polyester and cation-modified dacron blended yarn are made by following technology
(1) and hair: with and crude oil and a spot of antistatic additive remove static, profit is added on the cashmere, stewing hair 12-24 hour again with terylene shop layer, the last machine 17-19% that gets damp again;
(2) carding: the control workshop moisture temperature, are greater than 20 ℃ in spring, autumn, winter, be less than 32 ℃ summer, humidity is controlled at 65-75%, and technological parameter spaces greatly, little speed ratio;
(3) dividing sinker: divide standard yarn, heavy yarn, fine gauze;
(4) winder: with air splicer joint;
(5) piece together line;
(6) double twisting;
(7) finished product: moisture regain is controlled at 11-13%.
The specific embodiment:
One, select cashmere and triangle polyester and cation-modified terylene, proportioning raw materials is as follows:
Two, yam count: 2/26Nm
Three, processing method
(1) and the hair: the easy static electrification of raw material, spin star FX902 and crude oil with Beijing, suitably add a spot of antistatic additive again and remove static, profit is added on the cashmere, cashmere and antistatic additive and and the weight ratio of crude oil be: 100: 2-4: the stewing hair of 2-4 15 hours again with terylene shop layer, the last machine 17-19% that gets damp again;
(2) carding: guarantee that equipment state is good; Rubbing plate, leather strap quality homogeneous, the leather strap smooth surface, uniform tension in order, the washboard frictional behaviour is good; The control workshop moisture temperature, spring, autumn, season are higher than 20 ℃ of summers winter less than 32 ℃ at 22-25 ℃,, humidity is controlled at 65-75%, and technological parameter spaces greatly, little speed ratio;
(3) dividing sinker: divide standard yarn, heavy yarn, fine gauze;
(4) winder: with air splicer joint;
(5) piece together line; Control tension force, the size that is shaped is consistent, with air splicer joint;
(6) double twisting;
(7) make finished product: moisture regain is controlled at 11-13%.
Claims (2)
1. cashmere and triangle polyester and cation-modified dacron blended yarn are made up of cashmere, cation-modified terylene and triangle section terylene, it is characterized in that by weight:
Cashmere: 60-70%
Cation-modified terylene: 25-30%
Triangular-section terylene: 5-10%
Yam count: 2/26Nm.
2. cashmere according to claim 1 and triangle polyester and cation-modified dacron blended yarn is characterized in that being made by following technology:
(1) and hair: with and crude oil and a spot of antistatic additive remove static, profit is added on the cashmere, stewing hair 12-24 hour again with terylene shop layer, the last machine 17-19% that gets damp again;
(2) carding: the control workshop moisture temperature, spring, autumn, season are higher than 20 ℃ of summers winter less than 32 ℃ at 22-25 ℃, and humidity is controlled at 65-75%, and technological parameter spaces greatly, little speed ratio;
(3) dividing sinker: divide standard yarn, heavy yarn, fine gauze;
(4) winder: with air splicer joint;
(5) piece together line;
(6) double twisting;
(7) finished product: moisture regain is controlled at 11-13%.