CN101381205A - 一种彩色玻璃马赛克的加工方法 - Google Patents
一种彩色玻璃马赛克的加工方法 Download PDFInfo
- Publication number
- CN101381205A CN101381205A CNA2007100301282A CN200710030128A CN101381205A CN 101381205 A CN101381205 A CN 101381205A CN A2007100301282 A CNA2007100301282 A CN A2007100301282A CN 200710030128 A CN200710030128 A CN 200710030128A CN 101381205 A CN101381205 A CN 101381205A
- Authority
- CN
- China
- Prior art keywords
- glass mosaic
- film
- minutes
- mosaic
- glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种彩色玻璃马赛克的加工方法，其加工步骤如下：(1)将玻璃马赛克表面清洁，用棉布清洁水将污汁擦掉烘干；(2)把清洁后的玻璃马赛克放入低真空度为(3PA至－2P)，工作电压为450至600V的真空炉内镀钛膜或氧氮化钛膜，镀钛膜和氧氮化钛膜的电流为8至12A，工作时间为磁控溅射1－10分钟，多弧溅射2－4分钟；(3)将镀钛膜玻璃马赛克放进窖炉火烧，火烧温度为450至950摄氏度，火烧工作时间30至90分钟。采用本发明加工方加工出的玻璃马赛克不但色泽多样且热稳定性好，化学稳定性好，具备耐酸耐碱性，增强玻璃硬度，耐磨性强，在不同光照渐变成幻彩。
Description
技术领域:
本发明涉及一种彩色玻璃马赛克的加工方法。
背景技术
专利号为200520053475.3的实用新型公开了一种二合一金属玛赛克瓷块，该玛赛克由金属层和陶瓷层组成，表层为金属层，底层为陶瓷层，它们之间相互固接在一起；本实用新型由于在表层采用了金属层，在整个地板上使用时，就显得较为辉煌，如果金属是采用钛或其他具有对人体有益的金属时，更具有治病作用等。
专利号为200520053472.X的实用新型公开了一种三合一金属玻璃玛赛克，该玛赛克由金属层、玻璃层和陶瓷层组成，表层为金属层，底层为陶瓷层，中间层为玻璃层，它们之间相互固接在一起；由于本实用新型在表层采用了金属层，在整个地板上使用时，就显得较为辉煌，如果金属是采用钛或其他具有对人体有益的金属时，更具有治病作用等。
专利号为85101975的发明专利公开一种生产彩色玻璃玛赛克的新方法--烧结法，是以废旧玻璃为原料，并对其分类洗涤、破碎、筛分至要求的粒度后，配加适量的着色剂、粘结剂和水，经混匀后，在模具中压制成型，然后中温烧结玻化成彩色玻璃玛赛克.用该方法生产出来的产品，成本低、抗压强度高、尺寸精确、外形规整、品种齐全、拼装构形美观、大方、城乡都可使用该方法生产彩色玻璃玛赛克.这种产品是现代高级建筑物装饰及大型艺术镶嵌壁画的理想材料。
但是，以上玻璃马赛克色彩单调，不丰富，耐酸耐碱腐性性能差，硬度也不够，耐磨性不强。
发明内容
本发明要解决的技术问题是提供彩色玻璃马赛克的加工方法，采用此方法加工出的彩色玻璃马赛克，不但色泽多样且具备耐酸耐碱腐性，增强玻璃硬度，耐磨性强，在不同光照渐变成幻彩。
本发明的技术解决方案是，一种彩色玻璃马赛克的加工方法，其加工步骤如下:
(1)将玻璃马赛克表面清洁，用棉布清洁水将污汁擦掉烘干；
(2)把清洁后的玻璃马赛克放入低真空度为(3PA至-2P)，工作电压为450至600V的真空炉内镀钛膜或氧氮化钛膜，镀钛膜和氧氮化钛膜的电流为8至12A，工作时间为磁控溅射1-10分钟，多弧溅射2-4分钟；
(3)将镀钛膜玻璃马赛克放进窖炉火烧，火烧温度为450至950摄氏度，火烧工作时间30至90分钟。
采用本发明加工方加工出的玻璃马赛克不但色泽多样且热稳定性好，化学稳定性好，具备耐酸耐碱性，增强玻璃硬度，耐磨性强，在不同光照渐变成幻彩。
具体实施方式
下面结合实施例及附图对本发明进一步说明，本发明包括以下实施例，但不局限于以下实施例:
实施例一:
(1)将玻璃马赛克表面清洁，用棉布清洁水将污汁擦掉烘干；
(2)把清洁后的玻璃马赛克放入真空度为-2PA，工作电压为450V的真空炉内镀钛膜，镀钛膜的电流为8A，工作时间为磁控溅射1分钟，多弧溅射4分钟；
(3)将镀钛膜玻璃马赛克放进窖炉火烧，火烧温度为450摄氏度，火烧工作时间90分钟。
实施例二:
(1)将玻璃马赛克表面清洁，用棉布清洁水将污汁擦掉烘干；
(2)把清洁后的玻璃马赛克放入真空度为-2PA，工作电压为600V的真空炉内镀氧氮化钛膜，镀氧氮化钛膜的电流12A，工作时间为磁控溅射10分钟，多弧溅射2分钟；
(3)将镀钛膜玻璃马赛克放进窖炉火烧，火烧温度为950摄氏度，火烧工作时间60分钟。
实施例三:
(1)将玻璃马赛克表面清洁，用棉布清洁水将污汁擦掉烘干；
(2)把清洁后的玻璃马赛克放入真空度为-1PA，工作电压为500V的真空炉内镀钛膜，镀钛膜的电流为10A，工作时间为磁控溅射5分钟，多弧溅射3分钟；
(3)将镀钛膜玻璃马赛克放进窖炉火烧，火烧温度为800摄氏度，火烧工作时间90分钟。
实施例四:
(1)将玻璃马赛克表面清洁，用棉布清洁水将污汁擦掉烘干；
(2)把清洁后的玻璃马赛克放入真空度为3PA，工作电压为450V的真空炉内镀氧氮化钛膜，镀氧氮化钛膜的电流为8A，工作时间为磁控溅射8分钟，多弧溅射3分钟；
(3)将镀钛膜玻璃马赛克放进窖炉火烧，火烧温度为600摄氏度，火烧工作时间30分钟。
Claims (1)
1、一种彩色玻璃马赛克的加工方法，其特征在于:
(1)将玻璃马赛克表面清洁，用棉布清洁水将污汁擦掉烘干；
(2)把清洁后的玻璃马赛克放入低真空度为(3PA至-2P)，工作电压为450至600V的真空炉内镀钛膜或氧氮化钛膜，镀钛膜和氧氮化钛膜的电流为8至12A，工作时间为磁控溅射1-10分钟，多弧溅射2-4分钟；
(3)将镀钛膜玻璃马赛克放进窖炉火烧，火烧温度为450至950摄氏度，火烧工作时间30至90分钟。