CN102504404B - 一种低光泽度消光雾度分布可控bopp薄膜 - Google Patents

一种低光泽度消光雾度分布可控bopp薄膜 Download PDF

Info

Publication number
CN102504404B
CN102504404B CN201110287270.1A CN201110287270A CN102504404B CN 102504404 B CN102504404 B CN 102504404B CN 201110287270 A CN201110287270 A CN 201110287270A CN 102504404 B CN102504404 B CN 102504404B
Authority
CN
China
Prior art keywords
polypropylene
film
bopp
controlled
low
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201110287270.1A
Other languages
English (en)
Other versions
CN102504404A (zh
Inventor
余大双
柳瑞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suqian Gettel Plastic Co.,Ltd.
Original Assignee
余大双
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 余大双 filed Critical 余大双
Priority to CN201110287270.1A priority Critical patent/CN102504404B/zh
Publication of CN102504404A publication Critical patent/CN102504404A/zh
Application granted granted Critical
Publication of CN102504404B publication Critical patent/CN102504404B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于新型材料技术领域,具体涉及一种低光泽度消光雾度分布可控BOPP薄膜及其制备方法,其特征在于包含以下组分(重量百分比):聚丙烯40~90%;消光剂1~40%;抗静电剂0~30%;抗粘连剂0.5~30%。其制备方法为:按照配方比例将原料在高速混合机中混合30min,再经单螺杆挤出机融入、纵向拉伸、横向拉伸后,得到产品,其中单螺杆挤出的工艺温度为200-270℃,螺杆转速控制在30~50r/min。本发明产品可对薄膜的雾度进行调控,还可将消光效果转移到纺织品、皮革以及金银卡纸材质上。

Description

一种低光泽度消光雾度分布可控BOPP薄膜
技术领域
[0001] 本发明属于新型材料技术领域,具体涉及一种低光泽度消光雾度分布可控BOPP薄膜及其制备方法,特别是一种可将消光效果转移至纺织品、皮革以及金银卡纸上的BOPP薄膜及其制备方法。
背景技术
[0002] 低光泽度消光BOPP薄膜光泽度低,呈漫反射,眼感柔和,具有良好的性价比、原料易得、产品质量稳定等特点,又容易通过抗静电、粘连或其他聚合物共混制成薄膜,因此长期以来以聚丙烯为原料的BOPP薄膜广泛应用于各种领域。
[0003] 美中不足的是,现有的消光膜由于添加消光剂的关系,表面亮点多,光泽度差,消光效果不理想,且薄膜力学性能降低,容易破损。专利CN101531078提到一种无抗粘连剂的BOPP消光膜及其制备方法,且消光剂分布均匀,消光效果好;同样在专利CN201144202中提到多层消光双向拉伸聚丙烯薄膜。但是,二者均未提及薄膜材料的力学性能和雾度可控的问题,更未提及其消光效果可否转移至纺织品、皮革以及金银卡纸材质上。
[0004] 本发明针对以上几个问题,采用了低光泽度消光BOPP薄膜生产技术,提高了产品质量。与传统的消光膜相比,其生产技术可将薄膜雾度在50 %~80%范围内加以调控,更重要的是消光效果不再单一局限在薄膜上,可通过涂布上胶技术转移至纺织品、皮革以及金银卡纸材质上,达到改变基材外观及品质的作用。
发明内容
[0005] 本发明的目的是解决现有技术中存在的亮点多、手感不好,雾度单一等问题,提供一种低光泽度消光雾度分布可控BOPP薄膜及其制备方法,并且可将消光效果转移至纺织品、皮革以及金银卡纸材质上。
[0006] 为实现上述目的,本发明采取以下技术方案:
[0007] —种低光泽度消光雾度分布可控BOPP薄膜,其特征在于,由以下质量配比的原料
制备成:
[0008]
聚丙烯 40~90%
消光剂 1~40%
[0009]
抗静电剂 O~30%
抗粘连剂 0.5~30%
[0010] 所述聚丙烯树脂为BOPP薄膜专用聚丙烯,其熔融指数在I~3g/10min之间;
[0011] 所述消光剂由聚丙烯、滑石粉、偶联剂以及聚乙烯组成,各组分含量(重量份)为:聚丙烯60份,滑石粉7~10份,偶联剂0.05~0.1份,聚乙烯40~50份,其中所述聚丙烯为无规共聚聚丙烯,其熔融指数MI在0.3~0.5mg/10min ;所述偶联剂为硅烷偶联剂或者钛酸酯偶联剂中的一种或几种,加入偶联剂的目的是对滑石粉进行改性;所述聚乙烯为高密度聚乙烯;
[0012] 所述的抗静电剂选自芥酸酰胺、乙氧基胺、单甘脂油酸酰胺中的一种或几种;
[0013] 所述的抗粘连剂选自二氧化硅和聚甲基丙烯酸甲酯(PMMA)中的一种或两种;
[0014] 所述消光剂制备方法为:将偶联剂用溶剂稀释,然后均匀的分散在滑石粉填料中,通过烘箱使溶剂挥发,再将烘干好的填料用告诉粉碎机粉碎成细粉,将该细粉与无规共聚聚丙烯和高密度聚乙烯在开炼机上机械共混,再经挤出机塑化造粒,制成球状颗粒,其中挤出温度为180~200°C。
[0015] 一种低光泽度消光薄膜的制备方法,其特征在于,该方法包括以下工艺步骤:将聚丙烯40_90wt%,抗静电剂0_30wt%,抗粘连剂0.5-30wt%,消光剂l-40wt%,经过精确称量,将上述原料在高速混合机中混合30min,再经单螺杆挤出机融入、纵向拉伸、横向拉伸后,得到产品。
[0016] 所述的单螺杆挤出的工艺温度为200-270°C,螺杆转速控制在30~50r/min。
[0017] 本发明有益效果:
[0018] 与现有的技术相比,本发明由于其消光剂由聚丙烯、滑石粉、偶联剂以及聚乙烯组成,且对滑石粉进行了偶联处理,制备的产品光泽度低且消光雾度分布可控,其光滑的纹理适用于书本封面包装,美观、大方;也可通过与纺织品、皮革以及金银卡纸材质复合,将消光效果转移,从而改变材质外观品质和功能用途。
具体实施方式
[0019] 以下结合实施例对本发明作进一`步详细说明,但它们不是对本发明的限定。
[0020] 在以下实施例中,
[0021] F280:中石化公司广品聚丙稀树脂;
[0022]消光剂:自制,将硅烷偶联剂0.08g用溶剂稀释,然后均匀的分散在9g滑石粉填料中,通过烘箱使溶剂挥发,再将烘干好的填料用告诉粉碎机粉碎成细粉,将该细粉与MI为0.4mg/10min的无规则共聚聚丙烯60g和高密度聚乙烯40g在开炼机上机械共混,再经挤出机塑化造粒,制成球状颗粒,其中挤出温度为185°C ;
[0023] 抗静电剂:上海佳摩公司产品;舒尔曼公司产品;
[0024] 抗粘连剂:舒尔曼公司产品;安配色公司产品;
[0025] 聚丙烯、消光剂抗静电剂和抗粘连剂经计量、混匀后,通过单螺杆挤出机、MDO、TDO和牵引进行物理化学反应后,即可得到该膜。工艺温度为200-270°C
[0026] 所得薄膜按照ISO测试标准制成相应样条,干态条件下进行测试。即在干燥器中状态条件24小时,然后在23±2°C、50±5°C相对湿度的环境下进行测试。
[0027] 按照ISOl 133标准测量熔融指数;
[0028] 按照IS0527标准测量拉伸强度;
[0029] 实施例1~3
[0030]
Figure CN102504404BD00051
[0033] 实施例4
[0034] 一种低光泽度消光雾度分布可控BOPP薄膜的制备方法,包括以下工艺步骤:取BOPP专用聚丙烯40份,消光剂40份,抗静电剂芥酸酰胺10份,抗粘连剂二氧化娃10份;经准确称量,将聚丙烯以及其他助剂按照顺序在高速混合机中混合30min,再经单螺杆挤出机融入、纵向拉伸、横向拉伸后,得到产品。挤出机温度控制在200-270 V,螺杆转速控制在30~50r/min。所得低光泽度消光膜经过涂布、上胶后与布类纺织品材质进行复合,再经烘干处理,薄膜剥离,消光效果即可转移至布类纺织品上。
[0035] 实施例5
[0036] 一种低光泽度消光雾度分布可控BOPP薄膜的制备方法,包括以下工艺步骤:取BOPP专用聚丙烯90份,消光剂8份,抗静电剂乙氧基胺1份,抗粘连剂PMMA 1份;经准确称量,将聚丙烯以及其他助剂依次投入高速混合机中混合30min,再经单螺杆挤出机融入、纵向拉伸、横向拉伸后,得到产品。挤出机温度控制在200-270°C,螺杆转速控制在30~50r/min0所得低光泽度消光膜经过涂布、上胶后与布类纺织品材质进行复合,再经烘干处理,薄膜剥离,消光效果即可转移至布类纺织品上。
[0037] 实施例6
[0038] 一种低光泽度消光雾度分布可控BOPP薄膜的制备方法,包括以下工艺步骤:取BOPP专用聚丙烯47份,消光剂3份,抗静电剂乙氧基胺30份,抗粘连剂二氧化硅20份,;经准确称量,将聚丙烯以及其他助剂按照顺序在高速混合机中混合30min,再经单螺杆挤出机融入、纵向拉伸、横向拉伸后,得到产品。挤出机温度控制在200-270 V,螺杆转速控制在30~50r/min。所得低光泽度消光膜经过涂布、上胶后与皮革类材质进行复合,再经烘干处理,薄膜剥离,消光效果即可转移至皮革类材质上。
[0039] 实施例7
[0040] 一种低光泽度消光雾度分布可控BOPP薄膜的制备方法,包括以下工艺步骤:取BOPP专用聚丙烯50份,消光剂10份,抗静电剂乙氧基胺10份,抗粘连剂二氧化硅30份;经准确称量,将聚丙烯以及其他助剂按顺序在高速混合机中混合30min,再经单螺杆挤出机融入、纵向拉伸、横向拉伸后,得到产品。挤出机温度控制在200-270 V,螺杆转速控制在30~50r/min。所得低光泽度消光膜经过涂布、上胶后与金卡纸类材质进行复合,再经烘干处理,薄膜剥离,消光效果即可转移至金卡纸类材质上。
[0041] 实施例8
[0042] 一种低光泽度消光雾度分布可控BOPP薄膜的制备方法,包括以下工艺步骤:取BOPP专用聚丙烯85份,消光剂11份,抗静电剂芥酸酰胺2份,抗粘连剂PMMA2份;经准确称量,将聚丙烯以及其他助剂按顺序在高速混合机中混合30min,再经单螺杆挤出机融入、纵向拉伸、横向拉伸后,得到产品。挤出机温度控制在200-270°C,螺杆转速控制在30~50r/min0所得低光泽度消光膜经过涂布、上胶后与银卡纸类材质进行复合,再经烘干处理,薄膜剥离,消光效果即可转移至 银卡纸类材质上。

Claims (2)

1.一种低光泽度消光雾度分布可控BOPP薄膜,其特征在于包含以下组分以及重量百分比:聚丙烯40~90% ;消光剂I~40% ;抗静电剂O~30% ;抗粘连剂0.5~30% ; 所述的聚丙烯为BOPP薄膜专用聚丙烯,其熔融指数在I~3g/10min之间; 所述的消光剂由聚丙烯、滑石粉、偶联剂以及聚乙烯组成,各组分含量(重量份)为••聚丙烯60份,滑石粉7~10份,偶联剂0.05~0.1份,聚乙烯40~50份,其中所述聚丙烯为无规共聚聚丙烯,其熔融指数MI在0.3~0.5mg/10min ;所述聚乙烯为高密度聚乙烯,其制备方法为:将偶联剂用溶剂稀释,然后均匀的分散在滑石粉填料中,通过烘箱使溶剂挥发,再将烘干好的填料用高速粉碎机粉碎成细粉,将该细粉与无规共聚聚丙烯和高密度聚乙烯在开炼机上机械共混,再经挤出机塑化造粒,制成球状颗粒,其中挤出温度为180~200°C ;所述的抗静电剂选自芥酸酰胺、乙氧基胺、单甘脂油酸酰胺中的一种或几种; 所述的抗粘连剂选自二氧化硅、聚甲基丙烯酸甲酯(PMMA)中的一种或两种; 所述的低光泽度消光雾度分布可控BOPP薄膜制备方法的特征在于,该方法包括以下工艺步骤:将聚丙烯,抗静电剂,抗粘连剂,消光剂,经过精确称量,将上述原料在高速混合机中混合30min,再经单螺杆挤出机融入、纵向拉伸、横向拉伸后,得到产品,其中单螺杆挤出工艺温度为200-270°C。
2.根据权利要求1所述的一种低光泽度消光雾度分布可控BOPP薄膜,其特征在于,所述的BOPP薄膜的雾度控制在50%~8`0%。
CN201110287270.1A 2011-09-23 2011-09-23 一种低光泽度消光雾度分布可控bopp薄膜 Active CN102504404B (zh)