CN101412846A - 尼龙66超韧级热塑性工程塑料 - Google Patents

尼龙66超韧级热塑性工程塑料 Download PDF

Info

Publication number
CN101412846A
CN101412846A CNA2007100470488A CN200710047048A CN101412846A CN 101412846 A CN101412846 A CN 101412846A CN A2007100470488 A CNA2007100470488 A CN A2007100470488A CN 200710047048 A CN200710047048 A CN 200710047048A CN 101412846 A CN101412846 A CN 101412846A
Authority
CN
China
Prior art keywords
nylon
ultra
engineering plastics
thermoplastic engineering
tough thermoplastic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2007100470488A
Other languages
English (en)
Inventor
陈勋森
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANGHAI NYTEX COMPOSITES PRODUCT CO Ltd
Original Assignee
SHANGHAI NYTEX COMPOSITES PRODUCT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI NYTEX COMPOSITES PRODUCT CO Ltd filed Critical SHANGHAI NYTEX COMPOSITES PRODUCT CO Ltd
Priority to CNA2007100470488A priority Critical patent/CN101412846A/zh
Publication of CN101412846A publication Critical patent/CN101412846A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种尼龙66超韧级热塑性工程塑料，该工程塑料包含尼龙66树脂、增韧中间体、聚乙烯、偶联剂，所述的尼龙66树脂为400－700重量份，所述的增韧中间体为100－300重量份，所述的聚乙烯为10－200重量份，所述的偶联剂为1－20重量份。与现有技术相比，本发明的尼龙66超韧级热塑性工程塑料具有良好的耐磨性、耐热性、耐油性及耐化学药品性，采用乙烯共聚物接枝马来酸酐体系进行增韧改性，改性后的超韧尼龙可以耐辐射，耐紫外线，并具有优异的机械强度，尤其是具有优异的低温耐冲击性能，可用于耐低温零部件，应用范围广。

Description

尼龙66超韧级热塑性工程塑料
技术领域
本发明涉及一种热塑性工程塑料，尤其涉及一种尼龙66超韧级热塑性工程塑料。
背景技术
尼龙是目前工程塑料中应用最为广泛的工程塑料之一，可应用于汽车、电子电器、办公用具、电动工具等各个方面，但是普通的尼龙，其耐冲击性较差，尤其是耐低温性能较差，因此限制了它在许多方面的应用。
发明内容
本发明的目的就是为了克服上述现有技术存在的缺陷而提供一种耐冲击性能佳、低温性能优异的尼龙66超韧级热塑性工程塑料。
本发明的目的可以通过以下技术方案来实现：尼龙66超韧级热塑性工程塑料，其特征在于，该工程塑料包含尼龙66树脂、增韧中间体、聚乙烯、偶联剂，所述的尼龙66树脂为400-700重量份，所述的增韧中间体为100-300重量份，所述的聚乙烯为10-200重量份，所述的偶联剂为1-20重量份。
所述的尼龙66树脂选自己二胺和己二酸通过直接或间接法缩聚生成的共聚物、尼龙66纱线经过挤出机制得的尼龙切片中的一种或两种。
所述的增韧中间体选自乙烯丁烯共聚物、乙烯丁烯共聚物接枝马来酸酐、乙烯丙烯共聚物、乙烯丙烯共聚物接枝马来酸酐中的一种或几种。
所述的聚乙烯包括乙烯通过高压聚合所得的聚合物。
所述的偶联剂包括R基三硅氧烷类化合物。
所述的R基选自氨基、羟基、乙烯基、环氧基、氰基、甲基丙烯酰氧基中的一种。
该工程塑料还包含稳定剂、润滑剂、脱模剂、成核剂、抗静电剂、颜料中的一种或几种。
与现有技术相比，本发明的尼龙66超韧级热塑性工程塑料具有良好的耐磨性、耐热性、耐油性及耐化学药品性，采用乙烯共聚物接枝马来酸酐体系进行增韧改性，改性后的超韧尼龙可以耐辐射，耐紫外线，并具有优异的机械强度，尤其是具有优异的低温耐冲击性能，可用于耐低温零部件，应用范围广。
具体实施方式
下面结合具体实施例对本发明作进一步说明。
实施例1
一种尼龙66超韧级热塑性工程塑料，包含下列组分及其重量份数：
 
组分 重量份数
尼龙66 650
乙烯丁烯共聚物 170
PE 150
乙烯基三甲氧基硅烷 20
有机硅 10
所得的尼龙66超韧级热塑性工程塑料的测试结果如下美标(ASTM)：
 
抗张强度(MPa) 35
延伸率(％) 150
抗折强度(MPa) 500
抗折弹性系数(MPa) 1500
Izod缺口冲击强度(KJ/m2) 100
低温缺口冲击强度(KJ/m2) 60
可以看出，本发明的尼龙66树脂材料，有较好的耐冲击性能。
实施例2
一种尼龙66超韧级热塑性工程塑料，包含下列组分及其重量份数：
 
组分 重量份数
尼龙66 650
乙烯丁烯共聚物接枝马来酸酐 170
 
PE 150
乙烯基三乙氧基硅烷 20
石蜡有机硅 28
所得的尼龙66超韧级热塑性工程塑料的测试结果如下美标(ASTM)：
 
抗张强度(MPa) 45
延伸率(％) 120
抗折强度(MPa) 580
抗折弹性系数(MPa) 1800
Izod缺口冲击强度(KJ/m2) 120
低温缺口冲击强度(KJ/m2) 90
可以看出，本发明的尼龙66树脂材料，有较好的耐冲击性能。
实施例3
一种尼龙66超韧级热塑性工程塑料，包含下列组分及其重量份数：
 
组分 重量份数
尼龙66 400
乙烯丙烯共聚物 100
PE 10
甲基三乙氧基硅烷 1
二苯亚甲基山梨醇硬脂酸三甲基氯化铵 55
所得的尼龙66超韧级热塑性工程塑料的测试结果如下美标(ASTM)：
 
抗张强度(MPa) 35
延伸率(％) 160
抗折强度(MPa) 500
抗折弹性系数(MPa) 1500
Izod缺口冲击强度(KJ/m2) 115
低温缺口冲击强度(KJ/m2) 100
实施例4
一种尼龙66超韧级热塑性工程塑料，包含下列组分及其重量份数：
 
组分 重量份数
尼龙66尼龙切片 400300
乙烯丙烯共聚物乙烯丙烯共聚物接枝马来酸酐 100200
PE 200
乙烯基三甲氧基硅烷甲基三乙氧基硅烷 55
硬脂酸钙聚乙烯蜡石蜡二苯亚甲基山梨醇硬脂酸二甲基戊基氯化铵颜料黄139颜料橙34 2222222
所得的尼龙66超韧级热塑性工程塑料的测试结果如下美标(ASTM)：
 
抗张强度(MPa) 40
延伸率(％) 160
抗折强度(MPa) 500
抗折弹性系数(MPa) 1500
Izod缺口冲击强度(KJ/m2) 110
低温缺口冲击强度(KJ/m2) 90

Claims (7)

1.尼龙66超韧级热塑性工程塑料，其特征在于，该工程塑料包含尼龙66树脂、增韧中间体、聚乙烯、偶联剂，所述的尼龙66树脂为400-700重量份，所述的增韧中间体为100-300重量份，所述的聚乙烯为10-200重量份，所述的偶联剂为1-20重量份。
2.根据权利要求1所述的尼龙66超韧级热塑性工程塑料，其特征在于，所述的尼龙66树脂选自己二胺和己二酸通过直接或间接法缩聚生成的共聚物、尼龙66纱线经过挤出机制得的尼龙切片中的一种或两种。
3.根据权利要求1所述的尼龙66超韧级热塑性工程塑料，其特征在于，所述的增韧中间体选自乙烯丁烯共聚物、乙烯丁烯共聚物接枝马来酸酐、乙烯丙烯共聚物、乙烯丙烯共聚物接枝马来酸酐中的一种或几种。
4.根据权利要求1所述的尼龙66超韧级热塑性工程塑料，其特征在于，所述的聚乙烯包括乙烯通过高压聚合所得的聚合物。
5.根据权利要求1所述的尼龙66超韧级热塑性工程塑料，其特征在于，所述的偶联剂包括R基三硅氧烷类化合物。
6.根据权利要求5所述的尼龙66超韧级热塑性工程塑料，其特征在于，所述的R基选自氨基、羟基、乙烯基、环氧基、氰基、甲基丙烯酰氧基中的一种。
7.根据权利要求1至6任一所述的尼龙66超韧级热塑性工程塑料，其特征在于，该工程塑料还包含稳定剂、润滑剂、脱模剂、成核剂、抗静电剂、颜料中的一种或几种。
CNA2007100470488A 2007-10-15 2007-10-15 尼龙66超韧级热塑性工程塑料 Pending CN101412846A (zh)