CN101544787A - 轮胎内层尼龙帘线合成胶 - Google Patents

轮胎内层尼龙帘线合成胶 Download PDF

Info

Publication number
CN101544787A
CN101544787A CN200910020129A CN200910020129A CN101544787A CN 101544787 A CN101544787 A CN 101544787A CN 200910020129 A CN200910020129 A CN 200910020129A CN 200910020129 A CN200910020129 A CN 200910020129A CN 101544787 A CN101544787 A CN 101544787A
Authority
CN
China
Prior art keywords
type
rubber
agent
tire
inner layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN200910020129A
Other languages
English (en)
Inventor
田家礼
张波
张宏文
施红影
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong Hengyu Rubber Co Ltd
Original Assignee
Shandong Hengyu Rubber Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shandong Hengyu Rubber Co Ltd filed Critical Shandong Hengyu Rubber Co Ltd
Priority to CN200910020129A priority Critical patent/CN101544787A/zh
Publication of CN101544787A publication Critical patent/CN101544787A/zh
Pending legal-status Critical Current

Abstract

本发明涉及合成橡胶领域中的一种轮胎内层尼龙帘线合成胶。其技术方案是：由下列重量份的原料组成：90份天然胶，8－12份丁苯胶，40－60份精细再生胶，3－5份氧化锌，2－3.5份硬脂酸，3－5份防老剂，1.5－3份增粘树脂，1.5－3份均匀剂，1－3份增塑剂，1.5－2.2份硅烷偶联剂，30－40份高耐磨炉黑，6－8份白炭黑，7.5－8.5份芳烃油，2－3份硫磺，1－2份硫化促进剂，0.1－0.25份防焦剂。本发明采用白炭黑、Si－69平衡硫化体系，避免了过硫化的问题，使得轮胎的整体性能得到大幅度地提高。配方中使用了大量精细再生橡胶替代天然胶，不仅节约了成本和资源，同时改善了内层帘线胶的炼胶和压延工艺性能。

Description

轮胎内层尼龙帘线合成胶
技术领域
本发明涉及合成橡胶领域中的一种轮胎内层尼龙帘线合成胶。
背景技术
斜交胎用内层尼龙帘线胶，在整个轮胎设计中是一个非常重要的原料配置部分。此配方设计的好坏直接影响到轮胎胎肩部位的耐热性能和挺性，进而影响到轮胎的整体使用寿命。
为了提高此胶与尼龙帘线的粘合力，通常考虑在配方中使用大比例的天然橡胶，同时辅以一定比例的氧化锌、硬脂酸、防老剂、增粘树脂、增塑剂、偶联剂和炭黑等，以增加其粘性。尽管如此，由于此胶料使用于轮胎内部贴近于硫化胶囊，轮胎硫化过程中受到的传热较多，经常由于硫化速度的设计偏差导致此胶料出现过硫化现象，降低了此胶料的性能，使轮胎在使用过程中，出现胎里跳线、帘布层间脱层等问题，而且由于使用较多份数的天然橡胶，一方面耗费大量的橡胶资源，另外一方面也导致了轮胎整体成本的增加，进而影响了产品的市场竞争力。
发明内容
本发明的目的就是针对现有技术存在的缺陷，主要围绕解决硫化过程中胎体帘线的过硫化问题和解决此配方的高成本问题而提出一种轮胎内层尼龙帘线合成胶。
其技术方案是：由下列重量份的原料组成：90份天然胶，8-12份丁苯胶，40-60份精细再生胶，3-5份氧化锌，2-3.5份硬脂酸，3-5份防老剂，1.5-3份增粘树脂，1.5-3份均匀剂，1-3份增塑剂，1.5-2.2份硅烷偶联剂，30-40份高耐磨炉黑，6-8份白炭黑，7.5-8.5份芳烃油，2-3份硫磺，1-2份硫化促进剂，0.1-0.25份防焦剂。
其中其中硬脂酸包括十八碳酸、十八酸、十八烷酸和十八碳烷酸的一种；防老剂是由1-3份RD型防老剂和1-3份4010NA型防老剂或BLE-W型防老剂或DTPD型防老剂中的任一种；均匀剂为A-78型均匀剂或A型增塑剂与T-78型均匀剂的混合物；增粘树脂为C5型增粘树脂；增塑剂为A型增塑剂；硅烷偶联剂为Si-69型硅烷偶联剂；高耐磨炉黑为N330型高耐磨炉黑；硫化促进剂为NOBS型和DM型硫化促进剂，防焦剂为CTP型防焦剂。
发明效果：由于采用白炭黑、Si-69平衡硫化体系，白炭黑、Si-69的存在与发生裂解的交联键又重新反应，使硫化过程中交联键的密度处于一种动态平衡中，从而避免了过硫化的问题，使得轮胎的整体性能得到大幅度地提高。配方中使用了大量精细再生橡胶替代天然胶，不仅节约了成本和资源，同时改善了内层帘线胶的炼胶和压延工艺性能。最终改善了斜交载重轮胎的硫化状况，全面提高了轮胎的质量，大大延长了轮胎的使用寿命。同时，节约了大量成本，提高了斜交轮胎的市场竞争力。
具体实施方式
实施例1，原料的组成(重量份)：90份天然胶，10份丁苯胶，50份精细再生胶，4份氧化锌，3份硬脂酸，1.5份RD型防老剂和1.5份4010NA型防老剂，1.5份C5型增粘树脂，1.5份A-78型均匀剂，1份A型增塑剂，2.2份Si-69型硅烷偶联剂，36份N330型高耐磨炉黑，7份白炭黑，8.5份芳烃油，2.3份普通硫磺，1.05份NOBS型和0.3份DM型硫化促进剂，0.15份CTP型防焦剂。
实施例2，原料的组成(重量份)：90份天然胶，8.5份丁苯胶，45份精细再生胶，3.5份氧化锌，2.5份硬脂酸，1.5份RD型防老剂和1.5份BLE-W型防老剂，1.5份C5型增粘树脂，1.5份A-78型均匀剂，1份A型增塑剂，2份Si-69型硅烷偶联剂，38份N330型高耐磨炉黑，8份白炭黑，8.5份芳烃油，2份普通硫磺，1.05份NOBS型和0.3份DM型硫化促进剂，0.15份CTP型防焦剂。
实施例3，原料的组成(重量份)：90份天然胶，10.5份丁苯胶，55份精细再生胶，3份氧化锌，2.5份硬脂酸，1.5份RD型防老剂和1.5份DTPD型防老剂，1.5份C5型增粘树脂，1.5份A-78型均匀剂，1份A型增塑剂，2份Si-69型硅烷偶联剂，38份N330型高耐磨炉黑，8份白炭黑，8.5份芳烃油，2份普通硫磺，1.05份NOBS型和0.3份DM型硫化促进剂，0.15份CTP型防焦剂。
上述仅仅列举出3个具体实施列，实验证明在本方案的比例范围内的任意组合，均能取得预期的效果。

Claims (2)

1、一种轮胎内层尼龙帘线合成胶，其特征是：由下列重量份的原料组成：90份天然胶，8-12份丁苯胶，40-60份精细再生胶，3-5份氧化锌，2-3.5份硬脂酸，3-5份防老剂，1.5-3份增粘树脂，1.5-3份均匀剂，1-3份增塑剂，1.5-2.2份硅烷偶联剂，30-40份高耐磨炉黑，6-8份白炭黑，7.5-8.5份芳烃油，2-3份硫磺，1-2份硫化促进剂，0.1-0.25份防焦剂。
2、根据权利要求1所述的轮胎内层尼龙帘线合成胶，其特征是：其中其中硬脂酸包括十八碳酸、十八酸、十八烷酸和十八碳烷酸的一种；防老剂是由1-3份RD型防老剂和1-3份4010NA型防老剂或BLE-W型防老剂或DTPD型防老剂中的任一种；均匀剂为A-78型均匀剂或A型增塑剂与T-78型均匀剂的混合物；增粘树脂为C5型增粘树脂；增塑剂为A型增塑剂；硅烷偶联剂为Si-69型硅烷偶联剂；高耐磨炉黑为N330型高耐磨炉黑；硫化促进剂为NOBS型和DM型硫化促进剂，防焦剂为CTP型防焦剂。
CN200910020129A 2009-03-31 2009-03-31 轮胎内层尼龙帘线合成胶 Pending CN101544787A (zh)