CN101550254A - 耐高温、防电晕高电阻的三元乙丙橡胶的制备技术 - Google Patents

耐高温、防电晕高电阻的三元乙丙橡胶的制备技术 Download PDF

Info

Publication number
CN101550254A
CN101550254A CNA2009101409537A CN200910140953A CN101550254A CN 101550254 A CN101550254 A CN 101550254A CN A2009101409537 A CNA2009101409537 A CN A2009101409537A CN 200910140953 A CN200910140953 A CN 200910140953A CN 101550254 A CN101550254 A CN 101550254A
Authority
CN
China
Prior art keywords
rubber
agent
resistance
prescription
ethylene propylene
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2009101409537A
Other languages
English (en)
Other versions
CN101550254B (zh
Inventor
尤建义
冯一东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN200910140953A priority Critical patent/CN101550254B/zh
Publication of CN101550254A publication Critical patent/CN101550254A/zh
Application granted granted Critical
Publication of CN101550254B publication Critical patent/CN101550254B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种耐高温、防电晕高电阻的三元乙丙橡胶的制备技术，包括配方、制备工艺。本发明通过增强配方、混炼制备工艺的技术方案，克服了现有技术的三元乙丙橡胶材料存在的耐温性能偏低的问题与不足，所提供的一种耐高温、防电晕高电阻的三元乙丙橡胶的制备技术，制备出耐温150℃的防电晕高电阻三元乙丙橡胶材料，满足了汽车工业对橡胶制品的耐热性能、电气强度的特殊要求，使三元乙丙橡胶制品达到了提高耐温性能、电气绝缘强度的目的。

Description

耐高温、防电晕高电阻的三元乙丙橡胶的制备技术
技术领域
本发明涉及橡胶改性材料的制备技术，具体是指用于制作汽车胶管的材料的一种耐高温、防电晕高电阻的三元乙丙橡胶的制备技术。
背景技术
三元乙丙橡胶是乙烯、丙烯以及非共轭二烯烃的三元共聚物，通过共混、共聚、填充、接枝、增强和分子复合改性，可获得各种综合性能良好，适合不同用途成本低廉的改性橡胶材料。
汽车冷却系统胶管要求耐温性能在140℃以上，在高海拔低气压地区，汽车的高压点火系统易发生电晕现象，因此要求其点火系统的高压导线的电气绝缘护套具有防电晕高电阻性能，现有技术的耐温胶管用三元乙丙橡胶材料耐温135℃，在用于制造汽车冷却系统胶管，高压电气绝缘护套等橡胶制品上存在耐温性能偏低的问题与不足。
发明内容
针对上述现有技术存在的问题与不足，本发明通过增强配方、混炼制备工艺的技术方案，提供一种耐高温、防电晕高电阻的三元乙丙橡胶的制备技术，制备出耐温150℃的防电晕高电阻三元乙丙橡胶材料，旨在满足汽车工业对橡胶制品的耐热性能、电气强度的特殊要求，使三元乙丙橡胶制品达到提高耐温性能、电气绝缘强度的目的。
本发明的目的是这样实现的：耐高温、防电晕高电阻的三元乙丙橡胶的制备技术，包括配方、制备工艺，其中：所述的配方为，橡胶原料：三元乙丙橡胶33.36％；补强剂：快压出炉黑7.68％、非污染高定伸半补强炉黑19.03％、矽丽粉21.70％；增塑剂：石蜡油12.68％；活性剂：氧化锌1.67％、硬脂酸0.33％、聚乙二醇1.34％；防老剂：2，2，4-三甲基-1，2-二氢化喹啉聚合体0.47％；硫化剂：过氧化二异丙苯1.17％、N，N’-间苯撑双马来酰亚胺0.57％；配方单位为重量百分比；所述的制备工艺为混炼，其中，
步骤一、调整密炼机温度：100℃，转速：32转/分钟，将橡胶原料及配方中的补强剂、增塑剂、活性剂、防老剂投入密炼机，密炼8分钟，胶温控制在150℃以下排胶，移至橡胶过滤挤出机，滤网由里至外为10目，50目，50目，过滤挤出，冷却，获得母炼胶，待用；
步骤二、将母炼胶投入开放式炼胶机，均匀加入配方中的硫化剂混炼，密炼2分钟，胶温控制在100℃以下，出片冷却，静置熟化8小时～240小时，获得的混炼胶，即为耐温150℃的防电晕高电阻三元乙丙橡胶材料，供制造汽车冷却胶管等制品使用。
以上制备技术制备的耐温150℃的防晕高电阻三元乙丙橡胶材料所制造的汽车胶管，经各项机械强度及理化指标的检测，均符合GB/T531、GB/T528、GB/T1690、GB/T3512、GB/T7762国家标准，并满足ELV指令要求。
上述，本发明通过增强配方、混炼制备工艺的技术方案，克服了现有技术的三元乙丙橡胶材料存在的耐温性能偏低的问题与不足，所提供的一种耐高温、防电晕高电阻的三元乙丙橡胶的制备技术，制备出耐温150℃的防电晕高电阻三元乙丙橡胶材料，满足了汽车工业对橡胶制品的耐热性能、电气强度的特殊要求，使三元乙丙橡胶制品达到了提高耐温性能、电气绝缘强度的目的。
实施例说明
以下通过具体实施例对本发明的耐高温、防电晕高电阻的三元乙丙橡胶的制备技术，作进一步详细说明，所属领域的技术人员可以参照实施例的配方及制备方法制得耐高温、防电晕高电阻的三元乙丙橡胶，但不应理解为对本发明的任何限制。
具体实施方式
实施例
品名：耐温150℃的防电晕高电阻三元乙丙橡胶材料
配方：配方单位为重量百分比
橡胶原料：三元乙丙橡胶33.36％；
补强剂：快压出炉黑7.68％、非污染高定伸半补强炉黑19.03％、矽丽粉21.70％；
增塑剂：石蜡油12.68％；
活性剂：氧化锌1.67％、硬脂酸0.33％、聚乙二醇1.34％；
防老剂：2，2，4-三甲基-1，2-二氢化喹啉聚合体0.47％；
硫化剂：过氧化二异丙苯1.17％、N，N’-间苯撑双马来酰亚胺0.57％。
制备
制备条件、设备
环境气压：一个大气压；
环境温度：室温；
制备设备：开放式炼胶机、加压式密炼机、橡胶过滤挤出机。
制备工艺流程：混炼，
步骤一、调整加压式密炼机温度：100℃，转速：32转/分钟，将橡胶原料及配方中的补强剂、增塑剂、活性剂、防老剂投入加压式密炼机，密炼8分钟，胶温控制在150℃以下排胶，移至橡胶过滤挤出机，滤网由里至外为10目，50目，50目，过滤挤出，冷却，获得母炼胶，待用；
步骤二、将母炼胶投入开放式炼胶机，均匀加入配方中的硫化剂混炼，密炼2分钟，胶温控制在100℃以下，出片冷却，静置熟化8小时～240小时，获得的混炼胶，即为耐温150℃的防电晕高电阻三元乙丙橡胶材料。

Claims (2)

1、耐高温、防电晕高电阻的三元乙丙橡胶的制备技术，包括配方、制备工艺，其特征在于：所述的配方为，橡胶原料：三元乙丙橡胶33.36％；补强剂：快压出炉黑7.68％、非污染高定伸半补强炉黑19.03％、矽丽粉21.70％；增塑剂：石蜡油12.68％；活性剂：氧化锌1.67％、硬脂酸0.33％、聚乙二醇1.34％；防老剂：2，2，4-三甲基-1，2-二氢化喹啉聚合体0.47％；硫化剂：过氧化二异丙苯1.17％、N，N’-间苯撑双马来酰亚胺0.57％；配方单位为重量百分比。
2、根据权利要求1所述的耐高温、防电晕高电阻的三元乙丙橡胶的制备技术，其特征在于：所述的制备工艺为混炼，
步骤一、调整密炼机温度：100℃，转速：32转/分钟，将橡胶原料及配方中的补强剂、增塑剂、活性剂、防老剂投入密炼机，密炼8分钟，胶温控制在150℃以下排胶，移至橡胶过滤挤出机，滤网由里至外为10目，50目，50目，过滤挤出，冷却，获得母炼胶，待用；
步骤二、将母炼胶投入开放式炼胶机，均匀加入配方中的硫化剂混炼，密炼2分钟，胶温控制在100℃以下，出片冷却，静置熟化8小时～240小时，获得的混炼胶，即为耐温150℃的防电晕高电阻三元乙丙橡胶材料。
CN200910140953A 2009-05-08 2009-05-08 耐高温、防电晕高电阻的三元乙丙橡胶的制备方法 Expired - Fee Related CN101550254B (zh)