CN113415049A - 一种防水面料及其制备方法 - Google Patents
一种防水面料及其制备方法 Download PDFInfo
- Publication number
- CN113415049A CN113415049A CN202110545643.4A CN202110545643A CN113415049A CN 113415049 A CN113415049 A CN 113415049A CN 202110545643 A CN202110545643 A CN 202110545643A CN 113415049 A CN113415049 A CN 113415049A
- Authority
- CN
- China
- Prior art keywords
- layer
- pvc
- base
- unwinding reel
- waterproof fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提出了一种防水面料及其制备方法，包括基层与PVC层，所述基层与所述PVC层之间这有粘合层，所述粘合层将所述基层与所述PVC层粘合在一起，所述PVC层由PVC颗粒原料加热至熔融状态后挤压制成，本说明书一个或多个实施方式提出的防水面料，由PVC颗粒先制作均匀的PVC层，再通过粘合层将PVC层粘附在基布上，保证了面料表面的平整性，进而保证了防水面料的质量。
Description
技术领域
本说明书一个或多个实施例涉及防水面料生产技术领域，特别是指一种防水面料及其制备方法。
背景技术
随着科技的不断发展和生活水平的提高，人们对于服装舒适性的要求也越来越高，除了遮体御寒、美观得体的款式等方面的方面的需求外，更注重服装的穿着舒适性，而服装穿着舒适度在很大程度上又取决于面料的性能。面料就是用来制作服装的材料。作为服装三要素之一，面料不仅可以诠释服装的风格和特性，而且直接左右着服装的色彩、造型的表现效果。
户外运动时，常常会出很多汗，也会遇到雾气、下雨等恶劣天气，这就要求服装需同时具备防水、保暖、透湿的功能来满足户外运动的高舒适性要求。防水保暖面料就是集防水、透湿、防风和保暖性能于一体的功能性面料。该面料主要运用于功能性服装，不仅能够及时排除人体的汗液和汗气，满足严寒风雪、大风天气等恶劣环境中人们活动时的穿着需要，也适用于人们日常生活对雨衣等的要求，具有非常广阔的发展前景。但现有技术中普通的防水面料通常是在基布的表层涂覆PVC涂层，现有的制备方法通常是直接将PVC原料涂覆在基布上，这样导致PVC层不均匀，最终导致面料表面不平整，其制备后的防水面料质量比较差。
发明内容
有鉴于此，本说明书一个或多个实施例的目的在于提出一种防水面料及其制备方法，用以解决上述问题的之一或全部。
基于上述目的本说明书一个或多个实施例提出的一种防水面料，包括基层与PVC层，所述基层与所述PVC层之间这有粘合层，所述粘合层将所述基层与所述PVC层粘合在一起，所述PVC层由PVC颗粒原料加热至熔融状态后挤压制成。
可选的，所述基层材料为棉布。
可选的，所述粘合层的材料配料的成分百分比为：苯乙烯12％、丙烯腈35％、丙烯酸乙酯53％。
可选的，所述PVC层的厚度为0.3-0.5mm。
一种防水面料的制备方法，包括如下步骤：
A、备料：将需要进行防水处理的基布放入清水中进行清洗，去除基布上的灰尘或其它杂质，清洗后将基布脱水干燥；
B、将PVC颗粒原料加热至熔融状态，采用挤压机对熔融状态的PVC原料进行挤压，制成PVC层；
C、对粘合层材料进行配料，并进行静止脱泡，将静止脱泡好的粘合材料制作成粘合层；
D、通过滚压装置将PVC层、粘合层与基布粘合在一起，形成防水面料。
可选的，所述滚压装置包括基布放卷盘、PVC层放卷盘与粘合层放卷盘，所述基布放卷盘与所述PVC层放卷盘沿竖直方向设置，所述粘合层放卷盘位于所述基布放卷盘与所述PVC层放卷盘之间的一侧，所述基布放卷盘与所述PVC层放卷盘的另一侧安装有上压合辊组与下压合辊组。
可选的，所述上压合辊组与所述下压合辊组结构相同，均包括压合电缸，两个所述压合电缸相对设置，所述压合电缸的输出端可转动的安装有压合辊。
可选的，所述上压合辊组与所述下压合辊组朝向所述粘合层放卷盘的一侧安装有两个热风管，两个所述热风管相对设置，两个所述热风管鼓出热风。
可选的，所述热风的温度为60-80℃。
从上面所述可以看出，本说明书一个或多个实施例提出的防水面料及其制备方法，由PVC颗粒先制作均匀的PVC层，再通过粘合层将PVC层粘附在基布上，保证了面料表面的平整性，进而保证了防水面料的质量。
附图说明
为了更清楚地说明本说明书一个或多个实施例或现有技术中的技术方案，下面将对实施例或现有技术描述中所需要使用的附图作简单地介绍，显而易见地，下面描述中的附图仅仅是本说明书一个或多个实施例，对于本领域普通技术人员来讲，在不付出创造性劳动的前提下，还可以根据这些附图获得其他的附图。
图1为本说明书一个或多个实施例的滚压装置的示意图；
其中、基布放卷盘1、PVC层放卷盘2、粘合层放卷盘3、压合电缸4、压合辊5、热风管6。
具体实施方式
为使本公开的目的、技术方案和优点更加清楚明白，以下结合具体实施例，对本公开进一步详细说明。
需要说明的是，除非另外定义，本说明书一个或多个实施例使用的技术术语或者科学术语应当为本公开所属领域内具有一般技能的人士所理解的通常意义。本说明书一个或多个实施例中使用的“第一”、“第二”以及类似的词语并不表示任何顺序、数量或者重要性，而只是用来区分不同的组成部分。“包括”或者“包含”等类似的词语意指出现该词前面的元件或者物件涵盖出现在该词后面列举的元件或者物件及其等同，而不排除其他元件或者物件。“连接”或者“相连”等类似的词语并非限定于物理的或者机械的连接，而是可以包括电性的连接，不管是直接的还是间接的。“上”、“下”、“左”、“右”等仅用于表示相对位置关系，当被描述对象的绝对位置改变后，则该相对位置关系也可能相应地改变。
基于上述目的本说明书一个或多个实施例提出的一种防水面料，包括基层与PVC层，所述基层与所述PVC层之间这有粘合层，所述粘合层将所述基层与所述PVC层粘合在一起，所述PVC层由PVC颗粒原料加热至熔融状态后挤压制成。
其中，由PVC颗粒先制作均匀的PVC层，再通过粘合层将PVC层粘附在基布上，保证了面料表面的平整性，进而保证了防水面料的质量。
可选的，所述基层材料为棉布。棉布保暖、柔和贴身、吸湿性和透气性好，作为基布能够提高面料的舒适性。
可选的，所述粘合层的材料配料的成分百分比为：苯乙烯12％、丙烯腈35％、丙烯酸乙酯53％。
可选的，所述PVC层的厚度为0.3-0.5mm。
还提出一种防水面料的制备方法，包括如下步骤：
A、备料：将需要进行防水处理的基布放入清水中进行清洗，去除基布上的灰尘或其它杂质，清洗后将基布脱水干燥；
B、将PVC颗粒原料加热至熔融状态，采用挤压机对熔融状态的PVC原料进行挤压，制成PVC层；
C、对粘合层材料进行配料，并进行静止脱泡，将静止脱泡好的粘合材料制作成粘合层；
D、通过滚压装置将PVC层、粘合层与基布粘合在一起，形成防水面料。
可选的，所述滚压装置包括基布放卷盘1、PVC层放卷盘2与粘合层放卷盘3，所述基布放卷盘1与所述PVC层放卷盘2沿竖直方向设置，所述粘合层放卷盘3位于所述基布放卷盘1与所述PVC层放卷盘2之间的一侧，所述基布放卷盘1与所述PVC层放卷盘2的另一侧安装有上压合辊5组与下压合辊5组。
可选的，所述上压合辊5组与所述下压合辊5组结构相同，均包括压合电缸4，两个所述压合电缸4相对设置，所述压合电缸4的输出端可转动的安装有压合辊5。
可选的，所述上压合辊5组与所述下压合辊5组朝向所述粘合层放卷盘3的一侧安装有两个热风管6，两个所述热风管6相对设置，两个所述热风管6鼓出热风。
可选的，所述热风的温度为60-80℃。
粘合形成防水面料的步骤为：
基布放卷盘1与PVC层放卷盘2分别放卷基布和PVC层，粘合层放卷盘3放卷粘合层，并将粘合层位于基布与PVC层之间，热风管6鼓出60-80℃的热风，增加粘合层的粘合力，两个压合电缸4带动压合辊5下压，将PVC层、粘合层与基布粘合在一起，形成防水面料；
本说明书一个或多个实施方式提出的防水面料，由PVC颗粒先制作均匀的PVC层，再通过粘合层将PVC层粘附在基布上，保证了面料表面的平整性，进而保证了防水面料的质量。
所属领域的普通技术人员应当理解：以上任何实施例的讨论仅为示例性的，并非旨在暗示本公开的范围(包括权利要求)被限于这些例子；在本公开的思路下，以上实施例或者不同实施例中的技术特征之间也可以进行组合，步骤可以以任意顺序实现，并存在如上所述的本说明书一个或多个实施例的不同方面的许多其它变化，为了简明它们没有在细节中提供。
尽管已经结合了本公开的具体实施例对本公开进行了描述，但是根据前面的描述，这些实施例的很多替换、修改和变型对本领域普通技术人员来说将是显而易见的。
本说明书一个或多个实施例旨在涵盖落入所附权利要求的宽泛范围之内的所有这样的替换、修改和变型。因此，凡在本说明书一个或多个实施例的精神和原则之内，所做的任何省略、修改、等同替换、改进等，均应包含在本公开的保护范围之内。
Claims (9)
1.一种防水面料，其特征在于，包括基层与PVC层，所述基层与所述PVC层之间这有粘合层，所述粘合层将所述基层与所述PVC层粘合在一起，所述PVC层由PVC颗粒原料加热至熔融状态后挤压制成。
2.根据权利要求1所述的防水面料，其特征在于，所述基层材料为棉布。
3.根据权利要求1所述的防水面料，其特征在于，所述粘合层的材料配料的成分百分比为：苯乙烯12％、丙烯腈35％、丙烯酸乙酯53％。
4.根据权利要求1所述的防水面料，其特征在于，所述PVC层的厚度为0.3-0.5mm。
5.根据权利要求1-4任一所述的防水面料的制备方法，其特征在于，包括如下步骤：
A、备料：将需要进行防水处理的基布放入清水中进行清洗，去除基布上的灰尘或其它杂质，清洗后将基布脱水干燥；
B、将PVC颗粒原料加热至熔融状态，采用挤压机对熔融状态的PVC原料进行挤压，制成PVC层；
C、对粘合层材料进行配料，并进行静止脱泡，将静止脱泡好的粘合材料制作成粘合层；
D、通过滚压装置将PVC层、粘合层与基布粘合在一起，形成防水面料。
6.根据权利要求5所述的防水面料及其制备方法，其特征在于，所述滚压装置包括基布放卷盘、PVC层放卷盘与粘合层放卷盘，所述基布放卷盘与所述PVC层放卷盘沿竖直方向设置，所述粘合层放卷盘位于所述基布放卷盘与所述PVC层放卷盘之间的一侧，所述基布放卷盘与所述PVC层放卷盘的另一侧安装有上压合辊组与下压合辊组。
7.根据权利要求5所述的防水面料及其制备方法，其特征在于，所述上压合辊组与所述下压合辊组结构相同，均包括压合电缸，两个所述压合电缸相对设置，所述压合电缸的输出端可转动的安装有压合辊。
8.根据权利要求5所述的防水面料及其制备方法，其特征在于，所述上压合辊组与所述下压合辊组朝向所述粘合层放卷盘的一侧安装有两个热风管，两个所述热风管相对设置，两个所述热风管鼓出热风。
9.根据权利要求8所述的防水面料及其制备方法，其特征在于，所述热风的温度为60-80℃。