CN101250361B - 一种抗开裂环保涂料及其制备方法 - Google Patents
一种抗开裂环保涂料及其制备方法 Download PDFInfo
- Publication number
- CN101250361B CN101250361B CN2008100267623A CN200810026762A CN101250361B CN 101250361 B CN101250361 B CN 101250361B CN 2008100267623 A CN2008100267623 A CN 2008100267623A CN 200810026762 A CN200810026762 A CN 200810026762A CN 101250361 B CN101250361 B CN 101250361B
- Authority
- CN
- China
- Prior art keywords
- cracking
- minute
- coating
- water
- stone sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种抗开裂环保涂料,其特征在于,它由如下组分配比构成,抗开裂环保涂料,其特征在于,它由如下组分重量百分比配比构成,水30-35%、助剂5-10%、粉料20-30%、弹性纯丙乳液和硅溶剂20-30%、强不裂纤维5-10%、彩石砂20-30%。本发明还公开了抗开裂环保涂料的制备方法。上述抗开裂环保涂料具有抗开裂效果好、成本低等优点。
Description
技术领域
本发明涉及一种抗开裂的环保型涂料及其制备方法。
背景技术
随着我国建筑业的迅猛发展,建筑涂料在内外墙体装饰中成为主要的装饰材料之一,它以优异的装饰性、耐久性、施工简便性及好的性能价格比越来越受市场的欢迎,在全国大中城市,特别是京、津、珠江三角洲、长江三角洲等经济发达地区,使用建筑涂料进行内外墙装饰,特别是外墙装饰工程逐年增加,但是随着工程量的增多,出现了一些较为普遍的工程质量问题,其中最为严重的是涂装经过一段时间(大多一年)后,墙体出现龟裂等现象,这不但给建筑物带来损失造成渗水等弊病,还使涂料丧失了装饰性,严重影响了涂料的声誉,这个问题如果得不到很好的解决,会阻碍建筑涂料的迅速发展,建筑墙面局部开裂的原因较为复杂,有建筑结构内部存在的不均匀的动态应力引发的结构裂缝,有外部温湿度变化等因素诱发的不均匀的膨胀或收缩,从而产生局部应力引发的细微裂缝等,也有为建筑墙体的基材在施工中留下孔隙、裂缝,加上天气、环境等因素,涂层容易出现膨胀收缩,尤其是外墙涂料漆膜有不同程度的大小裂纹,未能有效保护好建筑物,产生渗水、泛碱等不良现象,影响美观。前者不是装饰材料所能解决的,普通薄质材料层一半厚度不超过0.1mm,抗开裂应力的能力较低,当基材裂缝扩张或产生新的开裂时涂料层可能在对应位置开裂,丧失应有的保护和装饰功能。虽然目前也有采用抗裂剂制备的抗开裂涂料,如中国专利号为ZL 03 144229.3,申请日为2003.9.2,发明名称为外墙保温抗裂防水涂料用抗裂剂及其制备方法,抗裂剂重量组成:水10一30,纯丙烯酸乳液20一50,OP一10 0.1一0.4,乙二醇0.5一5,消泡剂0.05一0.2,防腐剂0.01一0.2,甲基纤维素0.01一1.5,40一80目玻璃微珠10-40,80一120目玻璃微珠10一40,0.5一2mm玻璃纤维0.1一1,2一4mm玻璃纤维0.2一1.5,0.5一5mm木纤维0.1一1.5。其制备方法包括:(1)甲基纤维素溶液的配制。(2)抗裂剂的配制。在容器中加入水和纯丙烯酸弹性乳液,然后在搅拌条件下徐徐加入其余组分制得抗裂剂。此专利主要采用不同纤维材料与纯丙烯酸弹性乳液等制成抗裂剂,制备方法比较简单,但抗裂效果不明显,生产成本高。
而涂料的制备工艺对涂料的性能的稳定质量也具有重要影响,因此选取一个合适的工艺也是十分必要的。
发明内容
本发明的目的是克服传统的技术之不足,提供一种生产成本低,能有效解决受温差影响而开裂问题、能按需配制成多种款式多功能的抗开裂效果好的环保涂料。
本发明的另一目的还在于提供一种生产效率高、产品质量稳定的抗开裂涂料的制备方法。
本抗开裂环保涂料,其特征在于,它由如下组分配比(重量百分比)构成,水30-35%、助剂5-10%、粉料20-30%、弹性纯丙乳液和硅溶剂20-30%、强不裂纤维5-10%、彩石砂20-30%。
助剂包括消泡剂、防霉剂、成膜剂、增稠剂。
强不裂纤维可选用木质纤维素等;
上述配方中还可加入有甲基纤维素作为保水剂。
弹性丙稀酸、有机硅改性丙稀酸树酯、聚氨酯树酯等为成膜物质加入溶剂、颜填料及各种助剂,经溶解分散、研磨而成,.它的特点是装饰效果好,使用寿命长。
本发明的抗开裂环保艺术涂料的制备方法如下:
a、首先将水、纤维素、助剂慢速分散5-15分钟;然后再高速分散10-20分钟;
b、将纯丙乳液与强不裂纤维低速搅拌8-15分钟;再添加到a步骤的混合液中中速搅拌8-15分钟;
c、按需加入各类彩石,低速搅拌10-20分钟,经检验构成成品。
本发明采用上述技术的解决方案所能达到的有益效果是:
一、本抗裂涂料是在弹性改性乳液中加入纤维,从而开发出的抗开裂涂料,它发挥了纤维不裂的特性,利用不同纤维材料形成的网状结构,可以起到加强筋的作用,有利于防止开裂;另外弹性乳液成膜后具有一定的弹性,可防止涂层产生裂纹;
二、本涂料配方组分简单,方便实施、制造成本低,可进行绿色生产,适应环保要求。
附图说明
图1为本发明的制备工艺流程图。
具体实施方式
本抗开裂环保涂料,它由如下组分重量百分比配比构成,水30%、助剂5%、粉料20%、纯丙弹性乳液20%、强不裂纤维5%、彩石20%。其具体工艺流程包括以下步骤,在搅拌容器中,将水、纤维素、助剂混合慢速分散10分钟,直至溶解成微透明溶液,再加入粉料混合进行高速分散15分钟,纯丙烯酸弹性乳液、纤维低速混合搅拌10分钟备用,再将上述混合液加入中速混合搅拌10分钟,再投入各类彩石,低速混合搅拌约15分钟,然后检验,即可包装入库。
本发明的高弹性抗开裂涂料的特殊要求,成膜物质需采用具有有一定高弹性能,高耐候性以及高防水性,本发明选用纯丙高弹乳液+硅溶胶,两者合一,能达到这一要求,基料选用大小粒径不同的粉料、天然彩石砂和强不裂纤维;天然彩砂以100目、60目、40目雪花白为主。助剂分类:消泡剂、防霉剂、成膜剂、增稠剂、润湿剂和自来水或去离子水等四大部分。
在施工过程中,本发明首先解决建筑墙面基层细微裂纹或裂缝(不包括结构性裂纹)专门配合弹性抗裂腻子,以满足这特殊要求,除提高抹灰砂浆柔性以减少基材开裂外,可在涂料层下批刮厚度为1-2mm的弹性抗开裂腻子,吸收开裂应力、缓冲裂纹扩展,同时填补墙体裂纹和缺陷,为涂料提供光滑、平整、稳定的涂饰表面提高装饰效果和耐久性。
解决基层裂纹问题的同时,发明人对涂层亦做出深入的了解,以及经过多次的试验证明本发明的艺术型厚浆外墙涂料为最好的抗开裂涂料,本发明抗开裂质感艺术涂料在原有高弹性的性能下加入强不裂纤维,作为一种新型的装潢材料,适合于室内外装潢,它以其变化无穷的立体花型纹理、多选择的合理性搭配展现独特的空间视角、丰富而生动令人耳目一新这种新型的厚浆弹性艺术涂料把墙面的平滑型时代带进了天然环保型凹凸涂料全新时代,相比普通涂料和瓷砖,演绎无尽的凹凸美感,光彩奇目,使墙面真正焕发光彩,并且永开裂不起泡不剥落及耐水耐候的特点,既适合大面积涂装,也适合于其它墙体材料配合点缀使用。
本发明所采用的设备及仪器
主要设备:分散机、分散缸、搅拌机、半成品贮槽、搅拌缸和计量检测相关用具。
本发明的施工工程流程:
基面处理→墙面找平→打磨养护清理→封闭底漆→做分隔缝→喷涂抗开裂质感艺术涂料→打磨→罩清面漆。
本发明的产品技术指标及依据
依据:JG/T24-2000合成树脂乳液砂壁状建筑涂料
Claims (2)
1.一种抗开裂环保涂料,其特征在于,它由如下组分重量百分比配比构成,水30-35%、助剂5-10%、粉料20-30%、弹性纯丙乳液和硅溶剂20-30%、强不裂纤维5-10%、天然彩石砂20-30%,上述各组份之和为100%;
所述助剂包括消泡剂、防霉剂、成膜剂、增稠剂;强不裂纤维选用木质纤维素;
上述配方中还加入有甲基纤维素作为保水剂;
上述配方中粉料及天然彩石砂和强不裂纤维选用大小粒径不同进行混合,其中天然彩石砂以100目、60目、40目雪花白为主。
2.一种制备权利要求1所述的抗开裂环保涂料的方法,其特征在于,其工艺步骤如下:
a、首先将水、甲基纤维素、助剂慢速分散5-15分钟;然后再高速分散10-20分钟;
b、将纯丙乳液与木质纤维素低速搅拌8-15分钟;再添加到a步骤的混合液中中速搅拌8-15分钟;
c、按需加入各类天然彩石砂,低速搅拌10-20分钟,经检验构成成品。