CN101725056B - 一种多功能面料及其制备方法 - Google Patents

一种多功能面料及其制备方法 Download PDF

Info

Publication number
CN101725056B
CN101725056B CN2009102351069A CN200910235106A CN101725056B CN 101725056 B CN101725056 B CN 101725056B CN 2009102351069 A CN2009102351069 A CN 2009102351069A CN 200910235106 A CN200910235106 A CN 200910235106A CN 101725056 B CN101725056 B CN 101725056B
Authority
CN
China
Prior art keywords
fabric
base cloth
bamboo charcoal
membrane
hot melt
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2009102351069A
Other languages
English (en)
Other versions
CN101725056A (zh
Inventor
毛志平
李正恩
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2009102351069A priority Critical patent/CN101725056B/zh
Publication of CN101725056A publication Critical patent/CN101725056A/zh
Application granted granted Critical
Publication of CN101725056B publication Critical patent/CN101725056B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种多功能面料及其制备方法,所述面料由基布、聚四氟乙烯膜、竹炭负离子PU膜三种材料复合制成,所述基布一侧表面依次粘贴聚四氟乙烯膜、竹炭负离子PU膜。其制备方法,包括下列步骤:(1)在70-90℃温度下,将热熔胶涂于基布的一侧表面,以织物上的热熔胶熔体作为粘合剂进行贴膜复合,先贴聚四氟乙烯膜,贴膜后的基布收卷,并在65-75%湿度、20-30℃环境下熟成45-50小时;(2)在70-90℃温度下,在步骤(1)得到的布料粘贴有聚四氟乙烯膜的表面,再涂热熔胶,然后贴竹炭负离子PU膜,贴膜后的基布收卷、并在65-75%湿度、20-30℃环境下熟成45-50小时。本发明具有防水、透湿、保温、除臭、抗菌等五项功能。

Description

一种多功能面料及其制备方法
技术领域:
本发明涉及人们穿着的面料,具体涉及具有多种保护功能的面料。
背景技术:
户外服已成为人们出行、旅游必备的用品之一。尤其是用于登山、极地科考、野外作战、滑雪、极限运动等严寒、潮湿、强风等特殊恶劣环境的户外服,更是在这些地区活动的人们不可缺少的用品。不仅要求其具有防雨、防严寒、强风等功能,而且要求其具有较好的穿着性能。为了实现这个目的,此前,本申请人提出过两项专利申请,如专利号为:2008200367576公开了名称为“多功能面料”,该面料是在具有防静电结构、附着有荧光层、防水层的面料表面,设置有透湿阻燃层。使面料同时具有防风、防水、透湿、阻燃、荧光、防静电、保暖等多项优良性能。又如专利号为:2009200360336公开了名称为“一种多功能面料”,该面料是在基布表面粘贴有防水、透湿、保温、防风功能层,在防风功能层表面粘贴有涤纶纤维布,使其同时具有防水、透湿、保温、防污、防风等多项优良性能。但上述面料都没有提供适合高湿环境下的人员穿着、既具有防水、透湿、保温等功能,又具有杀菌、除臭功能的面料。
发明内容:
本发明要解决的技术问题是提供一种带有杀菌功能的多功能面料,这种面料不仅具有防水、透湿、保温等功能,而且还具有杀菌功能。本发明同时提供这种面料的制备方法。
本发明通过以下技术方案解决:
一种多功能面料,由基布、聚四氟乙烯膜、竹炭负离子PU膜三种材料复合制成,所述基布一侧表面依次粘贴聚四氟乙烯膜、竹炭负离子PU膜。所述基布为涤纶纤维布。
聚四氟乙烯膜的厚度为0.03-0.05mm,竹炭负离子PU膜的厚度为0.01-0.03mm。
一种多功能面料的制备方法,包括下列步骤:
(1)在70-90℃温度下,将热熔胶涂于基布的一侧表面,以织物上的热熔胶熔体作为粘合剂进行贴膜复合,先贴聚四氟乙烯膜,贴膜后的基布收卷,并在6575%湿度、20-30℃环境下熟成45-72小时;
(2)在70-90℃温度下,在步骤(1)得到的布料粘贴有聚四氟乙烯膜的表面,再涂热熔胶,然后贴竹炭负离子PU膜,贴膜后的基布收卷、并在65-75%湿度、20-30℃环境下熟成45-72小时。
步骤(1)、步骤(2)中所述的熟成时间分别优选为45-50小时。
本发明的功能机理:
防水透湿:主要通过贴合的聚四氟乙烯膜(PTFE薄膜)来实现。水蒸气分子直径为0.0004微米,雨水中直径最小的轻雾直径为20微米,毛毛雨的直径则高达400微米,而我们所使用的聚四氟乙烯膜,其孔隙直径介于水蒸气和雨水之间,因而可以实现即防水又透湿。
保温:涤纶织物通过复合聚四氟乙烯膜层,实现其防水、透湿、保温及防风功能。复合的竹炭负离子PU膜释放的负离子可以起到蓄热、抗菌、除臭功能,亦可增加穿着者的身心舒适度。
采用的技术标准:保暖性能采用GB/T11048-1993标准,热阻值(m2·K/W)达到0.00191以上,克罗值(clo)达0.123,保温率(%)达到16.0,负离子释放量采用JC/T1016-2006标准,负离子释放量达到790个/CM3
其他静水压、透水汽性、表面拒水性分别采用:ISO811:1981,ASTM E96:2005,ISO4920:1981。
综上,本发明采用涤纶针织布+聚四氟乙烯膜+黑色竹炭负离子PU膜三种材料复合制成,具有防水、透湿、保温、除臭、抗菌等五项功能。有效克服了在涤纶纤维布的表面仅贴聚四氟乙烯膜层水洗后微孔易堵塞、不耐摩擦、以及病菌可通过微孔侵入等缺陷。由于本发明在聚四氟乙烯膜表面贴有竹炭负离子PU膜,具有释放负离子功能,穿着更加舒服、卫生。
本发明释放的负离子数、实现的克罗值、热阻和保温率等指标,可满足极限严寒环境中的使用要求。
本发明适用于登山、极地科考、野外作战、滑雪、极限运动等严寒、潮湿、强风等特殊恶劣环境中使用。
附图说明:
图1为本发明立体示意图。
具体实施方式:
如图1所示,一种多功能面料,由涤纶针织布、聚四氟乙烯膜、竹炭负离子PU膜三种材料复合制成,所述涤纶针织布1的一侧表面依次粘贴聚四氟乙烯膜2、竹炭负离子PU膜3。
上述面料的制备方法,包括下列步骤:
(1)在本实施例中选用德国汉高生产的湿气反应型热熔胶,在80℃左右的温度下,将热熔胶涂于基布的一侧表面,以织物上的热熔胶溶体作为粘合剂进行贴膜复合,先贴聚四氟乙烯膜(膜的厚度为0.04mm),贴膜后的基布收卷,并在约70%的湿度、25℃左右环境下熟成约48小时,经检验后;
(2)在70-90℃温度下,在步骤(1)得到的布料粘贴有聚四氟乙烯膜的表面、涂如步骤(1)所述的热熔胶,接着贴竹炭负离子PU膜(膜的厚度为0.02mm),贴膜后的基布收卷、并在约70%的湿度、25℃左右环境下熟成约48小时,检验后即为成品。

Claims (4)

1.一种多功能面料,其特征在于:由聚四氟乙烯膜、基布、竹炭负离子PU膜三种材料复合制成,所述基布一侧表面依次粘贴聚四氟乙烯膜、竹炭负离子PU膜;
制备方法包括下列步骤:
(1)在70-90℃温度下,将热熔胶涂于基布的一侧表面,以基布上的热熔胶熔体作为粘合剂进行贴膜复合,先贴聚四氟乙烯膜,贴膜后的基布收卷,并在65-75%湿度、20-30℃环境下熟成45-72小时;
(2)在70-90℃温度下,在步骤(1)得到的基布粘贴有聚四氟乙烯膜的表面,再涂热熔胶,然后贴竹炭负离子PU膜,贴膜后的基布收卷、并在65-75%湿度、20-30℃环境下熟成45-72小时。
2.如权利要求1所述的一种多功能面料,其特征在于:所述基布为涤纶纤维布。
3.如权利要求1所述的一种多功能面料,其特征在于:聚四氟乙烯膜的厚度为0.03-0.05mm,竹炭负离子PU膜的厚度为0.01-0.03mm。
4.如权利要求1所述的一种多功能面料的制备方法,其特征在于:步骤(1)、步骤(2)中所述的熟成时间分别为45-50小时。
CN2009102351069A 2009-10-30 2009-10-30 一种多功能面料及其制备方法 Expired - Fee Related CN101725056B (zh)