CN101633806A - 一种亮光浆及其制备方法 - Google Patents

一种亮光浆及其制备方法 Download PDF

Info

Publication number
CN101633806A
CN101633806A CN 200910172902 CN200910172902A CN101633806A CN 101633806 A CN101633806 A CN 101633806A CN 200910172902 CN200910172902 CN 200910172902 CN 200910172902 A CN200910172902 A CN 200910172902A CN 101633806 A CN101633806 A CN 101633806A
Authority
CN
China
Prior art keywords
parts
luminous
powder
water treatment
polyester
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200910172902
Other languages
English (en)
Other versions
CN101633806B (zh
Inventor
王建军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 200910172902 priority Critical patent/CN101633806B/zh
Publication of CN101633806A publication Critical patent/CN101633806A/zh
Application granted granted Critical
Publication of CN101633806B publication Critical patent/CN101633806B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种亮光浆及其制备方法，该亮光浆的配方包括以下重量份的原料：聚氯乙烯粉80－120份；聚酯15－25份；明胶5－15份；松香甘油酯2－8份；乙醇乙酯5－15份；水处理夜光粉40－60克；UV光油20－40份；聚氨酯丙烯酸复合体40－60份；促进剂5－15份。本发明的方法是将聚氯乙烯粉、聚酯、明胶和松香甘油酯混合加热热溶，冷却后加入乙醇乙酯，搅拌均匀；将水处理夜光粉加入UV光油中搅拌均匀；将前两步中制备的物质混合搅拌均匀后，加入聚氨酯丙烯酸复合体，搅拌均匀用促进剂调节混合液的稀稠，搅拌均匀即可。本发明的亮光浆可以替代现有的墨汁、油墨、油彩、彩墙涂料、油漆等，具有环保、经久耐用、能够发出夜光的优点。

Description

一种亮光浆及其制备方法
技术领域
本发明属于日常用品领域，具体涉及一种亮光浆及其制备方法。
背景技术
墨汁在书法上已有上千年的历史，墨汁用于书写存在以下的缺点，不能用于书写室外的装饰宣传用语，墨汁本身不环保，而且颜色单一，不易长时间保存，用水容易冲洗掉。
现有技术中的油漆涂料在用于室外时，经日晒雨淋容易褪色，虽然一些油漆涂料能够用于书写室外的装饰宣传用语，但是功能单一。
发明内容
本发明是针对以上不足，提供一种环保、经久耐用、能够发出夜光的亮光浆。
本发明还提供了上述亮光浆的制备方法。
本发明解决其技术问题所采用的技术方案是：一种亮光浆，该亮光浆的配方包括以下重量份的原料：
聚氯乙烯粉80-120份；聚酯15-25份；明胶5-15份；松香甘油酯2-8份；乙醇乙酯5-15份；水处理夜光粉40-60克；UV光油20-40份；聚氨酯丙烯酸复合体40-60份；促进剂5-15份。
本发明更优选的技术方案是：一种亮光浆，该亮光浆的配方包括以下重量份的原料：
聚氯乙烯粉100份；聚酯20份；明胶10份；松香甘油酯5份；乙醇乙酯10份；水处理夜光粉50克；UV光油30份；聚氨酯丙烯酸复合体50份；促进剂10份。
所述的促进剂选自乙醇、乙烯、甘二酯中的一种。
本发明的另一种技术方案是提供上述亮光浆的制备方法，包括以下的步骤：
(1)将聚氯乙烯粉、聚酯、明胶和松香甘油酯混合加热到40-60℃热溶，待到全部溶化后，自然冷却到室温，加入乙醇乙酯，搅拌均匀；
(2)将水处理夜光粉加入UV光油中搅拌均匀；
(3)将步骤(1)和步骤(2)中制备的物质混合搅拌均匀后，加入聚氨酯丙烯酸复合体，搅拌均匀用促进剂调节混合液的稀稠，搅拌均匀即可。
所述的水处理夜光粉为过400-500目筛子的细粉；所述的加热采用水浴加热的方法。
聚氯乙烯粉起到饱和的作用，聚酯能保持粘稠度、硬度，明胶和松香甘油酯能够起到固化作用，乙醇乙酯起调节作用，水处理夜光粉起发光作用，UV光油起调节及散光作用，聚氨酯与丙烯酸复合体起到防水、防裂、调节浓度的作用。
本发明的亮光浆可以替代现有的墨汁、油墨、油彩、彩墙涂料、油漆等，可以在布料上、木板上或水泥墙面上写字，也可以作为室内彩墙的装饰涂料，白天彩图色彩鲜艳，能够美化环境，夜晚熄灯后会发光，使室内光线清晰，尤其适用于城市夜晚的外墙装饰，能够起到节能节电的作用。本发明的亮光浆不但环保，而且经久耐用，长时间风吹、日晒、雨淋不褪色。
具体实施方式
下面结合具体实施例对本发明进行进一步描述。
实施例1
按照下述重量称取原料(克)：
聚氯乙烯粉100克；聚酯20克；明胶10克；松香甘油酯5克；乙醇乙酯10克；水处理夜光粉50克；UV光油30克；聚氨酯丙烯酸复合体50克；80％的乙醇10克。
制备方法：
(1)将100克聚氯乙烯粉、20克聚酯、10克明胶和5克松香甘油酯混合，放入容器中，然后将容器放入热水中加热到50℃，使容器内的物质热溶，待到全部溶化后，自然冷却到室温，加入10克乙醇乙酯，搅拌均匀；聚酯购买于郑州巨丰贸易有限公司；
(2)将水处理夜光粉50克加入30克UV光油中搅拌均匀，夜光粉为过500目筛子的细粉；水处理夜光粉购买于北京华龙亚阳技术开发有限责任公司；
(3)将步骤(1)和步骤(2)中制备的物质混合搅拌均匀后，加入50克聚氨酯丙烯酸复合体，搅拌均匀用促进剂调节混合液的稀稠，搅拌均匀即可。聚氨酯丙烯酸复合体购买于北京华龙亚阳技术开发有限责任公司。
实施例2
按照下述重量称取原料(克)：
聚氯乙烯粉120克；聚酯25克；明胶5克；松香甘油酯3克；乙醇乙酯15克；水处理夜光粉60克；UV光油40克；聚氨酯丙烯酸复合体60克；90％的乙醇15克。
制备方法如实施例1。
实施例3
按照下述重量称取原料(克)：
聚氯乙烯粉80克；聚酯15克；明胶15克；松香甘油酯7克；乙醇乙酯5克；水处理夜光粉40克；UV光油20克；聚氨酯丙烯酸复合体40克；甘二酯5克。
制备方法如实施例1。
以上所述的实施例，只是本发明较优选的具体实施方式，本领域的技术人员在本发明技术方案范围内进行的通常变化和替换都应包含在本发明的保护范围内。

Claims (5)

1、一种亮光浆，该亮光浆的配方包括以下重量份的原料：
聚氯乙烯粉80-120份；聚酯15-25份；明胶5-15份；松香甘油酯2-8份；乙醇乙酯5-15份；水处理夜光粉40-60克；UV光油20-40份；聚氨酯丙烯酸复合体40-60份；促进剂5-15份。
2、根据权利要求1所述的亮光浆，其特征在于，该亮光浆的配方包括以下重量份的原料：
聚氯乙烯100份；聚酯20份；明胶10份；松香甘油酯5份；乙醇乙酯10份；水处理夜光粉50克；UV光油30份；聚氨酯丙烯酸复合体50份；促进剂10份。
3、根据权利要求1所述的亮光浆，其特征在于，所述的促进剂选自乙醇、乙烯、甘二酯中的一种，所述的乙醇的浓度为80％以上。
4、根据权利要求1、2或3所述的亮光浆的制备方法，其特征在于，包括以下的步骤：
(1)将聚氯乙烯粉、聚酯、明胶和松香甘油酯混合加热到40-60℃热溶，待到全部溶化后，冷却到室温，加入乙醇乙酯，搅拌均匀；
(2)将水处理夜光粉加入UV光油中搅拌均匀；
(3)将步骤(1)和步骤(2)中制备的物质混合搅拌均匀后，加入聚氨酯丙烯酸复合体，搅拌均匀用促进剂调节混合液的稀稠，搅拌均匀即可。
5、根据权利要求3所述的亮光浆的制备方法，其特征在于，
所述的水处理夜光粉为过400-500目筛子的细粉；所述的加热采用水浴加热的方法。
CN 200910172902 2009-09-03 2009-09-03 一种亮光浆及其制备方法 Expired - Fee Related CN101633806B (zh)