CN102408203A - Preparation method of coating type natural color sand flexible face brick and construction technology thereof - Google Patents
Preparation method of coating type natural color sand flexible face brick and construction technology thereof Download PDFInfo
- Publication number
- CN102408203A CN102408203A CN201110237917XA CN201110237917A CN102408203A CN 102408203 A CN102408203 A CN 102408203A CN 201110237917X A CN201110237917X A CN 201110237917XA CN 201110237917 A CN201110237917 A CN 201110237917A CN 102408203 A CN102408203 A CN 102408203A
- Authority
- CN
- China
- Prior art keywords
- natural colour
- face brick
- colour sand
- flexible face
- coated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of coating type natural color sand flexible face brick and a construction technology thereof, which belong to the field of building material. The face brick is prepared by mixing the following constituents in percentage by weight: 12-16% of water, 0.1-0.2% of cellulose, 15-22% of emulsion, 20-25% of 41-80 mesh natural color sand, 40-50% of 81-120 mesh natural color sand, 2-5% of 21-40 mesh natural color sand, 0.08-0.12% of PH regulator, 0.02-0.06% of defoaming agent, 0.8-1.2% of antifreezing agent, 0.1-1% of thickening agent and 0.02-0.1% of preservative. The invention has the advantages of better flexibility, energy saving, environment protection, stain resistance and coating durability of above 15 years, and is suitable for heat insulation finish coat out of outer wall.
Description
[technical field]
The present invention relates to the material in a kind of technical field of buildings, refer more particularly to a kind of batch and be coated with type natural colour sand system flexible face brick preparation method and construction technology thereof.
[background technology]
Along with the raising day by day of the continuous development, particularly living standards of the people of construction industry, people require more and more stricter to living environment, require also increasingly high to the heat preservation energy-saving of building.Safe, energy-conservation, insulation, comfortable, attractive in appearancely be the living environment that people pursued, so public building and residential building exterior wall all adopted external thermal insulation system,, the exterior wall finish layer has been had higher requirement in order to ensure the security of outer heat preservation system.Stone material is because of material price and the higher local interspersing that is mainly used in outer decoration of installation costs; Traditional tiles is fired mostly and is formed, and self is heavier, and the safety of buildings is brought hidden danger; Though common coating exterior wall latex paint price is honest and clean, be prone to stain, fade, work-ing life is short: market presses for a kind ofly can guarantee the outer heat preservation system security, can satisfy user preferences again and the novel finish coat of different face brick finishing effects is arranged.
Flexible face brick is as main base material with the natural sand of adopting; Is furnished with high molecular polymer; Again through the special decoration of exterior wall plane materiel that processes; Advantages such as flexible face brick rich color, thin thickness, light weight, flexible good, water proof anti-seepage, good endurance, construction letter make are used in the indoor and outdoor decorations of various buildingss, are particularly suitable for the decoration of exterior wall of the outer insulation of external wall.
At present, commonly utilize the scheme of true mineral varnish spraying as imitative brick finish coat on the market, this aspect has solved the substitution problem of imitative brick; But because the technology of its spraying, one side is had relatively high expectations to the workmen's, on the other hand; The loss of material waste is bigger, and the effect of spraying application is compared with face brick or bigger gap arranged, the easy dust of spraying effect; Not anti-contamination batch is coated with technology then to make the smooth dust of whole face to lack, and the good persistence of whole decorative effect is strong.
Therefore, the improvement of construction technology is extremely urgent.
[summary of the invention]
The technical issues that need to address of the present invention are to overcome the defective of prior art and product; Provide a kind of batch to be coated with type natural colour sand system flexible face brick preparation method and construction technology thereof; Having preferably, snappiness, energy-conserving and environment-protective, anti-contamination, coating endurance quality are suitable for the finish coat of external wall outer insulation more than 15 years.
For addressing the above problem, the present invention realizes through following technical scheme:
A kind of batch is coated with type natural colour sand system flexible face brick preparation method, is mixed by each component of following weight proportion: water 12%-16%, Mierocrystalline cellulose 0.1%-0.2%; Emulsion 15%-22%, 41-80 order natural colour sand 20%-25%, 81-120 order natural colour sand 40%-50%; The natural sand 2%-5% that adopts of 21-40 order, PH regulator 0.08%-0.12%, skimmer 0.02%-0.06%; Frostproofer 0.8%-1.2%, thickening material 0.1%-1%, sanitas 0.02%-0.1%.
Described water is edible pipeline water.
Described Mierocrystalline cellulose is a Natvosol.
Described emulsion is a pure acrylic acid fat polymerized emulsion.
Described 41-80 order natural colour sand, 81-120 order natural colour sand, the natural sand of adopting of 21-40 order are the occurring in nature natural colour sand.
Described PH regulator is the organic amine neutralizing agent, and model is AMP95.
Described skimmer is the HT-607 type.
Described frostproofer is a terepthaloyl moietie.
Described thickening material is a polyurethane associative thickener, and model is SN-612.
Described sanitas is Canadian promise moral C15.
Preparing method of the present invention is:
(1), presses column weight amount ratio and take by weighing raw material: water 12%-16%, Mierocrystalline cellulose 0.1%-0.2%, emulsion 15%-22%; 41-80 order natural colour sand 20%-25%, 81-120 order natural colour sand 40%-50%, the natural sand 2%-5% that adopts of 21-40 order; PH regulator 0.08%-0.12%, skimmer 0.02%-0.06%, frostproofer 0.8%-1.2%; Thickening material 0.1%-1%, sanitas 0.02%-0.1%:
(2), in stirrer, add following component: the skimmer of frostproofer, half weight, the above-mentioned water that takes by weighing, Mierocrystalline cellulose, emulsion, sanitas, stirring, adding natural colour sand, restir;
(3), add second half skimmer, PH regulator, stirring;
(4), add thickening material and regulate viscosity, stir, discharging gets final product.
The present invention discloses a kind of batch of construction technology that is coated with type natural colour sand system flexible face brick, construction technology comprises:
Dust, the greasy dirt on A, removing metope or outer heat preservation system surface, the planeness and the verticality of inspection metope are carried out levelling with leveling putty and are processed into putty layer, can reach construction required surface finish and verticality;
B, roller coat alkali resistant sealing jointing priming paint equably;
C, snap the line according to drawing requirement, paste continuous paper film or foam tape;
D, batch be coated with flexible face brick master material, full batch, with the foam tape equal height;
E, tear foam tape off:
F, polishing flexible face brick are repaired jointing priming paint;
G, last translucent cover finish paint.
Owing to adopted above technical scheme, compared with prior art, the present invention has following beneficial effect:
(1), all market purchasings at home of all raw materials, be main raw material with the occurring in nature natural colour sand, be equipped with pure-acrylic emulsion and various auxiliary agent is mixed and made into, so production cost is lower;
(2), the flexibility that adopted is coated with material can fully fit base material or lagging material, the characteristics of the plastic deformation that has make the extension that is coated with material reach synchronous consistent with contraction, have so just avoided the cracking of top coat, make coating have good water-repellancy:
(3), decorative cover used clear finish dustproof, infiltration, decorative cover had permanent keep a public place clean, anti-pollution timeliness, the coating weather resistance is suitable as the finish coat of external wall outer insulation more than 15 years very much;
(4), adopted and batch be coated with technology; Make the amount ratio spraying coating process that is coated with material reduce 30 percent, the use of foam tape makes coating can reach specified thickness again, need not large-scale preparation of construction; Only need simple floater just can be competent at, to workmen's also reduction greatly of requirement for restriction;
(5), greatly improved construction quality and speed, also the mass-producing construction for decorative cover provides condition and convenience, greatly reduces operating cost, reaches real environmental protection.
[description of drawings]
Fig. 1 is system component figure of the present invention:
Fig. 2 is the front view of construction body of wall of the present invention;
Fig. 3 is the sectional view of construction body of wall of the present invention.
Among Fig. 2,3: 1-metope or outer heat preservation system surface, 2-putty layer, 3-priming paint, 4-flexible face brick master material, the bright finishing paint of 5-, 6-paper film or foam tape.
[embodiment]
Below in conjunction with accompanying drawing and specific embodiment the present invention is further described:
A kind of batch is coated with type natural colour sand system flexible face brick preparation method, is mixed by each component of following weight proportion: water 12%-16%, Mierocrystalline cellulose 0.1%-0.2%; Emulsion 15%-22%, 41-80 order natural colour sand 20%-25%, 81-120 order natural colour sand 40%-50%; The natural sand 2%-5% that adopts of 21-40 order, PH regulator 0.08%-0.12%, skimmer 0.02%-0.06%; Frostproofer 0.8%-1.2%, thickening material 0.1%-1%, sanitas 0.02%-0.1%.
Described water is edible pipeline water.
Described Mierocrystalline cellulose is a Natvosol.
Described emulsion is a pure acrylic acid fat polymerized emulsion.
Described 41-80 order natural colour sand, 81-120 order natural colour sand, the natural sand of adopting of 21-40 order are the occurring in nature natural colour sand.
Described PH regulator is the organic amine neutralizing agent, and model is AMP95.
Described skimmer is the HT-607 type.
Described frostproofer is a terepthaloyl moietie.
Described thickening material is a polyurethane associative thickener, and model is SN-612.
Described sanitas is Canadian promise moral C15.
Preparing method of the present invention is:
(1), presses column weight amount ratio and take by weighing raw material: water 12%-16%, Mierocrystalline cellulose 01%-0.2%, emulsion 15%-22%; 41-80 order natural colour sand 20%-25%, 81-120 order natural colour sand 40%-50%, the natural sand 2%-5% that adopts of 21-40 order; PH regulator 0.08%-0.12%, skimmer 0.02%-0.06%, frostproofer 0.8%-1.2%; Thickening material 0.1%-1%, sanitas 0.02%-0.1%:
(2), in stirrer, add following component: the skimmer of frostproofer, half weight, the above-mentioned water that takes by weighing, Mierocrystalline cellulose, emulsion, sanitas, stirring, adding natural colour sand, restir;
(3), add second half skimmer, PH regulator, stirring;
(4), add thickening material and regulate viscosity, stir, discharging gets final product.
The present invention discloses a kind of batch of construction technology that is coated with type natural colour sand system flexible face brick, construction technology comprises:
Dust, the greasy dirt on A, removing metope or outer heat preservation system surface 1, the planeness and the verticality of inspection metope are carried out levelling with leveling putty and are processed into putty layer 2, can reach construction required surface finish and verticality:
B, roller coat alkali resistant sealing jointing priming paint 3 equably;
C, snap the line according to drawing requirement, paste continuous paper film or foam tape 6;
D, batch be coated with flexible face brick master material 4, full batch, with foam tape 6 equal height;
E, tear foam tape 6 off;
F, polishing flexible face brick are repaired jointing priming paint;
G, last translucent cover finish paint 5.
At last: above embodiment only in order to the explanation the present invention and and unrestricted technical scheme described in the invention; Therefore, although this specification sheets has carried out detailed explanation to the present invention with reference to each above-mentioned embodiment,, those of ordinary skill in the art should be appreciated that still and can make amendment or be equal to replacement the present invention; And all do not break away from the technical scheme and the improvement thereof of the spirit and scope of the present invention, and it all should be encompassed in the claim scope of the present invention.
Claims (11)
1. one kind batch is coated with type natural colour sand system flexible face brick preparation method, it is characterized in that: each the component flour mixed with adulterants by following weight proportion becomes: water 12%-16%, Mierocrystalline cellulose 0.1%-0.2%; Emulsion 15%-22%, 41-80 order natural colour sand 20%-25%, 81-120 order natural colour sand 40%-50%; The natural sand 2%-5% that adopts of 21-40 order, PH regulator 0.08%-0.12%, skimmer 0.02%-0.06%; Frostproofer 0.8%-1.2%, thickening material 0.1%-1%, sanitas 0.02%-0.1%.
2. a kind of batch according to claim 1 is coated with type natural colour sand system flexible face brick preparation method, and it is characterized in that: described Mierocrystalline cellulose is a Natvosol.
3. a kind of batch according to claim 1 is coated with type natural colour sand system flexible face brick preparation method, it is characterized in that: described emulsion is a pure acrylic acid fat polymerized emulsion.
4. a kind of batch according to claim 1 is coated with type natural colour sand system flexible face brick preparation method, it is characterized in that: described 41-80 order natural colour sand, 81-120 order natural colour sand, the natural sand of adopting of 21-40 order are the occurring in nature natural colour sand.
5. a kind of batch according to claim 1 is coated with type natural colour sand system flexible face brick preparation method, and it is characterized in that: described PH regulator is the organic amine neutralizing agent, and model is AMP95.
6. a kind of batch according to claim 1 is coated with type natural colour sand system flexible face brick preparation method, and it is characterized in that: described skimmer is the HT-607 type.
7. a kind of batch according to claim 1 is coated with type natural colour sand system flexible face brick preparation method, and it is characterized in that: described frostproofer is a terepthaloyl moietie.
8. a kind of batch according to claim 1 is coated with type natural colour sand system flexible face brick preparation method, and it is characterized in that: described thickening material is a polyurethane associative thickener, and model is SN-612.
9. a kind of batch according to claim 1 is coated with type natural colour sand system flexible face brick preparation method, it is characterized in that: described sanitas is Canadian promise moral C15.
10. a kind of batch according to claim 1 is coated with type natural colour sand system flexible face brick preparation method, and it is characterized in that: preparation method of the present invention is:
(1), presses column weight amount ratio and take by weighing raw material: water 12%-16%, Mierocrystalline cellulose 0.1%-0.2%, emulsion 15%-22%; 41-80 order natural colour sand 20%-25%, 81-120 order natural colour sand 40%-50%, the natural sand 2%-5% that adopts of 21-40 order; PH regulator 0.08%-0.12%, skimmer 0.02%-0.06%, frostproofer 0.8%-1.2%; Thickening material 0.1%-1%, sanitas 0.02%-0.1%;
(2), in stirrer, add following component: the skimmer of terepthaloyl moietie, half weight, the above-mentioned water that takes by weighing, Mierocrystalline cellulose, emulsion, frostproofer, sanitas, stirring, adding natural colour sand, restir;
(3), add second half skimmer, PH regulator, stirring;
(4), add thickening material and regulate viscosity, stir, discharging gets final product.
11. one kind batch of construction technology that is coated with type natural colour sand system flexible face brick, it is characterized in that: construction technology comprises:
Dust, the greasy dirt on A, removing metope or outer heat preservation system surface (1), the planeness and the verticality of inspection metope are carried out levelling with leveling putty and are processed into putty layer (2), can reach construction required surface finish and verticality;
B, roller coat alkali resistant sealing jointing priming paint (3) equably;
C, snap the line according to drawing requirement, paste continuous paper film or foam tape (6);
D, batch be coated with flexible face brick master material (4), full batch, same foam tape (6) equal height:
E, tear foam tape (6) off:
F, polishing flexible face brick are repaired jointing priming paint;
G, last translucent cover finish paint (5).