CN101648787A - 水泥基防水砂浆光敏抗紫外线保护剂 - Google Patents
水泥基防水砂浆光敏抗紫外线保护剂 Download PDFInfo
- Publication number
- CN101648787A CN101648787A CN200910054074A CN200910054074A CN101648787A CN 101648787 A CN101648787 A CN 101648787A CN 200910054074 A CN200910054074 A CN 200910054074A CN 200910054074 A CN200910054074 A CN 200910054074A CN 101648787 A CN101648787 A CN 101648787A
- Authority
- CN
- China
- Prior art keywords
- parts
- cement
- ultraviolet resistance
- waterproof mortar
- based waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种水泥基防水砂浆光敏抗紫外线保护剂，包括如下重量份的组分：明胶水溶液100份，硫酸铜10～20份，氢氧化钠1～2份，硫脲10～20份，3.3′－二乙基氧碳菁碘盐份菁吸光染料水溶液20～30份，氯化亚锡乙醇水溶液10～20份。本发明使砂浆内层得到保护，保护了高分子聚合物和颜料免遭紫外线的直接幅射，消除了砂浆表面粉化和表皮剥落及颜料的褪色现象的发生。
Description
技术领域
本发明涉及一种防水砂浆光敏抗紫外线保护剂。
背景技术
随着人类社会的不断发展进步，持续进行的经济增长，我国正进行大规模的经济建设，对建筑材料的需求非常巨大，新型建筑材料以其节能、环保、功能化、技术经济合理等优点在建筑工业中得到越来越广泛的应用，20世纪以后，建筑材料的发展更是进入了一个崭新的时代，以一批有机材料为主的化学建材异军突起，一些性能优异，具有特殊功能的新型建材相继出现，渗透到建筑业的各个方面，成为现代建筑的象征。新型材料的出现，也必然为带来新的问题，新的问题也要依靠新技术来解决。以水泥基有机防水砂浆为主体的建筑材料已成为当今必不可少的最重要的材料之一，高分子聚合物在水泥砂浆中的稳定性问题被越来越重视，尤其是高分子聚合物耐紫外线照射是一个非常突出的问题，水泥砂浆中的高分子聚合物长期受紫外线照射，容易发生裂变，致使砂浆表面粉化和表皮剥落，造成颜料褪色，造成砂浆性能主体受影响，人们已经采取了多种办法来解决这一问题，如砂浆中加入多种抗紫外线保护剂来保护，但由于受到水泥砂浆强碱体系的影响，这些抗紫外线保护剂没有在水泥砂浆体系中完全发挥很好的作用。
发明内容
本发明的目的在于提供一种水泥基防水砂浆光敏抗紫外线保护剂，以克服现有技术存在的上述缺陷。
本发明的水泥基防水砂浆光敏抗紫外线保护剂，包括如下重量份的组分：
明胶水溶液 100份
硫酸铜 10～20份
氢氧化钠 1～2份
硫脲 10～20份
3.3′-二乙基氧碳菁碘盐份菁吸光染料水溶液 20～30份
氯化亚锡乙醇水溶液 10～20份。
所述明胶水溶液的重量浓度为 0.6～1％；
所述3.3′-二乙基氧碳菁碘盐份菁吸光染料水溶液的重量浓度为0.2～1‰；
所述氯化亚锡乙醇水溶液的重量浓度为8～10％；
优选的，包括如下重量份的组分：
明胶水溶液 100份
硫酸铜 13～18份
氢氧化钠 1.3～1.8份
硫脲 13～18份
3.3′-二乙基氧碳菁碘盐份菁吸光染料水溶液 23～28份
氯化亚锡乙醇水溶液 13～18份。
所述水泥基防水砂浆光敏抗紫外线保护剂的制备方法，包括如下步骤：
(1)将所述明胶水溶液，升温至60～70℃，加入硫酸铜和氢氧化钠，分散，再加入硫脲，分散，获得胶溶液；
所述分散方法，如搅拌、剪切或均质等常规的方法；
(2)将所述3.3′-二乙基氧碳菁碘盐份菁吸光染料水溶液和氯化亚锡乙醇溶液加入胶溶液中，分散，获得所述水泥基防水砂浆光敏抗紫外线保护剂；
3.3′-二乙基氧碳菁碘盐份菁吸光染料可采用市售产品，如宁波春山化工有限公司制造的产品；
所述明胶是指动物的皮胶或骨胶；
本发明的水泥基防水砂浆光敏抗紫外线保护剂，可用于水泥砂浆中，添加重量为水泥砂浆的0.6～3％，所述水泥砂浆的配方在一般的手册上均有报道，如《砂浆配方创新设计与生产、应用工艺技术及质量检验检测实用手册》(北方工业出版社2008年3月出版)等。
本发明的水泥基防水砂浆光敏抗紫外线保护剂，采用了吸光染料、还原剂，氧化络合体系组成的胶溶物分散在水泥砂浆中，当水泥砂浆的外层受紫外线强烈照射时光能被吸光染料吸收，吸光染料是双健不稳定体系，受光能的影响，引发能量传递，使强还原剂氯化亚锡激发电子，络合物中的二价铜离子被逐步还原成铜原子，络合物中的铜离子不断向表面迁移，还原反应生成的铜原子产生了屏蔽效应，同时二价锡离子与明胶形成难溶于水的胶膜阻隔了紫外线，使砂浆内层得到保护，保护了高分子聚合物和颜料免遭紫外线的直接幅射，消除了砂浆表面粉化和表皮剥落及颜料的褪色现象的发生。
具体实施方式
实施例中，如无特别说明，组分均为重量份。
实施例1
配方：
重量浓度1％明胶溶液100份，硫酸铜10份，氢氧化钠1份，硫脲10份，重量浓度1‰的3.3′-二乙基氧碳菁碘盐份菁吸光染料水溶液20份，重量浓度10％氯化亚锡乙醇溶液10份；
制备方法：
将明胶溶液在搅拌机内搅拌20分钟，再升温至65℃，再加入硫酸铜；5分钟后，再加氢氧化钠，使胶液发生浑浊，5分钟后，再加入硫脲，使胶液变成透明，获得胶溶液；
将3.3′-二乙基氧碳菁碘盐份菁吸光染料溶液和氯化亚锡乙醇溶液加入到胶溶液中，30分钟后，将照明灯改成白炽灯(无紫外光)后，再加入氯化亚锡乙醇溶液，10分钟后，获得光敏抗紫外线保护剂，避光保存。
实施例2
配方：
重量浓度1％明胶溶液100份，硫酸铜15份，氢氧化钠1.5份，硫脲15份，重量浓度1‰的3.3′-二乙基氧碳菁碘盐份菁吸光染料25份，重量浓度10％氯化亚锡乙醇溶液15份。
制备方法同实施例1。
实施例3
配方：
重量浓度1％明胶溶液100份，硫酸铜20份，氢氧化钠2份，硫脲20份，重量
浓度1‰的3.3′-二乙基氧碳菁碘盐份菁吸光染料溶液30份，重量浓度1‰的10％氯化亚锡乙醇溶液20份。
制备方法同实施例1。
实施例4
配方：
重量浓度1％明胶溶液100份，硫酸铜13份，氢氧化钠1.3份，硫脲13份，重量浓度1‰的3.3′-二乙基氧碳菁碘盐份菁吸光染料23份，重量浓度10％氯化亚锡乙醇溶液13份。
制备方法同实施例1。
实施例5
配方：
重量浓度1％明胶溶液100份，硫酸铜18份，氢氧化钠1.8份，硫脲18份，重量浓度1‰的3.3′-二乙基氧碳菁碘盐份菁吸光染料溶液28份，重量浓度10％氯化亚锡乙醇溶液18份。
制备方法同实施例1。
实施例6
配方：
重量浓度1％明胶溶液100份，硫酸铜10份，氢氧化钠2份，硫脲20份，重量浓度1‰的3.3′-二乙基氧碳菁碘盐份菁吸光染料30份，重量浓度10％氯化亚锡乙醇溶液20份。
制备方法同实施例1。
实施例7
以上实施例均采用以下砂浆和对比样品进行应用试验；
一、实施例应用试验试件：
上海恒星建材科技公司产品：水泥基防水砂浆再加光敏抗紫外线保护剂。
二、空白应用试验试件：
上海恒星建材科技公司产品：水泥基防水砂浆。
三、对比1应用试验试件：
上海恒星建材科技公司产品：水泥基防水砂浆。加威海云清牌抗紫外线剂。
四、对比2应用试验试件：
上海恒星建材科技公司产品：水泥基防水砂浆。加美列塑胶科技公司抗紫外线剂。常温下，首先将水泥基防水砂浆搅拌混合均匀，再加入抗紫外线剂，继续搅拌混合均匀即可。
试件制作和测定方法按JC/T 984-2005(聚合物水泥基防水砂浆)的规定。结果见表1和表2
表1
表中，试1、试2、试3、试4、试5和试6分别为实施例1、2、3、4、5和6。
表2
结论：通过应用试验结果可以看出，应用本发明的光敏抗紫外线保护剂后，砂浆经人工老化(紫外线照射)后没有出现砂浆剥落粉化现象，而没有使用光敏抗紫外线保护剂的砂浆，均出现不同程度的剥落粉化现象，对比样品虽然有一定的抗紫外线作用，但在，砂浆经人工老化(紫外线照射)后，水泥基防水砂浆表面出现轻微粉化和剥落现象，对比1和2的抗紫外线剂在水泥砂浆中没有真正起到保护作用，说明本发明的光敏抗紫外线保护剂在水泥基防水砂浆中有非常好的抗紫外线保护作用.
Claims (6)
1.水泥基防水砂浆光敏抗紫外线保护剂，其特征在于，包括如下重量份的组分：
明胶水溶液 100份
硫酸铜 10～20份
氢氧化钠 1～2份
硫脲 10～20份
3.3′-二乙基氧碳菁碘盐份菁吸光染料水溶液 20～30份
氯化亚锡乙醇水溶液 10～20份。
2.根据权利要求1所述的水泥基防水砂浆光敏抗紫外线保护剂，其特征在于，所述明胶水溶液的重量浓度为0.6～1％；所述3.3′-二乙基氧碳菁碘盐份菁吸光染料水溶液的重量浓度为0.2～1‰；所述氯化亚锡乙醇水溶液的重量浓度为8～10％。
3.根据权利要求1所述的水泥基防水砂浆光敏抗紫外线保护剂，其特征在于，优选的，包括如下重量份的组分：
明胶水溶液 100份
硫酸铜 13～18份
氢氧化钠 1.3～1.8份
硫脲 13～18份
3.3′-二乙基氧碳菁碘盐份菁吸光染料水溶液 23～28份
氯化亚锡乙醇水溶液 13～18份。
4.根据权利要求1所述的水泥基防水砂浆光敏抗紫外线保护剂，其特征在于，所述明胶是指动物的皮胶或骨胶。
5.根据权利要求1～4任一项所述的水泥基防水砂浆光敏抗紫外线保护剂的制备方法，其特征在于，包括如下步骤：
(1)将所述明胶水溶液，升温至60～70℃，加入硫酸铜和氢氧化钠，分散，再加入硫脲，分散，获得胶溶液；
所述分散方法，如搅拌、剪切或均质等常规的方法；
(2)将所述3.3′-二乙基氧碳菁碘盐份菁吸光染料水溶液和氯化亚锡乙醇溶液加入胶溶液中，分散，获得所述水泥基防水砂浆光敏抗紫外线保护剂。