CN101676341B - 含有低挥发性化合物的涂料组合物 - Google Patents

含有低挥发性化合物的涂料组合物 Download PDF

Info

Publication number
CN101676341B
CN101676341B CN200910138444.0A CN200910138444A CN101676341B CN 101676341 B CN101676341 B CN 101676341B CN 200910138444 A CN200910138444 A CN 200910138444A CN 101676341 B CN101676341 B CN 101676341B
Authority
CN
China
Prior art keywords
group
coating composition
condensing agent
carbon atoms
general formula
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
CN200910138444.0A
Other languages
English (en)
Other versions
CN101676341A (zh
Inventor
L·B·勃兰登布格尔
B·西克尔斯蒂尔
M·J·欧文斯
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Industrial Solution Co
Xuanwei Headquarters Co
Xuanwei Investment Management Co ltd
Sherwin Williams Co
Valspar Corp
Original Assignee
Valspar Sourcing Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Valspar Sourcing Inc filed Critical Valspar Sourcing Inc
Publication of CN101676341A publication Critical patent/CN101676341A/zh
Application granted granted Critical
Publication of CN101676341B publication Critical patent/CN101676341B/zh
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

涂料组合物包含凝结剂和胶乳聚合物，其特征在于凝结剂中的挥发性有机物含量少于50％，并且该凝结剂可分散于涂料组合物中。

Description

含有低挥发性化合物的涂料组合物
本申请是申请日为2002年2月22日，申请号为02805352.4，发明名称为“含有低挥发性化合物的涂料组合物”的发明专利申请的分案申请。 
相关申请 
本申请要求在先申请的美国专利No.60/270,680提出的优先权，提交日期为2001年2月22日，此专利的的全部内容结合引用于本文中以作参考。 
发明背景 
涂料组合物，例如油漆，它包括胶乳聚合物颗粒，除了颜料和填充剂以外典型的也包括凝结剂(如凝结剂或成膜剂)。凝结剂的功能是作为溶剂，也作为聚合物颗粒的增塑剂，以软化胶乳聚合物颗粒，当它被涂布于表面并干燥后，有助于形成连续的涂层和膜。 
有用的凝结剂通常稳定存在于水中，并与其他典型用于油漆配制的组分，特别是胶乳聚合物相容，不损害胶乳基组合物的稳定性。它们通常具有足够的挥发性，使被涂布的涂层组合物在干燥时能挥发掉，但要比其他成分(如干燥抑制剂，防冻剂等)的挥发性差得多，使其挥发就更缓慢，从而延迟了薄膜的形成。但是，工业上通常更希望减少挥发性有机物的散发，以减少其对环境和健康的影响。 
政府已经制定法规，规定了允许释放到大气中的挥发性有机化合物的指标。为了减少挥发性有机化合物的量，新的高固含量涂料组合物已经被开发，而不包含挥发性化合物的粉末状涂料组合物能减少挥发性化合物的含量，或含有更低挥发性的化合物。但是，减少凝结剂，溶剂，增塑剂等的挥发性可能带来不利影响，如影响胶乳基涂料组合物所需性能的平衡。因此，要求可用于涂料组合物(如油漆)中的凝结剂，溶剂，增塑剂等不损害稳定性，相容性，成膜性或对被涂布涂料所要求满足的性质等。 
概述 
本发明提供了一类具有较低挥发性有机物含量的化合物。这些化合物可以用于涂料组合物(较好的是油漆)，如凝结剂，溶剂，增塑剂等。一种合适的凝结剂可分散于涂料组合物中，较好的是具有长时间的稳定性。这种化合物作为凝结剂使用时，优选在低于25℃(在4～10℃，最优选在4～5℃)时能促进胶乳基聚合物形 成聚合物膜。因此，提供一种涂料组合物，它包括胶乳聚合物和凝结剂(其功能也可以作为溶剂或增塑剂)。这些涂料组合物如同油漆涂布于基底上并被干燥。 
在一个实施例中，一种涂料组合物(优选油漆)包括：胶乳聚合物；和具有通式R1-(C(O)-Xr-O)n-R2的凝结剂，式中：R1是有机基团(较好的是碳原子数少于100)；X是两价有机基团(较好的是碳原子数2～8，更好的是碳原子数3～5)；r是0～1；n是1～10(较好的是n为1～5，更好的n为1～3，最好的n为2～3)；R2是氢或有机基团(较好的是碳原子数少于100)；当X不是-(CH2)s-(其中s是2～8)时，一个附带条件是R1包括至少三个碳原子；当r是0时，一个附带条件是凝结剂有少于两个脂族不饱和C-C键(较好的是，当r是0时，凝结剂不包括脂族不饱和C-C键，最好的是凝结剂不包括脂族不饱和C-C键)；其特征在于凝结剂中的挥发性有机物含量少于50％(较好的少于30％，更好的少于20％，最好少于15％)，并且所述凝结剂可分散于涂料组合物中。r优选1。 
在另一个实施例中，一种涂料组合物包括：胶乳聚合物；和具有通式R1-(C(O)-Xr-O)n-R2的凝结剂，式中：R1是有机基团；X是两价有机基团；r是0～1；n是1～10；R2是氢或有机基团；当X不是-(CH2)s-(其中s是2～8)时，一个附带条件是R1包括至少三个碳原子；一个附带条件是凝结剂不包括脂族不饱和C-C健；当R2是H时，一个附带条件是r是1；其特征在于凝结剂中的挥发性有机物含量少于50％，并且所述凝结剂可分散于涂料组合物中，促进胶乳聚合物在低于25℃，(优选4～10℃，更优选4～5℃)时形成聚合物膜。 
在另一个实施例中，一种涂料组合物包括：胶乳聚合物；和具有通式R1-(C(O)-Xr-O)n-R2的凝结剂，式中：R1具有通式R3-(CH2)m-(O(CH2)p)q-，其中R3是烷基或芳基；m是0～24，p是1～4，q是0～50；X具有通式-(CH2)s-，其中s是2～8；r是0～1；n是1～10；R2是氢或R1；其特征在于凝结剂中的挥发性有机物含量少于50％，所述凝结剂可分散于涂料组合物中，促进胶乳聚合物在低于25℃(优选4～10℃，更优选4～5℃)时形成聚合物膜。 
在另一个具体实例中，一种涂料组合物包括：胶乳聚合物；和具有通式R1-(C(O)-X-O)n-H的凝结剂，式中：R1是烃基部分或具有取代基的有机基团，所述取代基选自非过氧化氧原子，羟基及其组合物；X是两价的烃基部分或包含非过氧化氧原子和羰基的有机基团；n是1～10；其特征在于凝结剂中的挥发性有机物含量少于50％(较好的少于30％)，并且所述凝结剂可分散于涂料组合物中。 
还在另一个实施例中，一种涂料组合物包括：胶乳聚合物；和具有通式 R1-(C(O)-X-O)n-H的凝结剂，式中：R1是烃基部分或具有取代基的有机基团，所述取代基选自非过氧化氧原子，羟基及其组合；X具有通式-(CH2)s-，其中s是2～8；n是1～10；其特征在于凝结剂中的挥发性有机物含量少于50％(优选少于30％)，所述凝结剂可分散于涂料组合物中。 
在另一个具体实例中，一种涂料组合物包括：胶乳聚合物；和具有通式R1-(C(O)-X-O)n-H的凝结剂，式中：R1是烃基部分或含有非过氧化氧的有机基团；X是包含非过氧化氧和羰基的有机基团；n是1～10；其特征在于凝结剂中的挥发性有机物含量少于50％(优选少于30％)，所述凝结剂可分散于涂料组合物中。 
本发明也提供了涂布方法，其包括：提供如上所述的涂料组合物；将涂料组合物涂布于基底(如墙面)上；使涂料组合物干燥。 
定义 
术语“可分散的”用于本文中可分散的凝结剂的含义是：不用高剪切的混合，就能将凝结剂和涂料组合物混合形成均一混合物。 
术语“稳定的”用于本文中含有可分散凝结剂的涂料组合物的含义是：凝结剂在120°F(49℃)时静置四星期，不会与涂料组合物产生相分离。 
术语“挥发性有机物含量”和“VOC”在这里的含义是：采用ASTM D2369-90方法测定的化合物的挥发性。 
术语“有机基团”是指碳氢化合物(也就是烃基)基团，其在链中除了碳和氢还有其他可任选的元素，如氧，氮，硫和硅，它归类于脂族基团，环状基团，或脂族和环状基团的组合(如烷芳基和芳烷基)。术语“脂族基团”是指饱和的或不饱和的直链或支链碳氢化合物基团。这里所用的术语包括烷基，烯基和炔基，术语“烷基”是指饱和的直链或支链碳氢化合物基团，其包括甲基，乙基，异丙基，叔丁基，庚基，十二烷基，十八烷基，戊基，2-乙基己基等。术语“烯基”是指不饱和的直链或支链碳氢化合物基团，它有一个或多个C-C双健，如乙烯基。术语“炔基”是指不饱和的直链或支链碳氢化合物基团，它有一个或多个C-C三健。术语“环状基团”是指闭环状碳氢化合物基团，它被归类于脂环族基团，芳香族基团，或杂环族基团。术语“脂环族基团”是指环状碳氢化合物基团，它与脂族基团具有相类似的性质。术语“芳香族基团”或“芳基”是指单环或多环芳香族碳氢化合物基团。术语“杂环族团”是指闭环状碳氢化合物，它在环中有一个或多个除碳原子外的原子(如氮，氧，硫等)。 
对用于本发明涂料组合物的凝结剂中的有机基团被预先进行取代。作为对用于本专利申请全文中某些术语的讨论和所述的简化方式，术语“基团”和“部分”用于把化学品区分成为，前者允许取代或可以被取代，后者不允许取代或不可以被取代。因此，当术语“基团”用于描述化学取代基时，所述化学物质包括未被取代的基团和具有O，N，Si，或S原子的基团，例如，在链的(烷氧基)和羰基或其他习用的取代中。术语“部分”用于描述一个化合物或取代基时，只包括未被取代的化学物质。例如，词组“烷基基团”是指不仅包括纯开链饱和烃烷基取代基，如甲基，乙基，丙基，叔丁基等，而且包括烷基取代基按众所周知的方法被进一步取代，如羟基，烷氧基，烷基磺酰基，卤素原子，氰基，硝基，氨基，羧基等。因此“烷基基团”包括醚基，卤代烷基，硝基烷基，羧基烷基，羟基烷基，磺基烷基等。另一方面，词组“烷基部分”限于只有纯的开链饱和烃烷基取代基，如甲基，乙基，丙基，叔丁基等。术语“烃基部分”是指只含有碳和氢的未取代有机物部分。 
优选实施方案的详细描述 
本发明涉及包含凝结剂的涂料组合物，所述凝结剂也可任选地起到增塑剂和/或溶剂的作用以及其后制得的涂料。这些涂料组合物优选呈油漆形式。这些涂料组合物优选包括聚合物，较好的是胶乳聚合物，以及一种或多种凝结剂。这些凝结剂可分散于涂料组合物中，并具有较好的长时间的稳定性。(也就是，所述凝结剂在49℃时静置四星期不会与涂料组合物产生相分离。) 
本发明所述的涂料组合物具有较低挥发性有机物含量的优点，且不牺牲对涂布后(即干燥后)的涂料(如油漆)所要求的性质平衡。例如，由本发明的涂料组合物提供的涂布后涂料具有较好的耐擦洗性，通过下面实施例部分中所提出的测试方法的测试结果至少与TEXANOL相当，TEXANOL是由三甲基戊二醇和异丁酸合成的醇/酯化合物((H3C)2-CH-C(O)-O-CH2-C(CH3)2-CH2(OH)-CH(CH3)2)。 
涂料组合物优选包括具有较低挥发性有机物含量(VOC)的化合物，更优选具有较低分子量的化合物。用下面实施例部分中所提出的测试方法进行测试，以凝结剂起始重量为基准，挥发性有机物含量通常不大于50％，较好的不大于30％，更好的不大于20，最好不大于15％。这些化合物的数均分子量优选不大于750，更优选小于500。 
优选的是，这些化合物是好的凝结剂。也就是说，它们较好的对胶乳聚合物提供好的成膜性。更优选的是，特别希望这类化合物的基团在低温时(低于室温) 提供好的成膜性，其成膜性按下面实施例部分中所提出的测试方法测试。较好的，这些化合物优选在低于25℃(更优选在4～10℃，最优选在4～5℃)时促进胶乳聚合物形成聚合物膜。 
这些低VOC化合物优选具有通式，R1-(C(O)-Xr-O)n-R2，式中：n是1～10；R1是有机基团，优选碳原子数少于100，更优选碳原子数在3～24；R2是氢或有机基团，优选的是碳原子数少于100；X是两价有机基团，优选碳原子数在2～8，更优选碳原子数在3～5；r是0～1；n优选1～5，更优选1～3，最优选2～3。 
较好的，R1优选烃基部分，尽管在某些优选实施方案中R1是具有取代基的有机基团，所述取代基选自非过氧化氧原子，羰基，羟基及其组合；所述取代基更优选自非过氧化氧原子，羟基及其组合；最优选是非过氧化氧原子。在某些实施例中，R1具有通式R3-(CH2)m-(O(CH2)p)q-，其中R3是烷基或芳基；m是0～24，p是1～4(p优选1～2)，q是0～50。对于R1的优选通式中，m+pq优选小于23。 
X优选两价烃基部分，尽管在某些优选实施方案中X是具有取代基的有机基团，所述取代基选自非过氧化氧原子，羰基及其组合；所述取代基更优选自非过氧化氧原子和羰基。在某些实施例中，X具有通式-(CH2)s-，其中s是2～8；s优选3～5。 
R2优选氢，尽管在某些优选实施例中R2如同上述定义的R1。在某些具体实例中，当R2是氢时，r是1。 
在某些实施例中，当X不是-(CH2)s-(其中s是2～8时)时，R1包括至少三个碳原子；当r是0时，R1和R2一起(也就是涂料组合物)包括少于两个脂族不饱和C-C键；当r是0时，R1和R2一起(也就是涂料组合物)优选不包括任何脂族不饱和C-C键；R1和R2一起(也就是涂料组合物)更优选不包括任何脂族不饱和C-C键。 
在某些实施例中，R1是具有3～24碳原子和取代基的有机基团，所述取代基选自氧原子，羰基，羟基及其组合；R2是氢。 
这些化合物的优选基团具有通式R1-(C(O)-Xr-O)n-R2，其中：R1是有机基团；X是两价有机基团；r是0～1；n是1～10；R2是氢或有机基团；当X不是-(CH2)s-(其中s是2～8时)时，一个附带条件是R1包括至少三个碳原子；当r是0时，一个附带条件是凝结剂有少于两个脂族不饱和C-C健。例如，这些化合物可由己内酯和醇制得。 
这些化合物另一个优选基团具有通式R1-(C(O)-Xr-O)n-R2，其中：R1是有机基团；X是两价有机基团；r是0～1；n是1～10；R2是氢或有机基团；当X不是(CH2)s- (其中s是2～8时)时，一个附带条件是R1包括至少三个碳原子；一个附带条件是凝结剂不包括脂族不饱和C-C健；当R2是H时，一个附带条件是r是1。 
这些化合物另一个优选基团类有通式R1-(C(O)-Xr-O)n-R2，其中：R1具有通式R3-(CH2)m-(O(CH2)p)q-，其中R3是烷基或芳基；m是0～24，p是1～4，q是0～50；X具有通式-(CH2)s-(其中s是2～8)；r是0～1；n是1～10；R2是氢或R1。 
这些化合物另一个优选基团具有通式R1-(C(O)-X-O)n-H，其中：R1是烃基部分或具有取代基的有机基团，所述取代基选自非过氧化氧原子，羟基及其脂族；X是两价烃基部分或包含非过氧化氧原子和羰基的有机基团；n是1～10。例如，这些化合物可由新癸酸缩水甘油酯(如，CARDURA E 10)和羧酸反应制得。 
这些化合物另一个优选基团具有通式R1-(C(O)-X-O)n-H，其中：R1是烃基部分或具有取代基的有机基团，所述取代基选自非过氧化氧原子，羟基及其脂族；X具有通式-(CH2)s-，其中s是2～8；n是1～10。 
这些化合物另一个优选基团具有通式R1-(C(O)-X-O)n-H，其中：R1是烃基部分或包含非过氧化氧原子的有机基团；X是包含非过氧化氧原子和羰基的有机基团；n是1～10。 
这些化合物可以使用标准有机合成技术合成，这是本技术领域内有相关知识的人所众所周知的。具体的合成在下面实施例部分中阐述。 
本发明中涂料组合物的优选聚合物包括胶乳聚合物(也就是胶乳)。这些在油漆工艺技术中是众所周知的，通常是乳化或悬浮于水溶性介质中的颗粒。例如，它们包括含有不饱和烯键单体的聚合反应产物，如烷基和烷氧基丙烯酸酯或甲基丙烯酸酯，饱和的羧酸乙烯基酯，单烯烃，共轭双烯，可选地与一个或多个单体，如苯乙烯，甲基丙烯酸甲酯，丙烯酸丁酯，丙烯酸2-乙基己酯，醋酸乙烯酯，丙烯腈和氯乙烯一起。胶乳聚合物根据对生成涂料所需要的性质，可以有较宽的玻璃转化温度。 
本发明中涂料组合物所含聚合物的量和低VOC化合物包括达到满意效果所要求的量。较好的，一种或多种较低VOC化合物，它们在涂料组合物中起到较好的凝结剂的功能，以聚合物固体计，其量优选至少占1％重量百分比(wt-％)，更优选至少2wt-％，最优选至少5wt-％。一种或多种较低VOC化合物，它们在涂料组合物中以聚合物固体计，其量优选不大于50wt-％，更优选不大于25wt-％。当使用这些凝结剂的混合物时，在上述通式中变量的数值是一个平均值。 
本发明涂料组合物的其他组分包括那些在油漆配制中，通常使用的组分，如 颜料，填充剂，增稠剂，杀虫剂，防霉剂，表面活性剂，分散剂，消泡剂等。涂料组合物可以使用油漆工业所熟知的标准技术制备。 
实施例
下列实施例旨在理解本发明，而不是用于限制本发明的范围。除非另行注明，所有部分和百分比都以重量计。 
VOC测试： 
使用ASTM D-2369-90方法，测试凝结剂。在一个已称量的铝制盘子中称取约0.5克(g)凝结剂，然后放置于一个空气强制流动的烘箱中加热到110℃，停留时间1小时。盘子重新称量，失去的重量表示凝结剂中VOC的百分数(％)。 
耐擦洗性： 
用一个标准3-mil(0.0762毫米(mm))Bird膜涂布机(购自Byk Gardner)将涂料涂布在一块黑色乙烯基擦洗测试板上(购自Leneta公司)。涂膜在室温下干燥7天。用Gardner Abrasion测试器(购自Byk Gardner)，10g擦洗介质进行耐擦洗性测试。直到涂膜第一次被擦去，记录下擦洗的次数。 
低温凝结性(LTC)： 
用一个标准3-mil Bird膜涂布机将涂料涂布在一块Penopac纸板上(购自Leneta公司)。将板放入40°F(4.4℃)的冰箱中直到干燥。涂膜没有出现任何裂缝则认为通过测试。膜出现任何裂缝则被认为失败。 
实施例1 
制备凝结剂化合物 
操作1.凝结剂的制备 
在一个配置机械搅拌的500ml四口圆底烧瓶中，加入ε-己内酯(2-oxepanone)(174g)，1-十二烷醇(173g)，和FASCAT2003(辛酸亚锡，购自AtofinaChemicals)(0.2g)。将烧瓶中的物料加热到150℃，并保持直到采用色谱检测出的游离己内酯含量低于0.5％(约4小时)，然后冷却到室温。 
操作2-20.凝结剂的制备 
按照实施例1，操作1的步骤制备各种凝结剂。所不同的是将174g己内酯改变成根据表1A所列的数量，以及将实施例1，操作1中所使用的173g1-十二烷醇用表1A所列的醇和其量替代。 
表1A 
  操作   醇   己内酯(克)/  醇(克)   摩尔比  己内酯∶醇   ％VOC
  1   1-十二烷醇   174/173   1.64∶1   7.0％
  2   1-十二烷醇   200/163   2∶1   6.0％
  3   1-十二烷醇   225/147   2.5∶1   4.0％
  4   1-十二烷醇   240/130.5   3∶1   3.0％
  5   1-十二烷醇   265/108   4∶1   2.0％
  6   苄醇   228/108   2∶1   9.0％
  7   2，2，4-三甲基-1，3戊二醇(TMPD)   196/140   1.7∶1   15％
  8   2-乙基己醇，2mol EO   157/200   1.5∶1   10％
  9   2-氨基-2-甲基-1-丙醇(AMP-95)   228/71.2   2.5∶1   3.0％
  10   1-己醇   228/81.8   2.5∶1   5.0％
  11   2-丁氧基乙醇(丁基溶纤剂)   228/94.4   2.5∶1   8.0％
  12   1-丁醇   228/74.1   2.5∶1   7.0％
  13   2(2-丁氧基乙氧基)乙醇(丁基卡必醇)   228/129.8   2.5∶1   9.0％
  14   1-辛醇   228/104.2   2.5∶1   5.0％
  15   2-丙氧基乙醇(丙基溶纤剂)   228/83.2   2.5∶1   9.0％
  16   1-丙醇   228/48   2.5∶1   11.0％
  17   2-丁基-2-乙基-1，3丙二醇   174/98   2.5∶1   3.5％
  18   1，3-丁二醇   228/72   2.5∶1   3.0％
  19   2-甲氧基乙醇(甲基溶纤剂)   228/60.8   2.5∶1   7.0％
  20   2-乙氧基乙醇(溶纤剂)   228/72.1   2.5∶1   7.5％
*采用这种测试方法TEXANOL是99.5％VOC 
实施例2 
凝结剂化合物的制备 
操作1.由CARDURA E10制备凝结剂 
在一个配置机械搅拌的500ml四口圆底烧瓶中，加入CARDURAE10(新癸酸缩水甘油酯，购自SHELL Chemical)(228g)。将烧瓶加热到140℃，在90min内加入88g异丁酸。烧瓶的物料在140℃下维持2小时，然后冷却到室温。 
操作2-3.凝结剂的制备 
按照实施例2，操作1的步骤制备各种凝结剂。所不同的将实施例2，操作1中所使用的88g异丁酸被表2A所列的酸替代。 
表2A 
  操作   酸   数量(克)   ％VOC
  1   异丁酸   88   7.0％
  2   乙酸   60   9.0％
  3   丙酸   74   10.0％
实施例3 
涂料组合物的制备 
将列于表3A的组分混合，制备各种涂料组合物。在每一种涂料组合物中的凝结剂描述于实施例1和2。 
表3A 
  材料   说明   克
  水     62.0
  乙二醇     35.0
  AMP-95   胺，Angus   1.0
  TAMOL 731   分散剂，Rohm&Hass   10.0
  DEHYDRAN 1620   消泡剂，Cognis   1.0
  RCL-535   TiO2，Millennium   245.0
  KATHON LX 1.5％   杀虫剂，Rohm&Hass   1.7
     
  胶乳聚合物     453
  氢氧化铵     2.0
  凝结剂     26.3
  乙二醇     20.9
  SURFYNOL 504   表面活性剂，Air Products   1.0
  ACRYSOL RM-2020NPR   增稠剂，Rohm&Hass   4.0
  ACRYSOL RM-6   增稠剂，Rohm&Hass   31.0
  FOAMASTER SA-3   消泡剂，Cognis   3.5
  水     156.0
[0073] 表3B 
  实施例  1，步骤   醇   摩尔比  己内酯∶醇  擦洗(相对 TEXANOL)   LTC
  1   1-十二烷醇   1.7∶1   1.27   通过
  2   1-十二烷醇   2∶1   1.09   通过
  3   1-十二烷醇   2.5∶1     通过
  4   1-十二烷醇   3∶1   1.07   通过
  5   1-十二烷醇   4∶1   0.71   通过
  6   苄醇   2∶1     通过
  7   2，2，4-三甲基-1，3戊二醇(TMPD)   1.7∶1   0.81   通过
  8   2-乙基己醇，2mol EO   1.5∶1   0.96   通过
  9   2-氨基-2-甲基-1-丙醇(AMP-95)   2.5∶1     失败
  10   1-己醇   2.5∶1   1.10   通过
  11   2-丁氧基乙醇(丁基溶纤剂)   2.5∶1   1.35   通过
  12   1-丁醇   2.5∶1   1.27   通过
  13   2(2-丁氧基乙氧基)乙醇(丁基卡必醇)   2.5∶1     通过
  14   1-辛醇   2.5∶1     通过
  15   2-丙氧基乙醇(丙基溶纤剂)   2.5∶1     通过
  16   1-丙醇   2.5∶1     通过
  17   2-丁基-2-乙基-1，3丙二醇   2.5∶1     通过
  18   1，3-丁二醇   2.5∶1     失败
  19   2-甲氧基乙醇(甲基溶纤剂)   2.5∶1     通过
  20   2-乙氧基乙醇(溶纤剂)   2.5∶1     通过
TEXANOL LTC：通过，擦洗＝1.0 
表3C 
  实施例2，操作   酸   LTC
  1   异丁酸   通过
  2   乙酸   通过
  3   丙酸   通过
[0078] 表3D 
  实施例3，化合物   VOC   LTC
  苯甲酸异癸酯   15％   通过
  己二酸双(2-乙基己基)酯   0.6％   通过
通过本发明的优选实施方式的说明，本领域的技术人员将迅速领会上述学说可以应用于本权利要求范围内的其他实施方式。所有专利，专利文件和出版物的全部内容都将在此处逐一引用以作参考。 

Claims (15)

1.一种涂料组合物，包含：
胶乳聚合物；和
具有以下通式的凝结剂，
R1-(C(O)-X-O)n-R2
式中：
R1是选自脂族基团、环状基团或其组合的基团，其中所述环状基团是脂环族基团或杂环族基团；
X是两价有机基团；
n是1～10；
R2是氢或有机基团；
当X不是-(CH2)s-，其中s是2～8，时，一个附带条件是R1包含至少三个碳原子，
其特征在于采用ASTM D2369-90方法测定的所述凝结剂中的挥发性有机物含量(VOC)不大于15％，并且所述凝结剂可分散于所述涂料组合物中。
2.一种涂料组合物，包含：
胶乳聚合物，其包含乳化或悬浮于水溶性介质中的聚合物颗粒和表面活性剂；
相对于聚合物固体计为至少1重量％的具有以下通式的凝结剂，
R1-(C(O)-Xr-O)n-R2
式中：
R1是具有至少3个碳原子但少于100个碳原子的有机基团，其中所述有机基团是脂族基团、脂环族基团、杂环族基团或其组合；
X是两价有机基团；
r是0或1；
n是1～10；
R2是氢或具有少于100个碳原子的有机基团；
一个附带条件是R1和R2一起不包含任何脂族不饱和C-C键，
其特征在于采用ASTM D2369-90方法测定的所述凝结剂中的挥发性有机物含量不大于15％，所述凝结剂可分散于所述涂料组合物中，并且促进所述胶乳颗粒在将所述组合物涂布于表面上并使其干燥后形成连续涂层或膜。
3.一种涂料组合物，包含：
胶乳聚合物，其包含乳化或悬浮于水溶性介质中的聚合物颗粒和表面活性剂；
具有以下通式的凝结剂，
R1-(C(O)-Xr-O)n-R2
式中：
R1是具有3～24个碳原子的烃基部分，其中所述烃基部分是脂族部分、脂环族部分、杂环族部分或其组合；
X是具有2～8个碳原子的两价有机基团；
r是1；
n是1；
R2是具有少于100个碳原子的有机基团，并包含羰基；
一个附带条件是R1和R2一起不包含任何脂族不饱和C-C键，
其特征在于采用ASTM D2369-90方法测定的所述凝结剂中的挥发性有机物含量不大于50％，所述凝结剂可分散于所述涂料组合物中，并且促进所述胶乳颗粒在将所述组合物涂布于表面上并使其干燥后形成连续涂层或膜。
4.一种涂料组合物，包含：
胶乳聚合物，其包含乳化或悬浮于水溶性介质中的聚合物颗粒和表面活性剂；
相对于聚合物固体计为至少1重量％的具有以下通式的凝结剂，
R1-(C(O)-Xr-O)n-R2
式中：
R1是具有至少3个碳原子但少于100个碳原子的有机基团，其中所述有机基团是脂族基团、脂环族基团、杂环族基团或其组合；
X是两价有机基团；
r是0或1；
n是1～10；
R2是氢或具有少于100个碳原子的有机基团；
一个附带条件是R1和R2一起不包含任何脂族不饱和C-C键，
其特征在于所述具有通式的凝结剂可分散于所述涂料组合物中，并且促进所述胶乳颗粒在将所述组合物涂布于表面上并使其干燥后形成连续涂层或膜；以及
所述组合物包含多种凝结剂的混合物，采用ASTM D2369-90方法测定的所述混合物的平均合并挥发性有机物含量不大于15％。
5.一种涂料组合物，包含：
胶乳聚合物，其包含乳化或悬浮于水溶性介质中的聚合物颗粒和表面活性剂；
具有以下通式的凝结剂，
R1-(C(O)-Xr-O)n-R2
式中：
R1是具有3～24个碳原子的烃基部分，其中所述烃基部分是脂族部分、脂环族部分、杂环族部分或其组合；
X是具有2～8个碳原子的两价有机基团；
r是1；
n是1；
R2是具有少于100个碳原子的有机基团，并包含羰基；
一个附带条件是R1和R2一起不包含任何脂族不饱和C-C键，
其特征在于所述具有通式的凝结剂可分散于所述涂料组合物中，并且促进所述胶乳颗粒在将所述组合物涂布于表面上并使其干燥后形成连续涂层或膜；以及
所述组合物包含多种凝结剂的混合物，采用ASTM D2369-90方法测定的所述混合物的平均合并挥发性有机物含量不大于50％。
6.如权利要求1至5中任意一项所述的涂料组合物，其特征在于R1包含选自氧原子、羰基、羟基及其组合的取代基。
7.如权利要求1至5中任意一项所述的涂料组合物，其特征在于R1是脂族烃基部分并且包含3-24个碳原子。
8.如权利要求1至5中任意一项所述的涂料组合物，其特征在于R2包含3-24个碳原子和羰基。
9.如权利要求1、2和4中任意一项所述的涂料组合物，其特征在于X是具有2-8个碳原子的两价有机基团。
10.如权利要求1至5中任意一项所述的涂料组合物，其特征在于X是具有选自非过氧化氧原子、羰基及其组合的取代基的有机基团。
11.如权利要求1至5中任意一项所述的涂料组合物，其特征在于所述具有通式的凝结剂在49℃下静置四星期不会与所述涂料组合物产生相分离。
12.如权利要求1至5中任意一项所述的涂料组合物，其特征在于所述具有通式的凝结剂不包含脂族不饱和碳碳键。
13.如权利要求1至5中任意一项所述的涂料组合物，其特征在于所述具有通式的凝结剂在低于25℃的温度下促进所述胶乳聚合物形成聚合物膜。
14.如权利要求1至5中任意一项所述的涂料组合物，其特征在于所述具有通式的凝结剂具有不大于750的数均分子量。
15.如权利要求1至5中任意一项所述的涂料组合物，所述涂料组合物呈较低VOC油漆形式，其中所述聚合物颗粒包括烷基和烷氧基丙烯酸酯或甲基丙烯酸酯可选与苯乙烯、甲基丙烯酸甲酯、丙烯酸丁酯、丙烯酸2-乙基己酯、醋酸乙烯酯、丙烯腈和氯乙烯中的一个或多个的聚合产物。
CN200910138444.0A 2001-02-22 2002-02-22 含有低挥发性化合物的涂料组合物 Expired - Lifetime CN101676341B (zh)