CN102826812A - 水泥窑三次风管弯头用耐磨浇注料 - Google Patents

水泥窑三次风管弯头用耐磨浇注料 Download PDF

Info

Publication number
CN102826812A
CN102826812A CN2012103143690A CN201210314369A CN102826812A CN 102826812 A CN102826812 A CN 102826812A CN 2012103143690 A CN2012103143690 A CN 2012103143690A CN 201210314369 A CN201210314369 A CN 201210314369A CN 102826812 A CN102826812 A CN 102826812A
Authority
CN
China
Prior art keywords
content
particle diameter
powder
air pipe
wear
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012103143690A
Other languages
English (en)
Inventor
韩亚伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU HENGNAI FURNACE CHARGE GROUP CO Ltd
Original Assignee
JIANGSU HENGNAI FURNACE CHARGE GROUP CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU HENGNAI FURNACE CHARGE GROUP CO Ltd filed Critical JIANGSU HENGNAI FURNACE CHARGE GROUP CO Ltd
Priority to CN2012103143690A priority Critical patent/CN102826812A/zh
Publication of CN102826812A publication Critical patent/CN102826812A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种浇注料，特别是一种水泥窑三次风管弯头用耐磨浇注料，该浇注料的组分组成为：棕刚玉、红柱石、SiC、SiC细粉、红柱石粉、白刚玉粉、α-Al2O3微粉、SiO2微粉、纯铝酸钙水泥、耐热钢纤维、聚丙烯纤维和三聚磷酸钠。本发明的水泥窑三次风管弯头用耐磨浇注料的抗折抗压强度高、抗冲刷性、抗侵蚀性及热震稳定性能好、耐磨性能突出、吸水率低、流动性好。

Description

水泥窑三次风管弯头用耐磨浇注料
技术领域
本发明涉及一种浇注料，特别是一种水泥窑三次风管弯头用耐磨浇注料。
背景技术
目前，水泥窑三次风管弯头所使用的浇注料采用高铝矾土为主要原料，浇注料成品的抗冲刷性、抗侵蚀性及热震稳定性较差，吸水率较高，无法满足三次风管弯头等易磨损部位的长期使用。
发明内容
本发明要解决的技术问题是：针对背景技术中所述的水泥窑三次风管用浇注料存在的抗冲刷性、抗侵蚀性及抗热震稳定性等方面的不足，提供一种抗冲刷性、抗侵蚀性及抗热震稳定性好的水泥窑三次风管弯头用耐磨浇注料。
本发明解决其技术问题所采用的技术方案是：一种水泥窑三次风管弯头用耐磨浇注料，按质量百分比计，其组分组成为：
粒径为5～8mm的棕刚玉                0%～10%；
粒径为3～5mm的棕刚                  11%～30%；
粒径为1～3mm的棕刚玉                5%～12%；
粒径为0.088～1mm的棕刚玉            6%～17%；
粒径为0.088～1mm的红柱石            0%～10%；
粒径为1～3mm的SiC                   4%～17%；
SiC细粉                             2%～7%；
红柱石粉                            0～8%；
白刚玉粉               2%～9%；
α-Al2O3微粉           4%～9%；
SiO2微粉               3%～6%；
纯铝酸钙水泥           3%～8%；
耐热钢纤维             1%～4%；
上述各组分含量之和为100%。
一种水泥窑三次风管弯头用耐磨浇注料，按质量比计，其组分组成还可包括聚丙烯纤维和三聚磷酸钠，具体含量比例为：上述组分含量总量：聚丙烯纤维：三聚磷酸钠为1：（0.0008～0.003）：（0.001～0.003）。
所述棕刚玉中Al2O3含量≥93%，Fe2O3≤1.5%；红柱石中Al2O3含量≥60%；粒径为1～3mm的SiC和SiC细粉中SiC含量≥95%；红柱石粉中Al2O3含量≥61%；白刚玉粉中Al2O3含量≥95%；α-Al2O3微粉Al2O3含量≥93%；SiO2微粉中SiO2≥94%；纯铝酸钙水泥中Al2O3含量≥70%；聚丙烯纤维的熔点低于160℃。
本发明的耐磨浇注料的配方中，棕刚玉作为骨料，其为浇注料提供了优良的耐磨性能；白刚玉粉填充于骨料和其它颗粒之间，有效保证了浇注料的整体致密性，并且提高了抗折抗压强度；SiC的加入不但可保证浇注料的抗热震稳定性，而且其在高温下形成的保护膜可提高浇注料的抗侵蚀性；SiO2微粉和α-Al2O3微粉可增强浇注料的流动性和中高温强度；红柱石粉可增强浇注料的高温强度和耐磨性；纯铝酸钙水泥的加入提高了浇注料的结合性能；耐热钢纤维的加入提高了浇注料的抗剥落性能；配方中，棕刚玉骨料的气孔率较低，其通过合适的颗粒级配使得浇注料整体的吸水率较低。
有益效果：利用本发明技术方案制备的水泥窑三次风管弯头用耐磨浇注料，与现有高铝矾土浇注料相比，其抗折抗压强度高、抗冲刷性、抗侵蚀性及抗热震稳定性能好、耐磨性能突出、吸水率低、流动性好（相关性能指标见表一）。
表一本发明的耐磨浇注料的性能指标
Figure BDA00002072697600031
具体实施方式
本发明的耐磨浇注料的生产方法为：将配方中纯铝酸钙水泥和三聚磷酸钠准确称量并均匀混合，装入小包装袋；将配方中除纯铝酸钙水泥和三聚磷酸钠外的组分采用强制式搅拌机均匀搅拌，搅拌时间为5～8min，装入大包装袋，然后将小包装袋放入大包装袋内。该耐磨浇注料使用时只需将浇注料粉料运输至施工现场，然后加入物料总量的6%～7%的水，再搅拌5～8min，使物料混合均匀即可。本发明中，将浇注料预先制成干粉状，主要是防止物料变质，并且粉状料便于运输、包装和保存，施工方便。下面结合优选实施例对本发明做进一步说明。
实施例一
一种水泥窑三次风管弯头用耐磨浇注料，按质量百分比计，其组分组成为：
粒径为3～5mm的棕刚玉           29%；
粒径为1～3mm的棕刚玉           12%；
粒径为0.088～1mm的棕刚玉       10%；
粒径为0.088～1mm的红柱石          8%；
粒径为1～3mm的SiC                 12%；
SiC细粉                           4%；
红柱石粉                          2%；
白刚玉粉                          5%；
α-Al2O3微粉                      9%；
SiO2微粉                          3%；
纯铝酸钙水泥                      4%；
耐热钢纤维                        2%。
所述棕刚玉中Al2O3含量≥93%，Fe2O3≤1.5%；红柱石中Al2O3含量≥60%；粒径为1～3mm的SiC和SiC细粉中SiC含量≥95%；红柱石粉中Al2O3含量≥61%；白刚玉粉中Al2O3含量≥95%；α-Al2O3微粉中Al2O3含量≥93%；SiO2微粉中SiO2≥94%；纯铝酸钙水泥中Al2O3含量≥70%。该耐磨浇注料使用时只需加入物料总量的6%的水，再搅拌5～8min，使物料混合均匀即可。
实施例二
一种水泥窑三次风管弯头用耐磨浇注料，按质量百分比计，其组分组成为：
粒径为5～8mm的棕刚玉                            7%；
粒径为3～5mm的棕刚玉                            25%；
粒径为1～3mm的棕刚玉                            7%；
粒径为0.088～1mm的棕刚玉                        16%；
粒径为1～3mm的SiC                               14%；
SiC细粉                                         7%；
白刚玉粉                                        5%；
α-Al2O3微粉                   7%；
SiO2微粉                       5%；
纯铝酸钙水泥                   6%；
耐热钢纤维                    1%；
上述各组分含量之和为100%。
上述水泥窑三次风管弯头用耐磨浇注料，按质量比计，其组分组成还包括聚丙烯纤维和三聚磷酸钠，具体含量比例为：上述组分含量总量：聚丙烯纤维：三聚磷酸钠为1：0.002：0.0013。
该耐磨浇注料中各组分的指标含量同实施例一，聚丙烯纤维的熔点低于160℃；使用时只需加入物料总量的6.5%的水，再搅拌5～8min，使物料混合均匀即可。
实施例三
一种水泥窑三次风管弯头用耐磨浇注料，按质量百分比计，其组分组成为：
粒径为3～5mm的棕刚玉                        25%；
粒径为1～3mm的棕刚玉                        12%；
粒径为0.088～1mm的棕刚玉                    10%；
粒径为0.088～1mm的红柱石                    8%；
粒径为1～3mm的SiC                           12%；
SiC细粉                                     4%；
红柱石粉                                    2%；
白刚玉粉                                    5%；
α-Al2O3微粉                                9%；
SiO2微粉                                    3%；
纯铝酸钙水泥                 8%；
耐热钢纤维                   2%；
上述各组分含量之和为100%。
上述水泥窑三次风管弯头用耐磨浇注料，按质量比计，其组分组成还包括聚丙烯纤维和三聚磷酸钠，具体含量比例为：上述组分含量总量：聚丙烯纤维：三聚磷酸钠为1：0.0016：0.001。
该耐磨浇注料中各组分的指标含量同实施例一，聚丙烯纤维的熔点低于160℃；使用时只需加入物料总量的6%的水，再搅拌5～8min，使物料混合均匀即可。
按照上述实施例制得的耐磨浇注料的各项性能指标如下表所示：

Claims (3)

1.一种水泥窑三次风管弯头用耐磨浇注料，其特征是：按质量百分比计，其组分组成为：
粒径为5～8mm的棕刚玉                    0%～10%；
粒径为3～5mm的棕刚玉                    11%～30%；
粒径为1～3mm的棕刚玉                    5%～12%；
粒径为0.088～1mm的棕刚玉                6%～17%；
粒径为0.088～1mm的红柱石                0%～10%；
粒径为1～3mm的SiC                       4%～17%；
SiC细粉                                 2%～7%；
红柱石粉                                0～8%；
白刚玉粉                                2%～9%；
α-Al2O3微粉                            4%～9%；
SiO2微粉                                3%～6%；
纯铝酸钙水泥                            3%～8%；
耐热钢纤维                              1%～4%。
2.如权利要求1所述的水泥窑三次风管弯头用耐磨浇注料，其特征是：按质量比计，其组分组成还包括聚丙烯纤维和三聚磷酸钠，具体含量比例为：权利要求1中所述组分含量总量：聚丙烯纤维：三聚磷酸钠为1：（0.0008～0.003）：（0.001～0.003）。
3.如权利要求1或2所述的水泥窑三次风管弯头用耐磨浇注料，其特征是：所述棕刚玉中Al2O3含量≥93%，Fe2O3≤1.5%；红柱石中Al2O3含量≥60%；粒径为1～3mm的SiC和SiC细粉中SiC含量≥95%；红柱石粉中Al2O3含量≥61%；白刚玉粉中Al2O3含量≥95%；α-Al2O3微粉Al2O3含量≥93%；SiO2微粉中SiO2≥94%；纯铝酸钙水泥中Al2O3含量≥70%；聚丙烯纤维的熔点低于160℃。
CN2012103143690A 2012-08-29 2012-08-29 水泥窑三次风管弯头用耐磨浇注料 Pending CN102826812A (zh)