CN101337370B - 一种高密度荻草纤维板的制备方法 - Google Patents

一种高密度荻草纤维板的制备方法 Download PDF

Info

Publication number
CN101337370B
CN101337370B CN2008100190725A CN200810019072A CN101337370B CN 101337370 B CN101337370 B CN 101337370B CN 2008100190725 A CN2008100190725 A CN 2008100190725A CN 200810019072 A CN200810019072 A CN 200810019072A CN 101337370 B CN101337370 B CN 101337370B
Authority
CN
China
Prior art keywords
silver
high density
grass
fiber
fiber board
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2008100190725A
Other languages
English (en)
Other versions
CN101337370A (zh
Inventor
邓玉和
朱典想
王伟
朱捷
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanjing Forestry University
Original Assignee
Nanjing Forestry University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanjing Forestry University filed Critical Nanjing Forestry University
Priority to CN2008100190725A priority Critical patent/CN101337370B/zh
Publication of CN101337370A publication Critical patent/CN101337370A/zh
Application granted granted Critical
Publication of CN101337370B publication Critical patent/CN101337370B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明是涉及人造板领域的一项技术发明,它是采用辊压法生产薄型高密度荻草纤维板的制造方法。荻草植物纤维原料,经粉碎、蒸煮、纤维分离、施加脲醛树脂等胶粘剂和防水剂,在管道干燥机中使纤维的终含水率达到8-12%,铺装后的板坯,在辊压机中热压成厚度为2-10mm的高密度荻草纤维板。或荻草植物原料和木材,经粉碎和削片、纤维分离、干燥、铺装、预压后,在辊压机中制成高密度荻草/木材纤维板。本发明制造的高密度荻草纤维板生产工艺简单、成本低、强度高、制品的理化性能达到国家相关标准的要求。

Description

一种高密度荻草纤维板的制备方法
一、技术领域
本发明公开了一种利用辊压法生产薄型高密度荻草纤维板的制备方法。荻草经粉碎、蒸煮软化、纤维分离、纤维干燥、铺装、压辊热压,制成厚度范围为2.0-10mm的高密度荻草纤维板的方法。其主要技术特征为:利用脲醛树脂等胶粘剂采用压辊热压方式生产薄型高密度荻草纤维板。
二、背景技术
木材资源的短缺,迫使人们利用各种原料研究生产人造板,满足市场的需要和缓解木材资源的不足。利用禾本植物、采用不同的加工方式生产各种人造板是国内外关注的重点。荻草植物属于禾本科荻属(Triarrhena),分布广泛,属多年、群生植物,砍伐后来年生长更好,其产量高,能满足纤维板生产大批量的需求。荻草经分离后纤维形态好、得率高、采用压辊热压(辊压)法能生产出厚度薄、强度高、尺寸稳定性好的高密度荻草纤维板。其产品主要用于包装、地板、装修等领域,利用湖区丰富的荻草资源生产的薄型高密度荻草维板具广阔的应用前景。
三、发明内容
1.发明的目的
本发明的目的在于利用废弃的荻草资源,采用压辊热压方式生产薄型的高密度纤维板,提高荻草的利用价值和拓展新的产品;保护湖区的生态环境和生态平衡;充分利用荻草资源生产各种类型的纤维板。
2.技术方案
本发明涉及的是采用辊压法生产薄型的高密度荻草纤维板的方法,它的工艺步骤:
(1)粉碎机将荻草打碎,制成长度为30-90mm,宽度为1.2-3.5mm的杆状荻草;
(2)杆状荻草在180℃的预热蒸煮罐中蒸煮软化5-9分钟,由热磨机分离成荻草纤维;防水剂施加量为绝干纤维质量的1.0-1.5%;胶粘剂施加量10-14%;固化剂施加量0.6-1.0%;
(3)荻草纤维在管道干燥机内干燥,干燥温度为170-190℃,干燥后荻草纤维的终含水率为8-12%;
(4)真空机械或真空气流铺装机将荻草纤维铺装成规定厚度的板,铺装后的荻草纤维板由热压辊和加压辊压制成密度大于0.8g/cm3的高密度荻草纤维板;制成的高密度纤维板的厚度为2.0-10mm,热压辊面温度为150-200℃,热压时间为15-40S/mm,热压压力范围为2700-3500N/cm;
(5)热压后的高密度荻草纤维板在常温下经冷却、锯截工序制成薄型高密度荻草纤维板。
本发明的优点:制造方法简单,利用低价值的荻草生产高附加值的薄型高密度纤维板,产品性能稳定、强度变异性小、尺寸稳定。产品可以应用在包装、地板、建筑装修等行业。
四、具体实施方式
实施例1:
下面结合实例对本发明进行详细描述,但发明不限所给出的例子。
(1)粉碎后的荻草尺寸:长度为30-90mm,宽度为1.2-3.5mm;
(2)杆状荻草在180℃的蒸煮罐中蒸煮软化8分钟,然后分离成荻草纤维;防水剂施加量为绝干纤维质量的1.5%;胶粘剂施加量为绝干纤维质量的14%;固化剂施加量为固体胶质量的1.0%;
(3)干燥温度为170℃,干燥后荻草纤维的终含水率为11%;
(4)铺装后的荻草纤维板,由压辊压到密度0.85-0.95g/cm3,制成的高密度纤维板板厚度为6.0mm,热压辊面温度为180℃,热压时间为20S/mm,热压压力为2800N/cm,2950N/cm,3100N/cm;
(5)热压后的高密度纤维板材在常温下经冷却、锯截、存放48小时后,测定高密度荻草纤维板的性能。
(6)性能指标如下:
密度:      0.95g/cm3      0.90g/cm3      0.85g/cm3
内结合强度:1.62MPa        1.45MPa        1.45MPa
静曲强度:  35.9MPa        35.9MPa        35.7MPa
弹性模量:  5255MPa        4969MPa        4963MPa

Claims (1)

1.一种高密度荻草纤维板的制备方法,其特征是它的工艺步骤分:
(1)粉碎机将荻草打碎,制成长度为30-90mm,宽度为1.2-3.5mm的杆状荻草;
(2)杆状荻草在180℃蒸煮罐中蒸煮5-9分钟,热磨机将荻草分离成纤维;防水剂施加量为绝干纤维质量的1.0-1.5%;胶粘剂施加量为绝干纤维质量的10-14%;固化剂施加量为胶粘剂固体质量的0.6-1.0%;
(3)荻草纤维在管道干燥机内干燥,干燥温度为170-190℃,干燥后荻草纤维的终含水率为8-12%;
(4)真空机械或真空气流铺装机将荻草纤维铺装成规定厚度的板,铺装后的荻草纤维板由压辊热压制成密度为0.8g/cm3-0.95g/cm3的高密度荻草纤维板;高密度荻草纤维板的厚度为2.0-10mm,热压辊面温度为150-200℃,热压时间为15-40S/mm,热压压力范围为2700-3500N/cm;
(5)热压后的高密度纤维板在常温下经冷却、锯切工序制成薄型高密度荻草纤维板。 
CN2008100190725A 2008-01-11 2008-01-11 一种高密度荻草纤维板的制备方法 Expired - Fee Related CN101337370B (zh)