CN101397488A - 一种防火弹性密封胶及其制备方法 - Google Patents

一种防火弹性密封胶及其制备方法 Download PDF

Info

Publication number
CN101397488A
CN101397488A CNA200810046522XA CN200810046522A CN101397488A CN 101397488 A CN101397488 A CN 101397488A CN A200810046522X A CNA200810046522X A CN A200810046522XA CN 200810046522 A CN200810046522 A CN 200810046522A CN 101397488 A CN101397488 A CN 101397488A
Authority
CN
China
Prior art keywords
parts
agent
fire
fireproof
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA200810046522XA
Other languages
English (en)
Other versions
CN101397488B (zh
Inventor
雷茂林
康武
刘锦洪
刘保全
王松柏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nuclear Power Institute of China
Original Assignee
Nuclear Power Institute of China
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nuclear Power Institute of China filed Critical Nuclear Power Institute of China
Priority to CN200810046522XA priority Critical patent/CN101397488B/zh
Publication of CN101397488A publication Critical patent/CN101397488A/zh
Application granted granted Critical
Publication of CN101397488B publication Critical patent/CN101397488B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种防火弹性密封胶及其制备方法，该防火弹性密封胶是将丙烯酸酯弹性乳液、乙二醇、乳化剂、分散剂作为基料，并添加阻燃剂、无机填料、着色剂、偶联剂、增稠剂等辅料制备而成。其制备方法是将上述基料按一定重量份数加入混合器中，在搅拌条件下加入上述辅料，通过混合、加热和真空除水等操作，制成防火弹性密封胶。该密封胶隔热、耐火性好；附着力强、固化后弹性好；固化过程中无有机溶剂挥发，生产成本低。适用于各种穿墙电缆、电缆桥架及管道开口的防火分隔。

Description

一种防火弹性密封胶及其制备方法
技术领域
本发明涉及高分子防火封堵材料及其制备方法，具体涉及一种密封胶及其制备方法。
背景技术
防火弹性密封胶主要用于有较大位移的各种贯穿物如电缆、风管、油管、气管等穿过墙壁、楼板时形成的各种开口及电缆桥架的防火分隔。但目前使用的多数防火密封胶附着力和弹性差，在贯穿物受外界因素影响如温度变化、振动等易使防火密封胶与贯穿物或开口壁间形成缝隙，造成防火失效而需要重新换防火密封胶，费用较大。如03117403.5号中国专利，公开了一种“中性硅酮防火密封胶及其制造方法”，其阻燃硅酮密封胶尽管能阻燃，但遇火时膨胀性较差，如有贯穿件或开口壁间形成缝隙时，防火阻燃密封效果不好，生产成本较高。
发明内容
本发明的目的在于提供一种防火弹性密封胶及其制备方法。
本发明是这样实现的：
一种防火弹性密封胶，包括基料和辅料，其特征在于：所述弹性密封胶的基料包括：丙烯酸酯乳液、乙二醇、乳化剂和分散剂；辅料包括：阻燃剂、填料、着色剂、偶联剂、增稠剂和增塑剂，其配方组份按重量份数计为：
丙烯酸酯弹性乳液：100份
乙二醇：0.5～1.5份
乳化剂(OP-10壬基酚聚氧乙烯醚)：0.8～2份
分散剂(DA-01型丙烯酸钠与丙酰胺共聚物)：0.8～2份
增塑剂(邻苯二甲酸二甲酯或邻苯二甲酸二丁酯)：3～5份
阻燃剂：40～50份(其中阻燃氢氧化铝27～30份、阻燃硼酸锌8～10份、三聚氰胺氰尿酸盐5～10份)
着色剂(石墨粉)：0.3～1份
增稠剂：3～7份(气相沉积SiO21.5份、碱溶胀型改性丙烯酸类增稠剂TR-935 1.5～5.5份)
偶联剂(KH550)：3～5份
填料：40～60份(其中碳酸钙30～45份、钛白粉10～15份)
附加技术特征是：所述的增塑剂为邻苯二甲酸二甲酯或邻苯二甲酸二丁酯任一种。
防火弹性密封胶的制备方法，其特征在于：所述的制备方法如以下步骤：
(1)按所述配方组份，取丙烯酸酯弹性乳液100份，乙二醇0.5～1.5份、乳化剂0.8～2份、分散剂0.8～2份加入搅拌器中，在15～30℃下搅拌5min；
(2)按所述配方组份，在搅拌器中加入阻燃剂40～50份、无机填料40～60份、着色剂0.3～1份，搅拌30min后加入偶联剂3～5份，继续搅拌30min后加入增塑剂3～5份、增稠剂3～7份；
(3)利用搅拌发热及辅助加热系统缓慢升温至50℃，开真空调节至-0.085±0.002MPa继续升温至55±2℃，保持温度和真空度，搅拌2h即可。
本发明的效果在于：采用本发明的方法制成防火弹性密封胶，在使用过程中为室温下自然固化、无有机溶剂挥发，固化后附着力强、弹性好、密封性好、耐侯性好、能保持接缝的长久密封，其防火指标均达到GA161-1997《防火封堵材料的性能要求和实验方法》的技术要求。
具体实施方式
本发明的防火弹性密封胶由基料和辅料组成；基料是丙烯酸酯乳液、乙二醇、乳化剂、分散剂；辅料是阻燃剂、无机填料、着色剂、偶联剂、增稠剂、增塑剂。其配方组份按重量份数计为：
丙烯酸酯弹性乳液：100份。
乙二醇：0.5～1.5份
乳化剂：0.8～2份
分散剂：0.8～2份
增塑剂：3～5份(邻苯二甲酸二甲酯、邻苯二甲酸二丁酯)
阻燃剂：40～50份(其中阻燃氢氧化铝27～30份、阻燃硼酸锌8～10份、三聚氰胺氰尿酸盐5～10份)
着色剂：0.3～1份
增稠剂：3～7份(其中SiO21.5份、TR-935 1.5～5.5份)
偶联剂：3～5份
填料：40～60份(其中碳酸钙30～45份，钛白粉10～15份)
本发明的防火弹性密封胶的制备方法如下：
(1)按所述配方组份，取丙烯酸酯弹性乳液100份，乙二醇0.5～1.5份、乳化剂0.8～2份、分散剂0.8～2份加入搅拌器中，在15～30℃下搅拌5min；
(2)按所述配方组份，在搅拌器中加入阻燃剂40～50份、无机填料40～60份、着色剂0.3～1份，搅拌30min后加入偶联剂3～5份，继续搅拌30min后加入增塑剂3～5份、增稠剂3～7份；
(3)利用搅拌发热及辅助加热系统缓慢升温至50℃，开真空调节至-0.085±0.002MPa继续升温至55℃±2℃，保持温度和真空度，搅拌2h即可。
下面结合实施例对本发明进行详细描述：
实施例1
(1)取丙烯酸酯弹性乳液100份，乙二醇0.5份、OP-10乳化剂0.8份、DA-01分散剂0.8份加入混合器中，在15℃下搅拌5min；
(2)在搅拌器中加入阻燃剂阻燃氢氧化铝27份、硼酸锌8份、三聚氰胺氰尿酸盐5份，无机填料碳酸钙30份、钛白粉10份，着色剂碳黑0.3份，搅拌30min后加入KH550偶联剂3份，继续搅拌30min后加入增塑剂邻苯二甲酸二丁酯3份，增稠剂SiO2 1.5份和TR-935 1.5份；
(3)利用搅拌发热及辅助加热系统缓慢升温至50℃，开真空调节至-0.085±0.002MPa继续升温至55℃±2℃，保持温度和真空度，搅拌2h即可。
实施例2
(1)取丙烯酸酯弹性乳液100份，乙二醇1.5份、OP-10乳化剂2份、DA-01分散剂2份加入混合器中，在20℃下搅拌5min；
(2)在搅拌器中加入阻燃剂阻燃氢氧化铝30份、硼酸锌10份、三聚氰胺氰尿酸盐10份，无机填料碳酸钙45份、钛白粉15份，着色剂碳黑1份，搅拌30min后加入KH550偶联剂5份，继续搅拌30min后加入增塑剂邻苯二甲酸二丁酯5份，增稠剂SiO2 1.5份和TR-935 5.5份；
(3)同实施例1。
实施例3
(1)取丙烯酸酯弹性乳液100份，乙二醇0.8份、OP-10 1份、DA-01 1.2份加入混合器中，在25℃下搅拌5min；
(2)在搅拌器中加入阻燃剂阻燃氢氧化铝29份、硼酸锌9份、三聚氰胺氰尿酸盐8份，无机填料碳酸钙42份、钛白粉12份，着色剂碳黑0.7份，搅拌30min后加入KH550偶联剂4份，继续搅拌30min后加入邻苯二甲酸二甲酯4份，增稠剂SiO2 1.5份、TR-935 3.5份；
(3)同实施例1。
实施例4
(1)取丙烯酸酯弹性乳液100份，乙二醇1份、OP-10 1.5份、DA-01 0.8份加入混合器中，在30℃下搅拌5min；
(2)在搅拌器中加入阻燃剂：阻燃氢氧化铝28份、硼酸锌10份、三聚氰胺氰尿酸盐(MCA)7份，无机填料碳酸钙38份、钛白粉13份，着色剂碳黑0.8份，搅拌30min后加入KH550偶联剂3.5份，继续搅拌30min后加入邻苯二甲酸二甲酯3.5份，增稠剂SiO2 1.5份、TR-935 2.5份。
(3)同实施例1。

Claims (2)

1.一种防火弹性密封胶，包括基料和辅料，其特征在于：所述弹性密封胶的基料包括：丙烯酸酯乳液、乙二醇、乳化剂和分散剂；辅料包括：阻燃剂、填料、着色剂、偶联剂、增稠剂和增塑剂，其配方组份按重量份数计为：
丙烯酸酯弹性乳液：100份
乙二醇：0.5～1.5份；
乳化剂：OP-10壬基酚聚氧乙烯醚0.8～2份；
分散剂：DA-01型丙烯酸钠与丙酰胺共聚物0.8～2份；
增塑剂：邻苯二甲酸二甲酯或邻苯二甲酸二丁酯3～5份；
阻燃剂：阻燃氢氧化铝27～30份、阻燃硼酸锌8～10份、三聚氰胺氰尿酸盐5～10份，总计40～50份；
着色剂：石墨粉0.3～1份
增稠剂：气相沉积SiO21.5份、碱溶胀型改性丙烯酸类增稠剂TR-9351.5～5.5份，总计3～7份；
偶联剂：KH550  3～5份；
填料：碳酸钙30～45份、钛白粉10～15份，总计40～60份。
2.按照权利要求1所述的防火弹性密封胶的制备方法，其特征在于：所述的制备方法如以下步骤：
(1)按所述配方组份，取丙烯酸酯弹性乳液100份，乙二醇0.5～1.5份、乳化剂0.8～2份、分散剂0.8～2份加入搅拌器中，在15℃～30℃下搅拌5min；
(2)按所述配方组份，在搅拌器中加入阻燃剂40～50份、无机填料40～60份、着色剂0.3～1份，搅拌30min后加入偶联剂3～5份，继续搅拌30min后加入增塑剂3～5份、增稠剂3～7份；
(3)利用搅拌发热及辅助加热系统缓慢升温至50℃，开真空调节至-0.085±0.002MPa继续升温至55±2℃，保持温度和真空度，搅拌2h即可。
CN200810046522XA 2008-11-11 2008-11-11 一种防火弹性密封胶及其制备方法 Active CN101397488B (zh)