CN101698763A - 一种无苯塑料凹版复合油墨 - Google Patents
一种无苯塑料凹版复合油墨 Download PDFInfo
- Publication number
- CN101698763A CN101698763A CN 200910066252 CN200910066252A CN101698763A CN 101698763 A CN101698763 A CN 101698763A CN 200910066252 CN200910066252 CN 200910066252 CN 200910066252 A CN200910066252 A CN 200910066252A CN 101698763 A CN101698763 A CN 101698763A
- Authority
- CN
- China
- Prior art keywords
- benzene
- free plastic
- composite ink
- plastic rotogravure
- rotogravure composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种无苯塑料凹版复合油墨，其原料包括乙酸乙酯、填充料、乙酸仲丁酯、树脂、3500添加剂和颜料，各原料及重量配比为：乙酸仲丁酯46-70％、填充料1-3％、树脂10-12、3500添加剂0.5-1％、颜料9-30％、乙酸乙酯5-10％。将以上原料根据产品需要按比例进行混合加入研磨罐搅拌分散后研磨，至规定细度进行调整，即生产出超过行业标准的无苯塑料凹版复合油墨。该油墨用环保溶剂乙酸仲丁酯代替甲苯无毒、无害，有利于食品安全，利于人民身心健康；加入树脂包括氯化EVA和氯化聚丙烯可以使制品的附着牢度大大提高，同时更有利于热复合工艺；加入3500添加剂可以使制品抗静电效果更佳，同时分散性能更优，更有利于制品的储存。
Description
技术领域
本发明涉及一种塑料凹版复合油墨，特别是一种无苯塑料凹版复合油墨。
背景技术
传统塑料复合油墨是以甲苯、二甲苯为主溶剂，乙酯、丁酯、丁酮、异丙醇为辅溶剂或助溶剂。该油墨的优点是价格低廉、蒸发速度快、印刷适应性好、附着牢度优良、复合性能佳等，深受彩印行业青睐；缺点是溶剂残留量大，特别是苯含量超标。出于环保安全，美国以及欧洲的很多国家在食品包装领域所用的油墨、粘胶剂甚至包括膜材均制定了严格的环保卫生标准，苯类溶剂的存在更是被列为严格禁止的行列，而我国目前塑料薄膜包装标准GB/T10004-1998中规定了苯类溶剂不检出的要求。特别是根据2009年6月1日起施行的《食品安全法》相关规定，对食品包装进行了严格的监管。鉴于此，选择一种合适的环保溶剂替代甲苯、二甲苯已势在必行。
发明内容
本发明所要解决的技术问题是提供一种绿色、环保、且价格低廉的溶剂替代甲苯的无苯塑料凹版复合油墨。
本发明采用的技术方案是：
该无苯塑料凹版复合油墨，其原料包括溶剂乙酸乙酯和填充料，并加入环保溶剂乙酸仲丁酯、树脂、3500添加剂和颜料混合而成。上述各原料及其重量配比为：
乙酸仲丁酯40-70％、填充料0.5-5％、树脂8-12％、3500添加剂0.4-1％、颜料8-35％、乙酸乙酯5-15％；
作为本发明的一种优选方式，该无苯塑料凹版复合油墨的原料及重量配比为：
乙酸仲丁酯46-70％、填充料1-3％、树脂10-12、3500添加剂0.5-1％、颜料9-30％、乙酸乙酯5-10％；
所述乙酸仲丁酯为环保溶剂，无毒、无害、有效的杜绝了甲苯的使用，向环境友好型迈进。
所述填充料为高岭土。
所述树脂为氯化EVA和氯化聚丙烯。
所述3500添加剂系日本三洋化成公司生产。
所述颜料为钛白粉、联苯胺黄、6B300红、250碳黑或酞青蓝，加入上述任何一种按其重量比的有色颜料后即可生产出具有相应色彩的无苯油墨。
该油墨系将所述各原料根据产品需要按比例进行混合加入研磨罐搅拌分散后研磨，至规定细度进行调整，即可生产出用乙酸仲丁酯代替甲苯的无苯塑料凹版复合油墨。
本发明所公开的无苯塑料凹版复合油墨，其有益效果是：1.用乙酸仲丁酯代替甲苯无毒、无害，有利于食品安全，利于人民身心健康；2.加入树脂包括氯化EVA和氯化聚丙烯可以使制品的附着牢度大大提高，同时更有利于热复合工艺；3.加入3500添加剂可以使制品抗静电效果更佳，同时分散性能更优，更有利于制品的储存。
按照该无苯油墨配方，可生产出超过行业标准的无苯塑料凹版复合油墨。根据有关检测数据，其各项性能指标为：
1细度：10-15μm
2粘度：25-70S
3初干性：20-50mm
4附着牢度：≥85％
5苯类残留：无
总之，采用无毒、无害、价格低廉的乙酸仲丁酯生产的无苯塑料凹版复合油墨品质优于目前市场上销售的传统复合油墨，具有广阔的市场开发潜力。
具体实施方式：
以下介绍本发明的实施例。
实施例1无苯塑料凹版复合油墨配方：
原料名称 重量百分比
乙酸仲丁酯 50％
氯化EVA树脂 6％
氯化聚丙烯树脂 4％
钛白粉 30％
高岭土 3％
乙酸乙酯 6％
3500添加剂(日本产) 1％
以上配方经分散研磨调整后，即生产出无毒的无苯塑料凹版复合白墨。实施例2无苯塑料凹版复合油墨配方：
原料名称 重量百分比
氯化EVA树脂 6％
氯化聚丙烯树脂 4％
联苯胺黄 9％
乙酸仲丁脂 69％
乙酸乙酯 10％
高岭土 1.5％
3500添加剂(日本产) 0.5％
以上配方经分散研磨调整后，即生产出无毒的无苯塑料凹版复合黄墨。实施例3无苯塑料凹版复合油墨配方：
原料名称 重量百分比
氯化EVA树脂 7％
氯化聚丙烯树脂 4％
6B300红 9％
乙酸仲丁脂 68％
乙酸乙酯 10％
高岭土 1％
3500添加剂 1％
以上配方经分散研磨调整后，即生产出无苯、无毒塑料凹版复合无苯红墨。实施例4无苯塑料凹版复合油墨配方：
原料名称 重量百分比
氯化EVA树脂 7％
氯化聚丙烯树脂 4％
酞青蓝 9％
乙酸仲丁脂 68％
乙酸乙酯 10％
高岭土 1％
3500添加剂 1％
以上配方经分散研磨调整后，即生产出无毒的无苯塑料凹版复合蓝墨。实施例5无苯塑料凹版复合油墨配方：
原料名称 重量百分比
氯化EVA树脂 7％
氯化聚丙烯树脂 4％
250R 11％
乙酸仲丁脂 66％
乙酸乙酯 10％
高岭土 1％
3500添加剂 1％
以上配方经分散研磨调整后，即生产出无毒的无苯塑料凹版复合黑墨。
Claims (7)
1.一种无苯塑料凹版复合油墨，其特征在于：该油墨原料包括溶剂乙酸乙酯、填充料、乙酸仲丁酯、树脂、3500添加剂和颜料，各原料及其重量配比为：
乙酸仲丁酯40-70％、填充料0.5-5％、树脂8-12、3500添加剂(日本产)0.4-1％、颜料8-35％、乙酸乙酯5-15％。
2.根据权利要求1所述的无苯塑料凹版复合油墨，其特征在于：其原料及重量配比为：
乙酸仲丁酯46-70％、填充料1-3％、树脂10-12、3500添加剂0.5-1％、颜料9-30％、乙酸乙酯5-10％。
3.根据权利要求1或2所述的无苯塑料凹版复合油墨，其特征在于：所述填充料为高岭土。
4.根据权利要求1或2所述的无苯塑料凹版复合油墨，其特征在于：所述树脂为氯化EVA和氯化聚丙烯。
5.根据权利要求1或2所述的无苯塑料凹版复合油墨，其特征在于：所述3500添加剂系日本三洋化成公司生产。
6.根据权利要求1或2所述的无苯塑料凹版复合油墨，其特征在于：所述颜料为钛白粉、联苯胺黄、6B300红、250碳黑和酞青蓝中的任一种。
7.根据权利要求1或2所述的无苯塑料凹版复合油墨，其特征在于：该油墨系将所述各原料按比例进行混合加入研磨罐搅拌分散后研磨，至规定细度后进行调整即成该复合油墨。