CN101712560B - 一种高强度浇注料 - Google Patents

一种高强度浇注料 Download PDF

Info

Publication number
CN101712560B
CN101712560B CN2009100662788A CN200910066278A CN101712560B CN 101712560 B CN101712560 B CN 101712560B CN 2009100662788 A CN2009100662788 A CN 2009100662788A CN 200910066278 A CN200910066278 A CN 200910066278A CN 101712560 B CN101712560 B CN 101712560B
Authority
CN
China
Prior art keywords
strength
powder
castable
granularity
standard
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN2009100662788A
Other languages
English (en)
Other versions
CN101712560A (zh
Inventor
宋金标
宋禄峰
宋彩红
宋马峰
樊建令
卢中立
郭英超
付鸿正
樊召峰
孙艳秋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHENGZHOU ZHENJIN REFRACTORY CO Ltd
Original Assignee
ZHENGZHOU ZHENJIN REFRACTORY CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHENGZHOU ZHENJIN REFRACTORY CO Ltd filed Critical ZHENGZHOU ZHENJIN REFRACTORY CO Ltd
Priority to CN2009100662788A priority Critical patent/CN101712560B/zh
Publication of CN101712560A publication Critical patent/CN101712560A/zh
Application granted granted Critical
Publication of CN101712560B publication Critical patent/CN101712560B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种高强度浇注料，它是由下述原料按照重量份配制而成：铝矾土骨料4.8份；棕刚玉颗粒料2份；铝矾土粉料0.8份；氧化铝超微粉0.4份；碳化硅粉料0.6份；硅微粉0.3份；CA-70水泥0.6份；棕刚玉粉0.5份；总物料重量0.1％的三聚磷酸钠；总物料重量0.08％的六偏磷酸钠。本浇注料耐压强度高、抗折强度高、荷重软化温度高、抗热震稳定性好、在高温下具有微膨胀的特性、耐磨性能好等优点，成本比传统高强度浇注料降低约2/5，该产品可广泛应用于水泥窑窑口、预热器、篦冷机等对强度要求高、使用条件恶劣的窑炉，是替代刚玉质高强度浇注料的理想新产品。

Description

一种高强度浇注料
技术领域
本发明涉及水泥窑炉用浇注料，尤其是涉及一种成本低、使用寿命长的高强度浇注料。
背景技术
在水泥窑窑口、预热器、篦冷机等一些对强度要求高、使用条件恶劣的窑炉中，多用刚玉质高强度浇注料，由于刚玉材料的成本高，导致了原料成本高，使生产企业增大了生产成本。
发明内容
本发明的目的在于提供一种成本低且使用寿命长的高强度浇注料。
为实现上述目的，本发明可采取下述技术方案：
本发明所述的高强度浇注料，它是由原料铝矾土、棕刚玉、碳化硅、硅微粉、CA-70水泥、氧化铝粉和三聚磷酸钠、六偏磷酸钠按照下述重量份配制而成：
粒度8-5mm铝矾土料2.5份，0.075mm＜粒度＜5mm的铝矾土料2.3份；粒度3-1mm棕刚玉颗粒料2份；粒度≤0.075mm的铝矾土料0.8份；粒度≤0.025mm的氧化铝超微粉0.4份；粒度≤0.075mm的碳化硅粉料0.6份；粒度＜0.019mm的硅微粉0.3份；CA-70水泥0.6份；粒度＜0.053mm的棕刚玉粉0.5份；总物料重量0.1％的三聚磷酸钠；总物料重量0.08％的六偏磷酸钠。
所述铝矾土的标准为Al2O3≥80％，Fe2O3＜1.5％。
所述棕刚玉的标准为Al2O3≥97％，Fe2O3＜0.3％。
所述碳化硅的标准为SiC≥97％，Fe2O3≤1％。
所述硅微粉的标准为SiO2≥97％。
所述CA-70水泥的标准为Al2O3≥69％。
所述氧化铝粉的标准为Al2O3≥99％。
本发明的优点在于耐压强度高、抗折强度高、荷重软化温度高、抗热震稳定性好、在高温下具有微膨胀的特性、耐磨性能好等优点，虽然氧化铝含量相对于传统的高强度浇注料有所降低，但由于本产品的水泥用量大大降低，使氧化钙含量大大降低，其中掺加的碳化硅在中温时能够起到增加强度、增强蠕变性能、提高耐火度的作用而弥补了氧化铝含量不高的缺憾，相对于传统的高强度浇注料来说本品具有更高的耐压强度和抗折强度，因为采用了高铝矾土代替了传统高强度浇注料中的部分刚玉材料，其成本可比传统高强度浇注料降低约2/5，间接降低了因生产原料产生的消耗，同时使用寿命也比传统高强度浇注料有所提高。该产品可广泛应用于水泥窑窑口、预热器、篦冷机等对强度要求高、使用条件恶劣的窑炉，是替代刚玉质高强度浇注料的理想新产品。该产品的理化指标与传统高强度浇注料的理化指标相比结果见下表：
Figure G2009100662788D00021
具体实施方式
本发明所述的高强度浇注料，它是由原料铝矾土、棕刚玉、碳化硅、硅微粉、CA-70水泥、氧化铝粉和三聚磷酸钠、六偏磷酸钠按照下述重量份配制而成：
粒度8-5mm铝矾土料2.5份，0.075mm＜粒度＜5mm的铝矾土料2.3份；粒度3-1mm棕刚玉颗粒料2份；粒度≤0.075mm的铝矾土料0.8份；粒度≤0.025mm的氧化铝超微粉0.4份；粒度≤0.075mm的碳化硅粉料0.6份；粒度＜0.019mm的硅微粉0.3份；CA-70水泥0.6份；粒度＜0.053mm的棕刚玉粉0.5份；总物料重量0.1％的三聚磷酸钠；总物料重量0.08％的六偏磷酸钠；用颚式破碎机或圆锥破碎机将物料破碎至符合要求，除去CA-70水泥和三聚磷酸钠、六偏磷酸钠，将上述剩余物料置于强制搅拌机中混合均匀后装袋包装，水泥和三聚磷酸钠、六偏磷酸钠单独包装存放。
本项发明浇注料的施工加水量一般为干料总重量的5-6％。其它使用方法按一般浇注料施工方法进行，无需经过特殊养护。
其中，采用的铝矾土标准为Al2O3≥80％，Fe2O3＜1.5％。
采用的棕刚玉标准为Al2O3≥97％，Fe2O3＜0.3％。
采用的碳化硅标准为SiC≥97％，Fe2O3≤1％。
采用的硅微粉标准为SiO2≥97％。
采用的CA-70水泥标准为Al2O3≥69％。
采用的氧化铝粉标准为Al2O3≥99％。

Claims (7)

1.一种高强度浇注料，其特征在于：它是由原料铝矾土、棕刚玉、碳化硅、硅微粉、CA-70水泥、氧化铝粉和三聚磷酸钠、六偏磷酸钠按照下述重量份配制而成：
粒度8-5mm铝矾土料2.5份，0.075mm＜粒度＜5mm的铝矾土料2.3份；粒度3-1mm棕刚玉颗粒料2份；粒度≤0.075mm的铝矾土料0.8份；粒度≤0.025mm的氧化铝超微粉0.4份；粒度≤0.075mm的碳化硅粉料0.6份；粒度＜0.019mm的硅微粉0.3份；CA-70水泥0.6份；粒度＜0.053mm的棕刚玉粉0.5份；总物料重量0.1％的三聚磷酸钠；总物料重量0.08％的六偏磷酸钠。
2.根据权利要求1所述的高强度浇注料，其特征在于：所述铝矾土的标准为Al2O3≥80％，Fe2O3＜1.5％。
3.根据权利要求1所述的高强度浇注料，其特征在于：所述棕刚玉的标准为Al2O3≥97％，Fe2O3＜0.3％。
4.根据权利要求1所述的高强度浇注料，其特征在于：所述碳化硅的标准为SiC≥97％，Fe2O3≤1％。
5.根据权利要求1所述的高强度浇注料，其特征在于：所述硅微粉的标准为SiO2≥97％。
6.根据权利要求1所述的高强度浇注料，其特征在于：所述CA-70水泥的标准为Al2O3≥69％。
7.根据权利要求1所述的高强度浇注料，其特征在于：所述氧化铝粉的标准为Al2O3≥99％。
CN2009100662788A 2009-10-28 2009-10-28 一种高强度浇注料 Active CN101712560B (zh)