CN101280168A - 单组分加成型有机硅电子灌封胶 - Google Patents

单组分加成型有机硅电子灌封胶 Download PDF

Info

Publication number
CN101280168A
CN101280168A CNA2008100975595A CN200810097559A CN101280168A CN 101280168 A CN101280168 A CN 101280168A CN A2008100975595 A CNA2008100975595 A CN A2008100975595A CN 200810097559 A CN200810097559 A CN 200810097559A CN 101280168 A CN101280168 A CN 101280168A
Authority
CN
China
Prior art keywords
potting adhesive
single component
electronic potting
ethylene
component additional
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2008100975595A
Other languages
English (en)
Inventor
卢儒
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNA2008100975595A priority Critical patent/CN101280168A/zh
Publication of CN101280168A publication Critical patent/CN101280168A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种单组分加成型有机硅电子灌封胶,由乙烯基液体MQ树脂、乙烯基液体硅橡胶、含氢硅油、铂络合物、白碳黑、抑制剂制成。本发明避免了现有产品使用时需要混合的过程,节省了时间,大大提高了生产效率,使用方便。

Description

单组分加成型有机硅电子灌封胶
技术领域:
本发明涉及一种有机灌封胶。
背景技术:
市场上的有机灌封胶大多是双组分的,用时要进行混合。混合过程中含有大量气泡,需要很长时间才能进行灌封。
发明内容:
本发明的目的在于提供一种使用方便、生产效率高的单组分加成型有机硅电子灌封胶。
本发明的技术解决方案是:
一种单组分加成型有机硅电子灌封胶,其特征是:由下列重量百分比的组分制成:
乙烯基液体MQ树脂          10~40%
乙烯基液体硅橡胶          20~50%
含氢硅油                  3~15%
铂络合物                  0.5~1.5%
白碳黑                    10~30%
抑制剂                    1~5%。
抑制剂为炔醇、醚或氰类化合物。
乙烯基液体硅橡胶的乙烯基含量为1.5-15%,粘度为200-30000Pa·S。
乙烯基液体MQ树脂的乙烯基含量为0.2%-5%,粘度为500-1000Pa·S。
含氢硅油为分子链中间的含氢硅油,含氢量为1.0%-1.5%。
本发明避免了现有产品使用时需要混合的过程,节省了时间,大大提高了生产效率,使用方便。
下面结合实施例对本发明作进一步说明。
具体实施方式:
实施例1:
取乙烯基液体MQ树脂30g,乙烯基液体硅橡胶40g,含氢硅油8g,铂络合物0.008g,抑制剂0.008g,白炭黑10g,在干净容器中混合均匀常温静置去泡后灌装得成品。用于封装时直接灌注、加热抽真空即可,加热温度130-180℃。
其中抑制剂为炔醇、醚或氰类化合物(例丙炔醇、1,4-丁炔二醇、聚苯硫醚、甲基叔丁基醚、苯醚甲环唑、异丙醚、乙二醇单丁醚、乙二醇丁醚、、二苯醚,脂肪醇聚氧乙烯醚、八溴醚、乙氧氟草醚、聚苯醚、丙二醇丁醚、氰化氢等),乙烯基液体硅橡胶的乙烯基含量为1.5-15%,粘度为200-30000Pa·S。乙烯基液体MQ树脂的乙烯基含量为0.2%-5%,粘度为500-1000Pa·S。含氢硅油为分子链中间的含氢硅油,含氢量为1.0%-1.5%。
实施例2:
取乙烯基液体MQ树脂25g,乙烯基液体硅橡胶45g,含氢硅油7.5g,铂络合物0.008g,抑制剂0.008g,白炭黑15g,在干净容器中混合均匀常温静置去泡后灌装得成品。用于封装时直接灌注、加热抽真空即可,加热温度130-180℃。其余同实施例1。
实施例3:
取乙烯基液体MQ树脂20g,乙烯基液体硅橡胶50g,含氢硅油6.5g,铂络合物0.008g,抑制剂0.008g,白炭黑15g,在干净容器中混合均匀常温静置去泡后灌装得成品。用于封装时直接灌注、加热抽真空即可,加热温度130-180℃。
其余同实施例1。

Claims (5)

1、一种单组分加成型有机硅电子灌封胶,其特征是:由下列重量百分比的组分制成:
乙烯基液体MQ树脂        10~40%
乙烯基液体硅橡胶        20~50%
含氢硅油                3~15%
铂络合物                0.5~1.5%
白碳黑                  10~30%
抑制剂                  1~5%。
2、根据权利要求1所述的单组分加成型有机硅电子灌封胶,其特征是:抑制剂为炔醇、醚或氰类化合物。
3、根据权利要求1或2所述的单组分加成型有机硅电子灌封胶,其特征是:乙烯基液体硅橡胶的乙烯基含量为1.5-15%,粘度为200-30000Pa·S。
4、根据权利要求1或2所述的单组分加成型有机硅电子灌封胶,其特征是:乙烯基液体MQ树脂的乙烯基含量为0.2%-5%,粘度为500-1000Pa·S。
5、根据权利要求1或2所述的单组分加成型有机硅电子灌封胶,其特征是:含氢硅油为分子链中间的含氢硅油,含氢量为1.0%-1.5%。
CNA2008100975595A 2008-05-16 2008-05-16 单组分加成型有机硅电子灌封胶 Pending CN101280168A (zh)