CN101548843A - 一种釉下红陶餐具的制备方法 - Google Patents

一种釉下红陶餐具的制备方法 Download PDF

Info

Publication number
CN101548843A
CN101548843A CNA2009100392219A CN200910039221A CN101548843A CN 101548843 A CN101548843 A CN 101548843A CN A2009100392219 A CNA2009100392219 A CN A2009100392219A CN 200910039221 A CN200910039221 A CN 200910039221A CN 101548843 A CN101548843 A CN 101548843A
Authority
CN
China
Prior art keywords
hours
glaze
temperature
red
red pottery
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2009100392219A
Other languages
English (en)
Other versions
CN101548843B (zh
Inventor
翁汉荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Weng Hanrong
Weng Jinquan
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2009100392219A priority Critical patent/CN101548843B/zh
Publication of CN101548843A publication Critical patent/CN101548843A/zh
Application granted granted Critical
Publication of CN101548843B publication Critical patent/CN101548843B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供一种釉下红陶餐具的制备方法，包括以下步骤：(1)选料；(2)制作红陶瓷泥：(3)制作餐具坯体；(4)素烧，在氧化气氛下烧成，温度为950～1000℃，时间为7.5～8小时，保温7～8小时；(5)上底釉，表面装饰处理；(6)入窑烤色烘干，温度740～760℃，时间3～4小时，保温9～10小时；(7)上透明釉，釉烧，温度为1050～1100℃，时间为9～10小时，保温11～12小时；(8)检验、包装、入库。应用本发明，该红陶餐具具有重量轻、烧成温度较低、能耗低，产品破损后容易风化，减少对生态环境的污染；且产品的热稳定性能较好，保鲜性较佳，成品率高；采用釉下彩工艺，色彩鲜艳，不褪色，品质高雅，满足人们现代生活的需要。

Description

一种釉下红陶餐具的制备方法
技术领域
本发明涉及一种日用餐具的制备方法，尤其涉及一种釉下红陶餐具的制备方法。
背景技术
日用餐具主要由陶瓷制成，主要有强化瓷、高白瓷、骨瓷、美质瓷等陶瓷制品，这些陶瓷制品虽强化性能好，耐冲击、耐高温、其不足之处为烧成温度较高，能耗高，重量较重，保鲜保健性能效果一般，且产品经高温烧成不能风化降解，用后丢弃容易造成对环境污染，特别是生产过程产生的废次品形成陶瓷垃圾，更对生态环境造成污染和危害。而用红土瓷泥生产的红陶制品虽然有重量轻、烧成温度较低，能耗低，且产品破损后容易风化，但由于其质地较脆，目前仅应用于茶具、工艺品等，还没有应用于日用餐具，应用领域受到限制。
发明内容
为克服陶瓷餐具的不足，本发明的目的在于提供一种重量轻、烧成温度较低、能耗低，产品破损后容易风化，减少环境污染；且产品的热稳定性能较高，对食品保鲜性效果佳的餐具，满足人们现代生活的需要。
本发明解决其技术问题所采用的技术方案是：一种釉下红陶餐具的制备方法，包括以下步骤：
(1)选料：采用矿土或化合物为原料，按重量百分比为：紫泥土35～45％、红粘土25～35％、白粘土25～30％；
(2)制作红陶瓷泥：将按比例的红陶泥土矿混合加适量水经过球磨、搅拌加工12小时，过200目浆泥目筛，进行压干成型成为红陶瓷泥；
(3)制作红陶餐具坯体；
(4)素烧，将红陶餐具坯体在氧化气氛下烧成，烧成温度为950～1000℃，烧成时间为7.5～8小时，终点温度后，止火，保温7～8小时自然冷却，出窑；
(5)上底釉，进行表面装饰处理；
(6)入窑烤色烘干，烘干温度为740～760℃，时间为3～4小时，终点温度，止火，保温9～10小时；
(7)上透明釉，入窑进行釉烧，烧成温度为1050～1100℃，烧成时间为9～10小时，终点温度后，止火，保温11～12小时，冷却，出窑；
(8)检验、包装、入库。
上述步骤(3)所述制作红陶餐具坯体为采用滚压成型或注浆成型。
上述步骤(5)所述上底釉为上陶瓷白釉或色釉，所述表面装饰处理为贴花纸或绘制所需图案。
应用本发明，该红陶餐具具有重量轻、烧成温度较低、能耗低，与陶瓷制品相比，节能20％以上，减耗15％以上，产品破损后容易风化，减少对生态环境污染的优点；且产品的热稳定性能较好，达到200℃±20℃，可适合于微波炉使用；产品气孔大，对食品保鲜性效果也较佳，且该产品变型率小，规整度好，故可大大提高产品成品率；且该红陶餐具采用釉下彩工艺，产品花纹图案不褪色，色彩鲜艳，品质高雅，铅、镉溶出量远低于国家标准规定的指标，满足新时代人们所追求的高品位多层次，重视健康环保物质要求的需要。
具体实施方式
实施例：一种釉下红陶餐具的制备方法，包括以下步骤：
(1)选料：采用矿土或化合物为原料，按重量百分比为：紫泥土40％、红粘土30％、白粘土30％；
(2)制作红陶瓷泥：将按比例的红陶泥土矿混合加适量水经过球磨、搅拌加工12小时，过200目浆泥目筛，进行压干成型成为红陶瓷泥；
(3)采用滚压成型制作红陶餐具坯体；
(4)素烧，将红陶餐具坯体在氧化气氛下烧成，烧成温度为980℃，烧成时间为8小时，终点温度后，止火，保温7.5小时自然冷却，出窑；
(5)上陶瓷白釉，贴花纸；
(6)入窑烤色烘干，烘干温度为750℃，时间为4小时，终点温度，止火，保温9小时；
(7)上透明釉，入窑进行釉烧，烧成温度为1080℃，烧成时间为9小时，终点温度后，止火，保温12小时，冷却，出窑；
(8)检验、包装、入库。

Claims (3)

1、一种釉下红陶餐具的制备方法，包括以下步骤：
(1)选料：采用矿土或化合物为原料，按重量百分比为：紫泥土35～45％、红粘土25～35％、白粘土25～30％；
(2)制作红陶瓷泥：将按比例的红陶泥土矿混合加适量水经过球磨、搅拌加工12小时，过200目浆泥目筛，进行压干成型成为红陶瓷泥；
(3)制作红陶餐具坯体；
(4)素烧，将红陶餐具坯体在氧化气氛下烧成，烧成温度为950～1000℃，烧成时间为7.5～8小时，终点温度后，止火，保温7～8小时自然冷却，出窑；
(5)上底釉，进行表面装饰处理；
(6)入窑烤色烘干，烘干温度为740～760℃，时间为3～4小时，终点温度，止火，保温9～10小时；
(7)上透明釉，入窑进行釉烧，烧成温度为1050～1100℃，烧成时间为9～10小时，终点温度后，止火，保温11～12小时，冷却，出窑；
(8)检验、包装、入库。
2、根据权利要求1所述釉下红陶餐具的制备方法，其特征在于：步骤(3)所述制作红陶餐具坯体为采用滚压成型或注浆成型。
3、根据权利要求1所述釉下红陶餐具的制备方法，其特征在于：步骤(5)所述上底釉为上陶瓷白釉或色釉，所述表面装饰处理为贴花纸或绘制所需图案。
CN2009100392219A 2009-05-06 2009-05-06 一种釉下红陶餐具的制备方法 Expired - Fee Related CN101548843B (zh)