CN101709471A - 一种钛合金叶片的化铣方法 - Google Patents

一种钛合金叶片的化铣方法 Download PDF

Info

Publication number
CN101709471A
CN101709471A CN200910248412A CN200910248412A CN101709471A CN 101709471 A CN101709471 A CN 101709471A CN 200910248412 A CN200910248412 A CN 200910248412A CN 200910248412 A CN200910248412 A CN 200910248412A CN 101709471 A CN101709471 A CN 101709471A
Authority
CN
China
Prior art keywords
titanium alloy
alloy blade
solution
organic solvent
blade
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN200910248412A
Other languages
English (en)
Other versions
CN101709471B (zh
Inventor
陈晓峰
邰清安
史丽坤
张春刚
李晗晔
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
AECC Shenyang Liming Aero Engine Co Ltd
Original Assignee
Shenyang Liming Aero Engine Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shenyang Liming Aero Engine Group Co Ltd filed Critical Shenyang Liming Aero Engine Group Co Ltd
Priority to CN2009102484126A priority Critical patent/CN101709471B/zh
Publication of CN101709471A publication Critical patent/CN101709471A/zh
Application granted granted Critical
Publication of CN101709471B publication Critical patent/CN101709471B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种钛合金叶片的化铣方法，按以下步骤进行：(1)将终锻后的钛合金叶片水洗去除表面灰尘，然后采用有机溶剂去除表面油污，再去除有机溶剂；(2)将去除有机溶剂的钛合金叶片置于化铣溶液中浸没3～15min；(3)用室温水清洗去除表面残留的酸液，然后浸没在除灰溶液中，时间为3～15min；(4)将除灰结束后的钛合金叶片去除表面的残留的酸液。本发明的方法通过配制化铣溶液，可有效控制在叶片表面的腐蚀速率，使钛合金叶片满足精度要求；整个化铣过程方法简单，容易控制，实现了钛合金叶片的叶盘、叶背以及内缘，面无需加工可满足设计图要求。

Description

一种钛合金叶片的化铣方法
技术领域
本发明涉及叶片的制备方法，特别涉及一种钛合金叶片的化铣方法。
背景技术
钛合金叶片的制备过成一般包括坯料的制备、预锻、终锻等步骤，终锻结束后还要进行后期加工以达到精度要求，工艺步骤较复杂；同时钛合金叶片的制备过程中也有采用腐蚀叶片的步骤，其主要作用是将钛合金加热过程中产生的污染层去除，该步骤实施的温度较高，且腐蚀速率较低，精度也不能达到很高要求。
发明内容
针对上述技术问题，本发明提供一种钛合金叶片的化铣方法，目的在于通过设置化铣溶液，采用简单的化铣步骤，调节终锻后钛合金叶片的表面余量，使叶片不需要后期加工达到精度要求。
本发明的方法按以下步骤进行：
1、预处理：将终锻后的钛合金叶片水洗去除表面灰尘，然后采用有机溶剂去除表面油污，再用40～50℃热水浸泡去除有机溶剂。
2、浸没化铣：将去除有机溶剂的钛合金叶片置于化铣溶液中，在50～70℃条件下浸没3～15min，其中化铣溶液的成分按重量百分比为HF 30～50％，HNO3 30～50％，余量为水。
3、除灰：将化铣完成的钛合金叶片用室温水清洗去除表面残留的酸液，然后浸没在除灰溶液中，浸没时间为3～15min，其中除灰溶液的成分按重量百分比为HF 20～30％，HNO3 25～35％，余量为水。
4、后处理：将除灰结束后的钛合金叶片用室温水清洗去除表面的残留的酸液，再用60～70℃热水浸泡后将表面的水分吹干。
5、上述方法完成后测量钛合金叶片的尺寸，达到要求则完成钛合金叶片的制备，如果不符合要求的尺寸则重复上述步骤，在重复上述步骤1～4次的条件下能够获得满足精度要求的钛合金叶片。
上述的有机溶剂为乙醇或丙酮。
本发明的方法通过配制化铣溶液，可有效控制在叶片表面的腐蚀速率，腐蚀速率不低于0.01mm/min，同时通过预先测量钛合金叶片的尺寸，可以调节化铣时间和温度，由于化铣速度过慢或化铣时间过长将导致精锻后的钛合金叶片出现析氢现象，因此化铣过程要求控制化铣速率和时间，通过反复1～4次化铣，使钛合金叶片满足精度要求；本方法避免了终锻结束后复杂的余量去除工作，整个化铣过程方法简单，容易控制，实现了钛合金叶片的叶盘、叶背以及内缘，面无需加工可满足设计图要求。
附图说明
图1为本发明的钛合金叶片的化铣方法的流程示意图。
具体实施方式
本发明实施例中采用的氢氟酸为工业用氢氟酸。
本发明实施例中采用的硝酸为工业硝酸。
实施例1
采用氢氟酸、硝酸和水配制化铣溶液，化铣溶液的成分按重量百分比为HF 30％，HNO3 50％，余量为水。
将终锻后的钛合金叶片水洗去除表面灰尘，然后采用有机溶剂去除表面油污，再用40℃热水浸泡去除有机溶剂。
将去除有机溶剂的钛合金叶片置于化铣溶液中，在50℃条件下浸没15min。
将化铣完成的钛合金叶片用室温水清洗去除表面残留的酸液，然后浸没在除灰溶液中，浸没时间为15min，其中除灰溶液的成分按重量百分比为HF 20％，HNO3 25％，余量为水。
将除灰结束后的钛合金叶片用室温水清洗去除表面的残留的酸液，再用60℃热水浸泡后将表面的水分吹干。
上述方法完成后测量钛合金叶片的尺寸，达到精度要求。
实施例2
采用氢氟酸、硝酸和水配制化铣溶液，化铣溶液的成分按重量百分比为HF 50％，HNO3 30％，余量为水。
将终锻后的钛合金叶片水洗去除表面灰尘，然后采用有机溶剂去除表面油污，再用45℃热水浸泡去除有机溶剂。
将去除有机溶剂的钛合金叶片置于化铣溶液中，在60℃条件下浸没10min。
将化铣完成的钛合金叶片用室温水清洗去除表面残留的酸液，然后浸没在除灰溶液中，浸没时间为11min，其中除灰溶液的成分按重量百分比为HF 30％，HNO3 35％，余量为水。
将除灰结束后的钛合金叶片用室温水清洗去除表面的残留的酸液，再用65℃热水浸泡后将表面的水分吹干。
上述方法完成后测量钛合金叶片的尺寸，重复进行上述步骤4次后达到精度要求。
实施例3
采用氢氟酸、硝酸和水配制化铣溶液，化铣溶液的成分按重量百分比为HF 40％，HNO3 40％，余量为水。
将终锻后的钛合金叶片水洗去除表面灰尘，然后采用有机溶剂去除表面油污，再用50℃热水浸泡去除有机溶剂。
将去除有机溶剂的钛合金叶片置于化铣溶液中，在70℃条件下浸没3min。
将化铣完成的钛合金叶片用室温水清洗去除表面残留的酸液，然后浸没在除灰溶液中，浸没时间为3min，其中除灰溶液的成分按重量百分比为HF 25％，HNO3 30％，余量为水。
将除灰结束后的钛合金叶片用室温水清洗去除表面的残留的酸液，再用70℃热水浸泡后将表面的水分吹干。
上述方法完成后测量钛合金叶片的尺寸，重复进行上述步骤2次后达到精度要求。

Claims (4)

1.一种钛合金叶片的化铣方法，其特征在于按以下步骤进行：(1)将终锻后的钛合金叶片水洗去除表面灰尘，然后采用有机溶剂去除表面油污，再去除有机溶剂；(2)将去除有机溶剂的钛合金叶片置于化铣溶液中，在50～70℃条件下浸没3～15min，其中化铣溶液的成分按重量百分比为HF 30～50％，HNO330～50％，余量为水；(3)将化铣完成的钛合金叶片用室温水清洗去除表面残留的酸液，然后浸没在除灰溶液中，浸没时间为3～15min，其中除灰溶液的成分按重量百分比为HF 20～30％，HNO325～35％，余量为水；(4)将除灰结束后的钛合金叶片去除表面的残留的酸液。
2.根据权利要求1所述的一种钛合金叶片的化铣方法，其特征在于所述的有机溶剂为乙醇或丙酮。
3.根据权利要求1所述的一种钛合金叶片的化铣方法，其特征在于所述的去除有机溶剂是用40～50℃热水浸泡。
4.根据权利要求1所述的一种钛合金叶片的化铣方法，其特征在于所述的去除表面的残留的酸液是用室温水清洗去除表面的残留的酸液，再用60～70℃热水浸泡后将表面的水分吹干。
CN2009102484126A 2009-12-16 2009-12-16 一种钛合金叶片的化铣方法 Active CN101709471B (zh)