CN101230237A - 一种仿大理石效果天然云母漆及其制备方法 - Google Patents
一种仿大理石效果天然云母漆及其制备方法 Download PDFInfo
- Publication number
- CN101230237A CN101230237A CNA2008100263961A CN200810026396A CN101230237A CN 101230237 A CN101230237 A CN 101230237A CN A2008100263961 A CNA2008100263961 A CN A2008100263961A CN 200810026396 A CN200810026396 A CN 200810026396A CN 101230237 A CN101230237 A CN 101230237A
- Authority
- CN
- China
- Prior art keywords
- natural mica
- stirred
- marble
- added
- percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种仿大理石效果天然云母漆,其特征在于,它的重量组分比为,水30-35%、助剂5-10%、改性硅溶胶30-35%、彩石砂30-35%、天然云母片5-10%,各组份之和等于100%。所述配方中还还按需添加有纤维素。其制备方法步骤,首先,在搅拌容器中,将水、纤维素、助剂混合搅拌10-15分钟;其次,再加入改性硅溶胶混合进行搅拌10-15分钟,再将彩石砂加入其中混合搅拌10-15分钟;最后再投入天然云母片,球磨分散后,混合搅拌约10-15分钟,然后检验,包装即可出品。本发明具有性能优良,环保节能,且价格适中,有大理石独特的装饰效果等特点。
Description
技术领域
本发明涉及一种仿大理石效果的天然云母漆及其制备方法。
背景技术
近年来随着国家外墙保温节能技术的强制执行,原有的外墙饰面用的干挂石材、面砖、玻璃幕墙等含有隐性安全性方面的材料,国家已不再提倡使用,取而代之的是粘刷涂料或其他饰面材料。据报道:在欧美发达国家高层建筑采用外墙高级涂料装饰已高达90%,在日本亦已达到80%以上,在东南亚、新加坡、马来西亚等国高层建筑外墙必须采用涂料装饰以用法律形式固定下来,我国的高层建筑物外墙面用料多年来采用瓷砖、陶瓷锦砖为主的装饰材料,难免出现不同程度的粉化、裂纹和各种粘污,即使经常清洗也难以恢复原貌,费工费时浪费财力。无论是对新建筑物进行涂装还是对旧建筑物进行更新,赋予新的色彩一段时间后饰面层均会出现质量通病,中低档次外墙平涂以单薄的漆膜难免会出现基层的裂缝、粉化、脱落、褪色、花脸、有水锈、渗漏、使用年限短等弊端。如果处理不好这些问题,那么色彩绚丽城市建筑物也只是短暂的,日后影响了现代化城市形象。
众所周知,国内的涂料品种以低档为主流、价格便宜、品质性能差、难以满足国内高档建筑外饰面日益高档化和外墙保温层的特殊要求,装饰材料行业迫切需要一种满足各种性能要求的特殊涂装材料的出现。而现有的云母漆一般是由清漆和云母粉调和而成的,油漆中的云母颗粒依靠它独特的立体棱角分子结构,使通过它的光呈多角度折射,从而有钻石般的效果,与金属漆相比更有立体感,其装饰作用很好。然而采用云母粉调和而成的云母漆其无法体现出仿大理石的特殊的装饰效果,同时现有的云母漆的干燥的时间较普通漆更长,喷涂施工难度较大。
发明内容
本发明的目的是克服传统的处理技术,提供一种性能好、施工方便、具有仿大理石的独特装饰效果的天然云母漆。
本发明的大理石效果天然云母漆是在建筑涂料的基础上增加云母片构成,它的重量组分比为,水30-35%、助剂5-10%、改性硅溶胶30-35%、彩石砂30-35%、天然云母片5-10%,各组份之和等于100%。
上述配方中按需还可以添加有纤维素。
所述改性硅溶胶为硅丙树脂;彩石砂为60-120目、天然云母片为20目-200目;
本发明还提供了上述云母漆的制备方法,其制备方法步骤,首先,在搅拌容器中,将水、纤维素、助剂混合搅拌10-15分钟;其次,再加入改性硅溶胶混合进行搅拌10-15分钟,再将彩石砂加入其中混合搅拌10-15分钟;最后再投入天然云母片,球磨分散后,混合搅拌约10-15分钟,然后检验,包装即可出品。
本发明采用上述技术的解决方案所能达到的有益效果是:
一、由于配方中云母片其优良的绝缘性、耐热性、柔韧性、抗拉伸性、抗老化性等,使本云母漆成为涂料工业的新原料;且天然云母片主要结晶成单斜晶系、晶体成假六方薄片状、鳞片状、板状、假六方柱状,硬度2-3,比重2.73-3.20云母的折射率随铁的含量增高而相应增高,可由低正突起至中正突起,不含铁的变种薄片中无色,含铁愈高时颜色愈深,同时多色性和吸收性增强,云母片以上的特点加入涂料中不但对花岗岩的仿真度达100%,也符合国家环保、节能的法律法规要求,是新一代高性能、节能以及环保涂料。
二、装饰效果好,使用范围广;云母薄片密封了漆膜细孔后,可使涂层内应力的均匀性提高,从而增强漆膜的耐开裂性、耐侯性、耐酸碱性、表面光滑性、美观性等;能充分展现出花岗岩的纹理和质感,更加能体现出花岗岩的自然片状,提高涂料柔韧性以及云母片自身独特的折射性,提高涂料的档次。它的主要应用领域为建筑外墙涂料、内墙涂料、粉末涂料、防腐蚀涂料、耐高温涂料、马路划线漆、防火涂料等。
三、本云母漆制备工艺比较简单,方便实施,生产成本较低,符合″4E″原则,即经济(Economy)、能源(Energy)生态(Ecology)、效率(Efficiency)。
具体实施方式
本仿大理石效果的天然云母漆,按照高层建筑对饰面涂料的要求针对涂料的耐候性、防水性以及附着力的三大功能,首先选用合适成膜物质,根据反复的评估和实验分析,从苯丙树脂、纯丙树脂、醋丙树脂、硅丙树脂中选出硅丙树脂,最为合适骨料为天然彩石砂和天然的云母片,天然的彩石砂以80目雪花白和100目各种彩砂为主,天然云母片以实际要求的大小和颜色来搭配规格有20目、40目、60目、100目、200目,颜色主要有白云母、金云母、浅绿云母、黑云母、灰云母。助剂分为消泡剂、防霉剂、成膜剂、增稠剂、润湿剂、和自来水或去离子水等四大部分。它的具体重量组分配比为,水30%、助剂5%、硅丙树脂30%、彩石砂30%、天然云母片5%及按需添加的纤维素。
反复实验证明:当采用本发明的彩石砂为60-120目、天然云母片为20目-200目范围时,其具有较为突出的性能指标及效果。
本发明的主要设备有:分散机、分散缸、搅拌机、半成品贮槽、搅拌缸和计量、检测相关用具。其具体工艺流程包括以下步骤:在搅拌容器中,将水、纤维素、助剂混合经搅拌机搅拌10分钟,再加入硅丙树脂混合进行搅拌15分钟,再将彩石砂加入其中混合搅拌10分钟,再投入天然云母片,球磨分散后,混合搅拌约15分钟,然后检验,包装即可出品。依据JG/T24-2000合成树脂乳液砂壁状建筑涂料标准,经相关计量检测用具检测如下;
序号 | 检验项目 | 检验指标 | 检验值 | 单项判定 | |
1 | 容器中状态 | 搅拌后无结块呈均匀状态 | 搅拌后无结块呈均匀状态 | 符合 | |
2 | 施工性 | 涂刷无困难 | 涂刷无困难 | 符合 | |
3 | 低温稳定性 | 三次循环不变质 | 三次循环不变质 | 符合 | |
4 | 干燥时间 | 表干≤4 | 表干≤4 | 符合 | |
5 | 初期干燥抗裂性 | 无裂纹 | 无裂纹 | 符合 | |
6 | 耐水性 | 96h无异常 | 96h无异常 | 符合 | |
7 | 耐碱性 | 96h无异常 | 96h无异常 | 符合 | |
8 | 涂层耐温变化 | 10次涂层无粉化、开裂、剥落、起鼓,允许颜色轻微变化 | 符合 | ||
9 | 耐冲击性 | 涂层无裂纹、剥落及明显变形 | 符合 | ||
10 | 耐粘污性 | 5次循环试验后≤2级 | 符合 | ||
11 | 耐人工老化性 | 500h涂层无开裂、剥落、起鼓、粉化0级,变色≤1级 | 符合 | ||
12 | 粘结强度MPa | 标准状态 | ≥0.70 | 符合 | |
浸水后 | ≥0.50 |
总之,本发明的仿大理石天然云母漆,是专门针对高层高档外墙饰面和外墙保温层的特殊要求而研发的仿大理石涂料,能充分展现出花岗岩的纹理和质感的同时亦能保证长期雨淋不泛白、紫外线照射不泛黄、附着力强不起泡、不脱落、不剥落、不龟裂、容易清洗等优良特点,加入天然云母片更加能体现出花岗岩的自然片状,提高涂料柔韧性以及云母片自身独特的折射性,提高涂料的档次,环保节能,且价格适中,有利于市场推广。
Claims (5)
1.一种仿大理石效果天然云母漆,其特征在于,它的重量组分比为,水30-35%、助剂5-10%、改性硅溶胶30-35%、彩石砂30-35%、天然云母片5-10%,各组份之和等于100%。
2.根据权利要求1所述的仿大理石效果天然云母漆,其特征在于,所述配方中还按需添加有纤维素。
3.根据权利要求1所述的仿大理石效果天然云母漆,其特征在于,所述改性硅溶胶为硅丙树脂。
4.根据权利要求1或2所述的仿大理石效果天然云母漆,其特征在于,所述彩石砂为60-120目、天然云母片为20目-200目。
5.一种权利要求1至5所述仿大理石效果天然云母漆的制备方法,其特征在于,其制备步骤为,首先,在搅拌容器中,将水、纤维素、助剂按配比混合搅拌10-15分钟;其次,再加入改性硅溶胶混合进行搅拌10-15分钟,再将彩石砂加入其中混合搅拌10-15分钟;最后再投入天然云母片,球磨分散后,混合搅拌约10-15分钟,然后检验,包装即可出品。