CN104650768A - 一种建筑防水胶及其生产工艺 - Google Patents

一种建筑防水胶及其生产工艺 Download PDF

Info

Publication number
CN104650768A
CN104650768A CN201310578542.2A CN201310578542A CN104650768A CN 104650768 A CN104650768 A CN 104650768A CN 201310578542 A CN201310578542 A CN 201310578542A CN 104650768 A CN104650768 A CN 104650768A
Authority
CN
China
Prior art keywords
reactor
distilled water
minutes
polyvinyl alcohol
glue
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310578542.2A
Other languages
English (en)
Inventor
李晶华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HARBIN LONGDI BUILDING MATERIAL Co Ltd
Original Assignee
HARBIN LONGDI BUILDING MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HARBIN LONGDI BUILDING MATERIAL Co Ltd filed Critical HARBIN LONGDI BUILDING MATERIAL Co Ltd
Priority to CN201310578542.2A priority Critical patent/CN104650768A/zh
Publication of CN104650768A publication Critical patent/CN104650768A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种建筑防水胶及其生产工艺，由聚乙烯醇、2%、盐酸%0.03、反应剂%0.05、增稠剂%0.02、成膜增强剂%1.3、磷酸盐%3、片碱与蒸馏水构成。其生产工艺采用了常规加热、混合、调节PH值等技术手段，制备简单、造价低，水溶性好，成膜速度快，耐候性好，无污染，粘结强度高等技术优点。可广泛应用于各种建筑防水工程的施工。

Description

一种建筑防水胶及其生产工艺
技术领域：
本发明涉及化工材料领域，特别是涉及一种建筑防水胶及其生产工艺。
背景技术：
目前，在建筑施工中使用的防水胶有很多种。但均存在着生产工艺复杂、施工过程繁琐，费时费力，材料韧性差，工程造价高，污染环境等弊端，严重影响了建筑质量和广泛推广应用。
发明内容：
本发明的目的在于克服上述现有技术的缺陷，提供一种制备简单、施工工艺简便，造价低，且耐老化、防水、粘结性好的建筑防水胶及其生产工艺。
为实现上述技术目的，本发明采取的技术方案是：一种建筑防水胶及其生产工艺，其防水胶由聚乙烯醇、2%、盐酸%0.03、反应剂%0.05、增稠剂%0.02、成膜增强剂%1.3、磷酸盐%3、片碱与蒸馏水构成。
其生产工艺为：1、在反应釜内倒入蒸馏水，然后加热至60C°，将聚乙烯醇、盐酸、反应剂加入反应釜内搅拌；2、将反应釜内的液体加温升至100 C°，使聚乙烯醇完全溶解后，在此温度下使液体保持时间为50分钟；3、第二次向反应釜内倒入蒸馏水，使液体温度降至70 C°左右，并慢慢加入成膜增强剂反应40分钟左右；4、再向反应釜内加入片碱和蒸馏水，调节PH值，待其慢慢融化反应30分钟；5、然后将蒸馏水稀释50倍的增稠剂加入反应釜，反应40分钟；6、停止加温，并使反应釜自然降温至常温，将反应釜内的胶水放出即得本发明产品。
本发明具有价格低廉，配制工艺简单，水溶性好，成膜速度快，耐候性好，耐低温，无污染，粘结强度高，不透水等技术优点。可广泛应用于各种建筑防水工程的施工。
具体实施方式：
下面结合实施例对本发明做进一步说明：
一种建筑防水胶，由聚乙烯醇、2%、盐酸%0.03、反应剂%0.05、增稠剂%0.02、成膜增强剂%1.3、磷酸盐%3、片碱与蒸馏水构成。
其生产工艺是取500KG蒸馏水倒入反应釜内加热至60C°，将聚乙烯醇20KG、盐酸2 KG、反应剂1 KG加入反应釜内搅拌；将反应釜内的液体加温升至100 C°，使聚乙烯醇完全溶解后，在此温度下使液体保持时间为50分钟；第二次向反应釜内倒入蒸馏水200 KG，使液体温度降至70 C°左右，并慢慢加入成膜增强剂1.5 KG反应40分钟左右；再向反应釜内加入片碱0.3 KG，调节PH值，待其慢慢融化反应30分钟；然后,将蒸馏水稀释50倍的增稠剂加入反应釜，反应40分钟；停止加温，并使反应釜自然降温至常温，将反应釜内的胶水放出即得本发明产品。

Claims (2)

1.一种建筑防水胶及其生产工艺，其防水胶由聚乙烯醇、2%、盐酸%0.03、反应剂%0.05、增稠剂%0.02、成膜增强剂%1.3、磷酸盐%3、片碱与蒸馏水构成。
2.根据权利要求1所述一种建筑防水胶及其生产工艺，其生产工艺为：1、在反应釜内倒入蒸馏水，然后加热至60C°，将聚乙烯醇、盐酸、反应剂加入反应釜内搅拌；2、将反应釜内的液体加温升至100 C°，使聚乙烯醇完全溶解后，在此温度下使液体保持时间为50分钟；3、第二次向反应釜内倒入蒸馏水，使液体温度降至70 C°左右，并慢慢加入成膜增强剂反应40分钟左右；4、再向反应釜内加入片碱和蒸馏水，调节PH值，待其慢慢融化反应30分钟；5、然后将蒸馏水稀释50倍的增稠剂加入反应釜，反应40分钟；6、停止加温，并使反应釜自然降温至常温，将反应釜内的胶水放出即得本发明产品。
CN201310578542.2A 2013-11-19 2013-11-19 一种建筑防水胶及其生产工艺 Pending CN104650768A (zh)