CN101619186A - 一种溶剂型哑光转移镀铝涂料及其制备方法 - Google Patents
一种溶剂型哑光转移镀铝涂料及其制备方法 Download PDFInfo
- Publication number
- CN101619186A CN101619186A CN200910023519A CN200910023519A CN101619186A CN 101619186 A CN101619186 A CN 101619186A CN 200910023519 A CN200910023519 A CN 200910023519A CN 200910023519 A CN200910023519 A CN 200910023519A CN 101619186 A CN101619186 A CN 101619186A
- Authority
- CN
- China
- Prior art keywords
- solvent
- resin
- plating coating
- aluminium
- ethyl ester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供了一种溶剂型哑光转移镀铝涂料及其制备方法。该涂料由一定重量份的热塑性丙烯酸酯树脂、硝基纤维素树脂、氨基树脂、醇酸树脂、助剂和溶剂组成；制备方法为：将一部分溶剂加热后加入热塑性丙烯酸酯树脂，充分搅拌形成无色透明溶液；将另一部分溶剂加热后加入硝基纤维素树脂、氨基树脂和醇酸树脂，充分搅拌形成无色透明溶液，将两种无色透明溶液加入混合罐中混合，并加入助剂，用剩余溶剂调制即形成镀铝涂料。本发明镀铝涂料由于不加填充物和消光剂，所以转移效果好，印刷适应性好，稳定性好，产品转移后与纸张的粘结力好，对胶粘剂适应性强，镀铝哑光柔和，克服了填加哑光粉所带来的沉淀、不均和涂布易产生刮刀线的问题。
Description
技术领域
本发明涉及一种镀铝涂料及其制备方法，具体涉及一种用于哑光转移卡纸和哑光转移衬纸生产的溶剂型哑光转移镀铝涂料及其制备方法。
背景技术
哑光转移卡纸和哑光转移衬纸是现阶段转移卡纸和转移衬纸中的一种专门品种，主要是替代铝箔反裱复合卡纸和铝箔反裱复合衬纸的新型包装材料。在本发明之前，我公司与其它公司曾有用哑光粉为填加物而制成的哑光涂料，由于哑光粉的细度问题、不溶解性问题等，使得在制作产品的工艺过程中经常出现刮刀线及由于混合溶液沉淀而改变原有的哑光效果，特别是其树脂本身所具有的镜面光亮效果和原铝箔反裱哑光度的差距较大，难以实现相同表面效果的替代作用。
发明内容
本发明的目的是提供一种不加消光剂，转移效果好，印刷适应性好，转移后与纸张的粘结力好，对胶粘剂适应性强，镀铝哑光柔和，可根据产品不同要求，调制成不同的哑光效果的溶剂型哑光转移镀铝涂料。
为解决上述技术问题，本发明采用的技术方案是：一种溶剂型哑光转移镀铝涂料，其特征在于由以下重量份的原料组成：
热塑性丙烯酸酯树脂2-7份，
硝基纤维素树脂1-3份，
氨基树脂1-5份，
醇酸树脂1-6份，
助剂0.5-1份，
溶剂70-85份；
其中，所述热塑性丙烯酸酯树脂分子量为500-12000，玻璃化温度为40℃；所述氨基树脂分子量为1000-2000，玻璃化温度为80℃；所述醇酸树脂分子量为1000-2000，玻璃化温度为80℃；所述助剂为水溶性蜡乳液、润湿剂、流平剂和消泡剂中的一种或几种；所述溶剂为乙酯和丁酮的混合物，乙酯与丁酮的质量比为1∶1-4。
所述水溶性蜡乳液为聚乙烯蜡，所述润湿剂为改性有机硅氧烷，所述流平剂为聚硅氧烷类，所述消泡剂为改性硅酮。
本发明还提供了一种溶剂型哑光转移镀铝涂料的制备方法，其特征在于包括以下步骤：
(1)将10-25份的乙酯与丁酮混合溶液加热至75±3℃，然后逐步加入热塑性丙烯酸酯树脂，充分搅拌溶解形成无色透明溶液；
(2)将20-35份的乙酯与丁酮混合溶液加热至80℃，并逐步加入硝基纤维素树脂、氨基树脂和醇酸树脂，充分搅拌溶解形成无色透明溶液；
(3)将步骤(1)和步骤(2)中制备好的两种无色透明溶液加入同一个混合罐中混合，并加入助剂，用溶剂调制成粘度为27S、固含量为16-26wt％的溶液，即形成溶剂型哑光转移镀铝涂料，PH值为7-8.4。
本发明与现有技术相比具有以下优点：
1、本发明属于不加消光剂的转移镀铝涂料，克服了用哑光粉填加所带来的沉淀、不均和涂布易产生刮刀线的问题；
2、本发明产品由于不加填充物，所以转移效果好，印刷适应性好，应用领域广泛；
3、本发明产品转移后与纸张的粘结力好，对胶粘剂适应性强，镀铝哑光柔和，可根据产品不同要求，调制成不同的哑光效果；
4、本发明产品产品稳定性好。
下面通过实施例对本发明做进一步的详细描述。
具体实施方式
实施例1
本实施例的原料(重量份)组成为：
热塑性丙烯酸酯树脂7份，
硝基纤维素树脂3份，
氨基树脂5份，
醇酸树脂6份，
助剂1份，
溶剂85份；
其中，所述热塑性丙烯酸酯树脂分子量为500-12000，玻璃化温度为40℃，粘度为500-2000厘泊；所述氨基树脂分子量为1000-2000，玻璃化温度为80℃，粘度为50-500厘泊；所述醇酸树脂分子量为1000-2000，玻璃化温度为80℃，粘度为50-500厘泊；所述助剂为水溶性蜡乳液、润湿剂、流平剂和消泡剂中的一种或几种；所述溶剂为乙酯和丁酮的混合物，乙酯与丁酮的质量比为1∶1。所述水溶性蜡乳液为聚乙烯蜡，所述润湿剂为改性有机硅氧烷，所述流平剂为聚硅氧烷类，所述消泡剂为改性硅酮。
本实施例的制备方法为：
(1)将25份的乙酯与丁酮混合溶液加热至75±3℃，然后逐步加入热塑性丙烯酸酯树脂，充分搅拌溶解形成无色透明溶液；
(2)将35份的乙酯与丁酮混合溶液加热至80℃，并逐步加入硝基纤维素树脂、氨基树脂和醇酸树脂，充分搅拌溶解形成无色透明溶液；
(3)将步骤(1)和步骤(2)中制备好的两种无色透明溶液加入同一个混合罐中混合，并加入助剂，用溶剂调制成粘度为27S、固含量为16-26wt％的溶液，即形成溶剂型哑光转移镀铝涂料，PH值为7-8.4。
实施例2
本实施例的原料(重量份)组成为：
热塑性丙烯酸酯树脂2份，
硝基纤维素树脂1份，
氨基树脂1份，
醇酸树脂1份，
助剂0.5份，
溶剂70份；
其中，所述热塑性丙烯酸酯树脂分子量为500-12000，玻璃化温度为40℃，粘度为500-2000厘泊；所述氨基树脂分子量为1000-2000，玻璃化温度为80℃，粘度为50-500厘泊；所述醇酸树脂分子量为1000-2000，玻璃化温度为80℃，粘度为50-500厘泊；所述助剂为水溶性蜡乳液、润湿剂、流平剂和消泡剂中的一种或几种；所述溶剂为乙酯和丁酮的混合物，乙酯与丁酮的质量比为1∶2。所述水溶性蜡乳液为聚乙烯蜡，所述润湿剂为改性有机硅氧烷，所述流平剂为聚硅氧烷类，所述消泡剂为改性硅酮。
本实施例的制备方法为：
(1)将10份的乙酯与丁酮混合溶液加热至75±3℃，然后逐步加入热塑性丙烯酸酯树脂，充分搅拌溶解形成无色透明溶液；
(2)将20份的乙酯与丁酮混合溶液加热至80℃，并逐步加入硝基纤维素树脂、氨基树脂和醇酸树脂，充分搅拌溶解形成无色透明溶液；
(3)将步骤(1)和步骤(2)中制备好的两种无色透明溶液加入同一个混合罐中混合，并加入助剂，用溶剂调制成粘度为27S、固含量为16-26wt％的溶液，即形成溶剂型哑光转移镀铝涂料，PH值为7-8.4。
实施例3
本实施例的原料(重量份)组成为：
热塑性丙烯酸酯树脂5份，
硝基纤维素树脂2份，
氨基树脂3份，
醇酸树脂4份，
助剂0.75份，
溶剂78份；
其中，所述热塑性丙烯酸酯树脂分子量为500-12000，玻璃化温度为40℃，粘度为500-2000厘泊；所述氨基树脂分子量为1000-2000，玻璃化温度为80℃，粘度为50-500厘泊；所述醇酸树脂分子量为1000-2000，玻璃化温度为80℃，粘度为50-500厘泊；所述助剂为水溶性蜡乳液、润湿剂、流平剂和消泡剂中的一种或几种；所述溶剂为乙酯和丁酮的混合物，乙酯与丁酮的质量比为1∶3。所述水溶性蜡乳液为聚乙烯蜡，所述润湿剂为改性有机硅氧烷，所述流平剂为聚硅氧烷类，所述消泡剂为改性硅酮。
本实施例的制备方法为：
(1)将20份的乙酯与丁酮混合溶液加热至75±3℃，然后逐步加入热塑性丙烯酸酯树脂，充分搅拌溶解形成无色透明溶液；
(2)将30份的乙酯与丁酮混合溶液加热至80℃，并逐步加入硝基纤维素树脂、氨基树脂和醇酸树脂，充分搅拌溶解形成无色透明溶液；
(3)将步骤(1)和步骤(2)中制备好的两种无色透明溶液加入同一个混合罐中混合，并加入助剂，用溶剂调制成粘度为27S、固含量为16-26wt％的溶液，即形成溶剂型哑光转移镀铝涂料，PH值为7-8.4。
实施例4
本实施例的原料(重量份)组成为：
热塑性丙烯酸酯树脂6份，
硝基纤维素树脂2份，
氨基树脂4份，
醇酸树脂5份，
助剂1份，
溶剂80份；
其中，所述热塑性丙烯酸酯树脂分子量为500-12000，玻璃化温度为40℃，粘度为500-2000厘泊；所述氨基树脂分子量为1000-2000，玻璃化温度为80℃，粘度为50-500厘泊；所述醇酸树脂分子量为1000-2000，玻璃化温度为80℃，粘度为50-500厘泊；所述助剂为水溶性蜡乳液、润湿剂、流平剂和消泡剂中的一种或几种；所述溶剂为乙酯和丁酮的混合物，乙酯与丁酮的质量比为1∶4。所述水溶性蜡乳液为聚乙烯蜡，所述润湿剂为改性有机硅氧烷，所述流平剂为聚硅氧烷类，所述消泡剂为改性硅酮。
本实施例的制备方法为：
(1)将22份的乙酯与丁酮混合溶液加热至75±3℃，然后逐步加入热塑性丙烯酸酯树脂，充分搅拌溶解形成无色透明溶液；
(2)将33份的乙酯与丁酮混合溶液加热至80℃，并逐步加入硝基纤维素树脂、氨基树脂和醇酸树脂，充分搅拌溶解形成无色透明溶液；
(3)将步骤(1)和步骤(2)中制备好的两种无色透明溶液加入同一个混合罐中混合，并加入助剂，用溶剂调制成粘度为27S、固含量为16-26wt％的溶液，即形成溶剂型哑光转移镀铝涂料，PH值为7-8.4。
以上实施例制备的产品的性能指标为：
固含量 16-26wt％；
PH值 7.0-8.4；
粘度 27S(涂4-杯)；
玻璃化温度 -18℃。
Claims (3)
1.一种溶剂型哑光转移镀铝涂料，其特征在于由以下重量份的原料组成：
热塑性丙烯酸酯树脂 2-7份，
硝基纤维素树脂 1-3份，
氨基树脂 1-5份，
醇酸树脂 1-6份，
助剂 0.5-1份，
溶剂 70-85份；
其中，所述热塑性丙烯酸酯树脂分子量为500-12000，玻璃化温度为40℃；所述氨基树脂分子量为1000-2000，玻璃化温度为80℃；所述醇酸树脂分子量为1000-2000，玻璃化温度为80℃；所述助剂为水溶性蜡乳液、润湿剂、流平剂和消泡剂中的一种或几种；所述溶剂为乙酯和丁酮的混合物，乙酯与丁酮的质量比为1∶1-4。
2.根据权利要求1所述的一种水溶性转移镀铝涂料，其特征在于，所述水溶性蜡乳液为聚乙烯蜡，所述润湿剂为改性有机硅氧烷，所述流平剂为聚硅氧烷类，所述消泡剂为改性硅酮。
3.一种制备如权利要求1所述溶剂型哑光转移镀铝涂料的方法，其特征在于包括以下步骤：
(1)将10-25份的乙酯与丁酮混合溶液加热至75±3℃，然后逐步加入热塑性丙烯酸酯树脂，充分搅拌溶解形成无色透明溶液；
(2)将20-35份的乙酯与丁酮混合溶液加热至80℃，并逐步加入硝基纤维素树脂、氨基树脂和醇酸树脂，充分搅拌溶解形成无色透明溶液；
(3)将步骤(1)和步骤(2)中制备好的两种无色透明溶液加入同一个混合罐中混合，并加入助剂，用溶剂调制成粘度为27S、固含量为16-26wt％的溶液，即形成溶剂型哑光转移镀铝涂料，PH值为7-8.4。