CN101362382B - 回收ptfe挤压辅助剂的方法 - Google Patents
回收ptfe挤压辅助剂的方法 Download PDFInfo
- Publication number
- CN101362382B CN101362382B CN2008101987994A CN200810198799A CN101362382B CN 101362382 B CN101362382 B CN 101362382B CN 2008101987994 A CN2008101987994 A CN 2008101987994A CN 200810198799 A CN200810198799 A CN 200810198799A CN 101362382 B CN101362382 B CN 101362382B
- Authority
- CN
- China
- Prior art keywords
- ptfe
- confined space
- extruding
- drying plant
- mist
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种回收PTFE挤压辅助剂的方法，该方法是在相对密闭空间内将PTFE半成品的两端分别置于放卷机和收卷机上，使放卷机和收卷机之间的PTFE半成品依次经过烘干设备，将相对密闭空间外空气用送风机送入相对密闭空间内，使相对密闭空间内的压力高于烘干设备内混合气体压力，防止烘干设备内混合气体溢至相对密闭空间内，将位于烘干设备内含有挤压辅助剂的混合气体通过与烘干设备连接的引流管逼出相对密闭空间外，使通过引流管的混合气体经过冷凝装置，回收其中所有的挤压辅助剂。本发明可回收PTFE制品生产中的挤压辅助剂，以保护大气环境，回收利用挤压辅助剂，降低聚四氟乙烯膜的生产成本，并且工艺简单，易操作。
Description
技术领域
本发明涉及一种回收PTFE挤压辅助剂的方法。
背景技术
PTFE制品，即聚四氟乙烯制品的生产是将PTFE原料过筛后选取PTFE细粉末，在PTFE细粉末中加入挤压辅助搅和成有机溶胶，再将有机溶胶通过预压、挤压等工艺挤压成PTFE半成品，再依成品的种类决定后制程的加工方式，如将PTFE半成品可通过压延成型可制成成品如未烧结胶带、生料带、高拉力线、过滤膜、膨胀带、透气膜。另外一种将PTFE半成品直接与电线素材一起挤出或单独挤出经过烘箱，将其高温干燥使挤压辅助剂挥发，再进行烧结即可制成成品如绝缘电线、细管、细棒等等，如附图1所示。在传统的通过烘干工艺制备聚四氟乙烯制品的过程中，挥发后的挤压辅助剂通常是直接向大气中排放的，或是利用抽风机抽取再冷凝回收，效果不佳。这不仅会造成环境污染，同时也造成了挤压辅助剂的浪费，增加了聚四氟乙烯制品的生产成本。
发明内容
为了克服现有技术的不足，本发明提供一种回收聚四氟乙烯制品生产中的挤压辅助剂的方法，以保护大气环境，回收利用挤压辅助剂，降低聚四氟乙烯膜的生产成本。
本发明解决其技术问题所采用的技术方案是：
回收PTFE挤压辅助剂的方法，其特征在于该方法是在相对密闭空间内将挤出成型的PTFE半成品的两端分别置于放卷机和收卷机上，使放卷机和收卷机之间的PTFE半成品依次经过烘干设备，并将相对密闭空间外的空气利用送风机送入相对密闭空间内，以使相对密闭空间内的压力高于烘干设备内混合气体的压力，以防止烘干设备内的混合气体溢至相对密闭空间内，将位于相对密闭空间内的烘干设备内含有蒸发的挤压辅助剂的混合气体通过与烘干设备连接的引流管全部逼出相对密闭空间外，并使通过引流管的混合气体经过冷凝装置，以回收其中所有的挤压辅助剂。
本发明的有益效果是：通过本发明可回收聚四氟乙烯膜生产中的挤压辅助剂，以保护大气环境，回收利用挤压辅助剂，降低聚四氟乙烯膜的生产成本，并且本发明工艺简单，易操作。
附图说明
下面结合附图和实施例对本发明进一步说明。
图1是PTFE制品的工艺流程图；
图2、图3是本发明回收挤压辅助剂的平面布置图。
具体实施方式
如图2、图3所示，本发明公开的回收PTFE挤压辅助剂的方法，是在相对密闭的空间8内将挤出成型的PTFE半成品的两端分别置于放卷机1和收卷机2上，使放卷机1和收卷机2之间的PTFE半成品依次经过烘干设备3，将PTFE半成品烘干及纵向拉伸使挤压辅助剂挥发，并使烘干设备3内含有蒸发的挤压机辅助剂的混合气体通过与烘干设备连接的引流管4全部逼出室外，并使通过引流管4的混合气体经过冷凝装置5，以回收其中所有的挤压辅助剂，在引流管4上装有抽风机6，以达到辅助引流的效果。
在干燥回收的同时通过环保空调7等送风装置向密闭空间内输送新鲜空气，以使相对密闭空间内的压力高于烘干设备3内混合气体的压力，以防止烘干设备3内的混合气体溢至相对密闭空间内。
烘干设备3内的干燥温度和干燥速度可根据挤压辅助剂的种类及挥发长度来决定。如选用航空煤油作为挤压辅助剂，干燥温度可设定为200℃。并且烘箱应有足够的排风能力，以保证挥发物的排放。
本发明采用的冷凝方式可采用水冷凝等。
PTFE半成品可采用常规的方法制备，如：将PTFE原料过筛后取PTFE细粉末，在PTFE细粉末中加入作为挤压辅助剂的溶剂油，如航空煤油ISOP.M等搅和成有机溶胶，溶剂油的添加比例可根据工艺条件而定，如：使用的挤出缸内径为100mm，挤出口模内径为11mm，使用型号为F106的PTFE为原料，ISOPM为挤压辅助剂时，可选用的添加比例为每1kg PTFE中加入240～250克挤压辅助剂，再将有机溶胶通过预压、挤压等工艺挤压成PTFE半成品，接着经压延机压延、收卷成带状，再接下来经放卷、烘干、纵向拉伸、收卷、辅助剂收集等工作。如附图二所示。这时室外压力为100.31Kpa，室内压力为100.35Kpa，辅助剂则源源不断地冷凝滴入收集器，从而达到本发明的效果。
Claims (2)
1.回收PTFE挤压辅助剂的方法，其特征在于该方法是在相对密闭空间内将挤出成型的PTFE半成品的两端分别置于放卷机和收卷机上，使放卷机和收卷机之间的PTFE半成品依次经过烘干设备，并将相对密闭空间外的空气利用送风机送入相对密闭空间内，以使相对密闭空间内的压力高于烘于设备内混合气体的压力，以防止烘干设备内的混合气体溢至相对密闭空间内，将位于相对密闭空间内的烘干设备内含有蒸发的挤压辅助剂的混合气体通过与烘干设备连接的引流管全部逼出相对密闭空间外，并使通过引流管的混合气体经过冷凝装置，以回收其中所有的挤压辅助剂。
2.根据权利要求1所述的回收PTFE挤压辅助剂的方法，其特征在于在引流管路加设抽风机，达到辅助引流的效果。