CN101468922A - Method for manufacturing black and green silicon carbide silicon carbide wall brick - Google Patents
Method for manufacturing black and green silicon carbide silicon carbide wall brick Download PDFInfo
- Publication number
- CN101468922A CN101468922A CNA2007100601766A CN200710060176A CN101468922A CN 101468922 A CN101468922 A CN 101468922A CN A2007100601766 A CNA2007100601766 A CN A2007100601766A CN 200710060176 A CN200710060176 A CN 200710060176A CN 101468922 A CN101468922 A CN 101468922A
- Authority
- CN
- China
- Prior art keywords
- silicon carbide
- black
- brick
- color
- green silicon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a method for manufacturing black-green silicon carbide carborundum wall tiles. The method adopts the prior ceramic external tiles which are 20 to 30 yuan per square meter. The external tiles are used as base materials of the black-green silicon carbide carborundum wall tiles, and black-green silicon carbide carborundum is stuck on the base materials. The wall tiles on which black-green carborundum is stuck flash in the sunshine and moonlight, and flashing bodies are gem-type multi-surface crystals which are black-green silicon carbide particles and are basic materials of artificial gems. The gemlike materials as decoration on wall surfaces of districts show high grade and luxury.
Description
Technical field:
The invention belongs to building and ornament materials, specially refer to a kind of making method of black and green silicon carbide silicon carbide wall brick.
Background technology:
Present external wall of building decorative wall brick has many kinds, various ceramic wall tile is arranged, it all is chromatic that this wall brick has many, the light face is arranged in having, a kind of earthenware brick as suitable light mud kettle is arranged, also have a kind of thick pitted skin between porcelain and pottery to split and go through brick, this splitting gone through brick and had plenty of that cutting makes when scraping base, also useful puller system between two fit adobes therefrom reinforcing break, what want is the sort of natural section, this section has scraggly base brick fracture effect, more than these mostly are the products of industrialization roller kiln, output is fine, but price is all lower, and also having many exterior wall mosaic bricks also is industrialization product, extensive output like this and large-scale the use, in each building sub-district all is that machine-made appearance is arranged, and present real estate commercial city likes showing unique characteristics, and can embody the outer wall material of individual demand.The present invention has adopted the ceramic exterior wall tile of 20～30 yuan of every square meters of present production.Make a kind of base material of black and green silicon carbide silicon carbide wall brick of this exterior wall tile, sticking system black and green silicon carbide silicon carbide on this base material, be stained with wall brick sparking flash of light under sunlight and moonlight of black green gold emery, and this twinkler is a jewel type polygonal crystal, we know black and green silicon carbide particle, be the basic material of hard mass, the material as this jewel is decorated on the metope of sub-district, demonstrates high-grade and luxurious.
Technology contents:
The red-brown earthenware brick that the present invention adopts ceramic wall tile to produce, this henna clay brick tarnish, there are many micropores on the surface, helps the spraying of acrylic acid aqueous binding agent, and can be firm be bonding to oarse-grained black and green silicon carbide.The silicon carbide of black and the green main particle of silicon carbide are the abrasive material level silicon carbide that Chinese first grinding wheel factory produces, the particle of silicon carbide be 16 orders to 60 orders, it is in order there to be enough bonding surfaces long-pending that this particulate is selected.The surface-area that exposes of particle on the other hand, also be to be polyhedral, on every brick of such particle nearly more or less a hundred, every square metre is used about one kilogram, and price is 20 yuan, adds 10 yuan every square metre acrylic acid aqueous binding agent, on the stripe shape earthenware brick basis of 20 centimetres of former 6 cm x, every square meter increases by 30 yuan, and common popular red-brown potter's clay wall brick will become high-grade wall brick.
Specific embodiments:
1. with acrylic wall paint emulsion 800 grams, 100 gram water soluble acrylic acid oil colours are advanced in allotment, also can allocate 10 gram color magma of into dying factory production, and color can be henna, also can be made into other needed color, so also enrich the color kind of this product.
2. if do base material of the present invention with the porcelain wall brick of other color, ceramic tile as various light colour systems, that just makees binding agent with the transparent vibrin clear lacquer, must be on the clear lacquer that had just sprayed with this binding agent, all spread black or green silicon carbide silicon carbide particle rapidly, because this vibrin clear lacquer promptly can be dry after 10 minutes.
3. binding agent is sprayed on uniformly on the exterior wall clay brick of strip with spray gun, with the height of hand black or green silicon carbide are sprinkling upon on the clay brick that sprayed binding agent uniformly then from 1 meter, this particulate method of spreading is fragmentarily, always can not resemble the density emery cloth and the sand paper, be to surpass 50～60 particles on the brick of 20 centimetres of every 6 cm x, particulate is of a size of 16 orders and 36 purposes.
4. the above particulate material that dispenses can be manual, but also pipeline system divides spreading, and drying process can adopt loft drier flowing water or oven dry.Can pack cartonning after the oven dry and become product.The present invention is not afraid of any ultraviolet radiation, is not afraid of any erosion by wind and rain yet.
Claims (1)
1. the making method of a black and green silicon carbide silicon carbide wall brick is characterized in that:
(1) with acrylic wall paint emulsion 800 gram, 100 gram water soluble acrylic acid oil colours are advanced in allotment, also can allocate 10 gram color magma of into dying factory production, and color can be henna, also can be made into other needed color, so also enrich the color kind of this product.
(2) if do base material of the present invention with the porcelain wall brick of other color, ceramic tile as various light colour systems, that just makees binding agent with the transparent vibrin clear lacquer, must be on the clear lacquer that had just sprayed with this binding agent, all spread black or green silicon carbide silicon carbide particle rapidly, because this vibrin clear lacquer promptly can be dry after 10 minutes.
(3) binding agent is sprayed on uniformly on the exterior wall clay brick of strip with spray gun, with the height of hand black or green silicon carbide are sprinkling upon on the clay brick that sprayed binding agent uniformly then from 1 meter, this particulate method of spreading is fragmentarily, always can not resemble the density emery cloth and the sand paper, be to surpass 50～60 particles on the brick of 20 centimetres of every 6 cm x, particulate is of a size of 16 orders and 36 purposes.
(4) the above particulate material that dispenses can be manual, but also pipeline system divides spreading, and drying process can adopt loft drier flowing water or oven dry.Can pack cartonning after the oven dry and become product.The present invention is not afraid of any ultraviolet radiation, is not afraid of any erosion by wind and rain yet.