CN101407412B - 一种纳米复合活性生物陶瓷粉及加工工艺 - Google Patents
一种纳米复合活性生物陶瓷粉及加工工艺 Download PDFInfo
- Publication number
- CN101407412B CN101407412B CN2007100096521A CN200710009652A CN101407412B CN 101407412 B CN101407412 B CN 101407412B CN 2007100096521 A CN2007100096521 A CN 2007100096521A CN 200710009652 A CN200710009652 A CN 200710009652A CN 101407412 B CN101407412 B CN 101407412B
- Authority
- CN
- China
- Prior art keywords
- nanometer
- percent
- ceramic powder
- hours
- nano
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及日用陶瓷领域,具体涉及一种纳米复合活性生物陶瓷粉,包括纳米钇5%-10%,纳米银1%-5%,纳米锌5%-15%,氧化铁钛10%-20%,纳米电气石20%-35%,微米沸石25%-35%,该陶瓷材料添加到所有陶瓷釉料里,生产出来的陶瓷产品具有净化空气、防霉、除臭、自洁防污和抗菌性能,大肠杆菌、金黄色葡萄球菌达到大于99%,发射远红外线、释放负离子、对水质改善起到抗菌、净化、活化、PH值呈弱碱性、保持小分子团水和溶出人体所需微量元素效果。
Description
技术领域
本发明涉及日用陶瓷领域,具体涉及一种纳米复合活性生物陶瓷粉及加工工艺。
背景技术
陶瓷材料具有类似于金属的强度和比金属更为优越的耐磨性、耐高温性以及化学稳定性,可用于一般金属材料难以胜任的严酷环境。如高温、强腐蚀环境,另外,由陶瓷制成的机件重量轻,隔热性好,对提高能源利用效率具有重要意义,但由于其内在结构的原因,陶瓷材料脆性大,对内部缺陷敏感,裂纹一经产生往往就迅速扩展,使材料呈现无预兆灾难性的突然断裂,纳米复相陶瓷可分为三大类:内晶型纳米复相陶瓷、晶界型纳米复相陶瓷、纳米-纳米复相陶瓷,前二者为纳米-微米复合结构,实际上是一种纳米粒子增强微米基体的复合材料,由于基体的约束和隔离,纳米粒子在烧结时不容易长大,材料制备工艺相对简单,纳米-纳米复相陶瓷的基体和第二相晶粒都要保持在纳米尺度,由于纳米颗粒的巨大活性,在烧结过程中晶界扩散非常快,既有利于达到高致密度又极易发生晶粒快速生长,因而在最终将微结构控制在纳米量级是非常困难。
发明内容
本发明的目的是提供一种纳米复合活性生物陶瓷粉及加工工艺,该陶瓷粉具有净化空气、防霉、除臭、自洁防污和抗菌性能。
一种纳米复合活性生物陶瓷粉,包括纳米钇5%-10%,纳米银1%-5%,纳米锌5%-15%,氧化铁钛10%-20%,纳米电气石20%-35%,微米沸石25%-35%。
其加工工艺如下:按比例称取各成分,先将纳米级材料钇、银、锌混合均匀加水20%在60℃的烘房里发酵72小时、取出经窑温1000℃煅烧24小时,取出后再混合氧化铁钛,加水20%均匀,再次经窑温1000℃煅烧24小时,在取出后再次混合电气石、沸石加水20%均匀混合后在窑温1350℃进行煅烧24小时后,取出粉碎达到325目细粉,即得到材料一致的纳米级复合活性生物陶瓷粉,按5-20%的比例添加到陶瓷釉粉内。
该陶瓷材料添加到所有陶瓷釉料里,生产出来的陶瓷产品具有净化空气、防霉、除臭、自洁防污和抗菌性能,大肠杆菌、金黄色葡萄球菌达到大于99%,发射远红外线、释放负离子、对水质改善起到抗菌、净化、活化、PH值呈弱碱性、保持小分子团水和溶出人体所需微量元素效果。
具体实施方式
实施例1
一种纳米复合活性生物陶瓷粉,其加工工艺如:按比例称取各成分:纳米钇5%-10%,纳米银1%-5%,纳米锌5%-15%,氧化铁钛10%-20%,纳米电气石20%-35%,微米沸石25%-35%,先将纳米级材料钇、银、锌混合均匀加水20%在60℃的烘房里发酵72小时、取出经窑温1000℃煅烧24小时,取出后再混合氧化铁钛,加水20%均匀,再次经窑温1000℃煅烧24小时,在取出后再次混合电气石、沸石加水20%均匀混合后在窑温1350℃进行煅烧24小时后,取出粉碎达到325目细粉,即得到材料一致的纳米级/氧化物/矿物质复合活性生物陶瓷粉,按5-20%的比例添加到陶瓷釉粉内。
实施例2
一种纳米复合活性生物陶瓷粉,其加工工艺如:按比例称取各成分:纳米钇6千克,纳米银2千克,纳米锌7千克,氧化铁钛15千克,纳米电气石35千克,微米沸石35千克,先将纳米级材料钇、银、锌混合均匀加水20千克在60℃的烘房里发酵72小时、取出经窑温1000℃煅烧24小时,取出后再混合氧化铁钛,加水20千克均匀,再次经窑温1000℃煅烧24小时,在取出后再次混合电气石、沸石加水20千克均匀混合后在窑温1350℃进行煅烧24小时后,取出粉碎达到325目细粉,即得到材料一致的纳米级复合活性生物陶瓷粉100千克,按5-20%的比例添加到陶瓷釉粉内。本产品主要涉及空气净化及水处理的日用陶瓷、卫生洁具和建筑陶瓷,本陶瓷材料添加到所有陶瓷釉料里,生产出来的陶瓷产品具有净化空气、防霉、除臭、自洁防污和抗菌性能(大肠杆菌、金黄色葡萄球菌达到>99%),发射远红外线、释放负离子、对水质改善起到抗菌、净化、活化、PH值呈弱碱性、保持小分子团水和溶出人体所需微量元素效果;用于日用陶瓷,生态瓷、煲对普通水的结构改变、水质改善起到抗菌、净化、活化、PH值呈弱碱性、保持小分子团水、又能补充人体所需微量元素的生态健康饮用水,使烹饪的食物更好的保持原汁原味、细腻、新鲜可口上等会佳尧,用在卫生洁具和建筑陶瓷发射远红外线、释放负离子对净化室内空气中的醛、苯、氨和清除空气污染物起到抗菌、防霉、除臭、自洁功能的良好效果。利用稀土纳米级氧化钇激活锌、银离子起到广谱抗菌,铁、钛、矿物质电气石和沸石、产生远红外线和负离子、矿物质材料溶出人体所需的微量元素,经检测,在24小时内,对大肠杆菌的抗菌率大于99%,在24小时内,对金黄色葡萄球菌的抗菌率大于99%。
Claims (2)
1.一种纳米复合活性生物陶瓷粉,其特征在于:包括纳米钇5%-10%,纳米银1%-5%,纳米锌5%-15%,氧化铁钛10%-20%,纳米电气石20%-35%,微米沸石25%-35%。
2.根据权利要求1所述的纳米复合活性生物陶瓷粉,其特征在于:其加工工艺如下:按比例称取各成分,先将纳米级材料钇、银、锌混合均匀加水20%在60℃的烘房里发酵72小时、取出经窑温1000℃煅烧24小时,取出后再混合氧化铁钛,加水20%均匀,再次经窑温1000℃煅烧24小时,在取出后再次混合电气石、沸石加水20%均匀混合后在窑温1350℃进行煅烧24小时后,取出粉碎达到325目细粉,即得到材料一致的纳米级复合活性生物陶瓷粉,按5-20%的比例添加到陶瓷釉粉内。