CN101747116A - 一种控制磷酸二铵颜色的方法 - Google Patents

一种控制磷酸二铵颜色的方法 Download PDF

Info

Publication number
CN101747116A
CN101747116A CN200910273235A CN200910273235A CN101747116A CN 101747116 A CN101747116 A CN 101747116A CN 200910273235 A CN200910273235 A CN 200910273235A CN 200910273235 A CN200910273235 A CN 200910273235A CN 101747116 A CN101747116 A CN 101747116A
Authority
CN
China
Prior art keywords
phosphoric acid
diammonium phosphate
product
phosphate
slag
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN200910273235A
Other languages
English (en)
Other versions
CN101747116B (zh
Inventor
王仁宗
陈君
刘裕
阮自斌
李淑华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hubei Fubang New Material Co., Ltd
Original Assignee
HUBEI FUBANG CHEMICAL SCIENCE-TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HUBEI FUBANG CHEMICAL SCIENCE-TECHNOLOGY Co Ltd filed Critical HUBEI FUBANG CHEMICAL SCIENCE-TECHNOLOGY Co Ltd
Priority to CN200910273235A priority Critical patent/CN101747116B/zh
Publication of CN101747116A publication Critical patent/CN101747116A/zh
Application granted granted Critical
Publication of CN101747116B publication Critical patent/CN101747116B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种控制磷酸二铵颜色的方法，在湿法磷酸生产磷酸二铵过程中，在磷矿石中添加占磷矿石重量的0.1％-20％的烧渣或在磷酸中的添加占磷酸重量的0.1％-10％的烧渣，最后得到黄色的磷酸二铵，所述的烧渣为硫铁矿制酸过程中产生的副产品，主要成分是三氧化二铁，并含有铜、铅、钙、镁金属离子及硅、硫、磷杂质。本发明主要通过在磷矿石或磷酸中添加烧渣，使制备的磷酸二铵的颜色呈黄色，改变磷铵料浆的性质，改变造粒状况，提高造粒出料成球率，使产品结晶感得到加强，产品圆润度得到提高，产品颜色一致且稳定，产品的着色效果得到提高且不需要内着色剂和外包裹油。

Description

一种控制磷酸二铵颜色的方法
技术领域
本发明涉及化肥颜色领域，特别是涉及一种用于磷酸二铵化肥黄色控制领域。
背景技术
磷酸二铵生产工艺中，由于磷矿石中杂质元素的组成不同，不同地域的磷矿石经湿法磷酸工艺生产出来的磷酸二铵的颜色及成粒效果不同。工业化生产磷酸二铵随着磷精矿中杂质含量的变化，浓磷酸的杂质含量随之而变，磷酸二铵中和料浆的性质也随之改变，从而其颜色及成粒效果也随之而变。纯净的磷酸做出的磷酸二铵一般为白色，没有结晶感。
磷精矿中杂质离子主要是Fe3+、Mg2+、Al3+、Si4+、S2-等离子。因为有杂质离子的存在，磷酸二铵的造粒及颜色是不同的。不同的杂质离子会使磷酸二铵产品呈现出不同的颜色，如黄色、灰色、淡绿色等。这些颜色的存在，使磷酸二铵产品的外观不一致。为了使产品外观、颜色一致，一般采用着色剂将磷酸二铵颗粒进行染色和包裹。
铁等杂质离子存在并在一定范围内时，对磷酸二铵的造粒有帮助，使产品结晶体有刚性和透明感。在磷酸二铵生产过程中发现磷精矿中的杂质含量指数由10～12％下降至7～8％时，其造粒成粒状况较差，产品无结晶感，造粒出料粒级分布差且难以控制稳定，给磷酸二铵的生产和产品质量造成很大的影响。
而在磷精矿或者磷酸中添加金属杂质，以改变磷铵料浆的性质，改变造粒状况，提高造粒出料成球率，使产品结晶感得到加强，产品圆润度得到提高，产品颜色一致且稳定。同时使产品的着色效果得到提高，且内着色剂和外包裹油消耗均有降低。
发明内容
本发明的目的提供一种控制磷酸二铵颜色的方法，本方法主要通过在磷矿石或磷酸中添加烧渣，使制备的磷酸二铵的颜色呈黄色。改变磷铵料浆的性质，改变造粒状况，提高造粒出料成球率，使产品结晶感得到加强，产品圆润度得到提高，产品颜色一致且稳定，产品的着色效果得到提高且不需要内着色剂和外包裹油。
本发明通过以下的技术方案来实现：
一种控制磷酸二铵颜色的方法，在湿法磷酸生产磷酸二铵的方法中：首先磷矿石被硫酸分解生成磷酸，磷酸被氨中和生成磷酸二铵，其特征在于：在磷矿石被分解生成磷酸的过程中添加占磷矿石重量的0.1％-20％的烧渣或在已经生成的磷酸中的添加占磷酸重量的0.1％-10％的烧渣，最后磷酸与氨中和得到黄色的磷酸二铵，所述的烧渣为硫铁矿制酸过程中产生的副产品，主要成分是三氧化二铁，并含有铜、铅、钙、镁金属离子及硅、硫、磷杂质。
本发明与现有技术相比，其优点主要包括：
其一、通过控制烧渣的添加量，改善磷酸二铵的产品颜色，使用产品能呈现出颜色深浅一致的黄色。
其二、通过控制烧渣的添加量，改善磷酸二铵的产品粒子的圆润度、结晶的透感。
其三、通过控制烧渣的添加量，改变磷二铵料浆的性质，改变造粒状况，提高造粒出料成球率。
其四、通过控制烧渣的添加量，使产品的着色效果得到提高，并且不需要内着色剂和外包裹油，内着色剂和外包裹油消耗降低。
其五、合理利用了烧渣这一工业生产的副产品，可减少环境污染。
具体实施方式
实施例1：在湿法磷酸生产磷酸二铵过程中，在磷精矿中添加占磷精矿重量的2.5％的烧渣，其中烧渣中三氧化二铁的含量为50％，进入反应系统生产，制得的磷酸二铵产品呈浅黄色，颗粒圆润，有结晶感。
实施例2：在湿法磷酸生产磷酸二铵过程中，在磷精矿中添加占磷精矿重量的0.1％的烧渣，其中烧渣中三氧化二铁的含量为50％，进入反应系统生产，制得的磷酸二铵产品呈浅黄色，颗粒圆润，有结晶感。
实施例3：在湿法磷酸生产磷酸二铵过程中，在磷精矿中添加占磷精矿重量的5％的烧渣，其中烧渣中三氧化二铁的含量为50％，进入反应系统生产，制得的磷酸二铵产品呈黄色，颗粒圆润，有结晶感。
实施例4：在湿法磷酸生产磷酸二铵过程中，在磷精矿中添加占磷精矿重量的10％的烧渣，其中烧渣中三氧化二铁的含量为50％，进入反应系统生产，制得的磷酸二铵产品呈深黄色，颗粒圆润，有结晶感。
实施例5：在湿法磷酸生产磷酸二铵过程中，在磷精矿中添加占磷精矿重量的15％的烧渣，其中烧渣中三氧化二铁的含量为50％，进入反应系统生产，制得的磷酸二铵产品呈深黄色，颗粒圆润，有结晶感。
实施例6：在湿法磷酸生产磷酸二铵过程中，在磷精矿中添加占磷精矿重量的20％的烧渣，其中烧渣中三氧化二铁的含量为50％，进入反应系统生产，制得的磷酸二铵产品呈深黄色，颗粒圆润，有结晶感。
实施例7：在湿法磷酸生产磷酸二铵过程中，在磷酸中添加占磷酸重量的0.1％的烧渣，其中烧渣中三氧化二铁的含量为50％，进入反应系统生产，制得的磷酸二铵产品呈浅黄色，颗粒圆润，有结晶感。
实施例8：在湿法磷酸生产磷酸二铵过程中，在磷酸中添加占磷酸重量的2.5％的烧渣，其中烧渣中三氧化二铁的含量为50％，进入反应系统生产，制得的磷酸二铵产品呈黄色，颗粒圆润，有结晶感。
实施例9：在湿法磷酸生产磷酸二铵过程中，在磷酸中添加占磷酸重量的5％的烧渣，其中烧渣中三氧化二铁的含量为50％，进入反应系统生产，制得的磷酸二铵产品呈深黄色，颗粒圆润，有结晶感。
实施例10：在湿法磷酸生产磷酸二铵过程中，在磷酸中添加占磷酸重量的7.5％的烧渣，其中烧渣中三氧化二铁的含量为50％，进入反应系统生产，制得的磷酸二铵产品呈深黄色，颗粒圆润，有结晶感。
实施例11：在湿法磷酸生产磷酸二铵过程中，在磷酸中添加占磷酸重量的10％的烧渣，其中烧渣中三氧化二铁的含量为50％，进入反应系统生产，制得的磷酸二铵产品呈深黄色，颗粒圆润，有结晶感。

Claims (1)

1.一种控制磷酸二铵颜色的方法，在湿法磷酸生产磷酸二铵的方法中：首先磷矿石被硫酸分解生成磷酸，磷酸被氨中和生成磷酸二铵，其特征在于：在磷矿石被分解生成磷酸的过程中添加占磷矿石重量的0.1％-20％的烧渣或在已经生成的磷酸中的添加占磷酸重量的0.1％-10％的烧渣，最后磷酸与氨中和得到黄色的磷酸二铵，所述的烧渣为硫铁矿制酸过程中产生的副产品，主要成分是三氧化二铁，并含有铜、铅、钙、镁金属离子及硅、硫、磷杂质。
CN200910273235A 2009-12-11 2009-12-11 一种控制磷酸二铵颜色的方法 Active CN101747116B (zh)