CN101358105A - Synthesis of artificial marble lacquer - Google Patents
Synthesis of artificial marble lacquer Download PDFInfo
- Publication number
- CN101358105A CN101358105A CNA2007101434667A CN200710143466A CN101358105A CN 101358105 A CN101358105 A CN 101358105A CN A2007101434667 A CNA2007101434667 A CN A2007101434667A CN 200710143466 A CN200710143466 A CN 200710143466A CN 101358105 A CN101358105 A CN 101358105A
- Authority
- CN
- China
- Prior art keywords
- marble lacquer
- lacquer
- imitation marble
- synthesis
- above ratio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a composite imitation marble lacquer. The natural stone wall decoration material has the defects of large usage, high construction difficulty, poor safety, large color variation, monotone colors, high cost, etc. The composite imitation marble lacquer can replace the natural stone wall decoration material to resolve the defects. The composite imitation marble lacquer is mainly prepared with the following materials: colored sand, silicone-acrylate emulsion, plasma water, cellulose, organic amine, ethylene glycol, multi-functional assistant, defoamer, mildew preventive and filming assistant. The composite imitation marble lacquer has the following advantages: natural resources are saved, and the cost is low; the colors of the natural colored sand cannot easily be faded, moreover, the colors are diversified, the color variation is little, and the composite imitation marble lacquer is applicable to the decoration of the outer walls of buildings with various building styles and ethnical styles and has a natural and noble decoration effect and a high decoration grade; the composite imitation marble lacquer can seep into various basal surfaces, firmly adhere to the outer walls and resist cracking, and after being soaked in water for thirty days, the composite imitation marble lacquer does not turn into white and is not flaked; construction and filming cannot be affected by low-temperature and humid climates; as dense, transparent finish, the composite imitation marble lacquer can extremely resist stain, and the surface can be washed.
Description
Technical field
The present invention relates to the building materials paint field, relate in particular to a kind of synthesis of artificial marble lacquer that is used for decoration of exterior wall.
Background technology
Lithotome curtain wall decoration material is the external wall decorative material that grade is arranged by people's approval generally, its output value accounts for more than 20% of the material of construction gross output value, present domestic every year, nearly stone material more than 100,000 cubes was used for curtain wall decoration, consumption occupies first of the world, but stone material is non-renewable natural resource, excessively use and to destroy ecotope, with " the industry of current state key encourage growth, product and technology catalogue " be not inconsistent middle " promotion meets the strategy of sustainable development energetically; help economizing on resources and improving the ecological environment " that proposes, and the aberration of natural marble is big, from great, exist consumption big as external wall decorative material, difficulty of construction is big, poor stability, heterochromia is big and dull, defectives such as cost height.
Summary of the invention
The purpose of this invention is to provide a kind of synthesis of artificial marble lacquer that saving natural resource, color are various, cost is low, construction is simple and safe that is used for decoration of exterior wall.
The technical scheme that realizes above-mentioned purpose is:
Synthesis of artificial marble lacquer is mainly by raw material: color sand, organosilicon crylic acid latex, plasma water, Mierocrystalline cellulose, organic amine, ethylene glycol, multifunctional assistant, defoamer, mould inhibitor, film coalescence aid are made.
The weight proportion of above-mentioned raw materials is:
71.1 parts in color sand
15 parts of organosilicon crylic acid latexs
12 parts of plasma waters
0.2 part of Mierocrystalline cellulose
0.1 part of organic amine
0.3 part of ethylene glycol
0.4 part of multifunctional assistant
0.05 part of defoamer
0.05 part of mould inhibitor
0.8 part of film coalescence aid
The step for preparing synthesis of artificial marble lacquer by the above-mentioned raw materials proportioning is as follows:
1. the plasma water that will be got according to the above ratio adds stirrer, and starts stirrer; 2. add the Mierocrystalline cellulose of being got according to the above ratio, stirring at low speed to Mierocrystalline cellulose all dissolves; 3. add the multifunctional assistant of being got according to the above ratio, stirring at low speed 20 minutes; 4. add ethylene glycol, film coalescence aid, the organosilicon crylic acid latex of being got according to the above ratio successively, disperse to stir 30 minutes; 5. add defoamer, mould inhibitor, the organic amine of being got according to the above ratio more successively, disperse to stir 10 minutes; 6. at the color sand of determining to add according to the above ratio under still, the situation that is uniformly dispersed and being got, middling speed stirs and promptly made synthesis of artificial marble lacquer of the present invention in 30 minutes.
Raw material properties, the function of synthesis of artificial marble lacquer of the present invention are as follows:
Organosilicon crylic acid latex is the water-based emulsion that is formed by multiple esters of acrylic acid and organosilane monomer graft copolymerization, nontoxicity, non-corrosiveness, does not burn, and belongs to the aqueous substance non-dangerous goods; Film forming has higher gloss, preferable salt fog resistance, alkali resistance, preservative property, extremely strong sticking power, water-tolerant, weather-proof excellence.Can be directly used in the impregnating material of metallic substance, the finish paint of metallic paint, zinc rich paint, waterproof paint, wood lacquer and various coating, high-grade outer wall paint.
Mierocrystalline cellulose, molecular formula are (C
6H
10O
5) n, according to the difference of degree of esterification, nitrogen content about 11% be called collodion, be make spray paint, the raw material of film, zylonite.
Organic amine is that a class is the general name of the extraction agent of extraction functional group with the nitrogen-atoms, comprises primary amine RNH
2, secondary amine R
2NH, tertiary amine R
3N and quaternary ammonium salt R
4Four kinds of N+X-etc.
Ethylene glycol, molecular formula are HOCH
2CH
2OH, colourless clear feelings thick liquid, it is sweet to distinguish the flavor of.Main as the raw material of producing trevira (terylene), and be used for the production of other vibrin, unsaturated polyester resin, in addition, also be used to make tensio-active agent, softening agent, dyeing and finishing auxiliaries, siccative, softening agent, weaving and printing and dyeing with solvent etc.
Multifunctional assistant, the lower molecular weight organic amine compound, colourless or light yellow transparent liquid, it is a kind of multifunctional assistant as water-based system, its tool reduces foam, wetting, the effect that helps to disperse and regulate pH value in aqueous coating system, have extremely low volatility, can keep the stable of system pH value and viscosity chronically, the corrosion resistance of the package stability of raising product and pail pack, jar.
Defoamer can prevent that lubricating oil product from use producing foamy one class material.
Mould inhibitor can prevent that microorganism from causing mouldy medicament.
Film coalescence aid is to promote macromolecular compound plastic flow and recoverable deformation, improves coalescent performance, can be at film forming material in the construction temperature scope extensively.
The range of application of synthesis of artificial marble lacquer of the present invention is as follows:
Be suitable for basal plane: concrete, mortar, masonry, mosaic, ceramic tile face, plank, metal covering, the decoration of exterior wall of luxurious buildings such as bank, hotel, commercial building, villa reaches EPS, XPS, PC warming plate face.
Operation instruction:
1, should adopt and roll, spray, smear constructional method; 2, substrate surface require cleaning, firmly, smooth substantially, alkaline PH＜10, metope water ratio＜10%; 3, rise powder, alkalescence is heavier or the crack metope should use Benny's bottom closing paint earlier; 4, by design requirements, with the material lattice metope of drawing squares; 5, the main material of suggestion coating, the about 2.5kg/m of glue spread
2, two aspects lacquer, the about 5kg/m of glue spread
2
The present invention has following beneficial effect:
1. save natural resource, cost is low;
3. natural colour sand, the variation of not fugitive color, and color, aberration are little, are applicable to the decoration of exterior wall of different architectural styles, nationality amorous feedings building, and decorative effect is natural, luxurious, decorates of high grade.
4. permeable various basal planes adhere to firmly, and opposing be full of cracks is soaked after 30 days in water, do not return whitely, do not peel off.
5. the construction film forming is unaffected down for low temperature, humid climate.
6. be fine and close clear finish, extremely anti-contamination, surface capable of washing.
Embodiment
Now technical scheme of the present invention is described further by following examples.
1. get 12 parts of plasma waters, 0.2 part of Mierocrystalline cellulose, 0.1 part of organic amine, 0.3 part of ethylene glycol, 0.4 part of multifunctional assistant, 15 parts of organosilicon crylic acid latexs, 0.05 part of defoamer, 0.05 part of mould inhibitor, 0.8 part of film coalescence aid, 71.1 parts of color sand in proportion, 2. the plasma water of being got is added stirrer, and start stirrer; 3. add the Mierocrystalline cellulose got, stirring at low speed 20 minutes to Mierocrystalline cellulose all dissolves; 4. add the multifunctional assistant of being got, stirring at low speed 20 minutes; 5. adding ethylene glycol, film coalescence aid, the organosilicon crylic acid latex got successively disperses to stir 30 minutes; 6. adding defoamer, mould inhibitor, the organic amine got again successively disperses to stir 10 minutes; 7. determining to add color sand under still, the situation that is uniformly dispersed, middling speed stirs and promptly made the described synthesis of artificial marble lacquer of present embodiment in 30 minutes.
Claims (3)
1. synthesis of artificial marble lacquer, it is characterized in that: mainly by raw material: color sand, organosilicon crylic acid latex, plasma water, Mierocrystalline cellulose, organic amine, ethylene glycol, multifunctional assistant, defoamer, mould inhibitor, film coalescence aid are made.
2, synthesis of artificial marble lacquer according to claim 1 is characterized in that: be made up of the following weight proportion raw material:
71.1 parts in color sand
15 parts of organosilicon crylic acid latexs
12 parts of plasma waters
0.2 part of Mierocrystalline cellulose
0.1 part of organic amine
0.3 part of ethylene glycol
0.4 part of multifunctional assistant
0.05 part of defoamer
0.05 part of mould inhibitor
0.8 part of film coalescence aid
3, synthesis of artificial marble lacquer according to claim 1 and 2 is characterized in that its preparation process is as follows:
1. the plasma water that will be got according to the above ratio adds stirrer, and starts stirrer; 2. add the Mierocrystalline cellulose of being got according to the above ratio, stirring at low speed to Mierocrystalline cellulose all dissolves; 3. add the multifunctional assistant of being got according to the above ratio, stirring at low speed 20 minutes; 4. add ethylene glycol, film coalescence aid, the organosilicon crylic acid latex of being got according to the above ratio successively, disperse to stir 30 minutes; 5. add defoamer, mould inhibitor, the organic amine of being got according to the above ratio more successively, disperse to stir 10 minutes; 6. at the color sand of determining to add according to the above ratio under still, the situation that is uniformly dispersed and being got, middling speed stirs and promptly made synthesis of artificial marble lacquer of the present invention in 30 minutes.