CN101319427A - 含有聚乳酸纤维的织物 - Google Patents

含有聚乳酸纤维的织物 Download PDF

Info

Publication number
CN101319427A
CN101319427A CNA200710023336XA CN200710023336A CN101319427A CN 101319427 A CN101319427 A CN 101319427A CN A200710023336X A CNA200710023336X A CN A200710023336XA CN 200710023336 A CN200710023336 A CN 200710023336A CN 101319427 A CN101319427 A CN 101319427A
Authority
CN
China
Prior art keywords
fabric
polylactic
acid fiber
precursor
intensity
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA200710023336XA
Other languages
English (en)
Other versions
CN101319427B (zh
Inventor
戴家欣
施泽顺
佐藤正幸
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Toray Industries Inc
Original Assignee
Toray Fibers and Textiles Research Laboratories China Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toray Fibers and Textiles Research Laboratories China Co Ltd filed Critical Toray Fibers and Textiles Research Laboratories China Co Ltd
Priority to CN200710023336XA priority Critical patent/CN101319427B/zh
Publication of CN101319427A publication Critical patent/CN101319427A/zh
Application granted granted Critical
Publication of CN101319427B publication Critical patent/CN101319427B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种含有聚乳酸纤维的织物,该织物具有抗水解性,在120度高温处理30min后,从织物中抽出的聚乳酸纤维原丝的强度相对于原丝的初期强度而言,强度保持率为90-60%。本发明的织物(包括机织物、针织物)具有明显的抗水解性能。织物能在高温高压下染色,并且丝的强度不会大幅度的下降,从而有效解决了聚乳酸纤维难以染色的问题,织物可以染上各种颜色。

Description

含有聚乳酸纤维的织物
技术领域:
本发明涉及一种具有抗水解性的聚乳酸纤维的织物。
背景技术:
地球上的石油资源是有限的,总有一天会枯竭的。传统的聚酯系纤维已经不能满足人们的需求,所以必须开发出不依靠石油的天然纤维。近年来,随着人们生活水平的提高以及环保意识的增强,人们对天然可生物降解纤维的研究越来越重视,世界各国竟相研究和开发新的绿色环保纤维,其中于九十年代末刚刚实现工业化开发的聚乳酸纤维(PLA纤维)最引人注目。聚乳酸纤维可以从谷物中取得,通过玉米淀粉发酵,得到乳酸,再通过聚合得到聚交丙二酯,最后开环得到聚乳酸。并且聚乳酸具有天然可降解型,其制品废弃后在土壤中经微生物作用可分解为二氧化碳和水,而且燃烧时不会散发毒气,不会造成污染。
但是,正是由于聚乳酸纤维的天然性,不可避免的存在一些缺点。聚乳酸纤维具有优越的可降解性,导致其抗水解性能较差,其织物在染色过程中,经加压高温处理,其织物的强度会下降,并且运输途中在潮湿的海运途中必然会影响了聚乳酸纤维的本身性能,从而影响了聚乳酸纤维的广泛应用。
发明内容
本发明的目的在于提供一种具有抗水解性能的含有聚乳酸纤维的织物。
本发明的技术解决方案是:
一种含有聚乳酸纤维的织物,其特征是:该织物具有抗水解性,在120度高温处理30min后,从织物中抽出聚乳酸纤维原丝的强度相对于原丝的初期强度而言,强度保持率为90-60%。所述原丝的初期强度是指未经上述条件处理时从织物中抽出的聚乳酸纤维原丝的强度。
在湿度90%,温度70度的环境下处理10天后,从织物中抽出聚乳酸纤维原丝的强度相对于原丝的初期强度而言,强度保持率为90-60%。所述原丝的初期强度是指未经上述条件处理时从织物中抽出的聚乳酸纤维原丝的强度。
构成该织物的聚乳酸纤维中含有抗水解剂碳化二亚胺成分,其成分占聚乳酸纤维重量的0.5%-5%,加入后纤维的强度伸度均不变,并且在一定程度上有所提高,符合织物织造的要求。抗水解剂碳化二亚胺包括单体以及分子量在10000以上的聚合体,可以是固体液体等形态。织物中含有的聚乳酸纤维的成分占总质量比40%以上。织物是机织物时,至少经纱、纬纱中之一是聚乳酸纤维。构成该织物的聚乳酸纤维中的聚乳酸,其分子量在10万以上。
本发明的织物(包括机织物、针织物)具有明显的抗水解性能。织物能在高温高压下染色,并且丝的强度不会大幅度的下降,从而有效解决了聚乳酸纤维难以染色的问题,织物可以染上各种颜色。
下面结合实施例对本发明作进一步说明。
具体实施方式:
实施例1:
将含有4%重量聚炭化二亚胺抗水解剂的聚乳酸纤维作为机织物的经纱成分制成机织物,剪取一块织物,从中抽出一根PLA(聚乳酸纤维)原丝测定其强度P1,另外将制得的机织物在120℃水中加热30分钟后,从该织物中抽出一根PLA(聚乳酸纤维)原丝测定其强度P2,计算P2与P1的比值即强度保持率,达到85%。织物能在此条件(120℃水中加热30分钟)下进行染色。
上述制成的机织物在湿度90%、温度70℃的环境下处理10天后,从织物中抽出PLA原丝,测定其强度P3,计算P3与P1的比值即强度保持率,强度保持率为75%。
抗水解剂碳化二亚胺是单体或分子量在10000以上的聚合体。构成该织物的聚乳酸纤维中的聚乳酸,其分子量在10万以上。
实施例2:
将含有0.6%重量聚炭化二亚胺抗水解剂的聚乳酸纤维作为机织物的经纬纱成分制成机织物,剪取一块织物,从中抽出一根PLA(聚乳酸纤维)原丝测定其强度P1,另外将制得的机织物在120℃水中加热30分钟后,从该织物中抽出一根PLA(聚乳酸纤维)原丝测定其强度P2,计算P2与P1的比值即强度保持率,达到65%。织物能在此条件(120℃水中加热30分钟)下进行染色。
上述制成的机织物在湿度90%、温度70℃的环境下处理10天后,从织物中抽出PLA原丝,测定其强度P3,计算P3与P1的比值即强度保持率,强度保持率为65%。
抗水解剂碳化二亚胺是单体或分子量在10000以上的聚合体。构成该织物的聚乳酸纤维中的聚乳酸,其分子量在10万以上。
实施例3
将含有1.5%重量聚炭化二亚胺抗水解剂的聚乳酸纤维制成针织物,剪取一块织物,从中抽出一根PLA(聚乳酸纤维)原丝测定其强度P1,另外将制得的针织物在120℃水中加热30分钟后,从该织物中抽出一根PLA(聚乳酸纤维)原丝测定其强度P2,计算P2与P1的比值即强度保持率,达到75%。织物能在此条件(120℃水中加热30分钟)下进行染色。
抗水解剂碳化二亚胺是单体或分子量在10000以上的聚合体。构成该织物的聚乳酸纤维中的聚乳酸,其分子量在10万以上。
实施例4
将含有2%重量聚炭化二亚胺抗水解剂的聚乳酸纤维作为机织物的经纬纱成分制成机织物,剪取一块织物,从中抽出一根PLA(聚乳酸纤维)原丝测定其强度P1,另外将制得的机织物在120℃水中加热30分钟,然后在湿度90%、温度70℃的环境下处理10天后,从织物中抽出PLA原丝,测定其强度P3,计算P3与P1的比值即强度保持率,强度保持率为88%。
抗水解剂碳化二亚胺是单体或分子量在10000以上的聚合体。构成该织物的聚乳酸纤维中的聚乳酸,其分子量在10万以上。
对比例
1.未添加聚碳化二亚胺的聚乳酸纤维用来制成的织物,在热水中分别处理后抽出PLA其强度保持率如下表所示
  温度   5min   15min   30min
  120℃   65%   20%   10%
  110℃   70%   35%   20%
  100℃   85%   70%   40%
2.未添加聚碳化二亚胺的聚乳酸纤维用来制成的织物,在热水中分别处理后抽出PLA其强度保持率如下表所示(湿度90%)
  温度   7天
  50℃   85%
  70℃   10%

Claims (7)

1、一种含有聚乳酸纤维的织物,其特征是:该织物具有抗水解性,在120度高温处理30min后,从织物中抽出的聚乳酸纤维原丝的强度相对于原丝的初期强度而言,强度保持率为90-60%。
2、根据权利要求1所述的含有聚乳酸纤维的织物,其特征是:在湿度90%,温度70度的环境下处理10天后,从织物中抽出的聚乳酸纤维原丝的强度相对于原丝的初期强度而言,强度保持率为90-60%。
3、根据权利要求1或2所述的含有聚乳酸纤维的织物,其特征是:构成该织物的聚乳酸纤维中含有抗水解剂碳化二亚胺成分,其成分占聚乳酸纤维重量的0.5%-5%。
4、根据权利要求3所述的含有聚乳酸纤维的织物,其特征是:抗水解剂碳化二亚胺包括单体以及分子量在10000以上的聚合体。
5、根据权利要求1或2所述的含有聚乳酸纤维的织物,其特征是:织物中含有的聚乳酸纤维的成分占总质量比40%以上。
6、根据权利要求5所述的含有聚乳酸纤维的织物,其特征是:织物是机织物时,至少经纱、纬纱中之一是聚乳酸纤维。
7、根据权利要求1或2所述的含有聚乳酸纤维的织物,其特征是:构成该织物的聚乳酸纤维中的聚乳酸,其分子量在10万以上。
CN200710023336XA 2007-06-08 2007-06-08 含有聚乳酸纤维的织物 Expired - Fee Related CN101319427B (zh)