CN101619191B - 一种水溶性转移镀铝涂料及其制备方法 - Google Patents

一种水溶性转移镀铝涂料及其制备方法 Download PDF

Info

Publication number
CN101619191B
CN101619191B CN2009100235203A CN200910023520A CN101619191B CN 101619191 B CN101619191 B CN 101619191B CN 2009100235203 A CN2009100235203 A CN 2009100235203A CN 200910023520 A CN200910023520 A CN 200910023520A CN 101619191 B CN101619191 B CN 101619191B
Authority
CN
China
Prior art keywords
water
soluble
polyurethane emulsion
aqueous polyurethane
emulsion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2009100235203A
Other languages
English (en)
Other versions
CN101619191A (zh
Inventor
朱天社
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xi'an Great Sky New Material Co., Ltd.
Original Assignee
Xi'an Great Sky Science & Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Xi'an Great Sky Science & Technology Co Ltd filed Critical Xi'an Great Sky Science & Technology Co Ltd
Priority to CN2009100235203A priority Critical patent/CN101619191B/zh
Publication of CN101619191A publication Critical patent/CN101619191A/zh
Application granted granted Critical
Publication of CN101619191B publication Critical patent/CN101619191B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种水溶性转移镀铝涂料及其制备方法。该涂料由一定重量份的水性聚氨酯乳液、水性聚丙烯酸酯树脂、填充料、助剂、酒精和水组成；制备方法为：将水和酒精混合，加热后逐步加入水性聚丙烯酸酯树脂并搅匀获得水性聚丙烯酸酯树脂溶液；在水性聚氨酯乳液中加水，加热并搅匀，获得水性聚氨酯乳液水溶液；将两种溶液放入混合罐中混合，加热，然后加入填充料和助剂，均匀搅拌并用水调制便制得水溶性转移镀铝涂料。本发明产品为水性乳液，不含有机溶剂，绿色环保，无污染；产品对粘合剂的要求低，适应性好；产品转移后对印刷油墨的适应性好；该涂料成膜后耐老化；本发明产品由于溶剂为纯净水，所以使用成本低。

Description

一种水溶性转移镀铝涂料及其制备方法
技术领域
本发明涉及一种镀铝涂料及其制备方法，具体涉及一种用于转移卡纸和转移衬纸生产的水溶性转移镀铝涂料及其制备方法。
背景技术
转移卡纸和转移衬纸是现阶段替代铝箔复合卡纸、衬纸和镀铝膜复合卡纸的新型包装材料。在本发明之前，我公司和社会均有溶剂型转移涂料的生产和应用，由于有机溶剂挥发带来的环境问题、溶剂残留带来的成品纸张不能满足烟用材料对VOC标准的要求、应用成本问题等制约产业健康发展。
发明内容
本发明的目的是提供一种不含有机溶剂，绿色环保，无污染，产品转移以后对印刷油墨的适应性好，成膜后耐老化且使用成本低的水溶性转移镀铝涂料。
为解决上述技术问题，本发明采用的技术方案是：一种水溶性转移镀铝涂料，其特征在于由以下重量份的原料组成：
水性聚氨酯乳液5-10份，
水性聚丙烯酸酯树脂3-15份，
填充料5-10份，
助剂1-3份，
酒精10-30份，
水40-80份；
其中，所述水性聚氨酯乳液分子量为2000-5000，粘度为50-500厘泊；所述水溶性聚丙烯酸酯树脂分子量为1000-2000，粘度为200-400厘泊，玻璃化温度为80℃；所述填充料为水溶性弹性体树脂或/和成膜改进剂；所述助剂为水溶性蜡乳液、润湿剂、流平剂和消泡剂中的一种或几种。
所述水溶性弹性体树脂为合成丁苯乳液和丙烯酸压敏乳中的一种或两种，所述成膜改进剂为乙二醇醚，所述水溶性蜡乳液为聚乙烯蜡，所述润湿剂为改性有机硅氧烷，所述流平剂为聚硅氧烷类，所述消泡剂为改性硅酮。
本发明还提供一种水溶性转移镀铝涂料的制备方法，其特征在于包括以下步骤：
(1)将质量比为1-2∶1的水和酒精混合，加热至65±3℃，逐步加入水性聚丙烯酸酯树脂并均匀搅拌至全部溶解，获得水性聚丙烯酸酯树脂溶液；
(2)在水性聚氨酯乳液中加水性聚氨酯乳液质量1-3倍的水，加热至80℃并均匀搅拌至均匀混合，获得水性聚氨酯乳液水溶液；
(3)将步骤(1)中的水性聚丙烯酸酯树脂溶液和步骤(2)中的水性聚氨酯乳液水溶液放入混合罐中混合，加热至65±3℃，然后加入填充料和助剂，均匀搅拌并用水调制，便制得水溶性转移镀铝涂料，涂料固含量为15-30wt％，PH值为7-8.4。
本发明与现有技术相比具有以下优点：
1、本发明产品为水性乳液，不含有机溶剂，绿色环保，无污染；
2、本发明产品对粘合剂的要求低，适应性好；
3、本发明产品转移以后，对印刷油墨的适应性好；
4、该涂料成膜后耐老化；
5、本发明产品由于溶剂为纯净水，所以使用成本低。
下面通过实施例对本发明做进一步的详细描述。
具体实施方式
实施例1
本实施例的原料组成为：
水性聚氨酯乳液10份，
水性聚丙烯酸酯树脂15份，
填充料10份，
助剂3份，
酒精30份，
水80份；
其中，所述水性聚氨酯乳液分子量为2000-5000，粘度为50-500厘泊；所述水溶性聚丙烯酸酯树脂分子量为1000-2000，粘度为200-400厘泊，玻璃化温度为80℃；所述填充料为水溶性弹性体树脂或/和成膜改进剂；所述助剂为水溶性蜡乳液、润湿剂、流平剂和消泡剂中的一种或几种。所述水溶性弹性体树脂为合成丁苯乳液和丙烯酸压敏乳中的一种或两种，所述成膜改进剂为乙二醇醚，所述水溶性蜡乳液为聚乙烯蜡，所述润湿剂为改性有机硅氧烷，所述流平剂为聚硅氧烷类，所述消泡剂为改性硅酮。
本实施例的制备方法为：
(1)将质量比为1∶1的水和酒精混合，加热至65±3℃，逐步加入水性聚丙烯酸酯树脂并均匀搅拌至全部溶解，获得水性聚丙烯酸酯树脂溶液；
(2)在水性聚氨酯乳液中加水性聚氨酯乳液质量3倍的水，加热至80℃并均匀搅拌至均匀混合，获得水性聚氨酯乳液水溶液；
(3)将步骤(1)中的水性聚丙烯酸酯树脂溶液和步骤(2)中的水性聚氨酯乳液水溶液放入混合罐中混合，加热至65±3℃，然后加入填充料和助剂，均匀搅拌并用水调制，便制得水溶性转移镀铝涂料，涂料固含量为15-30wt％，PH值为7-8.4。
实施例2
本实施例的原料组成为：
水性聚氨酯乳液5份，
水性聚丙烯酸酯树脂3份，
填充料5份，
助剂1份，
酒精10份，
水40份；
其中，所述水性聚氨酯乳液分子量为2000-5000，粘度为50-500厘泊；所述水溶性聚丙烯酸酯树脂分子量为1000-2000，粘度为200-400厘泊，玻璃化温度为80℃；所述填充料为水溶性弹性体树脂或/和成膜改进剂；所述助剂为水溶性蜡乳液、润湿剂、流平剂和消泡剂中的一种或几种。所述水溶性弹性体树脂为合成丁苯乳液和丙烯酸压敏乳中的一种或两种，所述成膜改进剂为乙二醇醚，所述水溶性蜡乳液为聚乙烯蜡，所述润湿剂为改性有机硅氧烷，所述流平剂为聚硅氧烷类，所述消泡剂为改性硅酮。
本实施例的制备方法为：
(1)将质量比为2∶1的水和酒精混合，加热至65±3℃，逐步加入水性聚丙烯酸酯树脂并均匀搅拌至全部溶解，获得水性聚丙烯酸酯树脂溶液；
(2)在水性聚氨酯乳液中加水性聚氨酯乳液质量2倍的水，加热至80℃并均匀搅拌至均匀混合，获得水性聚氨酯乳液水溶液；
(3)将步骤(1)中的水性聚丙烯酸酯树脂溶液和步骤(2)中的水性聚氨酯乳液水溶液放入混合罐中混合，加热至65±3℃，然后加入填充料和助剂，均匀搅拌并用水调制，便制得水溶性转移镀铝涂料，涂料固含量为15-30wt％，PH值为7-8.4。
实施例3
本实施例的原料组成为：
水性聚氨酯乳液8份，
水性聚丙烯酸酯树脂10份，
填充料7份，
助剂2份，
酒精20份，
水60份；
其中，所述水性聚氨酯乳液分子量为2000-5000，粘度为50-500厘泊；所述水溶性聚丙烯酸酯树脂分子量为1000-2000，粘度为200-400厘泊，玻璃化温度为80℃；所述填充料为水溶性弹性体树脂或/和成膜改进剂；所述助剂为水溶性蜡乳液、润湿剂、流平剂和消泡剂中的一种或几种。所述水溶性弹性体树脂为合成丁苯乳液和丙烯酸压敏乳中的一种或两种，所述成膜改进剂为乙二醇醚，所述水溶性蜡乳液为聚乙烯蜡，所述润湿剂为改性有机硅氧烷，所述流平剂为聚硅氧烷类，所述消泡剂为改性硅酮。
本实施例的制备方法为：
(1)将质量比为1.5∶1的水和酒精混合，加热至65±3℃，逐步加入水性聚丙烯酸酯树脂并均匀搅拌至全部溶解，获得水性聚丙烯酸酯树脂溶液；
(2)在水性聚氨酯乳液中加水性聚氨酯乳液质量1倍的水，加热至80℃并均匀搅拌至均匀混合，获得水性聚氨酯乳液水溶液；
(3)将步骤(1)中的水性聚丙烯酸酯树脂溶液和步骤(2)中的水性聚氨酯乳液水溶液放入混合罐中混合，加热至65±3℃，然后加入填充料和助剂，均匀搅拌并用水调制，便制得水溶性转移镀铝涂料，涂料固含量为15-30wt％，PH值为7-8.4。
实施例4
本实施例的原料组成为：
水性聚氨酯乳液10份，
水性聚丙烯酸酯树脂10份，
填充料5份，
助剂2份，
酒精15份，
水50份；
其中，所述水性聚氨酯乳液分子量为2000-5000，粘度为50-500厘泊；所述水溶性聚丙烯酸酯树脂分子量为1000-2000，粘度为200-400厘泊，玻璃化温度为80℃；所述填充料为水溶性弹性体树脂或/和成膜改进剂；所述助剂为水溶性蜡乳液、润湿剂、流平剂和消泡剂中的一种或几种。所述水溶性弹性体树脂为合成丁苯乳液和丙烯酸压敏乳中的一种或两种，所述成膜改进剂为乙二醇醚，所述水溶性蜡乳液为聚乙烯蜡，所述润湿剂为改性有机硅氧烷，所述流平剂为聚硅氧烷类，所述消泡剂为改性硅酮。
本实施例的制备方法为：
(1)将质量比为2∶1的水和酒精混合，加热至65±3℃，逐步加入水性聚丙烯酸酯树脂并均匀搅拌至全部溶解，获得水性聚丙烯酸酯树脂溶液；
(2)在水性聚氨酯乳液中加水性聚氨酯乳液质量1倍的水，加热至80℃并均匀搅拌至均匀混合，获得水性聚氨酯乳液水溶液；
(3)将步骤(1)中的水性聚丙烯酸酯树脂溶液和步骤(2)中的水性聚氨酯乳液水溶液放入混合罐中混合，加热至65±3℃，然后加入填充料和助剂，均匀搅拌并用水调制，便制得水溶性转移镀铝涂料，涂料固含量为15-30wt％，PH值为7-8.4。
以上实施例制备的产品的性能指标为：
固含量      15-30wt％；
PH值        7.0-8.4；
粘度        26S(涂4-杯)；
水溶解度    可无限溶解；
玻璃化温度  -10℃。

Claims (3)

1.一种水溶性转移镀铝涂料，其特征在于由以下重量份的原料组成：
水性聚氨酯乳液5-10份，
水性聚丙烯酸酯树脂3-15份，
填充料5-10份，
助剂1-3份，
酒精10-30份，
水40-80份；
其中，所述水性聚氨酯乳液分子量为2000-5000，粘度为50-500厘泊；所述水性聚丙烯酸酯树脂分子量为1000-2000，粘度为200-400厘泊，玻璃化温度为80℃；所述填充料为水溶性弹性体树脂或/和成膜改进剂；所述助剂为水溶性蜡乳液、润湿剂、流平剂和消泡剂中的一种或几种。
2.根据权利要求1所述的一种水溶性转移镀铝涂料，其特征在于，所述水溶性弹性体树脂为合成丁苯乳液和丙烯酸压敏乳中的一种或两种，所述成膜改进剂为乙二醇醚，所述水溶性蜡乳液为聚乙烯蜡，所述润湿剂为改性有机硅氧烷，所述流平剂为聚硅氧烷，所述消泡剂为改性硅酮。
3.一种制备如权利要求1所述水溶性转移镀铝涂料的方法，其特征在于包括以下步骤：
(1)将质量比为1-2∶1的水和酒精混合，加热至65±3℃，逐步加入水性聚丙烯酸酯树脂并均匀搅拌至全部溶解，获得水性聚丙烯酸酯树脂溶液；
(2)在水性聚氨酯乳液中加水性聚氨酯乳液质量1-3倍的水，加热至80℃并均匀搅拌至均匀混合，获得水性聚氨酯乳液水溶液；
(3)将步骤(1)中的水性聚丙烯酸酯树脂溶液和步骤(2)中的水性聚氨酯乳液水溶液放入混合罐中混合，加热至65±3℃，然后加入填充料和助剂，均匀搅拌并用水调制，便制得水溶性转移镀铝涂料，涂料固含量为15-30wt％，PH值为7-8.4。
CN2009100235203A 2009-08-07 2009-08-07 一种水溶性转移镀铝涂料及其制备方法 Expired - Fee Related CN101619191B (zh)