CN101538449A - 氟橡胶蓄能器胶囊粘接剂 - Google Patents
氟橡胶蓄能器胶囊粘接剂 Download PDFInfo
- Publication number
- CN101538449A CN101538449A CN200910068680A CN200910068680A CN101538449A CN 101538449 A CN101538449 A CN 101538449A CN 200910068680 A CN200910068680 A CN 200910068680A CN 200910068680 A CN200910068680 A CN 200910068680A CN 101538449 A CN101538449 A CN 101538449A
- Authority
- CN
- China
- Prior art keywords
- adhesive
- fluorine rubber
- energy accumulator
- capsule
- bonding adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及橡胶粘接剂,尤其涉及一种氟橡胶蓄能器胶囊粘接剂。该粘接剂是由25-30%的氟橡胶、3-5%的白碳黑、1.5-3%的粘合剂及0.5-1%的硫化剂制备成的胶料与60-70%的丁酮混合而成。胶料是将氟橡胶、白碳黑、粘合剂及硫化剂上开炼机薄通10-12次,然后切成小碎块放入带盖的容器内;再将丁酮倒入容器内,盖上容器盖,与胶料混和2-3小时,然后进行搅拌,直到胶料完全溶解。本发明所产生的有益效果是:采取以上技术方案,解决了氟橡胶胶囊的粘接问题,经上百只胶囊生产,未出现接口开胶问题,从而扩大了蓄能器的使用范围;可广泛应用在航空、电厂、化工等领域。
Description
技术领域
本发明涉及橡胶粘接剂,尤其涉及一种氟橡胶蓄能器胶囊粘接剂。
背景技术
蓄能器胶囊通常在120℃以下的油介质中工作。但在实际工作中,一些系统的油温达到150--250℃,普通耐油橡胶满足不了使用要求;要使用特种橡胶,氟橡胶具有耐油,耐热的特性。由于氟橡胶是一种高饱和的含氟高聚物,因此,硫化氟橡胶的粘接是很困难的,一般采用环氧树脂粘接,如EC1838,由于环氧树脂的固化时间长,定型困难,使用温度低(≤120℃),弹性差,与氟橡胶的拉伸变形差距大,因此胶囊粘接口易开胶。目前,国内外市场上还没有适合氟橡胶胶囊的粘接剂。
发明内容
本发明的目的是要解决氟橡胶胶囊的粘接问题,要求粘接剂要有足够的粘接强度和较强的抗拉伸疲劳性,因此成功研制出一种氟橡胶蓄能器胶囊粘接剂。该粘接剂选用与胶囊相同的橡胶作为粘接剂胶料中的主要组分,通过试验和胶囊使用验正,该粘接剂能够满足胶囊的使用要求。
本发明为实现上述目的所采取的技术方案是:一种氟橡胶蓄能器胶囊粘接剂,是按重量百分比组成的组合物,其组分组成及各组分所占的百分比范围是:
氟橡胶 25-30% 白碳黑 3-5%
粘合剂 1.5-3% 硫化剂 0.5-1%
丁酮 60-70%。
氟橡胶蓄能器胶囊粘接剂的制备方法,包括以下步骤:
(1)、配制胶料
将25-30%的氟橡胶、3-5%的白碳黑、1.5-3%的粘合剂及0.5-1%的硫化剂上开炼机薄通10-12次,然后切成小碎块放入带盖的容器内;
(2)、配制胶液
将60-70%的丁酮倒入容器内,盖上容器盖,与胶料混和2-3小时,然后进行搅拌,直到胶料完全溶解。
本发明所产生的有益效果是:采取以上技术方案,解决了氟橡胶胶囊的粘接问题,经上百只胶囊生产,未出现接口开胶问题,从而扩大了蓄能器的使用范围;可广泛应用在航空、电厂、化工等领域。
具体实施方式
氟橡胶蓄能器胶囊粘接剂,是按重量百分比组成的组合物,其组分组成及各组分所占的百分比范围是:
氟橡胶2602 25-30% 白碳黑 3-5%
粘合剂 1.5-3% 硫化剂 0.5-1%
丁酮 60-70%。
其组分粘接剂是粘合剂RS和粘合剂A两种粘合剂。
氟橡胶蓄能器胶囊粘接剂的制备方法,包括以下步骤:
(1)、配制胶料
将25-30%的氟橡胶、3-5%的白碳黑、1.5-3%的粘合剂及0.5-1%的硫化剂上150开炼机薄通10-12次,然后切成小碎块放入带盖的容器内;
(2)、配制胶液
将60-70%的丁酮倒入容器内,盖上容器盖,与胶料混和2-3小时,然后进行搅拌,直到胶料完全溶解。
实施例一:氟橡胶蓄能器胶囊粘接剂是按重量百分比组成的组合物,其组分组成及各组分所占的最佳百分比是:
氟橡胶2602 28% 白碳黑 3.4%
粘合剂RS 1.2% 粘合剂A 0.6%
硫化剂 0.8% 丁酮 66%。
氟橡胶蓄能器胶囊粘接剂的制备方法,包括以下步骤:
(1)、配制胶料
将28%的氟橡胶2602、3.4%的白碳黑、1.2%的粘合剂RS、0.6%的粘合剂A及0.8%的硫化剂3#上150开炼机薄通10-12次,然后切成小碎块放入带盖的容器内;
(2)、配制胶液
将66%的丁酮倒入容器内,盖上容器盖,与胶料混和2-3小时,然后进行搅拌,直到胶料完全溶解。
实施例二:氟橡胶蓄能器胶囊粘接剂是按重量百分比组成的组合物,其组分组成及各组分所占的最佳百分比是:
氟橡胶2602 26% 白碳黑 3.8%
粘合剂RS 1.5% 粘合剂A 0.8%
硫化剂 0.9% 丁酮 67%。
氟橡胶蓄能器胶囊粘接剂的制备方法,包括以下步骤:
(1)、配制胶料
将26%的氟橡胶2602、3.8%的白碳黑、1.5%的粘合剂RS、0.8%的粘合剂A及0.9%的硫化剂3#上150开炼机薄通10-12次,然后切成小碎块放入带盖的容器内;
(2)、配制胶液
将67%的丁酮倒入容器内,盖上容器盖,与胶料混和2-3小时,然后进行搅拌,直到胶料完全溶解。
Claims (3)
1、一种氟橡胶蓄能器胶囊粘接剂,是按重量百分比组成的组合物,其组分组成及各组分所占的百分比范围是:
氟橡胶 25-30% 白碳黑 3-5%
粘合剂 1.5-3% 硫化剂 0.5-1%
丁酮 60-70%。
2、根据权利要求1所述的氟橡胶蓄能器胶囊粘接剂,其特征在于:其组分粘接剂是粘合剂RS和粘合剂A两种粘合剂。
3、一种氟橡胶蓄能器胶囊粘接剂的制备方法,包括以下步骤:
(1)、配制胶料
将25-30%的氟橡胶、3-5%的白碳黑、1.5-3%的粘合剂及0.5-1%的硫化剂上开炼机薄通10-12次,然后切成小碎块放入带盖的容器内;
(2)、配制胶液
将60-70%的丁酮倒入容器内,盖上容器盖,与胶料混和2-3小时,然后进行搅拌,直到胶料完全溶解。