CN101284284B - 钛铜复合型材的挤压工艺 - Google Patents
钛铜复合型材的挤压工艺 Download PDFInfo
- Publication number
- CN101284284B CN101284284B CN2008100182860A CN200810018286A CN101284284B CN 101284284 B CN101284284 B CN 101284284B CN 2008100182860 A CN2008100182860 A CN 2008100182860A CN 200810018286 A CN200810018286 A CN 200810018286A CN 101284284 B CN101284284 B CN 101284284B
- Authority
- CN
- China
- Prior art keywords
- titanium
- copper
- extrusion
- cylinder
- copper composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明钛铜复合型材的挤压工艺按照如下步骤实施：(1)先将金属钛按需要尺寸加工成筒型；(2)然后将金属铜熔化后倒入加工好的钛筒内；(3)在钛筒外包铜皮将钛筒整体包裹，外部包裹铜皮加热后起一定的润滑作用：(4)加热600度以上，挤压压力不低于500吨，挤压筒温度为保持在300-600度，用500吨以上的油压挤压机挤压成型；然后按设计要求精加工；检验；即为成品。本发明优点是钛铜复合工艺简单，结合牢靠，而且可以制造大尺寸复合材料。
Description
技术领域
本发明属于金属材料加工技术领域，特别是金属复合工艺技术。
背景技术
现有的金属复合方法主要包括爆炸复合、套管直接拉拔复合等工艺。爆炸复合技术条件高，对环境危害大。而直接拉拔复合尽管工艺简单，但是加工产品单一。只适合生产较小尺寸的园型复合棒材。
经过检索，采用爆炸复合的技术比如中国专利申请钛铜复合棒的包覆法制造工艺(申请号：200710017750.X)在铜板的上下表面贴覆一层钛合金板，通过爆炸复合等方法制成钛铜复合板，在钛铜复合板的两个侧面覆盖一层钛合金板，再将钛合金板与钛铜复合板的侧面通过焊接等方法连接，使得铜板周面被一层钛合金板全部包覆。由于钛合金板与夹层铜板贴合紧密，制造过程中钛合金板变形量极小，有效保证了钛合金板不会因变形量过大而破损，工艺过程简单高效，达到节约钛材、提高生产效率及降低生产成本的目的。但是这种爆炸复合工艺适合较大尺寸的板材复合，对于管材、棒材及其他型材则不适合。
采用直接拉拔复合方法的比如申请号为200710018909.×的涉及直径小于20mm的小规格圆形钛铜复合棒的制造方法，制造方法的实施过程分为：坯料准备、穿管、涂层、加热处理、拉拔、精整、检验、成品包装发货等八个主要步骤，采用本发明制造的小规格钛铜复合棒，钛铜金属层贴合牢固，钛铜断面均匀，能利用简单设备尽快实现小规格钛铜复合棒的国产化。这种在较低温度下拉拔复合的方法，对于小规格棒材有优势，但是钛铜之间结合强度较低，容易造成分层，同时，拉拔工艺由于场地和设备限制，不能加工较长尺寸的型材。
发明内容
本发明目的是提出一种钛铜复合型材的挤压工艺，以克服现有金属复合工艺的缺陷，通过大功率挤压机采用挤压工艺可以提高产量，降低成本，制造各种常用规格型号或者异型(方，扁，条等)以及较大尺寸钛铜复合材料。
实现上述发明目的的钛铜复合型材的挤压工艺是按照如下步骤实施的：
(1)先将金属钛按需要尺寸加工成筒型；
(2)然后将金属铜熔化后倒入加工好的钛筒内；
(3)在钛筒外包铜皮将钛筒整体包裹；
(4)加热至600度以上后挤压成型；
(5)按设计要求精加工；
(6)检验；
(7)成品。
加热温度控制在600度以上，挤压压力一般为不低于500吨。挤压筒温度为300-600度。
另外需要说明的是，挤压所采用的设备为500吨以上的油压挤压机或者水压挤压机均可。
本发明优点是可以按需生产，基本满足国际国内钛铜复合材料日新月异的设计要求，与其他加工工艺有着本质上的区别。通过高温高压挤压的钛铜复合型材结合的更加紧密，物理性能更高，强度更好，易于加工。就长度而言，经挤压的钛铜复合型材可以长达十米甚至几十米，克服了以往工艺无法加工超长要求的钛铜复合材料，满足设计不允许焊接的要求，减少焊接次数，或者不焊接，提高了整体性能。本发明还可应用于钛与其他金属复合材料的生产。
具体实施方式
本发明钛铜复合型材的挤压工艺按照如下步骤实施：(1)先将金属钛按需要尺寸加工成筒型；(2)然后将金属铜熔化后倒入加工好的钛筒内；(3)在钛筒外包铜皮将钛筒整体包裹，外部包裹铜皮加热后起一定的润滑作用：(4)加热600度以上，挤压压力不低于500吨，挤压筒温度为保持在300-600度，用500吨以上的油压挤压机挤压成型；然后按设计要求精加工；检验；即为成品。
Claims (2)
1.一种钛铜复合型材的挤压工艺，其特征是按照如下步骤实施：
(1)先将金属钛按需要尺寸加工成筒型；
(2)然后将金属铜熔化后倒入加工好的钛筒内；
(3)在钛筒外包铜皮将钛筒整体包裹；
(4)加热至600度以上后用挤压机挤压成型；
(5)按设计要求精加工；
(6)检验；
(7)成品。
2.根据权利要求1所述的钛铜复合型材的挤压工艺，其特征是加热温度控制在600度以上，挤压压力不低于500吨。