CN109020203A - Frosted elephant skin glaze and preparation method thereof - Google Patents
Frosted elephant skin glaze and preparation method thereof Download PDFInfo
- Publication number
- CN109020203A CN109020203A CN201811068570.9A CN201811068570A CN109020203A CN 109020203 A CN109020203 A CN 109020203A CN 201811068570 A CN201811068570 A CN 201811068570A CN 109020203 A CN109020203 A CN 109020203A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- component
- frosted
- elephant skin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of frosted elephant skin glaze and preparation method thereof, the mass parts of the component and each component that contain in glaze used in frosted elephant skin glaze are as follows: 20-30 parts of potassium feldspar；10-20 parts of albite；8-10 parts of calcite；7-10 parts of barium carbonate；It is scholar 8-10 parts viscous；8-10 parts of alumina powder；10-15 parts of red lead；10-15 parts of manganese oxide；0.5-1 parts of nickel oxide；1-2 parts of copper oxide.Glaze paint of the invention shows the feeling that the crenulation as rough paper wrinkles, and gives people a kind of senile form impression.
Description
Technical field
The present invention relates to a kind of frosted elephant skin glaze and preparation method thereof.
Background technique
Currently, the moulding of porcelain billet is the basis of quality product in porcelain industry, the allotment of glaze keeps porcelain more gorgeous
It is colorful.The porcelain billet of same moulding often because of the difference of glaze paint, and generates different influences to the vision of consumer, that is as rough
The glaze paint of paper the same crenulation wrinkle can make porcelain give people a kind of senile form, this be also current porcelain industry it is a kind of when
Still.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the deficiencies of existing technologies, a kind of frosted elephant skin glaze is provided, it
Glaze paint shows the feeling that the crenulation as rough paper wrinkles, and gives people a kind of senile form impression.
In order to solve the above-mentioned technical problem, the technical scheme is that a kind of frosted elephant skin glaze, glaze used in it
In the mass parts of component and each component that contain it is as follows:
20-30 parts of potassium feldspar；
10-20 parts of albite；
8-10 parts of calcite；
7-10 parts of barium carbonate；
It is scholar 8-10 parts viscous；
8-10 parts of alumina powder；
10-15 parts of red lead；
10-15 parts of manganese oxide；
0.5-1 parts of nickel oxide；
1-2 parts of copper oxide.
The present invention also provides a kind of preparation method of frosted elephant skin glaze, the step of method in contain:
S1: it stocks up according to each component and each component mass parts；
S2: according to material: ball: mass ratio=1:1:1.6 of water, wet ball grinding 12~16 hours, the glaze after ball milling crossed 325
After mesh, it is stand-by to be modulated into the glaze slip that specific gravity is 1.4~1.6；
S3: taking clean green body, soaked directly on green body using glaze slip glaze or bubble glaze or leaching glaze, then 1160 DEG C-
It is fired under 1230 DEG C of temperature environment.
After above-mentioned technical proposal, after firing, glaze paint is showed as rough paper frosted elephant skin glaze of the invention
The feeling of the same crenulation wrinkle gives people a kind of senile form impression.
Specific embodiment
In order that the present invention can be more clearly and readily understood, below according to specific embodiment, to the present invention make into
One step detailed description.
Embodiment one
The mass parts of a kind of frosted elephant skin glaze, the component and each component that contain in glaze used in it are as follows:
20 parts of potassium feldspar；
10 parts of albite；
8 parts of calcite；
7 parts of barium carbonate；
Viscous 8 parts of scholar；
8 parts of alumina powder；
10 parts of red lead；
10 parts of manganese oxide；
0.5 part of nickel oxide；
1 part of copper oxide.
Contain in the step of preparation method of the frosted elephant skin glaze, method:
S1: it stocks up according to each component and each component mass parts；
S2: according to material: ball: mass ratio=1:1:1.6 of water, wet ball grinding 12 hours, the glaze after ball milling crossed 325 meshes
Afterwards, it is stand-by to be modulated into the glaze slip that specific gravity is 1.4~1.6；
S3: taking clean green body, soaked directly on green body using glaze slip glaze or bubble glaze or leaching glaze, then 1160 DEG C-
It is fired under 1230 DEG C of temperature environment.
Embodiment two
The mass parts of a kind of frosted elephant skin glaze, the component and each component that contain in glaze used in it are as follows:
30 parts of potassium feldspar；
20 parts of albite；
10 parts of calcite；
10 parts of barium carbonate；
Viscous 10 parts of scholar；
10 parts of alumina powder；
15 parts of red lead；
15 parts of manganese oxide；
1 part of nickel oxide；
2 parts of copper oxide.
Contain in the step of preparation method of the frosted elephant skin glaze, method:
S1: it stocks up according to each component and each component mass parts；
S2: according to material: ball: mass ratio=1:1:1.6 of water, wet ball grinding 16 hours, the glaze after ball milling crossed 325 meshes
Afterwards, it is stand-by to be modulated into the glaze slip that specific gravity is 1.4~1.6；
S3: taking clean green body, soaked directly on green body using glaze slip glaze or bubble glaze or leaching glaze, then 1160 DEG C-
It is fired under 1230 DEG C of temperature environment.
Embodiment three
The mass parts of a kind of frosted elephant skin glaze, the component and each component that contain in glaze used in it are as follows:
25 parts of potassium feldspar；
15 parts of albite；
9 parts of calcite；
8 parts of barium carbonate；
Viscous 9 parts of scholar；
9 parts of alumina powder；
12 parts of red lead；
12 parts of manganese oxide；
0.8 part of nickel oxide；
1 part of copper oxide.
Contain in the step of preparation method of the frosted elephant skin glaze, method:
S1: it stocks up according to each component and each component mass parts；
S2: according to material: ball: mass ratio=1:1:1.6 of water, wet ball grinding 14 hours, the glaze after ball milling crossed 325 meshes
Afterwards, it is stand-by to be modulated into the glaze slip that specific gravity is 1.4~1.6；
S3: taking clean green body, soaked directly on green body using glaze slip glaze or bubble glaze or leaching glaze, then 1160 DEG C-
It is fired under 1230 DEG C of temperature environment.
The frosted elephant skin glaze that three above embodiment is prepared, glaze paint can show what the crenulation as rough paper wrinkled
Feel, meets design requirement.
Particular embodiments described above, pair present invention solves the technical problem that, technical scheme and beneficial effects carry out
It is further described, it should be understood that the above is only a specific embodiment of the present invention, is not limited to this
Invention, all within the spirits and principles of the present invention, any modification, equivalent substitution, improvement and etc. done should be included in this hair
Within bright protection scope.
Claims (2)
1. a kind of frosted elephant skin glaze, it is characterised in that the mass parts of the component and each component that contain in glaze used in it are such as
Under:
20-30 parts of potassium feldspar；
10-20 parts of albite；
8-10 parts of calcite；
7-10 parts of barium carbonate；
It is scholar 8-10 parts viscous；
8-10 parts of alumina powder；
10-15 parts of red lead；
10-15 parts of manganese oxide；
0.5-1 parts of nickel oxide；
1-2 parts of copper oxide.
2. a kind of preparation method of frosted elephant skin glaze as described in claim 1, it is characterised in that contain in the step of method:
S1: it stocks up according to each component and each component mass parts；
S2: according to material: ball: mass ratio=1:1:1.6 of water, wet ball grinding 12~16 hours, the glaze after ball milling crossed 325 meshes
Afterwards, it is stand-by to be modulated into the glaze slip that specific gravity is 1.4~1.6；
S3: taking clean green body, glaze or bubble glaze or leaching glaze is soaked directly on green body using glaze slip, then at 1160 DEG C -1230 DEG C
Temperature environment under fire.