CN101659566B - Suboptical black grinding glaze material - Google Patents
Suboptical black grinding glaze material Download PDFInfo
- Publication number
- CN101659566B CN101659566B CN2008102184767A CN200810218476A CN101659566B CN 101659566 B CN101659566 B CN 101659566B CN 2008102184767 A CN2008102184767 A CN 2008102184767A CN 200810218476 A CN200810218476 A CN 200810218476A CN 101659566 B CN101659566 B CN 101659566B
- Authority
- CN
- China
- Prior art keywords
- percent
- water
- calcite
- adjusting adhesive
- suboptical
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to the technical field of a glaze material, in particular to a suboptical black grinding glaze material which comprises the following components in percentages by weight: 20-40 percent of manganese oxide, 50-70 percent of viscosity-regulating agent, 1.5-4.5 percent of potassium feldspar, 0.2- 0.8 percent of calcite, 0.2-0.8 percent of iron oxide red, 0.01-0.05 percent of aluminum oxide, 0.05-0.3 percent of grass ash and the balance of water. The ceramic using the suboptical black grinding glaze material has good surface texture and moderate brightness; and the invention is widely applied to decoration.
Description
Technical field:
The present invention relates to the glaze technical field, particularly a kind of inferior light black frosted glaze.
Background technology:
Glaze is a kind ofly to have HS and a full-bodied material through what water, pigment, sticker and glaze basic components made.In the porcelain industry, the moulding of base substrate is very important at present, but the allotment of glaze more shows prominent position, and it can make ceramic product have abundant colors, beautiful appearance and receive the welcome in market deeply.The blank of same moulding often produces Different Effects because of the different visions to the human consumer of overglaze.The glaze that present ceramic product is executed all is a shiny surface, and brightness is too high, and does not have texture, on decorating, just receives bigger restriction.
Summary of the invention:
The objective of the invention is to overcome the deficiency of prior art, and provide a kind of texture good inferior light black frosted glaze.
For realizing above-mentioned purpose, the technical scheme that the present invention adopts is:
A kind of inferior light black frosted glaze, by weight percentage, contain following composition:
Manganese oxide 20～40%
Adjusting adhesive 50～70%
Potassium felspar sand 1.5～4.5%
Calcite 0.2～0.8%
Iron oxide red 0.2～0.8%
Aluminum oxide 0.01～0.05%
Plant ash 0.05～0.3%
Water surplus.
A kind of inferior light black frosted glaze, by weight percentage, contain following composition:
Manganese oxide 25～35%
Adjusting adhesive 55～65%
Potassium felspar sand 2.5～4.5%
Calcite 0.3～0.5%
Iron oxide red 0.3～0.5%
Aluminum oxide 0.02～0.04%
Plant ash 0.1～0.2%
Water surplus.
A kind of inferior light black frosted glaze, by weight percentage, contain following composition:
Manganese oxide 30%
Adjusting adhesive 60%
Potassium felspar sand 4.5%
Calcite 0.5%
Iron oxide red 0.5%
Aluminum oxide 0.03%
Plant ash 0.2%
Water 4.27%.
Said adjusting adhesive is 300～400 purpose pottery mud and water, counts 6: 4 blended mixture according to weight ratio.
Pottery mud is potter's clay, is meant to contain irony and have good plastic clay.Mineralogical composition is main with smectite, kaolin, is the basal component of glaze, and the staple of potassium felspar sand is K
2O, Al
2O
3And SiO
2, calcite is a flux, forms manganese, the compound no photo etching of calcium with manganese oxide, plant ash, and iron oxide red provides blood red pigment, and aluminum oxide is used to regulate firing temperature, and the staple of plant ash is a lime carbonate.
Beneficial effect of the present invention is: the present invention contains following composition by weight percentage: manganese oxide 20～40%, adjusting adhesive 50～70%; Potassium felspar sand 1.5～4.5%, calcite 0.2～0.8%, iron oxide red 0.2～0.8%; Aluminum oxide 0.01～0.05%, the water of plant ash 0.05～0.3% and surplus uses ceramic surface texture of the present invention good; Brightness is moderate, and the present invention is widely used on decorating.
Embodiment:
Following embodiment can make those skilled in the art more comprehensively understand the present invention, but does not limit the present invention in any way.
Embodiment 1
A kind of inferior light black frosted glaze, by weight percentage, contain following composition:
Manganese oxide 30%
Adjusting adhesive 60%
Potassium felspar sand 4.5%
Calcite 0.5%
Iron oxide red 0.5%
Aluminum oxide 0.03%
Plant ash 0.2%
Water 4.27%.
Said adjusting adhesive is 300 purpose pottery mud and water, counts 6: 4 blended mixture according to weight ratio.
Embodiment 2
A kind of inferior light black frosted glaze, by weight percentage, contain following composition:
Manganese oxide 35%
Adjusting adhesive 55%
Potassium felspar sand 2.5%
Calcite 0.3%
Iron oxide red 0.3%
Aluminum oxide 0.02%
Plant ash 0.1%
Water 6.78%.
Said adjusting adhesive is 400 purpose pottery mud and water, counts 6: 4 blended mixture according to weight ratio.
Embodiment 3
A kind of inferior light black frosted glaze, by weight percentage, contain following composition:
Manganese oxide 25%
Adjusting adhesive 65%
Potassium felspar sand 2.5%
Calcite 0.3%
Iron oxide red 0.3%
Aluminum oxide 0.02%
Plant ash 0.1%
Water 6.78%.
Said adjusting adhesive is 350 purpose pottery mud and water, counts 6: 4 blended mixture according to weight ratio.
Embodiment 4
A kind of inferior light black frosted glaze, by weight percentage, contain following composition:
Manganese oxide 30%
Adjusting adhesive 62%
Potassium felspar sand 3.5%
Calcite 0.5%
Iron oxide red 0.5%
Aluminum oxide 0.04%
Plant ash 0.2%
Water 3.26%.
Said adjusting adhesive is 380 purpose pottery mud and water, counts 6: 4 blended mixture according to weight ratio.
Certainly; The embodiment of the above is a preferred embodiments of the present invention, is not to limit practical range of the present invention; So all equivalences of being done according to the described prescription of claim of the present invention change or modify, and include in claim of the present invention.
Claims (3)
1. inferior light black frosted glaze is characterized in that: by weight percentage, contain following composition:
Manganese oxide 20～40%
Adjusting adhesive 50～70%
Potassium felspar sand 1.5～4.5%
Calcite 0.2～0.8%
Iron oxide red 0.2～0.8%
Aluminum oxide 0.01～0.05%
Plant ash 0.05～0.3%
Water surplus;
Wherein, said adjusting adhesive is 300～400 purpose pottery mud and water, counts the blended mixture of 6 ︰ 4 according to weight ratio.
2. a kind of inferior light black frosted glaze according to claim 1 is characterized in that: by weight percentage, contain following composition:
Manganese oxide 25～35%
Adjusting adhesive 55～65%
Potassium felspar sand 2.5～4.5%
Calcite 0.3～0.5%
Iron oxide red 0.3～0.5%
Aluminum oxide 0.02～0.04%
Plant ash 0.1～0.2%
Water surplus.
3. a kind of inferior light black frosted glaze according to claim 1 is characterized in that: by weight percentage, contain following composition:
Manganese oxide 30%
Adjusting adhesive 60%
Potassium felspar sand 4.5%
Calcite 0.5%
Iron oxide red 0.5%
Aluminum oxide 0.03%
Plant ash 0.2%
Water 4.27%.