CN101302300B - 一种防雾水晶膜及其制备方法 - Google Patents

一种防雾水晶膜及其制备方法 Download PDF

Info

Publication number
CN101302300B
CN101302300B CN200810032313XA CN200810032313A CN101302300B CN 101302300 B CN101302300 B CN 101302300B CN 200810032313X A CN200810032313X A CN 200810032313XA CN 200810032313 A CN200810032313 A CN 200810032313A CN 101302300 B CN101302300 B CN 101302300B
Authority
CN
China
Prior art keywords
crystal film
antifog
polypropylene
film
antiblocking agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN200810032313XA
Other languages
English (en)
Other versions
CN101302300A (zh
Inventor
姚瑱
余小双
张瑾瑾
朱自清
蔡爱明
黄新龙
张金忠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Jinpu Plastic Packaging Material Co ltd
Original Assignee
Shanghai Jinpu Plastic Packaging Material Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Jinpu Plastic Packaging Material Co ltd filed Critical Shanghai Jinpu Plastic Packaging Material Co ltd
Priority to CN200810032313XA priority Critical patent/CN101302300B/zh
Publication of CN101302300A publication Critical patent/CN101302300A/zh
Application granted granted Critical
Publication of CN101302300B publication Critical patent/CN101302300B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种防雾水晶膜及其制备方法，该方法包括以下工艺步骤：该方法包括以下工艺步骤：将聚丙烯树脂60-90％，抗静电剂0-10％，抗粘连剂0.5-10％，共聚聚丙烯1-20％，经混匀、计量后，经单螺杆挤出机、纵向拉伸、横向拉伸和牵引进行物理化学反应后，经双向拉伸得到该薄膜。与现有技术相比，本发明具有优异的防雾和热封性能、高爽滑性、耐穿刺性、高透明度并能够长久保鲜等特点。

Description

一种防雾水晶膜及其制备方法
技术领域
本发明涉及一种膜，尤其涉及一种防雾水晶膜及其制备方法。
背景技术
防雾水晶膜是一种防止水汽在薄膜表面形成结雾而影响透明度的功能性薄膜，早期主要用在农膜中。随着人们消费需求的改变，食品包装向方便、卫生、健康、新鲜等方向发展。在各种透明冷冻食品、高温恒温即食食品、酸甜果酱制品以及新鲜蔬果类的包装中，为防止产生水雾影响视觉效果，必须采用具有防雾性能的防雾膜进行包装。因此防雾水晶膜产品具有良好的市场前景。
发明内容
本发明的目的就是为了克服上述现有技术存在的缺陷而提供一种防雾、热封性的防雾水晶膜及其制备方法。
本发明的目的可以通过以下技术方案来实现：一种防雾水晶膜，其特征在于，该薄膜包括以下组分及含量(重量百分比)：
聚丙烯树脂    60-90％，
抗静电剂      0-10％，
抗粘连剂      0.5-10％，
共聚聚丙烯    1-20％。
所述的抗静电剂选自芥酸酰胺、乙氧基胺、单甘脂油酸酰胺中的一种或几种。
所述的抗粘连剂选自二氧化硅、硅类、有机硅中的一种或几种。
所述的共聚聚丙烯选自丙烯-乙烯共聚物、丙烯-乙烯-丁烯共聚物、丙烯-乙烯-辛烯共聚物的马来酸酐接枝改性物中的一种或几种。
一种防雾水晶膜的制备方法，其特征在于，该方法包括以下工艺步骤：将聚丙烯树脂60-90％，抗静电剂0-10％，抗粘连剂0.5-10％，共聚聚丙烯1-20％，经混匀、计量后，经单螺杆挤出机、纵向拉伸、横向拉伸和牵引进行物理化学反应后，经双向拉伸得到该薄膜。
所述的螺杆挤出工艺温度为200-270℃。
与现有技术相比，本发明以聚丙烯为原料的防雾、热封的防雾水晶膜，该新产品具有优异的防雾和热封性能、高爽滑性、耐穿刺性、高透明度并能够长久保鲜。可根据不同的被包装物品，不同的贮藏、贮存条件，不同的使用要求，选用不同的工艺条件，生产出不同性能及效果的防雾薄膜。
具体实施方式
以下结合具体实施例来说明本发明所涉及的防雾水晶膜及其制备方法。
在以下实施例中，F280表示：中石化公司产品聚丙烯树脂；
抗静电剂表示：上海佳摩公司产品；
共聚聚丙烯表示：中石化公司产品；
抗粘连剂表示：舒尔曼公司产品；
聚丙烯树脂、抗静电剂、抗粘连剂和共聚聚丙烯经混匀、计量后，经单螺杆挤出机、MDO、TDO和牵引进行物理化学反应后，即可得该薄膜。工艺温度为200-270℃。
所得薄膜按照ISO测试标准制成相应样条，干态条件下进行测试。即在干燥器中状态条件24小时，然后在23±2℃、50±5％相对湿度的环境下进行测试。
按照ISO 1133标准测量熔融指数；
实施例1～3
  实施例1   实施例2   实施例3
    F280(Kg)抗静电剂(Kg)抗粘连剂(Kg)共聚聚丙烯   895--5100   790--10200   69055300
性能测试如下：
  单位   实施例1   实施例2 实施例3
    热封强度   N/15mm     2.7     2.8     3.0
实施例4
一种防雾水晶膜的制备方法，包括以下工艺步骤：将聚丙烯树脂60kg，抗静电剂芥酸酰胺10kg，抗粘连剂二氧化硅10kg，共聚聚丙烯20kg经混匀、计量后，经单螺杆挤出机在200℃下、纵向拉伸(MDO)、横向拉伸(TDO)和牵引进行物理化学反应后，经双向拉伸得到该薄膜。
实施例5
一种防雾水晶膜的制备方法，包括以下工艺步骤：将聚丙烯树脂90kg，抗静电剂乙氧基胺4kg，抗粘连剂有机硅1kg，共聚聚丙烯5kg经混匀、计量后，经单螺杆挤出机在270℃下、纵向拉伸(MDO)、横向拉伸(TDO)和牵引进行物理化学反应后，经双向拉伸得到该薄膜。
实施例6
一种防雾水晶膜的制备方法，包括以下工艺步骤：将聚丙烯树脂90kg，抗静电剂乙氧基胺1kg，抗粘连剂有机硅8kg，共聚聚丙烯1kg经混匀、计量后，经单螺杆挤出机在270℃下、纵向拉伸(MDO)、横向拉伸(TDO)和牵引进行物理化学反应后，经双向拉伸得到该薄膜。
所述的共聚聚丙烯选自丙烯-乙烯共聚物、丙烯-乙烯-丁烯共聚物、丙烯-乙烯-辛烯共聚物的马来酸酐接枝改性物中的一种或几种。

Claims (2)

1.一种防雾水晶膜，其特征在于，该薄膜包括以下组分及重量百分比含量：
聚丙烯树脂    60-90％，
抗静电剂      0-10％，
抗粘连剂      0.5-10％，
共聚聚丙烯    1-20％；
所述的抗静电剂选自芥酸酰胺、乙氧基胺、单甘脂油酸酰胺中的一种或几种；
所述的抗粘连剂选自二氧化硅或有机硅中的一种或几种；
所述的共聚聚丙烯选自丙烯-乙烯共聚物、丙烯-乙烯-丁烯共聚物、丙烯-乙烯-辛烯共聚物的马来酸酐接枝改性物中的一种或几种。
2.一种如权利要求1所述的防雾水晶膜的制备方法，其特征在于，该方法包括以下工艺步骤：将聚丙烯树脂60-90wt％，抗静电剂0-10wt％，抗粘连剂0.5-10wt％，共聚聚丙烯1-20wt％，经混匀、计量后，经单螺杆挤出机、纵向拉伸、横向拉伸和牵引进行物理化学反应后，经双向拉伸得到该薄膜；
所述的螺杆挤出工艺温度为200-270℃。
CN200810032313XA 2008-01-04 2008-01-04 一种防雾水晶膜及其制备方法 Expired - Fee Related CN101302300B (zh)