CN101705068B - 保温隔音建筑涂料用微胶囊胶粘剂的制备 - Google Patents

保温隔音建筑涂料用微胶囊胶粘剂的制备 Download PDF

Info

Publication number
CN101705068B
CN101705068B CN2009101925850A CN200910192585A CN101705068B CN 101705068 B CN101705068 B CN 101705068B CN 2009101925850 A CN2009101925850 A CN 2009101925850A CN 200910192585 A CN200910192585 A CN 200910192585A CN 101705068 B CN101705068 B CN 101705068B
Authority
CN
China
Prior art keywords
heat
preserving
adhesive
capsulated
sound
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2009101925850A
Other languages
English (en)
Other versions
CN101705068A (zh
Inventor
万义玲
孙美红
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Ocean University
Original Assignee
Guangdong Ocean University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangdong Ocean University filed Critical Guangdong Ocean University
Priority to CN2009101925850A priority Critical patent/CN101705068B/zh
Publication of CN101705068A publication Critical patent/CN101705068A/zh
Application granted granted Critical
Publication of CN101705068B publication Critical patent/CN101705068B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种新型保温隔音建筑涂料用微胶囊胶粘剂的制备，在适当的压力下，让隔热良好的气体或温室气体通过锐孔自然溢出到含有乳化剂的水溶液中，搅拌使它均匀形成圆形气泡，然后，采用乳化缩聚技术，使三聚氰胺壁材缩聚形成囊，制备涂料用微胶囊胶粘剂。还公布了新型保温隔音建筑涂料用微胶囊胶粘剂。本发明新型，保温，隔音，节能，符合环保要求，光洁度好，粘度大，经济实惠、市场潜力大。

Description

保温隔音建筑涂料用微胶囊胶粘剂的制备
技术领域
本发明属于一种新型保温隔音建筑涂料用微胶囊胶粘剂的制备。 
背景技术
目前，国内外的建筑和装饰涂料用胶粘剂一般不具有保温隔音性能或保温隔音效果不佳。对于一些建筑涂料中添加保温隔音效果好的材料，但由于胶粘剂保温隔音效果差，导致涂料涂层保温隔音效果不佳。因此，开发具有保温隔音效果好的建筑涂料用胶粘剂势在必行。 
发明内容
本发明要解决的技术问题之一是，锐孔成微泡及微泡稳定性问题。针对锐孔成微泡难，采取了加压，缓冲控压，锐孔出气口直平、宽广，在一定浓度和PH＝6左右的乳化剂中搅拌，自然溢出。使微泡大小均匀，稳定。本发明要解决的技术问题之二是，三聚氰胺予聚体在水包气(G/W)缩聚成囊问题及囊的稳定性问题。针对三聚氰胺予聚体在水包气(G/W)缩聚成囊过程中稳定性差，选择恰当的浓度和分批加入三聚氰胺予聚体缩聚成囊，固化成型。 
本发明在3000～3200帕压力下，让隔热良好的气体通过锐孔自然溢出到含有乳化剂的水溶液中，搅拌使它均匀形成圆形气泡，然后，采用乳化缩聚技术，使三聚氰胺壁材缩聚形成囊，制备涂料用微胶囊胶粘剂； 
所述的微胶囊胶粘剂重量比组成为： 
乳化剂  1-5份 
三聚氰胺壁材的固含量：10-85份 
隔热良好的气体  1～10份 
所述的微胶囊胶粘剂的制备的制备工艺流程为： 
三聚氰胺+甲醛形成预聚体→乳化剂90℃水中溶解→锐孔成泡→三聚氰胺+甲醛予聚体→60℃～80℃搅拌5～8小时→冷却室温→尿素→调pH＝7～ 10出料。 
本技术的优点： 
1.新型 
目前，国内外的建筑和装饰涂料用胶粘剂一般不具有保温隔音性能或保温隔音效果不佳。本发明的涂料用微胶囊胶粘剂，是通过胶粘剂的微囊化，包囊隔热良好的气体(如空气)或温室气体(如二氧化碳)，增加胶粘剂涂层的弹性，减少能量交换和衰减声波的传递能量来达到保温隔音的目的。因此，本发明的涂料微胶囊胶粘剂，是一种新型保温隔音材料。 
2.保温 
微胶囊胶粘剂包囊了一层隔热系数较好的致密气体微囊，因此，保温效果更佳，有利于节能降耗。 
3.隔音 
微胶囊胶粘剂包囊了一层气体微囊，增加胶粘剂涂层的弹性，衰减声波的传递能量，达到隔音、降低噪音的目的。本发明技术符合环保要求。 
4.节能 
微胶囊胶粘剂包囊了一层隔热系数较好的致密气体微囊，因此，保温效果更佳，有利于节能降耗。 
5.性能佳 
光洁度好，粘度大。 
6.经济实惠、市场潜力大 
由于工艺简单。因此设备和原材料投资少，加上比表面积大，在单位面积上喷涂的价格就越低。以及产品符合环保要求。因此，产品具备很强的市场竞争力，以经济实惠型走向市场。另外，产品还可以作为特种纸和胶合板的保温隔音胶粘剂，进军纸业和板材市场。 
具体实施方式
本发明在适当的压力下，让隔热良好的气体或温室气体通过锐孔自然溢出到含有乳化剂的水溶液中，搅拌使它均匀形成圆形气泡，然后，采用乳化缩聚技术，使三聚氰胺壁材缩聚形成囊，制备涂料用微胶囊胶粘剂。 
本发明技术符合环保要求。整个制备过程都是在水环境下进行的，虽然 在制备过程中放入了甲醛，但浓度很低，加入尿素的吸收，完全符合环保要求。 
实施例1新型保温隔音建筑涂料用微胶囊胶粘剂配方 
芯材：空气，锐孔孔径：1.6微米，压力：3000～3200帕，持续通45分钟；壁材：三聚氰胺30份，乳化剂：司盘-60 1份，甲醛60ml，乙醇60ml 
实施例2新型保温隔音建筑涂料用微胶囊胶粘剂配方 
芯材：二氧化碳，锐孔孔径：1.6微米，压力：3000～3200帕，持续通45分钟；壁材：三聚氰胺30份，乳化剂：司盘-60 1份，甲醛60ml，乙醇60ml 
实施例3新型保温隔音建筑涂料用微胶囊胶粘剂的制备： 
(1)予聚体：取60份三聚氰胺+120ml(36％)甲醛+40ml水，缓慢升温至65℃至溶液澄清后，加120ml乙醇继续搅拌反应10分钟，放置备用。 
(2)乳化剂的溶解：取1份司盘-60，在45ml水中，缓慢升温至90℃，搅拌直至溶解。 
(3)锐孔成泡：取上述溶液，在60℃搅拌下通气45分钟。 
(4)缩聚成囊：在60℃搅拌下，在上述溶液中加入40ml予聚体反应30分钟，加入40ml予聚体，升温至80℃，待溶液变白后，加入30ml予聚体，继续搅拌让溶液变稠，降温至60℃继续搅拌30分钟。 
(5)出料：将上述溶液溶液冷却至室温，调PH＝7～10，加入少量尿素，出料。 

Claims (1)

1.一种保温隔音建筑涂料用微胶囊胶粘剂的制备，其特征是在3000～3200帕压力下，让隔热良好的气体通过锐孔自然溢出到含有乳化剂的水溶液中，搅拌使它均匀形成圆形气泡，然后，采用乳化缩聚技术，使三聚氰胺壁材缩聚形成囊，制备涂料用微胶囊胶粘剂；
所述的微胶囊胶粘剂重量比组成为：
乳化剂    1-5份
三聚氰胺壁材的固含量：10-85份
隔热良好的气体1～10份
所述的微胶囊胶粘剂的制备工艺流程为：
三聚氰胺+甲醛形成预聚体→乳化剂90℃水中溶解→锐孔成泡→三聚氰胺+甲醛予聚体→60℃～80℃搅拌5～8小时→冷却室温→尿素→调pH＝7～10出料。 
CN2009101925850A 2009-09-17 2009-09-17 保温隔音建筑涂料用微胶囊胶粘剂的制备 Expired - Fee Related CN101705068B (zh)