CN101302409A - 玉米淀粉高强度粘合剂 - Google Patents

玉米淀粉高强度粘合剂 Download PDF

Info

Publication number
CN101302409A
CN101302409A CNA2007100218887A CN200710021888A CN101302409A CN 101302409 A CN101302409 A CN 101302409A CN A2007100218887 A CNA2007100218887 A CN A2007100218887A CN 200710021888 A CN200710021888 A CN 200710021888A CN 101302409 A CN101302409 A CN 101302409A
Authority
CN
China
Prior art keywords
kilograms
water
reactor
adhesives
cornstarch
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CNA2007100218887A
Other languages
English (en)
Inventor
李延禄
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNA2007100218887A priority Critical patent/CN101302409A/zh
Publication of CN101302409A publication Critical patent/CN101302409A/zh
Withdrawn legal-status Critical Current

Abstract

本发明提供一种玉米淀粉高强度粘合剂，其主要技术特征是，采用玉米面粉为原料，将玉米面预处理，其反应条件：反应温度为60－65℃；通过添加其它无机助剂，制得的粘合剂成本低、初粘性好、粘度适当、干燥较快、不易凝胶、粘接强度较高、合成的粘合剂无毒、符合环保要求，能取代合成高分子乳液粘合剂及水玻璃而广泛应用于瓦楞纸箱、粘贴壁纸、邮票、啤酒瓶标签、信封封口等领域，合成工艺简单，设备投资小。

Description

玉米淀粉高强度粘合剂
技术领域
本发明涉及一种粘合剂，具体说是一种玉米淀粉高强度粘合剂。
背景技术
由于粘合剂的使用对象不同，淀粉的产地、质量、气候条件、温湿度变化等因素的不同，其原料中淀粉与水的配比亦应有所不同，水量显多会降低粘度，过少则影响目产品的流动性，故不能用固定不变的相同配比。为了提高其粘合强度，还要加入适量添加剂。
发明内容
1、原料配比
30％的双氧水∶0.1-0.2浓度30％的烧碱∶0.86-0.96硼砂∶0.2-0.4玉米淀粉∶12-14水∶82-86生产玉米淀粉高强度粘合剂，原料与水产比例应掌握在1∶5-7间。
2、生产工艺
生产玉米淀粉高强度粘合剂可用于2千立升工业搪瓷反应锅2只，每次投放淀粉320公斤，在气温21-25℃情况下，可制成粘合剂2496公斤。具体工艺操作过程如下：1、在一号反应锅内加入960公斤水(总水量1/2)，加热到60-65℃(整个工艺过程温度均应控制在60-65℃之间)；2、将320公斤淀粉加入水中，边加边搅拌，同时加入1/4用量的烧碱液搅拌；3、将浓度30％的双氧水3.2公斤加约10倍水稀释，然后加入一号反应锅搅拌均匀，如非机械连续搅拌可每10-15分钟搅拌一次，进行1-2小时，使物料充分氧化；4、将剩余的3/4碱液(30％碱液总用量约72公斤)一次加入锅内搅拌，进行糊化；5、将二号反应锅内加热到60-65℃的热水1060公斤泵入一号反应锅内进行稀释，搅拌溶液；6、将硼砂5.2公斤加10倍水溶解调匀后，加入一号锅内进行搅拌，至呈半透明状即可。在整个制作过程中必须充分搅拌，否则易产生凝固结块，降低粘度和堵塞输送管道。
具体实施方式
1、原料配比
30％的双氧水∶0.1-0.2浓度30％的烧碱∶0.86-0.96硼砂∶0.2-0.4玉米淀粉∶12-14水∶82-86生产玉米淀粉高强度粘合剂，原料与水产比例应掌握在1∶5-7间。
2、生产工艺
生产玉米淀粉高强度粘合剂可用于2千立升工业搪瓷反应锅2只，每次投放淀粉320公斤，在气温21-25℃情况下，可制成粘合剂2496公斤。具体工艺操作过程如下：1、在一号反应锅内加入960公斤水(总水量1/2)，加热到60-65℃(整个工艺过程温度均应控制在60-65℃之间)；2、将320公斤淀粉加入水中，边加边搅拌，同时加入1/4用量的烧碱液搅拌；3、将浓度30％的双氧水3.2公斤加约10倍水稀释，然后加入一号反应锅搅拌均匀，如非机械连续搅拌可每10-15分钟搅拌一次，进行1-2小时，使物料充分氧化；4、将剩余的3/4碱液(30％碱液总用量约72公斤)一次加入锅内搅拌，进行糊化；5、将二号反应锅内加热到60-65℃的热水1060公斤泵入一号反应锅内进行稀释，搅拌溶液；6、将硼砂5.2公斤加10倍水溶解调匀后，加入一号锅内进行搅拌，至呈半透明状即可。在整个制作过程中必须充分搅拌，否则易产生凝固结块，降低粘度和堵塞输送管道。

Claims (2)

1、原料配比
30％的双氧水：0.1-0.2浓度30％的烧碱：0.86-0.96硼砂：0.2-0.4玉米淀粉：12-14水：82-86生产玉米淀粉高强度粘合剂，原料与水产比例应掌握在1∶5-7间。
2、生产工艺
生产玉米淀粉高强度粘合剂可用于2千立升工业搪瓷反应锅2只，每次投放淀粉320公斤，在气温21-25℃情况下，可制成粘合剂2496公斤。具体工艺操作过程如下：1、在一号反应锅内加入960公斤水，加热到60-65℃；2、将320公斤淀粉加入水中，边加边搅拌，同时加入1/4用量的烧碱液搅拌；3、将浓度30％的双氧水3.2公斤加约10倍水稀释，然后加入一号反应锅搅拌均匀，如非机械连续搅拌可每10-15分钟搅拌一次，进行1-2小时，使物料充分氧化；4、将剩余的3/4碱液一次加入锅内搅拌，进行糊化；5、将二号反应锅内加热到60-65℃的热水1060公斤泵入一号反应锅内进行稀释，搅拌溶液；6、将硼砂5.2公斤加10倍水溶解调匀后，加入一号锅内进行搅拌，至呈半透明状即可。在整个制作过程中必须充分搅拌，否则易产生凝固结块，降低粘度和堵塞输送管道。
CNA2007100218887A 2007-05-09 2007-05-09 玉米淀粉高强度粘合剂 Withdrawn CN101302409A (zh)